Mechanics of Materials Commons^™

Microstructural Characterization Of Overaged Gtd-111 Hp Turbine Buckets, Oscar Quintero

Open Access Theses & Dissertations

Superalloys are metallic materials that exhibit excellent mechanical strength and creep resistance at high temperatures. They have good surface stability and are corrosion resistant. Superalloys are mostly used in the aerospace industry, gas turbine engines and blades (hot zones of gas turbines), and where extreme heat is encountered. The focus of this research was on the GTD-111 Ni-base superalloy, which is a General Electric (GE) proprietary superalloy mostly used in gas turbine blades with the form of high pressure or first stage buckets. This alloys features better mechanical properties, creep resistance, and a higher stress rupture temperature than the commonly …

Impacting Testing Of High Temperature Ceramics Through The Use Of A Vitiated Heater For Hot And Cold Fire Collisions, Adrian Trejo

Open Access Theses & Dissertations

Material testing is a crucial step during the design process as particular materials serve as safety and life saving conditions. In this study, a MoSi2 is chosen as the target specimen to undergo impact under high temperatures. An impact apparatus is designed and constructed for the purpose of propelling alumina particles at high velocities. A nozzle using compressed nitrogen gas is used to fire the particle at the desired velocities. Due to the possibility of thermal shock occurring at higher temperatures, a separate nozzle utilizing vitiation heating is designed to fire the particle at equally higher temperatures to prove the …

Failure Analysis And Materials Characterization Of Hip Implants, Amanda Marie Bastidos

Open Access Theses & Dissertations

This research focused on the microstructural characterization and failure analysis of hip implant components. The main hip components analyzed were the femoral heads and the ultra-high molecular weight polyethylene (UHMWPE) liners. Previous research has shown that hip implants tend to fail by the PE liners due to adhesive and abrasive wear, delamination, and third body particles (metals, ceramics, and PE). The methods and procedures for analyzing the said failures consisted of non-destructive and destructive evaluations. Non-destructive evaluations included of techniques such as visual characterization and dye penetrant inspection (DPI)-which displayed macroscopic surface details and presented initial clues as to the …

Observed Superspin-Glass Behavior In Ni0.5zn0.5fe2o4 Nanoparticles, Antony Adair

Open Access Theses & Dissertations

In this investigation we seek to identify the magnetic behavior of Ni0.5Zn0.5Fe2O4 nanoparticles though AC-susceptibility and DC-magnetization measurements. Powder x-ray diffraction was performed to determine the purity and average diameter ( ~ 9nm) of the particles. Aditionally, structure was confirmed by comparison through the International Centre for Diffraction Data's Powder Diffraction File [52] (PDF # 08-0234).

Zero-field cooled and field cooled DC magnetization measurements (bifurcation and blocking temperature), as well as M(H) hysteresis (below and above the blocking temperature) lead us to initially suggest that the material may in fact be superparamagnetic. However, further investigation of the real AC susceptibility …

Temperature-Induced Phenomena In Systems Of Magnetic Nanoparticles, Abdul Wazed Bhuiya

Open Access Theses & Dissertations

Magnetic nanoparticle ensembles have received a lot of attention, stemming in part from their current and potential applications in biomedicine and in the development of high-density magnetic storage media. Key to the functionality of these systems are microscopic structures and mechanisms that make them exhibit unique properties and behave differently from their bulk counterparts.

We studied microscopic structures and processes that dictate macroscopic properties, behavior and functionality of magnetic nanoparticle ensembles. As the temperature T strongly influences the magnetic behavior of these systems, we studied temperature dependent magnetic properties using AC-susceptibility and DC-magnetization measurements carried out over a broad range …

Microstructural Characterization And Heat Treatment Of A-286 Turbine Buckets, Christopher Michael Bradley

Open Access Theses & Dissertations

A-286 is an iron-based superalloy used extensively in land-based gas turbines for 2nd stage (low pressure) buckets and 1st and 2nd stage wheels. Although A-286 may appear to some as just another austenitic stainless steel, its elevated temperature properties are attributed to ' precipitate structures, effective distributions of alloy carbides in the forms of M23C6, M6C and MC, and solid solution strengthening. Unfortunately over the course of these components service lives microstructural degradation develops in the form of η-phase formation. The presence of η-phase, especially in large quantities, can have a negative effect on stress rupture properties. Resistance to creep …

Spectroscopic Characterizations Of Organic/Inorganic Nanocomposites, Jayesh Rasikalal Govani

Open Access Theses & Dissertations

Inorganic potassium dihydrogen phosphate (KDP) is widely known for its value as a nonlinear optical material. In this study, pure and l-arginine-doped KDP single crystals were grown by the slow solvent evaporation technique and further subjected to infrared absorption and Raman studies for the confirmation of chemical group functionalization and possible bonding between the organic and inorganic materials. The appearance in the infrared absorption spectra of additional vibrational lines, which mostly originate from disturbed N-H, C-H, and C-N bonds of the l-arginine-doped salt, confirm the interaction between KDP and the organic material. This affirmation is supported by more evidence from …

Effects Of Build Orientation, Aging, And Pre-Conditioning On Mechanical Properties For Stereolithography-Manufactured Astm Type I Specimens Using A Design Of Experiments Approach, Karina Puebla

Open Access Theses & Dissertations

With industry's growing focus on the rapid manufacturing (RM) of end-use products, rapid prototyping (RP) or layered manufacturing (LM) machines that were originally designed to build prototypes may now be required to build functional end-use products. To successfully accomplish the transition, the available materials utilized in RP must provide the performance required for RM. The specific technology used must also be capable of producing repeatable and reproducible parts in regards to mechanical and dimensional properties.

A design of experiments approach was performed to determine the effects of build orientation, aging, and pre-conditioning on the mechanical properties. To perform the investigations, …

Computational Modeling Studies Of The Structures And Properties Of Organotin(Iv) And Stannyl-Thioether Systems With Comparisons To X-Ray Crystallography, Michelle R. Stem Joseph

Open Access Theses & Dissertations

Controlling the toxic effects of organotin(IV) compounds involves engineering the structure of the molecules to optimize their properties. Molecular engineering, coupled with improved capabilities to generate reliable computational optimization models (COMs), will enable researchers to have greater success at harnessing the highly specific cytotoxicity of organotins. For example, as the thio_n ligand phenyl groups were replaced with Cl atoms, the S-Sn intramolecularity was strengthened, the bond distance decreased, and the stannyl tetrahedral structure was deformed from its triphenyl conformation. With each substitution, conformation deformations lowered the damaging bioactivity levels of thio_n. Bonding various ligands to organotin(IV) compounds …

High Temperature Oxidation Behavior Of Nb-20mo-15si-5b-20cr Alloy, Julieta Angelica Ventura

Open Access Theses & Dissertations

Materials for high temperature applications, such as jet engines, gas turbines and turbine blades, require a balanced combination of physical and chemical properties to withstand the aggressive environments in which they are utilized. Some of the properties required are high strength, low density, high melting point and good oxidation resistance at elevated temperatures [1-3]. For this reason, the microstructure and oxidation behavior of the Nb-20Mo-15Si-5B-20Cr alloy (at.%) has been studied as a potential candidate to replace Nickel-based alloys currently used in the aerospace industry.

Short term oxidation (STO) and long term oxidation (LTO) studies have been performed in air for …

Exploring Poly(Ethylene Glycol) As A Suitable Material For Peripheral Nerve Regeneration Scaffolds Manufactured By Stereolithography, Nubia Zuverza

Open Access Theses & Dissertations

One of the challenges in tissue engineering is to have spatial and temporal control over the biological elements within a scaffold used to guide regeneration for example of transected nerves. Some of the physical and chemical characteristics to regulate include incorporation of bioactive domains and release of chemical signals. This study presents the use of stereolithography (SL) to incorporate localized domains for cell adhesion in addition to include releasable nerve growth factor (NGF) in the process of building poly(ethylene glycol)diacrylate (PEGda) hydrogel scaffolds. Besides providing sites for cell attachment, an ideal nerve guidance conduit (NGC) should be able to release …

The Role Of Silicon Content On Environmental Degradations Of T91 Steels, Ajit K. Roy, D. Maitra, Pankaj Kumar

Mechanical Engineering Faculty Research

T91 grade steels showed a gradual enhancement in tensile ductility at ambient temperature due to an increase in Si content from 0.5 to 2.0 weight percent (wt.%). However, the ultimate tensile strength was reduced only above 1.5 wt.% Si. The corrosion potential became more active in an acidic solution with increasing temperature. The cracking susceptibility in a similar environment under a slow-strain-rate (SSR) condition was enhanced at higher temperatures showing reduced ductility, time to failure, and true failure stress. Cathodic potentials applied to the test specimens in SSR testing caused an enhanced cracking tendency at 30 and 60°C, suggesting hydrogen …

Tensile Deformation Of A Nickel-Base Alloy At Elevated Temperatures, Ajit K. Roy, Anand Venkatesh, Vikram Marthandam

Mechanical Engineering Faculty Research

The results of tensile testing involving Waspaloy indicate that the failure strain was gradually reduced at temperatures ranging between ambient and 300 °C. Further, serrations were observed in the engineering stress versus strain diagrams in the temperature range of 300-600 °C. The reduced failure strain and the formation of serrations in these temperature regimes could be the result of dynamic strain aging of this alloy. The extent of work hardening due to plastic deformation was reduced at temperatures above 300 °C. A combination of ductile and intergranular brittle failures was seen at temperatures above 600 °C. γ′ was detected at …

Development Of Low Temperature Alpha Alumina Coatings By Ac Magnetron Sputtering, Andrew Cloud

Mechanical Engineering Undergraduate Honors Theses

Alpha-phase aluminum oxide thin films were created using an Isoflux ICM-10 dual target inverted cylindrical magnetron sputtering system using mid-frequency AC power supplies. Alpha alumina films were deposited at a magnetron power of 6 kW, 50% oxygen partial pressure by volume, and -35 V DC bias. Film thickness, substrate material, and position and orientation within the deposition chamber were varied. To ensure the deposition conditions are suitable for alloys, the substrate temperature was measured using temperature indicating liquids. The experimental results, supported by Explicit Euler numerical analysis, revealed a steady state temperature of ~480°C at 6kW. Transmission electron microscopy (TEM) …

Stereolithography Of Poly(Ethylene Glycol) Hydrogels With Application In Tissue Engineering As Peripheral Nerve Regeneration Scaffolds, Karina Arcaute

Open Access Theses & Dissertations

In recent years, rapid prototyping (RP) technologies initially developed to create prototypes prior to production for the automotive, aerospace, and other industries, have found applications in tissue engineering (TE). Several different RP technologies are being used to fabricate biocompatible 3D structures with controlled micro- and macro-scale characteristics. The focus of this research was to explore the capabilities of the RP technology, stereolithography (SL), for creating complex, 3D scaffolds with applications in TE using a photocrosslinkable biopolymer, poly(ethylene glycol) (PEG). The primary objective was to create an implantable multi-lumen nerve guidance conduit (NGC) for the regeneration of peripheral nerves.

Studies of …

A Study Of The Interaction Of Thioindigo Dye, With Several Inorganic Host Materials, Alejandra Ramirez

Open Access Theses & Dissertations

Maya Blue has been the focus of numerous studies and is believed to be a mixture of palygorskite clay and indigo dye.^1,2 Several derivatives of this pigment have been developed with intriguing properties. For instance, the dye thioindigo reacts with the palygorskite clay to exhibit a broad range of colors from red to blue under UV-Vis excitation. Based on FT-Raman and computer simulation, previous work performed in our group could relate indigo and thioindigo interaction to the aluminum sites in the framework. super>3,4

The work performed with other inorganic host materials such as, layer structures and zeolites have …

Microstructures And Viscoelastic Properties Of Anisotropic Magnetorheological Elastomers, Lin Chen

Articles

The microstructures and viscoelastic properties of anisotropic magnetorheological elastomers were investigated in this paper. The measurement results show that their mechanical properties are greatly dependent on the magnetic flux density applied in preparation. A finite-column model was proposed to describe the relations between the microstructures and the viscoelastic properties. The simulation results agree well with the experimental results.

Investigation On Magnetorheological Elastomers Based On Natural Rubber, Lin Chen

Articles

Magnetorheological Elastomers (MR Elastomers or MREs) are a kind of novel smart material, whose mechanical, electrical, magnetic properties are controllable under applied magnetic fields. They have attracted increasing attentions and broad application prospects. But conventional MREs are limited to wide applications because their MR effects and mechanical performances are not high enough. This paper aims to optimize the fabrication method and to fabricate good natural rubber based MREs with high modulus by investigating the influences of a variety of fabrication conditions on the MREs performances, such as matrix type, external magnetic flux density, and temperature, plasticizer and iron particles. Among …

Influence Of Van Der Waals Forces On Increasing The Strength And Toughness In Dynamic Fracture Of Nanofibre Networks: A Peridynamic Approach, Florin Bobaru Ph.D.

Department of Engineering Mechanics: Faculty Publications

The peridynamic method is used here to analyse the effect of van der Waals forces on the mechanical behaviour and strength and toughness properties of three-dimensional nanofibre networks under imposed stretch deformation. The peridynamic formulation allows for a natural inclusion of long-range forces (such as van der Waals forces) by considering all interactions as ‘long-range’. We use van der Waals interactions only between different fibres and do not need to model individual atoms. Fracture is introduced at the microstructural (peridynamic bond) level for the microelastic type bonds, while van der Waals bonds can reform at any time. We conduct statistical …

Effects Of Polishing Shot-Peened Surfaces On Fretting Fatigue Behavior Of Ti-6al-4v, Kasey S. Scheel

Theses and Dissertations

The research of this thesis was done to investigate the effects of polishing a shot-peened specimen of Ti-6Al-4V on the fretting fatigue life of that specimen. The shot-peening process, though one of the most beneficial techniques in prolonging fretting fatigue life, creates a textured surface that may lead to problems on the micro level. This research was done in an attempt to further improve the peening process by examining the effects of another surface treatment to be used in conjunction, surface polishing. The rough peened surface may contain abrupt changes in surface geometry that act as stress risers, which are …

Wear Analysis Of Cu-Al Coating On Ti-6al-4v Under Fretting, Karl N. Murray

Theses and Dissertations

The effects of changes in the coefficient of friction (CoF) between the contacting surfaces on the fretting wear characteristics of Cu-Al coating on Ti-6Al-4V were investigated. This Cu-Al coating is part of a system that is applied to titanium turbine blades to reduce fretting at the interface. In the application, there is a solid lubricant that is added on top of the coating as an assembly aid and to help reduce the friction while the lubricant remains within the contact. Previous studies have researched the characteristics of the coating without the additional lubricant. In this study, liquid motor oil was …

Validation Of A Scaled Plane Strain Hypervelocity Gouging Model, Ronald J. Pendleton

Theses and Dissertations

The phenomenon of high speed impact is of great interest to the Air Force of Scientific Research and the Air Force Research Laboratory's Holloman High Speed test track. Rocket sled tests at the facility frequently are limited to velocities lower than actually attainable due to damage to the rail in the form of gouges. Direct observation of the gouging phenomenon is not currently possible. This leaves computational modeling as the only means to study the phenomenon. A computer model has previously been used to model the development of gouging at the Holloman High Speed Test Track. However, this model has …

Cracking Of Martensitic Alloy Ep-823 Under Controlled Potential, Ajit K. Roy, M. K. Hossain

Mechanical Engineering Faculty Research

The susceptibility of martensitic Alloy EP-823 to stress corrosion cracking was evaluated with and without an applied cathodic potential using the slow-strain-rate (SSR) testing technique. The magnitude of the applied potential was based on the corrosion potential determined by cyclic polarization. The cracking susceptibility in an acidic environment at different temperatures was expressed in terms of the true failure stress (ơ_f), time to failure (TTF), and ductility parameters, including percent elongation (%El) and percent reduction in area (%RA). The data indicate that the magnitudes of ơ_r, TTF, %El, and %RA were reduced due to cathodic charging. …

Tensile Properties Of Martensitic Stainless Steels At Elevated Temperatures, Ajit K. Roy, Srinivasarao R. Kukatla, Bhagath Yarlagadda, V. N. Potluri, Martin Lewis, Brendan O'Toole

Mechanical Engineering Faculty Research

Tensile properties of quenched and tempered martensitic alloys EP-823, HT-9, and 422 were evaluated at temperatures ranging from ambient to 600 °C as a function of three different tempering times. The results indicated that the yield strength, ultimate tensile strength, and the failure strength were gradually reduced with increasing temperature. The ductility parameters were enhanced at elevated temperatures due to increased plastic flow. However, the tempering time did not significantly influence these properties. The evaluation of the fracture surfaces by scanning electron microscopy revealed reduced cracking and dimpled microstructures, indicating enhanced ductility at higher testing temperatures.

Residual Stress Characterization In Structural Materials By Destructive And Nondestructive Techniques, Ajit K. Roy, Anand Venkatesh, Vikram Marthandam, Satish Dronavalli, Douglas P. Wells, Ronald Rogge

Mechanical Engineering Faculty Research

Transmutation of nuclear waste is currently being considered to transform long-lived isotopes to species with relatively short half-lives and reduced radioactivity through capture and decay of minor actinides and fission products. This process is intended for geologic disposal of spent nuclear fuels for shorter durations in the proposed Yucca Mountain repository. The molten lead-bismuth-eutectic will be used as a target and coolant during transmutation, which will be contained in a subsystem vessel made from materials such as austenitic (304L) and martensitic (EP-823 and HT-9) stainless steels. The structural materials used in this vessel will be subjected to welding operations and …

Tensile Stress Rupture Behavior Of A Woven Ceramic Matrix Composite In Humid Environments At Intermediate Temperature, Kevin J. Larochelle

Theses and Dissertations

Stress rupture tests on the Sylramic^TM fiber with an in-situ layer of boron nitride, boron nitride interphase, and SiC matrix ceramic matrix composite were performed at 550°C and 750°C with 0.0, 0.2, or 0.6 atm partial pressure of water vapor, pH₂O. The 550°C, 100-hr strengths were 75%, 65% and 51% of the monotonic room temperature tensile strength, respectively. At 750°C, the strengths were 67%, 51%, and 49%, respectively. Field Emission Scanning Electron Microscopy analysis estimated the total embrittlement times for 550°C with 0.0, 0.2, and 0.6 atm pH₂O were >63 hrs, >38 hrs, and between …

An Investigation Of A Simplified Gouging Model, Gregory S. Rickerd

Theses and Dissertations

Gouging is a type of structural failure that becomes important when two metals slide against each other at velocities in the range of 1.5 kilometers per second. A computer model has previously been used to model the development of gouging at the Holloman High Speed Test Track. This model has not been experimentally verified to be correct, due to the complexity of the model. This research develops a simplified model that can be experimentally verified. The computer program utilized in this research was studied to determine the most appropriate options to use in simulations. This was accomplished by modeling a …

Stress Corrosion Cracking Resistance Of Martensitic Stainless Steels For Transmutation Applications, Phani P. Gudipati

UNLV Theses, Dissertations, Professional Papers, and Capstones

The susceptibility of Alloy EP-823 to stress corrosion cracking has been evaluated using smooth and notched cylindrical specimens in neutral and acidic solutions at ambient and elevated temperatures using constant load and slow strain rate testing (SSR) techniques. C-ring and U-bend specimens have also been tested in the acidic solution. The effect of hydrogen on the cracking susceptibility has been evaluated under controlled cathodic potential. While no failures were observed with smooth specimens at constant load, the notched specimens showed failure. The SSR test results indicate that the true failure stress (o'_f), time to failure and ductility parameters …

Stress Corrosion Cracking And Hydrogen Embrittlement Of Martensitic Alloy Ep-823, Mohammad K. Hossain

UNLV Theses, Dissertations, Professional Papers, and Capstones

This investigation is focused on the evaluation of stress corrosion cracking (SCC), localized corrosion, and hydrogen embrittlement (HE) susceptibility of martensitic Alloy EP-823 in neutral and acidic solutions at ambient and elevated temperatures. While no failures were observed in smooth specimens in the neutral solution, failures were noticed in the 90°C acidic solution at constant-load (CL) leading to a threshold stress (O'_th) of 102 ksi. The presence of a notch reduced the O'_th value to 91 ksi in a similar environment. The ductility (%El and %RA), time-to-failure (TTF), and true failure stress (O'_r) were gradually …

Environmental Effects On Corrosion Properties Of Alloy 22, K. S. Raja, L. G. Mcmillion, Shantanu A. Namjoshi, Paige Russel, Raymond E. Keeler, Amy J. Smiecinski

Publications (YM)

During the regulatory life of the Yucca Mountain High Level Nuclear Waste (HLNW) repository the primary engineered barrier that is to prevent release of radioactive material into the environment is proposed to be a Corrosion-Resistant Material (CRM) outer shell covering the Waste Package (WP) container. The current selection for the CRM is Alloy 22 (UNS N06022), a Ni-Cr-Mo-W-Fe alloy. Alloy 22 forms a defective chromic oxide passive film which results in excellent corrosion resistance; the presence of molybdenum in Alloy 22 offers corrosion resistance in reducing environments as well as oxidizing environments.