Catalytic Activities Of Electrochemically Dealloyed Pt(Pd)-Cu Catalysts For Oxygen Reduction Reaction,
2012
Stanford Synchrotron Radiation Light Source, SLAC National Accelerator Laboratory, California 94025, USA;
Catalytic Activities Of Electrochemically Dealloyed Pt(Pd)-Cu Catalysts For Oxygen Reduction Reaction, Rui-Zhi Yang, Strasser Peter, Toney Michael
Journal of Electrochemistry
The electrochemically dealloyed Pt(Pd)-Cu catalysts were prepared by electrochemical dealloying of Cu3Pt(Pd) and their catalytic activities toward oxygen reduction reaction (ORR) were studied in 0.1 mol·L-1 HClO4 . solutions. The structural features of the dealloyed Pt(Pd)-Cu were revealed by synchrotron-based anomalous X-ray diffraction (AXRD) and surface X-ray scattering (SXS) at an atomic scale. We established a relationship between the structure and the catalytic activity by comparing the ORR activity and the structure of dealloyed Cu3Pt nanoparticles with similarly dealloyed Cu3Pt thin films and Cu3Pt(111). The enhancement in the activity of …
Electrocatalytic Oxidation Of Ethanol On Ni-P-Tio2 Composite Coating Electrodes,
2012
Faculty of Light Industry and Chemical Engineering, Guangdong University of Technology,Guangzhou 510006,China
Electrocatalytic Oxidation Of Ethanol On Ni-P-Tio2 Composite Coating Electrodes, Guang-Hui Hu, Hai-Xia Zeng, Zhi-Gang Wei, Zhan-Chang Pan, Shu-Guang Xie, Yan-Di Zou
Journal of Electrochemistry
The Ni-P-TiO2 composite coating electrodes with different contents of TiO2 particulates were prepared by electroless plating technique from Ni-P plating bath containing TiO2 powders on brass. Cyclic voltammetry, linear sweep voltammetry (LSV), chronoamperometry and electrochemical impedance spectroscopy (EIS) were used to test the electrochemical performance of Ni-P-TiO2/Cu electrodes. It was indicated that the Ni-P-TiO2/Cu electrodes exhibited very strong electrocatalytic activity toward the oxidation of ethanol in alkaline medium at ambient temperature. The electrocatalytic activity of ethanol oxidation on the Ni-P-TiO2 electrodes depended on the amounts of TiO2 in the coatings. The …
Electrocatalytic Study Of Pseudomonas Aeruginosa Bte-1 Strain,
2012
Jiangsu provincial Key Laboratory of Environmental Materials and Engineering, and Department of Chemistry and Chemical Engineering, Yangzhou University, Yangzhou 225002, Jiangsu,China;
Electrocatalytic Study Of Pseudomonas Aeruginosa Bte-1 Strain, Ping Zhou, En-Ren Zhang, Li Zhou, Guo-Wang Diao, Jun-Le Niu
Journal of Electrochemistry
The aim of the present study is to investigate the electrocatalytic activity of electricity-producing Pseudomonas aeruginosa BTE-1 strain under anaerobic conditions. Pseudomonas aeruginosa BTE-1 was inoculated into anaerobic three-electrode electrochemical cells, and the electrocatalytic activity was measured at poised potentials. HPLC and cyclic voltammetry were used to detect potential electron mediators in solutions. Experimental results showed that no detectable pyocyanine was excreted by P. aeruginosa BTE-1 strain in the anaerobic electrochemcial cells, and P. aeruginosa BTE-1 exhibited direct electrocatalytic activity through the formation of biofilm on the electrode surface which was induced by the electron transfer from the cells of …
Synthesis And Electrochemical Performance Of Xlifepo4·Yli3V2(Po4)3 Composites,
2012
China Iron and Steel Research Institute Group, Beijing 100081, China;Beijing Central Press Union Technology Co LTD., Beijing 100041, China;
Synthesis And Electrochemical Performance Of Xlifepo4·Yli3V2(Po4)3 Composites, Ping-Ping Ma, Zhi-Jian Liu, Jian-Hua Xia, Yu Chen, Pu Hu, Zhi-Chao Lu, Ding-Guo Xia
Journal of Electrochemistry
A series of xLiFePO4·yLi3V2(PO4)3 composites were systematically synthesized through solid state reactions by variations in the proportions of LiFePO4 and Li3V2(PO4)3. The properties of the prepared compounds were investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical measurements. The capacity of 162.7 mAh/g at 0.2 C rate was obtained with the relatively good cycle stability and good conductivity for 0.95LiFePO4·0.05Li3V2(PO4)3 due to more uniformed distributed and smaller particle sizes.
Progress And Perspective Of Fuel Cell Technology,
2012
Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, Liaoning, China;
Progress And Perspective Of Fuel Cell Technology, Ming Hou, Bao-Lian Yi
Journal of Electrochemistry
Fuel cell, a clean and high-efficiency electrochemical power source, has being paid much attention worldwide recent years. In this paper, the progress and perspective of fuel cell technology are elucidated in detail. Fuel cells have been applied in some special fields such as spacecraft, shuttle and submarines. However, in the areas of transportation, stationary station and portable power source, fuel cells are still under demonstration due to the durability and cost problems. The reliability and surrounding survivability of fuel cells should be enhanced in the special application. Meanwhile, the durability and cost of fuel cells are the main issues to …
Development Of Tailor-Designed Gold-Platinum Nanoparticles Binary Catalysts For Efficient Formic Acid Electrooxidation,
2012
The British University in Egypt
Development Of Tailor-Designed Gold-Platinum Nanoparticles Binary Catalysts For Efficient Formic Acid Electrooxidation, Islam M. Al-Akraa Dr, Ahmad M. Mohammad Prof, Mohamed S. El-Deab Prof, Bahgat E. El-Anadouli Prof
Chemical Engineering
The modification of a glassy carbon (GC) electrode with platinum (PtNPs) and gold (AuNPs) nanoparticles is targeted to fabricate efficient anodes for the electrooxidation of formic acid (FA). A proper adjustment of the deposition sequence of PtNPs and AuNPs could eventually enhance the electrocatalytic activity of the electrode in such a way that suppresses the CO poisoning effect during FA oxidation. The highest catalytic activity is obtained at the Au/Pt/GC electrode (with PtNPs firstly deposited on the GC electrode followed by AuNPs). This superb enhancement is quantified by comparing the relative ratio of the direct vs. the indirect oxidation peaks …
Investigation Of Carbon Corrosion Resistance Of Cnt Containing Electrode,
2012
University of South Carolina - Columbia
Investigation Of Carbon Corrosion Resistance Of Cnt Containing Electrode, Diana Larrabee, William A. Rigdon, Eli Mcpherson, Joshua Sightler, Xinyu Huang
Faculty Publications
Carbon support corrosion is one of the major degradation mechanisms of polymer electrolyte membrane (PEM) fuel cell. Carbon oxidation occurs in PEM electrode and is accelerated at high potential created by adverse operating conditions and improper distribution of reactants and products [1, 2, 3]. Carbon corrosion can lead to the thinning of the electrode layer and severe performance degradation. The detailed mechanisms of carbon support corrosion induced performance loss are still not fully understood; it is believed that the following events contribute to the decay: (1) structural collapse of the porous electrode due to the loss of carbon; (2) carbon …
Application Of Electrospinning Technique In The Fabrication Of A Composite Electrode For Pemfc,
2012
University of South Carolina - Columbia
Application Of Electrospinning Technique In The Fabrication Of A Composite Electrode For Pemfc, Joshua Sightler, Eli Mcpherson, William A. Rigdon, Xinyu Huang
Faculty Publications
The Pt/C catalysts were mixed with carbon nanotube (CNT), Nafion™ dispersion and a fiber former, polymer poly-acrylic acid (PAA), to form an ink. The ink was deposited onto aluminum foil attached to a rotating collector via an electrospinning process. The ink composition, mixing procedure, and the E-spin parameters were studied for producing a uniform nanofiber mat on the aluminum substrate. The fiber-mat containing active catalyst ingredients was heat treated and decal transferred onto a Nafion membrane to form a membrane electrode assembly (MEA).
Application Of Thin Film Analysis Techniques And Controlled Reaction Environments To Model And Enhance Biomass Utilization By Cellulolytic Bacteria,
2012
University of Kentucky
Application Of Thin Film Analysis Techniques And Controlled Reaction Environments To Model And Enhance Biomass Utilization By Cellulolytic Bacteria, Hsin-Fen Li
Theses and Dissertations--Chemical and Materials Engineering
Cellulose from energy crops or agriculture residues can be utilized as a sustainable energy resource to produce biofuels such as ethanol. The process of converting cellulose into solvents and biofuels requires the saccharification of cellulose into soluble, fermentable sugars. However, challenges to cellulosic biofuel production include increasing the activity of cellulose-degrading enzymes (cellulases) and increasing solvent (ethanol) yield while minimizing the co-production of organic acids. This work applies novel surface analysis techniques and fermentation reactor perturbations to quantify, manipulate, and model enzymatic and metabolic processes critical to the efficient production of cellulosic biofuels.
Surface analysis techniques utilizing cellulose thin film …
Microemulsion Preparation And Electrochemical Characterization Of Pt/C, Ptir/C Electrocatalysts,
2011
Institute of Fuel Cell, Shanghai Jiao Tong University, Shanghai 200240, China
Microemulsion Preparation And Electrochemical Characterization Of Pt/C, Ptir/C Electrocatalysts, Ya-Ping Zeng, Sheng Sui
Journal of Electrochemistry
The Pt/C electrocatalysts were prepared by three different systems and the PtIr/C electrocatalysts were prepared with four different Ir contents. The samples were characterized by X-ray diffraction (XRD), transmission electron microscope (TEM), cyclic voltammetry (CV), potentiostatic and potentiodynamic polarizations measurements. The experimental results confirmed that the electrocatalyst particles prepared by the microemulsion method were well distributed on XC-72R supports with the active particle sizes of 5～10nm and good electrocatalysts activity. The Pt85Ir15/C electrocatalysts showed the highest overall electrochemical activity in unitized regenerative fuel cell.
Electrochemical Properties Of Tungstogermanate And Electrocatalysis Of H2O2 On Gew11Co/P-Opd/Gc Electrode,
2011
Institute of Environmental and Analytical Sciences, College of Chemistry and Chemical Engineering, Henan liniversity, Kaifeng 475004, Henan, China
Electrochemical Properties Of Tungstogermanate And Electrocatalysis Of H2O2 On Gew11Co/P-Opd/Gc Electrode, Li-Li Zhu, Jian-Ying Qu, Jue Wang, Hao-Yue Feng
Journal of Electrochemistry
The electrochemical properties of Co-substituted trimeric tungstogermanate containing Keggin fragments were studied. Cyclic voltammograms revealed two couples of reversible redox peaks on glassy carbon (GC) electrode in acid solutions. They corresponded to two-electron reductions accompanying by the additions of four protons and three protons, respectively, both were controlled by adsorption. The differences in the peak potentials of 2-electron-4-proton and 2-electron-3-proton reactions were 31 mV and 35 mV, respectively..Furthermore, the tungstogermanate (GeW11Co) modified GC electrode with functionalization by poly(o-phenylenediamine) (P-oPD) was prepared readily by electropolymerization. The GeW11Co/P-oPD/GC electrode could electrocatalyze the reduction of hydrogen peroxide, which showed good stability and quick …
Preparation And Characterization Of The Lani0.6Fe0.4O3-δ Cathode For Intermediate Temperature Solid Oxide Fuel Cell,
2011
Institute of Fuel Cell, School of Mechanical Engineering, Shanghai jiaotong lniversity, Shanghai 200240,China
Preparation And Characterization Of The Lani0.6Fe0.4O3-δ Cathode For Intermediate Temperature Solid Oxide Fuel Cell, Hang Liu, Bo Huang, Xin-Jian Zhu
Journal of Electrochemistry
The LaNi0.6Fe0.4O3-δ as cathode material for intermediate temperature solid oxide fuel cell was prepared using a combustion synthesis technique. The X-ray diffraction (XRD) pattern showed that the single-phase LaNi0.6Fe0.4O3-δ perovskite could be obtained after heat treatment at 600°C. The TEM and SEM images of the synthesized powders revealed that the grains were 50-100nm. According to the electrochemical impedance spectra (EIS), the polarization resistance of the symmetric cell LaNi0.6Fe0.4O3-δ/ScSZ/LaNi0.6Fe0.4O3-δ sintered at 1050°C was the smallest (0.70Ω·cm2, 0.27Ω·cm2 …
Dynamic Modeling And Characteristic Analysis Of Proton Exchange Membrane Fuel Cell,
2011
Chongqing Automobile college, Chongqing University of Technology,Chongqing, 400054,China;
Dynamic Modeling And Characteristic Analysis Of Proton Exchange Membrane Fuel Cell, Qiu-Hong Jia, Ming Han, Bin Deng, Cai-Zhi Zhang
Journal of Electrochemistry
In this paper, a dynamic model of PEMFC is developed to estimate the dynamic performance of PEMFC by analyzing in detail the influence factors of voltage of PEMFC including various losses. The partial pressure of hydrogen and oxygen is obtained using the differential form of the ideal-gas equation in this model. The steady-state model is obtained by setting reasonable parameter values. The simulation results and experimental results have good consistency, which shows that the simulation model is correct, reasonable and effective. It analyzed the dynamic response characteristics of the output voltage and the partial pressure of hydrogen in condition of …
Indirect Electrochemical Reduction And Cotton Dyeing Process In Fe(Ⅲ)-Oxalate-Calcium Gluconate System,
2011
Key Laboratory of Scienee & Technology of Eco-Textile, Ministry of Education, Donghua Unversity, Shanghai 201620, China
Indirect Electrochemical Reduction And Cotton Dyeing Process In Fe(Ⅲ)-Oxalate-Calcium Gluconate System, Qing-Zhi Wang, Wei Wang
Journal of Electrochemistry
The electrochemical behavior and possible reaction mechanism in Fe(Ⅲ)-oxalate-calcium gluconate system were studied by cyclic voltammetry. The results showed that Fe(Ⅱ)-gluconate was the final reductant. The reduction time, the working voltage and the cathode area influenced the current efficiency. The high current efficiency of 89% for the indirect electrochemical reduction of Vat Scarlet R could be achieved with reduction time of 10 min, working voltage of 4 V and cathode area of 40 cm2 in Fe(Ⅲ)-oxalate-calcium gluconate system.
Preparation And Capacitance Characteristics Of Nickel Oxide Electrode With Mesh-Like Structure,
2011
College of Petrochemical Technology, Lanzhou University of Technology, Lanzhou 730050, China
Preparation And Capacitance Characteristics Of Nickel Oxide Electrode With Mesh-Like Structure, Hui Xu, Zhen-Jun Peng, Dong-Hong Guo, Jun-Ling Li
Journal of Electrochemistry
The mesh-like structure of NiO electrode was obtained by first preparing the precursors via hydrothermal process using nickel sulfate and carbamide as reactants, sodium hexametaphosphate as a surfactant, and followed by calcination of the precursors at 400 ℃. The structure, morphology and capacitance characteristics of NiO electrode were characterized by XRD, SEM and constant current charge-discharge testing techniques. The effects of hydrothermal temperatures on the electrochemical properties of NiO electrode were investigated. The results showed that the better property of nickel oxide was obtained when the mole ratio of nickel to urea was 1:4 and the hydrothermal temperature was 140℃. …
Evaluation Of Cathode Materials For Low Temperature (500-700c) Solid Oxide Fuel Cells,
2011
University of Connecticut - Storrs
Evaluation Of Cathode Materials For Low Temperature (500-700c) Solid Oxide Fuel Cells, Alexander M. Lassman
Master's Theses
Solid oxide fuel cells (SOFC) have gained a great deal of interest, due to their potential for high efficiency power generation and ability to utilize hydrogen fuel, as well as various hydrocarbon-based fuels. A recent trend in SOFC development has been towards lower operating temperatures (500-700°C), which can substantially reduce the cost and complexity of the system. This thesis presents an investigation into state of the art Ba- and La- based cathode materials for use in low temperature (500-700°C) solid oxide fuel cells.
Synthesis of A-site deficient [A=0.97] Ba0.5Sr0.5Co0.8Fe0.2O3 (BSCF) was …
Electrochemical Performance Of Tin Dioxide/Carbon Xerogel Composites As Anode Materials For Lithium-Ion Batteries,
2011
State Key Laboratory of Physical Chemistry of Solid Surfaces, Department of Chemistry,College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005, Fujian, China;
Electrochemical Performance Of Tin Dioxide/Carbon Xerogel Composites As Anode Materials For Lithium-Ion Batteries, Xiao-Jing Liu, Lin-Lin Qin, Yi-Ning Shi, Ming-Sen Zheng, Quan-Feng Dong
Journal of Electrochemistry
The tin dioxide/carbon xerogel composites were synthesized by using vacuum infiltration method. Structural characterization and morphology of the composites were investigated by using XRD, TEM and SEM techniques. BET test was performed to determine the pore size distributions of carbon xerogels and the composites. The results showed that the nano-sized SnO2 particles (5~10 nm) were encapsulated in the pores of carbon xerogels. During the electrochemical tests the SnO2 in the composites exhibited capacity retention of 61.9% after 100 cycles of charge-discharge tests at 100 mA/g.
Synthesis Of Limnpo4/C Used As Cathode Material For Lithium Ion Batteries,
2011
Dalian University of Technology School of Chemical Engineering School of Petrochemical Engineering, Dalian,116024;
Synthesis Of Limnpo4/C Used As Cathode Material For Lithium Ion Batteries, Xin Yang, Xue-Wu Liu, Gui-Chang Liu, Zhi-Cong Shi, Xin Li, Guo-Hua Chen
Journal of Electrochemistry
The LiMnPO4/C composites were prepared using a solid-state reaction with addition of the resorcinol formaldehyde resin as the carbon source. The effects of reaction temperature and time on the crystal structure, morphology and electrochemical properties of the LiMnPO4/C composites were investigated. The results show that the best performance was achieved with the LiMnPO4/C composites synthesized at 600 oC for 12 h which had the particle sizes about 100~200 nm. The initial discharge capacities were 121.6 mAh·g-1 at 0.02C, 110 mAh·g-1 at 0.1C and more than 60 mAh·g-1 at 1C. An …
Synthesis And Electrochemical Behaviors Of Li2Coxmn1-XSio4 As A Cathode Material For Lithium-Ion Batteries,
2011
State Key Laboratory of Physical Chemistry of Solid Surfaces , College ofChemistry and ChemicalEngineering,Xiamen University, Xiamen 361005,Fujian, China
Synthesis And Electrochemical Behaviors Of Li2Coxmn1-XSio4 As A Cathode Material For Lithium-Ion Batteries, Lin Wang, Dong-Ping Lv, Yong Yang
Journal of Electrochemistry
We have successfully synthesized Li2CoxMn1-xSiO4/C (x=0, 0.1, 0.3, 0.5, 1)/C composites using hydrothermal assisted sol-gel process and ball-milling method. The results of X-ray diffraction show that the solid solutions of Li2CoxMn1-xSiO4 can be achieved when x≤0.3. The initial capacities increase from 70 mAh·g-1 of Li2MnSiO4/C to 105 mAh·g-1 of Li2Co0.3Mn0.7SiO4/C. Cyclic Voltammetry (CV) curves show that the replacement of Mn with Co can reduce the electrochemical polarization, making the insertion-extraction reaction …
Applied Control Strategies At A Cogeneration Plant,
2011
University of Connecticut
Applied Control Strategies At A Cogeneration Plant, Joseph William Burns
Master's Theses
The purpose of this paper is to demonstrate the effectiveness of “classical strategies for dynamic control” on authentic cogeneration processes. These strategies are applied to several processes at the University of Connecticut’s cogeneration plant. Case studies of their applications are presented in this paper. Strategies that are applied include the following:
1) The classical SISO feedback structure
2) The First Order Plus Dead Time (FOPDT) process model
3) The Internal Model Control (IMC) correlations for PI controller tuning
4) Static feed forward with feedback trim
5) Cascade Control