Open Access. Powered by Scholars. Published by Universities.®
- Discipline
- Keyword
-
- Bibliometric analysis (2)
- 3D printing (1)
- Al 2O 3 (1)
- Aluminum oxide (1)
- Ceramic on‐demand extrusion (1)
-
- Dielectric constant (1)
- Energy density (1)
- Energy storage (1)
- Extrusion freeforming (1)
- Extrusion‐based additive manufacturing (1)
- Fused deposition (1)
- Green Route (1)
- Mechanical properties (1)
- Metal Matrix Composite (1)
- Polymer Composite (1)
- Radiation drying (1)
- Rice Husk (1)
- Robocasting (1)
- Silica (1)
Articles 1 - 7 of 7
Full-Text Articles in Ceramic Materials
Research Trend Of Metal Matrix Composites Reinforced With Silica Extracted By Green Route: A Bibliometric Analysis, Rinku Datkhile, Meena Laad, Babaji Ghule
Research Trend Of Metal Matrix Composites Reinforced With Silica Extracted By Green Route: A Bibliometric Analysis, Rinku Datkhile, Meena Laad, Babaji Ghule
Library Philosophy and Practice (e-journal)
Metal Matrix Composites have acquired an important place in the engineering applications due to their distinctive characteristics such as high specific strength, lower specific gravity, improved material stiffness, better durability, enhanced creep and fatigue strength etc. Worldwide scientists are working on the improvement of mechanical properties of composite materials. The present work attempts to summarise all the research carried out on metal matrix composites reinforced with silica extracted by green route and provides up-to-date research material for researchers who are interested in the field of composites with metal matrices. Scopus databases and software such as Gephi Vos Viewer and Table2Net …
A Bibliometric Survey On Polymer Composites In Energy Storage Applications, Babaji Ghule, Meena Laad
A Bibliometric Survey On Polymer Composites In Energy Storage Applications, Babaji Ghule, Meena Laad
Library Philosophy and Practice (e-journal)
Ceramic polymer composites have gained a significant place in energy storage applications for electrical capacitors due to their distinguished properties. There is a huge demand of capacitors with high energy density, high dielectric strength, negligibly low dielectric loss, light weight, chemically less reactive in energy storage applications. These requirements can be fulfilled by ceramic polymer composites only which exhibit all the above-mentioned characteristics. Considering the huge demand of such capacitors, it has attracted the attention of researchers around the world. The present work attempts to summarise all the research conducted on Polymer Composites for energy storage applications and provides an …
Fabricating Zirconia Parts With Organic Support Material By The Ceramic On-Demand Extrusion Process, Wenbin Li, Amir Ghazanfari, Devin Mcmillen, Andrew Scherff, Ming Leu, Gregory Hilmas
Fabricating Zirconia Parts With Organic Support Material By The Ceramic On-Demand Extrusion Process, Wenbin Li, Amir Ghazanfari, Devin Mcmillen, Andrew Scherff, Ming Leu, Gregory Hilmas
Faculty Publications, Mechanical Engineering
Ceramic On-Demand Extrusion (CODE) is an extrusion-based additive manufacturing process recently developed for fabricating dense, functional ceramic components. This paper presents a further development of this process and focuses on fabricating 3 mol% yttria-stabilized zirconia (3YSZ) components that cannot be fabricated without using support structures. The 3YSZ paste is deposited through the main nozzle, and a polycaprolactone (PCL) pellet feedstock is melted and deposited through an auxiliary nozzle to build support structures. After a green part is printed and dried, the support structures are removed by heating the part to ~70°C to melt the PCL. The part is then sintered …
Mechanical Characterization Of Parts Produced By Ceramic On‐Demand Extrusion Process, Amir Ghazanfari, Wenbin Li, Ming Leu, Gregory Hilmas
Mechanical Characterization Of Parts Produced By Ceramic On‐Demand Extrusion Process, Amir Ghazanfari, Wenbin Li, Ming Leu, Gregory Hilmas
Faculty Publications, Mechanical Engineering
Ceramic On‐Demand Extrusion (CODE) is an additive manufacturing process recently developed to produce dense three‐dimensional ceramic components. In this paper, the properties of parts produced using this freeform extrusion fabrication process are described. High solids loading (~60 vol%) alumina paste was prepared to fabricate parts and standard test methods were employed to examine their properties including the density, strength, Young's modulus, Weibull modulus, toughness, and hardness. Microstructural evaluation was also performed to measure the grain size and critical flaw size. The results indicate that the properties of parts surpass most other ceramic additive manufacturing processes and match conventional fabrication techniques.
Properties Of Partially Stabilized Zirconia Components Fabricated By The Ceramic On-Demand Extrusion Process, Wenbin Li, Amir Ghazanfari, Devin Mcmillen, Ming Leu, Gregory Hilmas, Jeremy Watts
Properties Of Partially Stabilized Zirconia Components Fabricated By The Ceramic On-Demand Extrusion Process, Wenbin Li, Amir Ghazanfari, Devin Mcmillen, Ming Leu, Gregory Hilmas, Jeremy Watts
Faculty Publications, Mechanical Engineering
The Ceramic On-Demand Extrusion (CODE) process is a novel additive manufacturing process for fabricating dense ceramic components from aqueous pastes of high solids loading. In this study, 3 mol% Y2O3 stabilized tetragonal zirconia polycrystal (3Y-TZP) parts were fabricated using the CODE process. The parts were then dried in a humidity controlled environmental chamber and sintered under atmospheric pressure. Mechanical properties of the sintered parts were examined using ASTM standard test techniques, including density, Young’s modulus, flexural strength, Weibull modulus, fracture toughness and Vickers hardness. The microstructure was analyzed, and grain size was measured using scanning electron microscopy. The results compared …
A Novel Extrusion-Based Additive Manufacturing Process For Ceramic Parts, Amir Ghazanfari, Wenbin Li, Ming Leu, Gregory Hilmas
A Novel Extrusion-Based Additive Manufacturing Process For Ceramic Parts, Amir Ghazanfari, Wenbin Li, Ming Leu, Gregory Hilmas
Faculty Publications, Mechanical Engineering
An extrusion-based additive manufacturing process, called the Ceramic On-Demand Extrusion (CODE) process, for producing three-dimensional ceramic components with near theoretical density is introduced in this paper. In this process, an aqueous paste of ceramic particles with a very low binder content (<1 vol%) is extruded through a moving nozzle at room temperature. After a layer is deposited, it is surrounded by oil (to a level just below the top surface of most recent layer) to preclude non-uniform evaporation from the sides. Infrared radiation is then used to partially, and uniformly, dry the just-deposited layer so that the yield stress of the paste increases and the part maintains its shape. The same procedure is repeated for every layer until part fabrication is completed. Several sample parts for various applications were produced using this process and their properties were obtained. The results indicate that the proposed method enables fabrication of large, dense ceramic parts with complex geometries.
Methods Of Extrusion On Demand For High Solids Loading Ceramic Paste In Freeform Extrusion Fabrication, Wenbin Li, Amir Ghazanfari, Ming Leu, Robert Landers
Methods Of Extrusion On Demand For High Solids Loading Ceramic Paste In Freeform Extrusion Fabrication, Wenbin Li, Amir Ghazanfari, Ming Leu, Robert Landers
Faculty Publications, Mechanical Engineering
Fabrication of highly dense parts with complex geometry by paste-extrusion-based solid freeform fabrication processes requires a precise control of the extrusion flow rate to dispense material on demand, which is often referred as Extrusion-On-Demand (EOD). The extrusion process for aqueous ceramic pastes is complex and difficult to control due to their non-Newtonian behavior, compressibility and inhomogeneity. In this study, three methods of EOD (based on ram extruder, needle valve, and auger valve) are introduced and investigated for the extrusion of high solids loading (i.e., >50%, volumetric) aqueous alumina paste. Optimal extrusion process parameters for these methods are determined through printing …