Ceramic Materials Commons^™

Influence Of Chemical Reactions In Magnesia-Graphite Refractories: I, Effects On Texture And High-Temperature Mechanical Properties, Carmen Baudín, Carlos Alvarez, Robert E. Moore

Materials Science and Engineering Faculty Research & Creative Works

Four formulations of magnesia-graphite-aluminum metal (antioxidant) bricks were prepared from the same raw materials, using the standard commercial practices. Chemical analysis and determination of room-temperature modulus of rupture and Young's modulus, as well as a complete microstructural characterization of the as-received materials, were performed. For high-temperature modulus-of-rupture and Young's modulus data, test samples of the four brick compositions were heated to 1000°, 1200°, and 1450 °C in flowing argon (< 1000 ppm oxygen at 1000 °C) and then loaded mechanically in flexure. Modulus-of-elasticity values ranged from 3.7 to 16.2 GPa and reflected strong effects of aluminum-metal concentration and treatment temperature. Young's modulus evolution with temperature was determined by the evolution of the micro-structure in the bulk of the specimens. Modulus-of-rupture values ranged from 6 to 21 MPa, and their evolution with temperature was determined by the evolution of the micro-structure in the bulk of the specimens at the lower testing temperatures (T≤1200 °C) and by phase assemblages in the surface regions of the specimens - essentially by the presence of the dense MgO zone - at 1450 °C.

Influence Of Chemical Reactions In Magnesia-Graphite Refractories: Ii, Effects Of Aluminum And Graphite Contents In Generic Products, Carmen Baudín, Carlos Alvarez, Robert E. Moore

Materials Science and Engineering Faculty Research & Creative Works

A group of magnesia-graphite and magnesia-graphite-aluminum materials, the compositions of which represent a wide range of graphite contents (approximately 10-16.4 wt.%), aluminum contents (0-5.2 wt.%), and MgO and graphite qualities, were fabricated, using standard commercial practices. Chemical analysis and determination of room-temperature modulus of rupture (MOR) and Young's modulus, as well as a complete microstructural characterization of the as-received materials, were performed. Mechanical characterization at high temperature (1000°, 1200°, and 1450 °C) was done in terms of Young's modulus and MOR in an argon atmosphere (°C). Modulus-of-elasticity values ranged from 4 to 16 GPa, and their evolution with temperature was …

Neuron Scattering Studies Of The Magnetic Fluctuations In Yba2cu3o7−Δ, Herbert A. Mook, Pengcheng Dai, Rodney Dale Hunt, Fatih Dogan

Materials Science and Engineering Faculty Research & Creative Works

Neutron scattering measurements were made on the spin fluctuations in YBa₂Cu₃O_7−δ for different oxygen doping levels. Incommensurability is clearly observed for oxygen concentrations of 6.6 and 6.7 and is suggested for the 6.93. Measurements of the resonance for the O6.6 concentration show that it exists in a broadened and less intense form at temperatures much higher than T_c.

Iron Phosphate Compositions For Containment Of Hazardous Metal Waste, D. E. Day

Materials Science and Engineering Faculty Research & Creative Works

An improved iron phosphate waste form for the vitrification, containment and long-term disposition of hazardous metal waste such as radioactive nuclear waste is provided. The waste form comprises a rigid iron phosphate matrix resulting from the cooling of a melt formed by heating a batch mixture comprising the metal waste and a matrix-forming component. The waste form comprises from about 30 to about 70 weight percent P205 and from about 25 to about 50 weight percent iron oxide and has metals present in the metal waste chemically dissolved therein. The concentration of iron oxide in the waste form along with …

Incommensurate Magnetic Fluctuations In Yba2⁢Cu3⁢O6.6, Pengcheng Dai, Herbert A. Mook, Fatih Dogan

Materials Science and Engineering Faculty Research & Creative Works

We use inelastic neutron scattering to demonstrate that the low-frequency magnetic fluctuations in YBa₂Cu₃O_6.6 (T_c= 62.7 K) change from commensurate to incommensurate on cooling with the incommensurability first appearing at temperatures above T_c. For the energies studied, the susceptibility at incommensurate positions increases on cooling below T_c, accompanied by a suppression of the spin fluctuations at the commensurate points. These results suggest that incommensurate spin fluctuations may be a common feature for all cuprate superconductors.

Incommensurate Magnetic Fluctuations In Yba2cu3o6.6, Pengcheng Dai, Hernert A. Mook, Fatih Dogan

Materials Science and Engineering Faculty Research & Creative Works

We use inelastic neutron scattering to demonstrate that the low-frequency magnetic fluctuations in YBa₂Cu ₃O_6.6 (T_c=62.7 K) change from commensurate to incommensurate on cooling with the incommensurability first appearing at temperatures above T_c. For the energies studied, the susceptibility at incommensurate positions increases on cooling below T_c, accompanied by a suppression of the spin fluctuations at the commensurate points. These results suggest that incommensurate spin fluctuations may be a common feature for all cuprate superconductors.

Dai Et Al. Reply:, Pengcheng Dai, Mohana Yethiraj, Herbert A. Mook, Terrence B. Lindemer, Fatih Dogan

Materials Science and Engineering Faculty Research & Creative Works

No abstract provided.

Evolution Of In Situ Refractories In The 20th Century, William E. Lee, Robert E. Moore

Materials Science and Engineering Faculty Research & Creative Works

A common theme over the past 100 years in refractories science and technology has been to generate a protective refractories layer in a high-temperature container, often by reaction of the refractory materials with the contents (glass, slag, or atmosphere). The history of refractories during the 20th century is used in this review to illustrate how techniques - such as slag splashing, in situ spinel generation in castables, magnesia dense layer formation in magnesia-carbon brick in steelmaking, clinker adhesion in cement kilns, and viscous boundary layer generation in glass tanks - have evolved to their present status.

Absolute Measurements Of The High-Frequency Magnetic Dynamics In Hihg-Tc Superconductors, Stephen M. Hayden, Gabriel Aeppli, Pengcheng Dai, Herbert A. Mook, Toby G. Perring, S-W Cheong, Zachary Fisk, Fatih Dogan, Thomas E. Mason

Materials Science and Engineering Faculty Research & Creative Works

We review recent measurements of the high-frequency dynamic magnetic susceptibility in the high-T~ superconducting systems La_2-xSr_xCuO₄ and YBa₂Cu₃O_6+x. Experiments were performed using the chopper spectrometers HET and MARI at the ISIS spallation source. We have placed our measurements on an absolute intensity scale; this allows systematic trends to be seen and comparisons with theory to be made. We find that the insulating S = ½ antiferromagnetic parent compounds show a dramatic renormalization of the spin wave intensity. The effect of doping on the response is to cause broadenings in …

Pseudogap And Incommensurate Magnetic Fluctuations In Yba2cu3o6.6, Pengcheng Dai, Herbert A. Mook, Fatih Dogan

Materials Science and Engineering Faculty Research & Creative Works

Unpolarized inelastic neutron scattering is used to study the temperature and wave vector dependence of the dynamical magnetic susceptibility, X"(q, w), of a well-characterized single-crystal YBa2Cu3O6.6 (Tc = 62.7 K). We find that a pseudo gap opens in the spin-fluctuation spectrum at temperatures well above Tc. We speculate that the appearance of the low-frequency incommensurate fluctuations is associated with the opening of the pseudo gap. To within the error of the measurements, a gap in the spin-fluctuation spectrum is found in the superconducting state.

Pseudogap And Incommensurate Magnetic Fluctuations In Yba2cu3o6.6, Pengcheng Dai, Herbert A. Mook, Fatih Dogan

Materials Science and Engineering Faculty Research & Creative Works

Unpolarized inelastic neutron scattering is used to study the temperature and wave vector dependence of the dynamical magnetic susceptibility X"(q,w) of a well-characterized single-crystal YBa₂Cu₃O_6.6 (Tc = 62.7 K). We find that a pseudogap opens in the spin-fluctuation spectrum at temperatures well above T_c. We speculate that the appearance of the low-frequency incommensurate fluctuations is associated with the opening of the pseudogap. To within the error of the measurements, a gap in the spin-fluctuation spectrum is found in the superconducting state.

Optically Transparent Composite Material And Process For Preparing Same, D. E. Day, James O. Stoffer, John M. Barr

Materials Science and Engineering Faculty Research & Creative Works

Glass ribbon-reinforced transparent polymer composites which provide excellent optical transparency and a low distortion level over a wide temperature range while exhibiting superior mechanical properties as compared to non- reinforced polymer counterparts, and equivalent properties as compared to glass fiber-reinforced counterparts.

Spin Dynamics Of Er3+ In Erba2cu3o7−Δ, S. Skanthkumar, J. W. Lynn, Fatih Dogan

Materials Science and Engineering Faculty Research & Creative Works

Neutron scattering techniques are used to study the magnetic excitations of the Er ions in superconducting ErBa₂Cu₃O₇, a system where the Er ions order antiferromagnetically at TN=0.62 K and the sublattice magnetization obeys the relation for a 2D S=1/2 Ising model. Our data, which were taken on a cold neutron triple axis spectrometer using a horizontally focusing analyzer, reveal that there is a large gap of about 0.20 meV in the excitation spectrum, about four times the thermal energy kTN, as expected for an Ising system. However, we also observe dispersion of the spin …

Spin Dynamics Of Er3+ In Erba2cu3o7−Δ, Suntharalingam Skanthakumar, Jeffrey W. Lynn, Fatih Dogan

Materials Science and Engineering Faculty Research & Creative Works

Neutron scattering techniques are used to study the magnetic excitations of the Er ions in superconducting ErBa₂Cu₃O₇, a system where the Er ions order antiferromagnetically at T_N=0.62 K and the sublattice magnetization obeys the relation for a 2D S=1/2 Ising model. Our data, which were taken on a cold neutron triple axis spectrometer using a horizontally focusing analyzer, reveal that there is a large gap of about 0.20 meV in the excitation spectrum, about four times the thermal energy kT_N, as expected for an Ising system. However, we also observe …

Immobilization Of Radioactive Materials In Iron Phosphate Glass, Melissa G. Mesko

Doctoral Dissertations

"The current study investigates the feasibility of using iron phosphate glass for the immobilization of radioactive wastes considered incompatible with borosilicate glass. Wastes may be incompatible with borosilicate glass due to high phosphorus content (Hanford tank sludges), the presence of halides (CsCl and SrF₂ capsules), or large amounts of uranium (SNF).

Between 20 and 60 wt% Hanford tank sludge was vitrified with an iron phosphate glass at ≤ 1200°C in 1 hour. The chemical durability of iron phosphate glassy wasteforms was as good as, or better than a reference borosilicate glass (10^-9 g/cm²/min) in distilled water …

Evaluation Of Unified Interaction Parameter Model Parameters For Calculating Activities Of Ferromanganese Alloys: Mn-Fe-C, Mn-Fe-Si, Mn-C-Si, And Mn-Fe-C-Si Systems, L. I. Hongjie, Arthur E. Morris

Materials Science and Engineering Faculty Research & Creative Works

Interaction parameters for Mn-based alloys were evaluated using both carbon solubility and activity data for species in binary and ternary manganese alloys. The parameters at 1400 °C are the following εcc = -4.5; εccc = 58.8; εFeCC = 1.5; εFeCC = 2.5; In γC0 = -1.15 . εsisi = 15.5; εsisisi = 2.69; εFeSi = 2.5; εcsi = 12.4; εccsi = 27.5; In γSi0 = -7.46 The unified interaction parameter model (UIPM) was used to calculate the activity coefficients of species and the solubility of carbon in ferromanganese alloys (up to quaternary Mn-Fe-C-Si). The results were in good agreement with …

Chemical Durability Of Lead-Oxide-Based, Thick-Film Binder Glasses, Douglas M. Mattox, Joshua H. Robinson

Materials Science and Engineering Faculty Research & Creative Works

Lead-oxide-bearing glasses are incompatible with aluminum nitride metallization's, and federal legislation is recommending their replacement in thick-film electronics and labeling. To evaluate alternatives, the benchmark chemical durability's of the lead borosilicate and lead aluminate thick-film binder glasses have been determined. Aluminum oxide (Al2O3) benefits water durability moderately, acid durability substantially, and basic durability indistinguishably. The rate of attack in water is approximately two orders of magnitude greater than for soda-lime glass. The thermal contractions of the glasses are compatible. An apparent, spontaneous phase separation in the Al2O3-free glass is suppressed by Al2O3 that is included as a batch component.

Magnetic Dynamics In Underdoped Yba2⁢Cu3⁢O7−X: Direct Observation Of A Superconducting Gap, Pengcheng Dai, Mohana Yethiraj, Herbert A. Mook, Terrence B. Lindemer, Fatih Dogan

Materials Science and Engineering Faculty Research & Creative Works

Polarized and unpolarized triple-axis neutron measurements were performed on an underdoped crystal of YBa₂⁢Cu_3⁢O_7−x (x = 0.4 ±0.02, T_c = 62.7⁢K). Our results indicate, contrary to earlier evidence, that the spin excitations in the superconducting state are essentially the same as those in the fully doped material except that the unusual 41 meV resonance is observed at 34.8 meV. The normal state spin excitations are characterized by a weakly energy-dependent continuum whose temperature dependence shows the clear signature of a superconducting gap at T_c. The enhancement at the resonance is accompanied by …

Low Temperature Hydrothermal Synthesis Of Nanophase Batio3 And Bafe12019 Powders, Fatih Dogan, Shawn O'Rourke, Mao-Xu Qian, Mehmet Sarikaya

Materials Science and Engineering Faculty Research & Creative Works

Nanocrystalline powders with an average particle size of 50 nm have been synthesized in two materials systems under hydrothermal conditions below 100°C. Processing variables, such as temperature, concentration and molar ratio of reactants and reaction time were optimized to obtain particles of reduced size and stoichiometric compositions. Hydrothermal reaction takes place between Ba (OH)₂ solution and titanium/iron precursors in sealed polyethylene bottles in the BaTiO₃ and BaFe12019 systems, respectively. While crystalline BaTiO₃ forms relatively fast within a few hours, formation of fully crystalline and stoichiometric BaFe12019 require considerably longer reaction times up to several weeks and strongly …

Magnetic Dynamics In Underdoped Yba2cu3o72x: Direct Observation Of A Superconducting Gap, Pengcheng Dai, Mehmet Yethiraj, Herbert A. Mook, T. B. Lindemer, Fatih Dogan

Materials Science and Engineering Faculty Research & Creative Works

Polarized and unpolarized triple-axis neutron measurements were performed on an underdoped crystal of YBa₂Cu₃O_7-x (x 0.4 6 0.02, T_c 62.7 K). Our results indicate, contrary to earlier evidence, that the spin excitations in the superconducting state are essentially the same as those in the fully doped material except that the unusual 41 meV resonance is observed at 34.8 meV. The normal state spin excitations are characterized by a weakly energy-dependent continuum whose temperature dependence shows the clear signature of a superconducting gap at T_c. The enhancement at the resonance is accompanied by …

Recent Developments In Extrusion Freeform Fabrication (Eff) Utilizing Non-Aqueous Gel Casting Formulations, Greg Hilmas, John L. Lombardi, Robert A. Hoffman, Kevin Stuffle

Materials Science and Engineering Faculty Research & Creative Works

Extrusion Freeform Fabrication (EFF) was shown to be an extremely versatile method for fabricating Functionally Graded Materials (FGMs) The approach is inexpensive and potentially feasible for grading between any thermodynamically compatible ceramic-metal, ceramic-ceramic, or metal-metal material combination. Several material systems were investigated in this study including alumina-304 stainless steel, zirconia-304 stainless steel, alumina-Inconel 625, zirconiaInconel625, alumina-nickel aluminide, zirconia-nickel aluminide, titanium carbide-InconeI625, titanium diboride-nickel aluminide, and tungsten carbide-nickel aluminide. A controlled gradient was demonstrated between the end members for all of the above compositions. The FGMs were hot pressed to achieve near theoretical densities, providing flexural strengths as high as 1000 …

Incommensurate One-Dimensional Fluctuations In Yba2⁢Cu3⁢O6.93, Herbert A. Mook, Pengcheng Dai, Kamel Salama, Dominic Lee, Fatih Dogan, Gabriel Aeppli, Andrew T. Boothroyd, Mark E. Mostoller

Materials Science and Engineering Faculty Research & Creative Works

A novel neutron scattering technique has been utilized to discover one-dimensional fluctuations with a very sharply defined modulation period of 16.65⁢Å along the b⁡(a) direction in YBa₂⁢Cu_3⁢O_6.93. The fluctuations are found to be absent in the reduced oxygen compound YBa_2⁢Cu_3⁢O_6.15. The wave vector of the fluctuations is consistent with accepted values of 2⁢k_F for the Cu-O chains.

Incommensurate One-Dimensional Fluctuations In Yba2cu3o6.93, Herbert A. Mook, Pengcheng Dai, K. Salama, D. Lee, Fatih Dogan, G. Aeppli, A. T. Boothroyd, M. E. Mostoller

Materials Science and Engineering Faculty Research & Creative Works

A novel neutron scattering technique has been utilized to discover one-dimensional fluctuations with a very sharply defined modulation period of 16.65 Å along the ba direction in YBa₂Cu₃O_6.93. The fluctuations are found to be absent in the reduced oxygen compound YBa₂Cu₃O_6.15. The wave vector of the fluctuations is consistent with accepted values of 2kF for the Cu-O chains.

Q Dependence Of Self-Energy Effects Of The Plane Oxygen Vibration In Yba2cu3o7, D. Reznik, Bernard Keimer, Fatih Dogan, Ilhan A. Aksay

Materials Science and Engineering Faculty Research & Creative Works

We have measured the temperature dependence of the peak position and linewidth of the 42.5 meV phonon branch in a twinned single crystal of YBa₂Cu₃O₇ as a function of wave vector q. In the (100)/(010) direction in the Brillouin zone, considerable softening and broadening occur below the superconducting transition temperature T_c at some values of q. We observe an order of magnitude smaller softening and no linewidth broadening for q in the (110) / (1⁢1⁢0^-) direction. Possible implications of these findings for the symmetry of the superconducting order parameter are …

Phonon And Magnetic Neutron Scattering At 41 Mev In Yba2cu3o7, Hung Fai Fong, Bernard Keimer, Pw Anderson, D. Reznik, Fatih Dogan, Ilhan A. Aksay

Materials Science and Engineering Faculty Research & Creative Works

We report inelastic neutron scattering measurements at excitation energies ħ⁢w∼41 meV in YBa₂Cu₃O₇. We separate magnetic and phonon contributions to the scattering cross section by a detailed analysis of the momentum dependence of the scattered intensity. The previously reported broad peak around q = (π/a,π/a) in the normal state can be entirely accounted for by a phonon which primarily involves vibrations of the in-plane oxygen. Magnetic scattering centered around 41 meV and q = (π/a,π/a) appears in the superconducting state only. Theoretical implications of …

Radiolabeled Protein Composition And Method For Radiation Synovectomy, D. E. Day, Gary J. Ehrhardt, Kurt R. Zinn

Materials Science and Engineering Faculty Research & Creative Works

A radiolabeled protein composition adapted for radiation therapy which comprises a radioisotope and a protein material containing about 6 or more percent amino acids which have a sulfhydryl-containing side chain. A method for carrying out radiation synovectomy of arthritic joints. Rhenium radiolabeled protein micro- spheres are administered which contain cysteine and other amino acids. A method for radiolabeling a protein composition whereby the composition is treated with a reducing agent capable of reducing disulfides to sulfhydryls prior to radiolabeling.

Iron Phosphate Glasses As A Potential Nuclear Waste Disposal Medium, Melissa G. Mesko

Masters Theses

”Phosphate glasses containing large amounts of Fe₂O₃ (up to 43wt%) were studied to determine their potential suitability as nuclear waste disposal glasses for high level radioactive wastes containing large concentrations of iron oxide, phosphate, and fluoride compounds. Glass formation and chemical durability was the prime focus of this study, while properties such as density, thermal expansion, dilatometric softening temperature, and devitrification temperature were examined as well. It was found that large amounts of simulated nuclear waste material (up to 44.4wt% Cs₂O or 37.5wt% SrO) could be incorporated into the base iron phosphate glass while retaining …

Vortex Lattice Symmetry And Electronic Structure In Yba2cu3o7, Bernhard Keimer, Wan Y. Shih, Ross W. Erwin, Jeffrey W. Lynn, Fatih Dogan, Ilhan A. Aksay

Materials Science and Engineering Faculty Research & Creative Works

We report a small angle neutron scattering study of the vortex lattice in YBa₂Cu₃O₇ in magnetic fields of 0.5≤ H ≤5 T applied along and close to the c axis. Over the entire field range, the vortices form an oblique lattice with two nearly equal lattice constants and an angle of 73° between primitive vectors. Numerical calculations suggest that variations of the superconducting order parameter near the vortex core are important in stabilizing this structure. An analysis that accounts for the fourfold symmetry of the vortex core qualitatively explains both the symmetry and the orientation …

Investigation Into The Behavior Of Geometrically Nonlinear Composite Arches, John C. Bailey

Theses and Dissertations

This research modifies the existing finite element formulation of a potential energy based large deformation and moderate rotation theory. Hermitian shape functions replace the existing linear bending angle interpolations. Negligible differences between the two formulations indicate the underlying kinematics limit the accuracy, not the finite element interpolations. Using the new program, numerous nonlinear arch geometries are modeled to investigate the effects of arc length and thickness variations. Local and global snapping phenomena are captured as well as through the thickness shear driven nonlinearities.

Fatigue Behavior Of A Cross-Ply Ceramic Matrix Composite At Elevated Temperature Under Tension-Tension Loading, Craig D. Steiner

Theses and Dissertations

This study investigated the fatigue behavior and damage mechanisms of a [0-90]_4s SiC-MAS ceramic matrix composite under tension-tension loading at two elevated temperatures and two frequencies. Stress and strain hystereses, maximum and minimum strain, and modulus of elasticity were evaluated to characterize the material behavior. Microscopy and fractography were used to evaluate damage progression and mechanisms. Fatigue life was independent of frequency at both temperatures.