Potential Fluctuations Of 7075 Aluminum Alloy Under Thin Electrolyte Layers, Su-Jing Chen, Qing-Ming Yuan, Jian-Ping He, Xiao-Lei Liu

Journal of Electrochemistry

Lens tissues adsorbing 3.5% sodium chloride solution were used to simulate thin electrolyte layers. The 7075 aluminum alloy was immersed under the thin electrolyte layers for 0, 4, 6, 8 and 12 h respectively. Then the fluctuations of natural-corrosion potentials of the alloy were monitored. The fluctuations of natural-corrosion potential were observed rather small in the initial corrosion stages after 6h immersion, and the positive peaks of potential appeared. However the amplitudes reached 20mV after 4h and 12h immersion. The RMS of natural-corrosion potentials decreased with corrosion time at first and then increased. It reached a minimum at 4 h. …

Application Of Nickel Foam Electrode For Electroreduction Intermediate Of Purine, Hui-Wen Yang, Xi-En Hu, Xue-Jun Wang

Journal of Electrochemistry

Nickel foam with weight uniformity, good porosity ,pore size and low resistivity as a three-dimensional cathode was used in a filter-press electrochemical reactor. The H₂SO₄ as supporting electrolyte, separator of cation ion exchange membrane, and the lead plate as an anode were used. The cyclic system consisted of electroreduction reactor, pump, store tank and ampere meter. NAU was electroreduced in the cathode chamber of the reactor. Purine intermediate was synthesized with DAU, and the results were compared with those of iron powder reduction process. A peak current in the electroreduction process was detected. The current density of …

Ni-Mo-P Alloy By Electroless Deposition And Its Properties, Sen-Lin Wang, Xin-Ren Lan, Ting-Ting Huang, Jun-Mo Jin, Ji-Bei Ling, Zhi-Ming Chen

Journal of Electrochemistry

The electroless Ni-Mo-P alloy has been deposited from the alkaline bath containing boric acid as a buffer agent and sodium citrate as a complexing agent. The effect of deposition parameters, such as pH and concentration of (NH₄)₆Mo₇O₂₄·4H₂O on the plating rate, the composition, the structure and the microhardness of the coating was examined. It was found that the presence of molybdenum has an inhibitory effect on the alloys deposition. As a consequence, the percentage of molybdenumin the Ni-Mo-P coatings never reaches high values, which was lower than 20 at%. It …

Using Electrodeposition To Fabricate Mould For Polymer Microfluidic Chip, Yi Luo, De-Nan Chu, Zhi-Feng Lou, Chong Liu, Li-Ding Wang

Journal of Electrochemistry

Many researches have been focused on polymer microfluidic chip in recent years and the mould plays an important role in its fabrication process. Using electrodepositingmethod to fabricate a metal mould for polymer microfluidic chip has been presented in this paper. An ultra-thick photoresist SU-8 was coated on a pretreated metal plate, after photolithography, nickel was electrodeposited in the patterned SU-8, then was removed the SU-8 to obtain a final metal mould. This methodreduces workload of electrodeposit largely. Applying counter current before deposit, adding additive to solution and vacuum anneal after demould have been used to improve the binding force between …

Preparation, Characterization And Electrochemical Properties Of Nano Tio2-Cnt-Pt On Ti Substrate Complex Electrode, Dao-Bao Chu, De-Xiang Feng, Jin-Hua Zhang, Xiao-Hua Li

Journal of Electrochemistry

The nanoTiO₂-CNT-Pt on Ti substrate complex electrodes were prepared from precursor of (Ti(OEt)₄) directly hydrolyzed and by cyclic voltammograms electroplating method . The XRD and SEM results showed that the nano TiO₂ (anatase) particle sizes ranged 5~10 nm and the Pt nanoparticle (average size 9nm) dispersed uniformly on nanoTiO₂-CNT film surface. The electrocatalytic activity of Ti/nanoTiO₂-CNT-Pt electrode was investigated by cyclic voltammetry and chronopotentiogram. The results indicated that the Ti/nanoTiO₂-CNT-Pt electrode exhibited very high electrocatalytic activity and stability for the electro-oxidation of methanol at room temperature. When Pt loading …

A Comparison On Structural Sensitive Adsorption Of Sb On Au Single Crystalline Electrodes, Jia-Wei Yang, Wang-Huo Shang, Qiong Wu, Bing-Wei Mao

Journal of Electrochemistry

We compare the behaviors of irreversible adsorption of Sb(III) and its reduction, underpotential deposition of Sbon Au(111) and Au(100) as well as mutual interactions of the processes. Based on in-situ scanning tunneling microscopic and cyclic voltammetric results, the substrate structure not only influence anion adsorptionbehavior and thus the Sb adsorption structure, but also the stability of its own structure. On Au(111) surface,the irreversibly adsorbed dense and disordered SbO⁺ film structure remains after reduction of the film; while on Au(100)surface, due to the coadsorption of SO₄^2-, an ordered(2×2)structure is formed after reduction. UPD of Sb on Au(111) …

A Preliminary Study Of Electrocrystallization Of Bismuth On Glassy Carbon, Min-Li Yang, Zhan-Jun Zhang

Journal of Electrochemistry

The electrocrystallization of bismuth on glassy carbon electrodes (GCEs) from nitrate solutions was studied by cyclic voltammetry and chronoamperometry. Cyclic voltammograms exhibit a crossover between the cathodic and anodic branches, characteristic of the formation of bismuth nuclei on GCEs, and show that the bismuth electrocrystallization on GCEs is a diffusion-controlled reaction. The current transients were analyzed with the Scharifker and the Heerman equations. With the increaseof Bi³⁺ concentration, the non-dimensional plots leaned to the theoretical curve for 3D instantaneous nucleation and growth. The overpotential dependence of nucleation and growth mechanism was also found. With the increase of overpotential, the …

Preparation And Characterization Of Mcm-41/Pvdf-Hfp Composite Microporous Polymer Electrolytes For Li-Ion Batteries, Zuo-Feng Chen, Yan-Xia Jiang, Quan-Chao Zhuang, Quan-Feng Dong, Shi-Gang Sun

Journal of Electrochemistry

MCM-41/vinylidine fluoride-hexafluropropene copolymer (PVdF-HFP) composite microporous polymer electrolytes were prepared with mixed solvent of N, N-Dimethylformamide (DMF) and acetone. The influence of MCM-41 and nano-SiO₂ on the porous structure of the microporous polymer electrolytes were studied with SEM. The results show that MCM-41 could take the place of the plasticizer in the process of making pores, and bring the preparation of microporous membranes easily. The preliminary electrochemical tests showed that the ion conductivity of composite microporous polymer electrolyte with 10% MCM-41 was about 10^-3 S cm^-1, and the performance of batteries was improved. The mesoporous MCM-41selected …

Investigation On Ru-Ti-Ir-Sn Oxide Anode Coatings For Electrolyzing Seawater, Ke Wang, Yan Han, Lei-Yuan Wang, Xiao-Ling Zhang, Yu-Pu Sun

Journal of Electrochemistry

The anode coatings of Ru-Ti-Ir-Sn oxide with various compositions were prepared by thermal decomposition. The physical and electrochemical properties of the coatings were characterized by scanning electron microscope (SEM), energy dispersive X-ray detector (EDX), accelerated life, current efficiency, anti-Mn²⁺ contamination, polarization curveandcyclic voltammetry tests. The results showed thatthe anode coating with optimized formula possessed excellent overall properties for electrolyzing seawater.

Structure And Corrosion Electrochemical Properties Of Self-Assembled (3-Mercaptopropyl) Trimethoxysilane Films On Copper Electrode, Ling Huang, Ke-Fa Lin, Fang-Zu Yang, Shu-Kai Xu, Shao-Min Zhou

Journal of Electrochemistry

A self-assembled monolayer of (3-mercaptopropyl) trimethoxysilane(MPTS) was formed on a electrochemical polished copper surface electrode. The corrosion protection abilities of the monolayer were evaluated in 5% NaCl solution using electrochemical linear polarization. The effects of deposition time and silane concentration on corrosion of copper were also discussed. The surface structure of MPTS films was measured by FT-IR and SEM. It was found that the corrosion resistance of copper was reduced markedly owing to the MPTS monolayers formation on copper. The MPTS monolayer retarded the reduction of dissolved oxygen and inhibited the growth of copper oxide in the NaCl solution. FT-IR …

Study On Synthesis Of M-Phenoxy Benzoic Acid By Electrolysis Oxidation Method, Wei Xu, Chong-Tao Zhao

Journal of Electrochemistry

The m-phenoxy benzoic acid was synthesized by oxidation m-phenoxy toluene using Cr(Ⅵ)as oxidation media, which was prepared by electrolysis oxidation of Cr(Ⅲ)in the electrochemical bath using Nafion 417 as a diaphragm, Pb-PbO₂ as an anode and Pb as cathode. The effect factors on the electrochemical oxidation of Cr(Ⅲ)to Cr(Ⅵ)in this electrolysis were studied. Furthermore, the optimal conditions for electronic synthesis of m-phenoxy benzoic acid were also discussed.

The Preparation And Performance Of The Aqueous Matrix For Molten Carbonate Fuel Cells, Hua-Xin Lin, Mo-Jie Ceng, Bao-Lian Yi

Journal of Electrochemistry

PVA matrix of MCFC was prepared from the α-LiAlO₂ powder, and polyvinylalcohol(PVA), Compared with the conventional PVB matrix, higher porosity, higher thermal weight loss and smaller maximum pore diameter were achieved for PVA matrix. Single cell was assembled with PVA matrix. At reaction gas pressure of 0.9 MPa, under reaction gas utilization of 20%, at 300 and 428.57 mA·cm^-2, the cell voltage was 0.849 and 0.739 V respectively, and the output power density was 254.7 and 316.7 mW·cm^-2 respectively, which are higher than those of the cell assembled with PVB matrix. During thermal cycles, the cell …

The Synthesis, Characteristics And Performance Of Cnt Composites As Anodic Materials In Litium-Ion Battery, Quan-Feng Dong, Ming-Sen Zheng, Zhen-Cai Huang, Ming-Gang Jin, Ya-Ding Zhan, Zu-Geng Lin

Journal of Electrochemistry

As an anodic material for lithium ion battery the carbon nano-tube (CNT) and some compounds based on tin have ever been investigated intensively. The fruited progress has not been made yet, however. In this paper the composites of CNT and Sn/SnO₂ were synthesized employing two methods and characterized by SEM and XRD. And the electrochemical performance of the composites was investigated.

The Effect Of Oxidant On Structure And Properties Of Pan/Ptfe Conducting Composite Membrane, Chang-Yuan Tao, Jing Chen, Jun Du, Cai-Xin Sun

Journal of Electrochemistry

The PAn/PTFE conducting composite membrane was prepared by means of in-situ permeating chemical polymerization, with (NH₄)₂S₂O₈ and Na₃VO₄ being used as an oxidant respectively. The polymerization-growth behavior of the aniline by using different oxidant was compared. In addition, the oxidant effect on the structure and properties of conducting composite membrane was discussed. The results of SEM micrographs, pore size distribution and electrochemical methods suggested that using either oxidants could also induce the product with small pore size and dense pore structure. Compared with (NH₄)₂S₂O …

Static And Modal Analysis Of The Magnetic Levitation Vehicle, Santosh Kumar Desetty

Mechanical & Aerospace Engineering Theses & Dissertations

The magnetic levitation train project at Old Dominion University has been stalled due to many technical problems. The control system is the main component of the vehicle, which is supposed to maintain an intended gap of 1 cm between the vehicle and the track while traveling, hence providing a smooth ride. The goal of the project is to document the mathematics of the complete system so that the control algorithm can be implemented and modified with the expectation of obtaining an improved levitation and propulsion.

The complete system includes the vehicle, the track, and the concrete guide-way. The focus of …

Tensile Properties Of Martensitic Stainless Steels At Elevated Temperatures, Ajit K. Roy, Srinivasarao R. Kukatla, Bhagath Yarlagadda, V. N. Potluri, Martin Lewis, Brendan O'Toole

Mechanical Engineering Faculty Research

Tensile properties of quenched and tempered martensitic alloys EP-823, HT-9, and 422 were evaluated at temperatures ranging from ambient to 600 °C as a function of three different tempering times. The results indicated that the yield strength, ultimate tensile strength, and the failure strength were gradually reduced with increasing temperature. The ductility parameters were enhanced at elevated temperatures due to increased plastic flow. However, the tempering time did not significantly influence these properties. The evaluation of the fracture surfaces by scanning electron microscopy revealed reduced cracking and dimpled microstructures, indicating enhanced ductility at higher testing temperatures.

Residual Stress Characterization In Structural Materials By Destructive And Nondestructive Techniques, Ajit K. Roy, Anand Venkatesh, Vikram Marthandam, Satish Dronavalli, Douglas P. Wells, Ronald Rogge

Mechanical Engineering Faculty Research

Transmutation of nuclear waste is currently being considered to transform long-lived isotopes to species with relatively short half-lives and reduced radioactivity through capture and decay of minor actinides and fission products. This process is intended for geologic disposal of spent nuclear fuels for shorter durations in the proposed Yucca Mountain repository. The molten lead-bismuth-eutectic will be used as a target and coolant during transmutation, which will be contained in a subsystem vessel made from materials such as austenitic (304L) and martensitic (EP-823 and HT-9) stainless steels. The structural materials used in this vessel will be subjected to welding operations and …

Steady State Stress In A Coated Infinite Half-Space Subjected To A Moving Load, Jason M. Cruthirds

Theses and Dissertations

This research investigates the use of coatings to mitigate the stress distribution into an infinite half-space. High energy impact phenomenon at velocities exceeding the speed of sound is an important area of interest to the Air Force Research Laboratory. Holloman Air Force Base's High Speed Test Track sustains significant damage due to this phenomenon. In this thesis, the track system and coating are modeled analytically with equations of motion in terms of linear displacements. Coating thickness and material properties of epoxy or polymer laminates are investigated to understand their affect of stress distribution in the rail. An analytic solution is …

Fatigue Behavior Of A Functionally-Graded Titanium Matrix Composite, Scott R. Cunningham

Theses and Dissertations

Functionally-graded Titanium Matrix Composites are an attempt to utilize the high-strength properties of a titanium matrix composite with a monolithic alloy having the more practical machining qualities. This work studied the mechanical characteristics of the joint region as a first step toward future evaluation of this material. The scope of this effort involved testing under monotonic tension and fatigue loading conditions. Mechanical properties and cyclic behavior were evaluated for the joint area and then compared to those of the parent materials. The results of this study found that the strength of the transition region was slightly higher than the unreinforced …

Analysis Of Computational Methods For The Treatment Of Material Interfaces, Minh C. Nguyen

Theses and Dissertations

Rocket sled tests at the Air Force Research Laboratory's Holloman High Speed Test Track frequently approach velocities where gouging development becomes the limiting factor to achieving higher operating velocities. Direct observation of the gouging process is not possible so computational modeling is necessary to study the phenomenon. Since gouging development is dependent on the impact surface conditions, the method used to model material interfaces directly affects the accuracy of the solution. Three methods are available in the hydrocode CTH to handle material interfaces: 1) materials are joined at the interface, 2) a frictionless slide line is inserted, and 3) a …

Creep-Rupture Behavior Of An Oxide/Oxide Ceramic Matrix Composite At Elevated Temperatures In Air And Steam Environments, Lee B. Harlen

Theses and Dissertations

Oxide/oxide ceramic matrix composites (CMCs) are being considered for applications such as jet engine combustion chambers and afterburner flaps. Nextel™ 720/A (N720/A), an oxide/oxide CMC with an alumina matrix and no interphase at the fiber-matrix interface, was developed specifically to provide improved long-term properties and performance at 1200°C. This study focused on experimental investigation of creep behavior of N720/A [0/90] at elevated temperatures in laboratory air and in 100% steam environment. Monotonic tensile tests to failure were performed at 23, 1200, and 1330°C. Ultimate tensile strength (UTS) values were established and monotonic stress-strain curves were produced. Creep-rupture tests at 1200°C …

Tensile Stress Rupture Behavior Of A Woven Ceramic Matrix Composite In Humid Environments At Intermediate Temperature, Kevin J. Larochelle

Theses and Dissertations

Stress rupture tests on the Sylramic^TM fiber with an in-situ layer of boron nitride, boron nitride interphase, and SiC matrix ceramic matrix composite were performed at 550°C and 750°C with 0.0, 0.2, or 0.6 atm partial pressure of water vapor, pH₂O. The 550°C, 100-hr strengths were 75%, 65% and 51% of the monotonic room temperature tensile strength, respectively. At 750°C, the strengths were 67%, 51%, and 49%, respectively. Field Emission Scanning Electron Microscopy analysis estimated the total embrittlement times for 550°C with 0.0, 0.2, and 0.6 atm pH₂O were >63 hrs, >38 hrs, and between …

An Investigation Of A Simplified Gouging Model, Gregory S. Rickerd

Theses and Dissertations

Gouging is a type of structural failure that becomes important when two metals slide against each other at velocities in the range of 1.5 kilometers per second. A computer model has previously been used to model the development of gouging at the Holloman High Speed Test Track. This model has not been experimentally verified to be correct, due to the complexity of the model. This research develops a simplified model that can be experimentally verified. The computer program utilized in this research was studied to determine the most appropriate options to use in simulations. This was accomplished by modeling a …

Anodic Polarization Behaviors Of Carbon Steel In Bicarbonate Solution, Jing-Mao Zhao, Yu Zuo

Journal of Electrochemistry

The anodic polarization curves of mild steel were measured in sodium bicarbonate solution of various concentrations, and the surface products were analyzed by XPS. Two anodic current peaks and two passive zones are observed in all the curves. When HCO₃^- ions concentration is below 0.1mol/L, the two peaks are so close that the first passive zone is difficult to be observed. When HCO₃^- ions concentration is above 0.1 mol/L, the first peak appears clear, while the second becomes smaller. The XPS results indicate that the out layer of film formed at a higher potential is mainly …

Preparation And Characterization Of Lini0.85Co0.10(Timg)0.025O2 As Cathode Materials For Lithium-Ion Batteries, Xian-Jun Zhu, Hong-Hao Chen, Hui Zhan, Dai-Ling Yang, Yun-Hong Zhou

Journal of Electrochemistry

Cathode material of LiNi_0.85Co_0.10(TiMg)_0.025O₂ were prepared by solid state reaction at 725℃ for 24 h from LiOH·H₂O, Ni₂O₃, Co₂O₃, TiO₂ and Mg(OH)₂ under flowing oxygen, and were characterized by TG-DTA, XRD, SEM and electrochemical tests. Effort to simultaneously doped LiNiO₂ with Co-Ti-Mg has been tried to improve the cathode performance. The results show that co-doping definitely has a large beneficial effect in increasing the capacity (182.7mAh/g of the first discharge capacity for  LiNi_0.85Co_0.10(TiMg)_0.025O_{2 …}

Corrosion Resistance For Tio2 Thin Films Coated 316l Stainless Steel In The Nacl Solution, Guang-Xia Shen, Yi-Cong Chen, Chang-Jian Lin

Journal of Electrochemistry

The nano-TiO₂ thin films have been deposited on the 316L stainless steel by sol-gel and the dip-coating methods. Hydrothermal post-treatment leads to crack-free coatings. Meanwhile, the surface structure and properties are optimized. Surface morphology, structure and properties are characterized by XRD, and SEM technologies. The results have shown that the surface of coatings is porous, uniform and orderly, the particle diameters are in the range of 15~18 nm and the pores are about 4~8 nm and TiO₂ is anatase. The results of electrochemical measurements show that in the NaCl solution with pH ≥ 2 and concentration below 1mol/L, …

Corrosion Behavior Of Mg2-XLaXNi And Mg2-XCeXNi Hydrogen Storage Alloy, Hai-Chang Zhang, Hua-Bin Yang, Jun-Hong Wang, Zuo-Xiang Zhou

Journal of Electrochemistry

The corrosion behavior of Mg-base hydrogen storage alloys has been investigated by potentiodynamic polarization and EIS. The results showed that the corrosion current density (i_corr) and the electrochemical polarized resistance of Mg_2-xCe_xNi alloys decreased with x increase, while i_corr of Mg_2-xLa_xNi alloys increased and the electrochemical polarized resistance of Mg_2-xLa_xNi alloys increased first, then decreased with x increase. SEM results showed that the surface of Mg_1.85Ce_0.15Ni alloy was relatively even while the surface of Mg_2-xLa_xNi alloy had …

A Study Of Metal Borides As High Capacity Anode Materials For Aqueous Primary Batteries, Ya-Dong Wang, Xin-Ping Ai, Han-Xi Yang

Journal of Electrochemistry

The transition metal borides VB₂ and TiB₂ were tested as high capacity anode materials and their electrochemical behaviors were studied by cyclic voltammetry and discharge measurements. The experimental results indicated that transition metal borides VB₂ and TiB₂ electrodes can deliver exceptionally high discharge capacity of over 3100 mAh/g and 1 600 mAh/g respectively, corresponding to 11- and 6-electron oxidation reaction, although their parent elements V, Ti and boron, are almost completely electrochemically inert. The different electrochemical activitis were probably due to the electrochemical activation of boron, which clamp the potential to passivation for Ti and activity …

Electrochemical Performance Of Gel Polymer Electrolyte Prepared By Thermal Initiating Polymerization Of Acrylates, Jin-Dan Piao, Li-Xia Yuan, Xin-Ping Ai, Han-Xi Yang, Yu-Liang Cao

Journal of Electrochemistry

A gel polymer electrolyte was prepared by thermal initiating polymerization of the acrylates in the EC/EMC/DMC electrolyte solution at 100℃. The LiCoO₂/MCMB polymer cells were assembled and their electrochemical properties were evaluated at various charge-discharge rate and temperatures. The ionic conductivity of the polymer electrolyte containing 85wt.% liquid electrolyte is around 3.2×10^-3 S·cm^-1  at 20℃ and 5.6×10^-4 S·cm^-1 at -30℃ respectively. The gel polymer electrolyte has good electrochemical stability up to 4.5V versus Li/Li⁺.The first charge-discharge efficiency of the polymer cell at 0.2C rate is almost 92.1%. The discharge capacity of the …

Application Of Carbon Paste Electrode On The Electrogenerative-Leaching Process Of Sulfide Minerals, Shao-Fen Wang, Zheng Fang, Yun-Yan Wang

Journal of Electrochemistry

The cyclic voltammetry curves of sulfide mineral electrodes or corresponding carbon paste electrodes in NaCl electrolytes have been obtained in this study. The experimental results indicate that acetylene black (revealed) the electro-catalytic propertyin the electrogenerative-leaching process of sulfide minerals. The output currentand potential of carbon paste electrodes were increased to some degrees while the activation energies were lower.