Mechanical Properties Of Boride Based Ceramics, Alec Murchie

Doctoral Dissertations

“This research focuses on the elevated mechanical properties of diboride based materials at room and elevated temperatures. These materials include a ZrB₂ ceramic, a ZrB₂-WC-SiC ceramic, and a (Hf,Mo,Nb,Ta,W,Zr)B₂ high entropy boride (HEB). The room temperature flexural strength for the ZrB₂ ceramic was 447 MPa and the fracture toughness was 2.3 MPa·m^1/2. The strength decreased to 196 MPa at 1800°C, and then increased to 360 MPa at 2300°C. The fracture toughness increased to 3.1 MPa·m^1/2 at 2200°C. The strength up to 1800°C was likely controlled by a combination of effects: surface damage …

Investigation Of The Thermodynamics Of Iron Phosphate Melts And Stability Of Iron Phosphate Glasses: Effects Of Composition And Iron Redox Ratio, Melodie Linda Schmitt

Doctoral Dissertations

“Iron phosphate glasses with Fe/P = 0.33 - 0.67, O/P = 3.0 - 3.5 and Fe²⁺/ΣFe = 0.16- 0.52 were prepared by altering batch compositions and melt conditions. Thermal analyses indicate polyphosphate glasses with intermediate chain lengths are most stable against devitrification. Heterogeneous crystallization occurs on the glass surface and is dependent on iron valence state, particle size, heating rate, temperature and oxygen availability in the atmosphere. Oxidation of ferrous iron on the glass surface occurs at temperatures as low as Tg, and thus crystallization behavior and stability can be altered via post-melt heat treatments. A novel preparation …

Bulk Nanostructured Steels For Nuclear Reactor And Extreme Environment Applications, Maalavan Arivu

Doctoral Dissertations

"Candidate accident tolerant FeCrAl fuel (ATF) claddings for light water reactors (LWRs) need to be thinner than current Zircaloys owing to higher neutronic penalty, demanding an improvement in strength. Therefore, equal channel angular pressing (ECAP), and high-pressure torsion (HPT) were used to produce bulk ultra-fine grained and nanocrystalline Kanthal-D [KD; Fe-21Cr-5Al-0.026C (wt.%) alloy] which resulted in an improvement in strength of up to 3 times their nominal strength from grain boundary strengthening, and dislocation strengthening. Dynamic recovery was promoted due to ECAP at 520 oC rendering it with a large area fraction of less mobile low angle grain boundaries (LAGBs) …

Joining Of Ultra-High Temperature Ceramics To The Same And Refractory Metals Via Fusion Welding, Jecee Jarman

Doctoral Dissertations

"This research focuses on the joining of ultra-high temperature ceramics to either themselves or refractory metals/alloys via fusion welding and the mechanical strength of produced joints. The ceramics studied consisted of compositions within a diboride-carbide-carbide ternary system while metals studied consisted of molybdenum and a molybdenum alloy. SiC-ZrB2-ZrC ceramics on a binary join between pure SiC and the ternary eutectic composition were found to be weldable when SiC content was below ~57.5 vol%. Compositions above 57.5 vol% SiC were unweldable based on pitting and off-gassing behavior. Welded strength of ceramics was ~180-300 MPa in the SiC-ZrB2-ZrC ternary eutectic composition, ~180-220 …

Peritectic Behavior Detection And Prediction In Fe-C-Si-Mn-Al System, Damilola Balogun

Doctoral Dissertations

"The non-uniformity of shell growth in the continuous casting of peritectic steels constitutes a major barrier to the commercial production of many steel grades such as Advanced high strength steels (AHSS), transformation induced plasticity (TRIP) steels, abrasion-resistant steels, advanced armor plate steels, and many newly proposed steel grades that contain high levels of silicon, manganese, and aluminum.

The shell growth non-uniformity experienced in the continuous casting of peritectic steels results in the formation of defects in the as-cast slab and therefore increases the operating risk from cast aborts and breakouts. The ability to predict and avoid peritectic behavior at the …

Oxidation Of Silicon Carbide And Graphite For High Temperature Gas-Cooled Reactor Applications, Adam Thomas Bratten

Doctoral Dissertations

"This research focuses on the oxidation behavior of silicon carbide and matrix grade graphite, specifically as it pertains to accident scenarios in Gen IV thermal spectrum high temperature gas cooled nuclear reactors. It is imperative to understand the oxidation behavior of such materials to predict their response to off-normal environments and certify their accident tolerance to implement Gen IV reactors. The onset of oxidation temperature of matrix graphite was found to have a strong dependence on the microstructure, and therefore processing parameters, of the materials. The A3-3 type grade contained regions of partially graphitized carbon that were more disordered and …

Processing To Enable Direct-Write Additive Manufacturing Of Ceramics And Ceramic Composites, Austin Martin

Doctoral Dissertations

"This research focuses on the processing of novel feedstocks for and during direct-write additive manufacturing (AM), specifically the direct ink writing (DIW) and Ceramic On-Demand Extrusion (CODE) manufacturing processes, in order to produce ceramic and ceramic-based composite components. Strongly dispersed, concentrated (φ = 0.42), nanoparticle (d₅₀ ~0.3 µm), zirconia (ZrO₂) pastes were used to print densely filled, large continuous volume (≳ 1 cm³) ceramic components. An elastic shear modulus (G’) of 56,000 Pa and yield stresses between 6 and 10 Pa allowed for printed components of 34.5 mm in height over 115 layers without slumping …

Molten Steel Interactions With Tundish Linings And Refractory Glazes, Tyler Michael Richards

Doctoral Dissertations

"In the final stages of casting, molten steel is in contact with two main types of refractories: the working lining of the tundish used to serve as an intermediate vessel between the ladle and copper mold, and the various glazed carbon-bearing refractories used to control the flow of steel from the ladle to the tundish and from the tundish to the mold. If steel interacts with these refractories in such a way as to result in the formation of inclusions, it may be too late to remove them, leading to degradation of the steel’s mechanical properties. Understanding these interactions and …

Development And Application Of Ensemble Machine Learning Algorithms To Enable A Priori, High-Fidelity, And Prompt Predictions And Optimizations Of Complex Materials And Systems, Taihao Han

Doctoral Dissertations

"Complex materials consisting of multiple chemical components/phases have been widely used in different engineering applications that have strict criteria. To optimize the mixture design of complex materials, researchers invest enormous resources in cumbersome experiments. However, due to substantial variations in precursors and processing techniques, it has been challenging to develop theoretical frameworks (i.e., empirical models) that could produce reliable predictions of properties of complex materials. In recent years, scientists have harnessed the power of machine learning (ML) and “Big” data to uncover the underlying mixture design-property correlations and produce high-fidelity predictions of properties of complex materials. The ML models autonomously …

The Influence Of Different Crystal Modifiers On Ultra-Low Embodied Energy Curing Fiber-Reinforced Cement Composites, Passakorn Sonprasarn, Wichit Prakaypan, Sureerat Polsilapa, Nuntaporn Kongkajun, Edward A. Laitila, Nutthita Chuankrerkkul, Parinya Chakartnarodom

Michigan Tech Publications, Part 1

Fiber-reinforced cement composites (FRCC) are widely used in the construction of houses and commercial buildings in many countries such as the United States, the United Kingdom, the European countries, and the Asian countries such as China, India, and Thailand. Conventionally, the FRCC is manufactured from Portland cement, silica sand, and cellulose fiber using the so-called autoclaved curing under a designate hydrothermal condition to accelerate the hydration reaction resulting in superior properties. However, the autoclave-curing process needs a huge investment and generates highly environmental impact specially greenhouse gases due to its heavy energy consumption. Hence, this research aims to develop the …

Stimuli-Responsive Chitosan-Based Hydrogels For Antibiotic Delivery, Tu Tran Vo Minh

Chulalongkorn University Theses and Dissertations (Chula ETD)

This study aims to investigate hydrogels fabricated via green approaches for drug delivery application. Biocompatible polymer-based drug delivery systems (DDS) have gained popularity in recent years because of their ability to improve the efficacy and safety of drug delivery by providing targeted and sustained release of drugs to reduce the frequency of dosing, making it more convenient for patients. Chitosan is one of the polymers commonly used for this purpose due to their higher water retention and porosity, which create space for loading medicine into the matrix. However, the potential utilization of endogenous and exogenous stimuli controlling drug release still …

An Approach For Material Model Identification Of A Composite Coating Using Micro-Indentation And Multi-Scale Simulations, Pouya Shojaei, Riccardo Scazzosi, Mohamed Trabia, Brendan O’Toole, Marco Giglio, Xing Zhang, Yiliang Liao, Andrea Manes

Mechanical Engineering Faculty Research

While deposited thin film coatings can help enhance surface characteristics such as hardness and friction, their effective incorporation in product design is restricted by the limited understand-ing of their mechanical behavior. To address this, an approach combining micro-indentation and meso/micro-scale simulations was proposed. In this approach, micro-indentation testing was conducted on both the coating and the substrate. A meso-scale uniaxial compression finite element model was developed to obtain a material model of the coating. This material model was incorporated within an axisymmetric micro-scale model of the coating to simulate the indentation. The proposed approach was applied to a Ti/SiC metal …

Nanomechanical Characterization And Comparison Of Additively Manufactured Grcop-42 Alloy, Trupti Suresh Mali

Electronic Theses and Dissertations

In an aggressive thermomechanical environment, the superior mechanical as well as thermal properties of materials play an essential role. GRCop which is a copper-based alloy developed by NASA has the potential to fulfill the requirements necessary for hightemperature applications such as the combustion chamber of liquid rocket engines. The first alloy of this family, GRCop-84 (Cu-8 wt.% Cr-4 wt.% Nb) was discovered followed with the development of GRCop-42 (Cu-4 wt.% Cr, 2 wt.% Nb). The reduction in alloying element percentage enhanced thermal conductivity with less built time while maintaining the strength of the material. The conventional fabrication is replaced with …

Moisture Content Prediction In Polymer Composites Using Machine Learning Techniques, Partha Pratim Das, Monjur Morshed Rabby, Vamsee Vadlamudi, Rassel Raihan

Institute of Predictive Performance Methodologies (IPPM-UTARI)-Archive

The principal objective of this study is to employ non-destructive broadband dielectric spectroscopy/impedance spectroscopy and machine learning techniques to estimate the moisture content in FRP composites under hygrothermal aging. Here, classification and regression machine learning models that can accurately predict the current moisture saturation state are developed using the frequency domain dielectric response of the composite, in conjunction with the time domain hygrothermal aging effect. First, to categorize the composites based on the present state of the absorbed moisture supervised classification learning models (i.e., quadratic discriminant analysis (QDA), support vector machine (SVM), and artificial neural network-based multilayer perceptron (MLP) classifier) …

Evaluation Of Static Recrystallization And Grain Growth Kinetics Of Hot-Rolled Az31 Alloy, Salaheddine Sadi, Abdelkader Hanna, Thierr Baudin, Anne-Laure Helbert, François Brisset, Djamel Bradai, Hiba Azzeddine

Journal of Metals, Materials and Minerals

The static recrystallization/grain growth kinetics of the AZ31 (Mg-3Al-1Zn, wt%) alloy were investigated employing Vickers microhardness and electron backscatter diffraction (EBSD) measurements. The AZ31 alloy was subject to a hot-rolling for 70% of thickness reduction and then annealed at various temperatures (150°C, 250°C, and 350°C) from 5 min to 24 h. First, the static recrystallization kinetics were analysed by means of the Johnson-Mehl-Avrami-Kolmogorov (JMAK) model. The results showed that the recrystallization occurred under two regimes both involving their own Avrami exponent/ activation energy. In regime I, the Avrami exponent was found in the range of 1.5-0.35 depending on the annealing …

Effect Of Al Addition On Crystal Structure Of Algan/Gan On Gaas (001) Substrate Grown By Metalorganic Vapor Phase Epitaxy, Nattamon Suwannaharn, Sakuntam Sanorpim, Suphakan Kijamnajsuk, Visittapong Yordsri, Noppadon Nuntawong, Kentaro Onabe

Journal of Metals, Materials and Minerals

Effects of Al addition on a structural phase modification in AlGaN/GaN films on GaAs  substrate grown by MOVPE have been investigated. To examine the effect of Al addition, AlGaN/GaN films were grown with varied a molar flow ratio of TMAl to the total group-III elements of 0, 0.15, and 0.30. Quantity of hexagonal phase incorporation was evaluated by the ratios of integrated XRD intensity of hexagonal  plane to cubic  plane from reciprocal space mappings. The diffraction geometry factor was considered in the calculation. The results suggest that GaN primarily contains a hexagonal phase with a small fraction of a cubic …

Facile Synthesis Of Heterostructured G-C3n4/Ag -Tio2 Photocatalysts With Enhanced Visible-Light Photocatalytic Performance, Chonnipha Tangwongputti, Prasert Reubroycharoen, Pornapa Sujaridworakun

Journal of Metals, Materials and Minerals

In this study, the g-C3N4/Ag-TiO2 composite photocatalysts were prepared to enhance the efficient utilization of solar energy. The g-C3N4 was synthesized by facile heat treatment of urea at 600℃ for 4 h, and 0.05 wt% to 3 wt% Ag-TiO2 were obtained through the chemical reduction method. The composite photocatalysts were prepared by mixing the g-C3N4 and Ag-TiO2 with a weight ratio of 50:50 at room temperature. The photocatalytic efficiency was carried out by using 0.05 g of photocatalysts with 10 mg·L-1 of rhodamine B 120 mL under 60 min of visible light irradiation. The experimental results indicated that a sample …

Effect Of Pre-Carbonization Temperature On The Porous Structure And Electrochemical Properties Of Activated Carbon Fibers Derived From Kapok For Supercapacitor Applications, Nu Myat Thazin, Nattapat Chaiammart, Myo Myo Thu, Gasidit Panomsuwan

Journal of Metals, Materials and Minerals

Activated carbon fibers (ACFs) were successfully synthesized from kapok via a two-step process: (i) pre-carbonization and (ii) chemical activation. The pre-carbonization temperature was varied at 300℃, 400℃, and 500℃. The mixing ratio of the pre-carbonized product and potassium hydroxide (KOH) was 3:1, while the activation temperature was 800℃. The effect of pre-carbonization temperature on the morphology, surface area and porosity, chemical functional group, and phase structure of ACFs was investigated and discussed. The characterization results showed that ACFs exhibited an amorphous carbon structure with a hollow fiber shape resembling the kapok. The specific surface area decreased from 487 m2×g-1 to …

Effects Of Milling Time On Sintering Properties And Formation Of Interface Al4c3 On Graphite Reinforced Al-4.5cu-1.5mg Nanocomposite, Angga Khairul Fahmi, Haris Rudianto, Agus Sukarto Wismogroho, Wahyu Bambang Widayatno, Didik Aryanto, Bambang Hermanto

Journal of Metals, Materials and Minerals

Aluminum-based metal matrix nanocomposites have been extensively researched and developed for aerospace and automotive applications. Al-4.5Cu-1.5Mg with 0.5 wt% graphite were milled for 2 h, 4 h, 6 h, and 8 h using shaker mill under argon gas. The phenomena of deformation, fracturing, and cold welding during shaker mill were investigated to observe how the shaker mill effects on their morphology and formation of intermetallic phases due to its very high speed. Sintering under ultra-high purity argon gas for 99.9999% was done to produce high density materials. Intermetallic phase Al4C3 was found as a result reaction between aluminum and graphite …

Influence Of Six-Step Heat Treatment On Microstructures And Mechanical Properties Of 5160 Alloy Steel, Pattama Apichai

Journal of Metals, Materials and Minerals

AISI 5160 alloy steel grade with complete martensite structure to get the high-strength steel sheets quenched at 900 (Q1), 870 (Q2), 840 (Q3) and 810°C (Q4), respectively and temped at 780°C (Q5) and 680°C (Q6), respectively. The results show ferrite and pearlite microstructural appeared in as-sheet conditions. The strengthening rarely increased with increasing heat treatment steps, while the percentage elongation gradually decreased. The hardness change was secure with that of strengthening for the quenched martensite. In contrast, differences between the initial martensite hardness were no noticeable changes. The Q4 hardening involved the peak hardness and maximum ultimate tensile strength due …

Biodiesel Production From Waste Cooking Oil Using A New Heterogeneous Catalyst Sro Doped Cao Nanoparticles, Apisit Prokaewa, Siwaporn Meejoo Smith, Apanee Luengnaruemitchai, Mathi Kandiah, Supakorn Boonyuen

Journal of Metals, Materials and Minerals

Biodiesel production from waste palm cooking oil (WPCO) was studied. Calcium oxide with a strontium ion additive (Sr-CaO) was employed as a catalyst in transesterification reaction of used palm oil with methanol. The Sr-CaO was synthesized by co-precipitation method between SrCl2 and Ca(NO3)2, then calcined at 900°C for 5 h. The catalyst was characterized by using thermo-gravimetric analysis (TGA), X-ray diffraction (XRD), Scanning electron microscope (SEM), and Fourier transform infrared spectrometer (FT-IR). The morphology and elements content of Sr and Ca in the catalyst were confirmed by SEM-EDX. The approximate catalyst diameter is 12.6±5.9 µm. The highest conversion was 99.33% …

Study Of The Effect Of Ph, Conditioning And Flotation Time On The Flotation Efficiency Of Phosphate Ores By A Soybean Oil Collector, Zohra Farid, Mohamed Abdennouri, Noureddine Barka, Youness Jannani, M'Hamed Sadiq

Journal of Metals, Materials and Minerals

The mid-low grade of phosphate ore, rich by the silicate and carbonate gangue minerals needs a special treatment using the flotation process. Where the collectors play a pivotal role. This study was conducted to enrich an untreated phosphate ore (without washing, desliming, hydrocycling, etc.), with an eco-friendly and economic collector based on soybean oil. Different analytical techniques such as UV-Visible, ATR-FTIR spectrometric and XRD were used in order to analyse and characterize the flotation products. The effects of the parameters, pulp pH, conditioning time and flotation time on gangue removal efficiency by flotation, were investigated. Flotation tests were applied for …

The Finished Polyester Fabric With Hot Nh4oh Pretreatment And Mixed Zno-Zn(Oh)2 Nanoparticles For Hydrophobic Property, Samroeng Narakaew, Sittipong Au-Pree, Wipanoot Baison, Siwat Thungprasert, Itsariya Wattalo, Pranpreeya Jaipor, Theeraporn Promanan, Sukee Sukdee, Pakorn Santakij, Chainet Chanogkun, Kanjana Ruttanateerawichien, Aphiruk Chaisena, Pattama Apichai, Phiphop Narakaew

Journal of Metals, Materials and Minerals

This work aims to modify the hydrophobic coated polyester fabrics using 2%w/v ammonium hydroxide (NH4OH) at 90℃ prior and subsequently dipped in two difference aqueous zinc solution batchs containing 0.6%w/v zinc precursors with/without starch and NH4OH, finally dehydration, and characterized by the attenuated total reflection - Fourier transform Infrared (ATR-FTIR) and Raman spectroscopy (Raman), X-ray diffraction (XRD), Field emission scanning electron microscope (FE-SEM), Energy dipersive spectrometry (EDX), and Water contact angle (WCA) of 10 mL dropping at 23℃ and humidity of 63%. Raman spectra and XRD patterns results showed e-zinc hydroxide (e-Zn(OH)2), zinc oxide nanoparticle (ZnO NP) and ZnO-starch nanocomposite …

Epoxidized Natural Rubber/Silane Modified Silica Nanocomposites Prepared In Latex Stage, Supat Moolsin, Duangkamon Sawangkan

Journal of Metals, Materials and Minerals

Epoxidized natural rubber (ENR) was synthesized from natural rubber (NR) latex via in situ epoxidation using HCOOH and H2O2. The prepared ENR with 22 mol% epoxidation (ENR-22) was reinforced with silane modified silica (SMS) nanoparticles with different SMS loading in latex stage. The tensile properties, thermal stability, oil resistance and morphology of the ENR-22/SMS nanocomposites were investigated. The tensile strength was improved significantly and gained the maximum point at 7.5 phr SMS content. The thermogravimetric analysis showed an increased initial degradation temperature with the addition of SMS, suggesting higher thermal stability of the nanocomposites. The oil resistance of ENR-22/SMS nanocomposites …

Use Of Oil Palm Frond Waste To Reinforce Poly(Lactic Acid) Based Composites With The Improvement Of Interfacial Adhesion By Alkali Treatment, Nattakarn Hongsriphan, Jidapa Subsanga, Pimpisa Suebsai, Sunisa Sitthipong, Pajaera Patanathabutr

Journal of Metals, Materials and Minerals

Oil palm frond waste was used as reinforcing fibers for biodegradable poly(lactic acid) or PLA in order to produce green composites that increased the value of agricultural waste. The alkali-treated oil palm frond (OPF) fibers of 30 wt% or 40 wt% were compounded with PLA and moulded into specimens. The alkali treatment was 0 wt%, 1 wt%, 3 wt%, and 5 wt% of the fibers for compatibility improvement with PLA matrix. It was found that the alkali-treated PLA/OPF composites adding 30 wt% and 40 wt% had the flexural modulus to be about 55% and 75% higher than those without the …

Design, Development And Characterization Of A Mid-Frequency (35 Khz) Tonpilz Transducer Array From 0.675pmn-0.325pt Piezoceramics, Merve Nur Çiftçi, Berk Değirmenci, Irem Böbrek, Sedat Alkoy, Aykut Aykaç, Muhammet Boz, Ayşe Berksoy-Yavuz, Ezgi Yalcin, Namik K. Gozuacik, Ebru Menşur

Journal of Metals, Materials and Minerals

A mid-frequency tonpilz transducer array was designed and analyzed by finite element method using commercial ATILA code and constructed using piezoceramic rings with lead magnesium niobate (PMN)-lead titanate (PT) composition. The morphotropic phase boundary (MPB) 0.675Pb(Mg1/3Nb2/3)O3-0.325PbTiO3 composition was chosen to obtain higher performance from the transducer due to the superior dielectric and electromechanical properties of the MPB compositions. A pure perovskite phase was obtained from the ceramics. Piezoelectric charge coefficient (d33) was measured as 435 pC×N-1. Single tonpilz element and an array consisting of 7-unit array were constructed and later potted in polyurethane for underwater measurements. A second array was …

Amino-Containing Polymer-Coated Magnetite Nanoparticles As Nano-Adsorbents For Bisphenol A: Synthesis, Kinetic And Thermodynamic Study, Jakkrit Tummachote, Metha Rutnakornpituk, Duangdao Channei, Filip Kielar, Boonjira Rutnakornpituk

Journal of Metals, Materials and Minerals

Magnetite nanoparticles coated with poly(dimethyl aminoethyl methacrylate) (PDMAEMA@MNPs) and their quarternized form (PQDMAEMA@MNPs) were successfully synthesized and used as nano-adsorbents for bisphenol A (BPA). The particles were spherical with the average particle size between 10 and 20 nm in diameter with a moderate degree of nanoclustering (ca.150-200 particles/cluster). In terms of adsorption properties, the PDMAEMA@MNPs exhibited a higher BPA adsorption capacity (1.05 mg/g MNP at pH 9) than the quaternized form (0.50 mg/g MNP at pH 9). Equilibrium isotherm, kinetic, and thermodynamic characteristics of BPA adsorption on the PDMAEMA@MNPs were investigated. It was found that the BPA adsorption …

Elastic Properties Of Boro-Tellurite Glasses Doped With Europium Oxide, Chinnappareddy Devaraja, G. V. Jagadeesha Gowda, Bheemaiah Eraiah, G. K. Narasihma Murthy

Journal of Metals, Materials and Minerals

The glass series of xEu2O3-5PbO-25TeO2-(70-x) B2O3, where x=0.1 mol% to 0.6 mol% were prepared by employing the conventional melt quenching method. The non-crystallinity of prepared BTE glasses was examined by the X-ray diffraction method. The very important mechanical properties such as elastic moduli, Debye temperature, Poisson’s ratio, fractional bond connectivity, softening temperature, acoustic impedance, and the thermal expansion coefficient of the BTE glasses have been studied by measuring ultrasonic velocity. The experimental results indicate that the calculated parameters strongly depend on increasing Eu2O3 concentration. The elastic moduli of the prepared samples were found to decrease with Eu2O3 concentration and this …

Enhanced Photocatalytic Activity Of Zno Nanostructures Deposited On Mesh Through Electrochemical Deposition And Thermal Oxidation, Chantana Aiempanakit, Thongchai Phantaporn, Kamon Aiempanakit

Journal of Metals, Materials and Minerals

This article reported that the properties of zinc oxide (ZnO) nanostructures were modified by the thermal oxidation process at different temperatures in the range of 200℃ to 600℃ for 1 h. The Zn films were deposited on a stainless steel mesh by using the electrochemical deposition technique. The elemental composition of Zn and O was exhibited via energy-dispersed X-ray spectroscopy in which the atomic ratio of O/Zn increased with the increase of oxidation temperature. The results showed that oxidation temperature has a significant effect on the morphological and crystal structure. The nanosheet structure of the as-deposited film transferred to the …

Brazilein Modified Zinc Oxide Nanorods With Enhanced Visible Light-Responsive Photocatalytic Efficiency, Montri Aiempanakit, Penpicha Sudjai, Kittiyaporn Singsumphan, Sakchai Laksee, Cheewita Suwanchawalit

Journal of Metals, Materials and Minerals

Photocatalytic efficiency of ZnO nanorods has been investigated with respect to the concentration of brazilein. Brazilein modified ZnO nanorods were prepared by an impregnation process with 1.0%w/v, 2.5%w/v, and 5.0%w/v of brazilein solution.  In order to correlate the variation in concentration distributions and photocatalytic performance, the phase composition, optical properties, and photo-catalytic activities of brazilein modified ZnO nanorods prepared with different brazilein concentrations have been investigated and compared to an unmodified ZnO nanorods. The photocatalytic properties were measured in terms of indigo carmine degradation under visible light irradiation. It was found that ZnO nanorods with the highest visible light-responsive photocatalytic …