Mechanics of Materials Commons^™

Phase Stability And Segregation In Alloy 22 Base Metal And Weldments, Jeffrey Lacombe, Shantanu A. Namjoshi, Paige Russel, Raymond E. Keeler, Amy J. Smiecinski

Publications (YM)

The current design of the waste disposal containers relies heavily on encasement in a multi-layered container, featuring a corrosion barrier of Alloy 22, a Ni-Cr-Mo-W based alloy with excellent corrosion resistance over a wide range of conditions. The fundamental concern from the perspective of the Yucca Mountain Project, however, is the inherent uncertainty in the (very) long-term stability of the base metal and welds. Should the properties of the selected materials change over the long service life of the waste packages, it is conceivable that the desired performance characteristics (such as corrosion reistance) will become compromised, leading to premature failure …

Embrittlement And Localized Corrosion In Alloy Ht-9, Sudheer Sama

UNLV Theses, Dissertations, Professional Papers, and Capstones

This investigation is focused on the evaluation of stress corrosion cracking (SCC), hydrogen embrittlement (HE) and localized corrosion susceptibility of Alloy HT -9 in neutral and acidic solutions at 30, 60 and 90°C. Constant-load and slow-strain-rate (SSR) testing techniques were used to evaluate the SCC and HE behavior of this alloy by using smooth and notched tensile specimens. Hydrogen effect on the cracking behavior was evaluated by applying cathodic (negative) potential to the test specimens. Localized corrosion susceptibility was evaluated by cyclic potentiodynamic polarization technique. The results of constant load SCC testing showed a threshold stress at 80% of the …

Environment-Induced Degradations In A Target Structural Material For Transmutation Applications, Ramprashad Prabhakaran

UNLV Theses, Dissertations, Professional Papers, and Capstones

This investigation is focused on the evaluation of stress corrosion cracking (SCC) and localized corrosion behavior of Type 422 stainless steel in aqueous environments at ambient and elevated temperature. The results of constant load SCC testing using smooth specimens showed no failure in the neutral solution but a threshold stress of 97 ksi was observed in the 90°C acidic environment. SCC testing by the slow-strain-rate test method indicate that the time-to-failure, true failure stress and ductility parameters were gradually reduced with increasing temperature, showing more pronounced effect in the acidic solution. The application of a controlled cathodic potential showed further …

Modeling, Optimization, And Flow Visualization Of Chemical Etching Process In Niobium Cavities, Sathish K. Subramanian

UNLV Theses, Dissertations, Professional Papers, and Capstones

Niobium cavities are important component of the linear accelerators. Researchers have concluded that buffered chemical polishing on the inner surface of the cavity improves its performance. However the mechanism of chemical polishing is not well understood. A finite element computational fluid dynamics (CFD) model was developed to simulate the fluid flow characteristics of chemical etching process inside the cavity. The CFD model is then used to optimize the baffle design. The analysis confirmed the observation of other researchers that the iris section of the cavity received more etching than the equator regions. The baffle, which directs flow towards the walls …

The Evaluation Of The Damping Characteristics Of A Hard Coating On Titanium, Christopher M. Blackwell

Theses and Dissertations

Engine failures due to fatigue have cost the Air Force an estimated $400 million dollars per year over the past two decades (Garrison, 2001). Damping treatments capable of reducing the internal stresses of fan and turbine blades to levels where fatigue is less likely to occur have the potential for reducing cost while enhancing reliability. This research evaluates the damping characteristics of magnesium aluminate spinel, MgO+Al₂O₃, (mag spinel) on titanium plates. The material and aspect ratio were chosen to approximate the low aspect ratio blades found in military gas turbine fans. The plates were tested with …

Fatigue Response Of Thin Stiffened Aluminum Cracked Panels Repaired With Bonded Composite Patches, Jason B. Avram

Theses and Dissertations

This research investigated the fatigue response of precracked and patched 2024-T3 Aluminum panels with stiffeners. Patches were single-sided, unidirectional three ply boron/epoxy. Stiffeners were 2024-T3 aluminum and were riveted and bonded on. Disbonds were introduced into the repair bondline by inserting teflon strips. Three disbond configurations were investigated rack tip disbond (CTD) located at the edge of the patch in the path of crack propagation, full-width disbond (FWD) covering the entire crack, and end disbond (ED) located at each end of the patch and covering the full width. Each repaired panel was subjected to tension/tension cyclic fatigue with a maximum …

Mechanics Of A Functionally-Graded Titanium Matrix Composite, G. Brandt Miller

Theses and Dissertations

Functionally-graded Titanium Matrix Composites, (F/G TMCs) combine the ideal properties of titanium matrix composites with the more practical machining qualities of monolithic (unreinforced) alloy. This material shows great promise in application to aerospace structural components - even in parts whose design requirements have defied the use of composite materials in the past. Successful implementation of such a material would lead to enhanced aircraft performance. However, the basic properties of a functionally-graded titanium matrix composite need to be investigated. The composite/alloy transition region, or joint area, may be less strong than its constituents and therefore determine the overall performance of the …

Effect Of Temperature On Short-Term Creep Rupture Response In Polymer Matrix Pultruded Composites, Robert Harold Munson

Mechanical & Aerospace Engineering Theses & Dissertations

Polymer matrix pultruded composites have increasingly been used in applications where high strength-to-weight ratio and corrosion resistance are needed. Bridge and pier components are a couple of recent applications due the composite's resistance to corrosion from salt water. In applications of this sort, the material will commonly be subjected to sizable static loads while exposed to varying weather conditions. In using pultruded composites for these applications safely, a better understanding of the material's response to ambient conditions is necessary.

In this thesis, rectangular specimens of a polyester matrix glass reinforced pultruded composite sheet are subjected to both static tensile loading …

Thickness Effects On A Cracked Aluminum Plate With Composite Patch Repair, Joel J. Schubbe

Theses and Dissertations

Post-repair fatigue crack growth was investigated in 3.175, 4.826, and 6.35 mm thick aluminum panels asymmetrically repaired with boron/epoxy composite patches bonded to the plates with FM73 sheet adhesive. Patches were uniaxial with patch to panel stiffness ratios ranging from 0.46 to 1.3. Experimental fatigue tests were carried out at 120 MPa, R=0.1, and 10 Hz (sinusoidal) to measure patched and unpatched face crack lengths, center crack opening displacements, and selected strains. Crack growth data was acquired using optical, eddy current, and post-test analysis methods. Crack growth rates were calculated using the incremental polynomial method. A three-layer Mindlin plate finite …

An Experimental Investigation Of Bolt Preload Relaxation In Pultruded Gfrp Composite Joints, Srinivas Ravi

Mechanical & Aerospace Engineering Theses & Dissertations

Mechanically fastened joints in pultruded composites are necessary for reasons of maintenance, repair, and assembly. Pultruded composites utilize polymers as matrices and therefore are susceptible to time-dependent effects. The positive effects of increasing the clamping force in bolted joints are well known. To maintain a safe operation of the assembly a minimum clamping force must be guaranteed. But since these materials show time-dependent effects, the bolt-preload relaxes over a period of time. The present study is aimed at investigating the bolt preload relaxation. In this study 1/2 in. thick pultruded sheets were first tested under compression in the thickness direction. …

Wear And Friction Behavior Of Metal Impregnated Microporous Carbon Composites, Gultekin Goller, D. P. Koty, Surendra N. Tewari, M. Singh, A. Tekin

Chemical & Biomedical Engineering Faculty Publications

Metal-matrix composites have been prepared by pressure-infiltration casting of copper-base alloy melts into microporous carbon preforms. The carbon preforms contained varying proportions of amorphous carbon and graphite. Load dependence of the wear and friction behavior of the composite pins has been examined under ambient conditions against cast-iron plates, using a pin-on-plate reciprocating wear tester. The wear resistance of the composite is significantly improved, as compared with the base alloy. Contrary to the normally expected behavior, the addition of graphite to the amorphous carbon does not reduce the friction coefficient, especially at high loads. The wear and friction behavior of the …

Effects Of Elevated Temperature On The Physical Aging Of A High Temperature Thermoplastic Resin And Composite, Mark Feldman

Mechanical & Aerospace Engineering Theses & Dissertations

Development of a High Speed Civil Transport is considered by the commercial aviation industry to be one of the next big challenges for our national aircraft industry. Critical to the success of this aircraft is the development of advanced polymeric composites for both the primary and secondary structures and the predictive methodology necessary for assessment of long term durability. While polymeric composites offer an excellent strength to weight ratio a key disadvantage is the time dependent properties exhibited by the polymer matrix which can age and ultimately effect the resultant stiffness of a laminate.

Experimental studies were performed to determine …

Thermal Stresses In End-Heated Layered Media, Jerry R. Couick

Theses and Dissertations

Thermal stresses in semi-infinite layered beams heated on the end are calculated using an extension to simple bimetallic thermostat theory. Recently, researchers have used the concept of interfacial compliance to determine interlaminar stresses in a simple thermostat of finite length subjected to a uniform temperature increase. In the present work, the thermostat theory is extended to apply to the beams of interest. A closed-form solution to the problem is obtained. It is not applicable within about one beam thickness (St Venant boundary region) of the end. Various classes of layered materials are analyzed to determine if significant stresses exist outside …

An Investigation Of Hole Size Effects In A Composite Material During Tensile Fracture, David Floyd Moore

Mechanical & Aerospace Engineering Theses & Dissertations

An experimental investigation was conducted to evaluate the hole size effects, i.e., the reduction in strength with an increase in hole size at a constant stress concentration factor, for a glass fiber reinforced epoxy crossply laminate during tensile fracture. The characteristic dimension according to the point-stress and average-stress criteria of the two-parameter models proposed by Whitney and Nuismer were determined and compared for a circular hole, optimized circular hole, square hole with radiused corners and square hole with sharp corners. Modified versions of the two-parameter models proposed by Karlak and Pipes, Wetherhold, and Gillespie were also compared. On the basis …

Development Of Nial-Based Intermetallic Alloys: Effect Of Chromium Addition, R. Tiwari, Surendra N. Tewari, R. Asthana, A. Garg

Chemical & Biomedical Engineering Faculty Publications

The mechanical behavior of dual-phase NiAl(Cr) microstructures, consisting of elongated primary NiAl grains aligned with an intergranular NiAl-Cr eutectic phase, produced by extrusion of a cast NiAl(Cr) alloy, has been examined. Chromium addition to create a dual phase NiAl-based aligned microstructure leads to large increases in the yield strength but no significant toughness improvement. This is achieved primarily by solid solution hardening and precipitation hardening. The constitutional hardening rate resulting from deviations from stoichiometry in the nickel-rich NiAl was estimated to be about 66 MPa per atomic per cent of nickel.

Nonlinear Finite Element Micromechanic Analysis Of Thermoplastic Composite Of Recycled High Density Polyethylene Reinforced With Short Glass Fibers, Qiming Lou

Masters Theses

This thesis studied the nonlinear micromechanic behavior of thermoplastic composite of recycled high density polyethylene (HDPE) reinforced with short glass fibers using finite element method. The composite material was modeled using a micromechanic unit cell to simulate the stress distribution between the plastic matrix and the fiber in the composite. Nonlinear behavior of recycled HDPE and imperfect bonding between the fiber and matrix were investigated. Load-bearing capability of the fiber was evaluated using stress partition ratio (SPR) in the composite models. The effect of fiber aspect ratio on the stress distribution of the composite was studied to optimize the material …

Investigation Into The Behavior Of Geometrically Nonlinear Composite Arches, John C. Bailey

Theses and Dissertations

This research modifies the existing finite element formulation of a potential energy based large deformation and moderate rotation theory. Hermitian shape functions replace the existing linear bending angle interpolations. Negligible differences between the two formulations indicate the underlying kinematics limit the accuracy, not the finite element interpolations. Using the new program, numerous nonlinear arch geometries are modeled to investigate the effects of arc length and thickness variations. Local and global snapping phenomena are captured as well as through the thickness shear driven nonlinearities.

Fatigue Behavior Of A Cross-Ply Ceramic Matrix Composite At Elevated Temperature Under Tension-Tension Loading, Craig D. Steiner

Theses and Dissertations

This study investigated the fatigue behavior and damage mechanisms of a [0-90]_4s SiC-MAS ceramic matrix composite under tension-tension loading at two elevated temperatures and two frequencies. Stress and strain hystereses, maximum and minimum strain, and modulus of elasticity were evaluated to characterize the material behavior. Microscopy and fractography were used to evaluate damage progression and mechanisms. Fatigue life was independent of frequency at both temperatures.

Characterization Of Fatigue Behavior Of 2-D Woven Fabric Reinforced Ceramic Matrix Composite At Elevated Temperature, Daniel J. Groner

Theses and Dissertations

This study investigated the fatigue behavior and associated damage mechanisms in notched and unnotched enhanced Sic-SiC ceramic matrix composite specimens at 1100°C. Stiffness degradation, strain variation, and hysteresis were evaluated to characterize material behavior. Microscopic examination was performed to characterize damage mechanisms. During high cycle-low stress fatigue tests, far less fiber-matrix interface debond was evident than in low cycle-high stress fatigue tests. Notched specimens exhibited minimal stress concentration during monotonic tensile testing and minimal notch sensitivity during fatigue testing. Damage mechanisms were also similar to unnotched.

Fatigue Behavior Of A Cross-Ply Ceramic Matrix Composite Subjected To Tension-Tension Cycling With Hold Time, Scott A. Grant

Theses and Dissertations

This study was carried out to investigate the elevated temperature behavior of the SiC-MAS5 cross- ply [0-90]_4S ceramic matrix composite manufactured by Corning Inc. to fatigue with loading waveforms that combine the characteristics of stress rupture and high cycle fatigue. The test results were compiled in the form of S-N (cycles to failure), S-T (exposure time versus cycles to failure), S-S (energy exposure versus cycles to failure), normalized modulus degradation, strain progression, and hysteresis loop progression. From the mechanical behavior demonstrated by these curves, relationships between the effect of the environment and loading waveform were developed. In addition, a …

Investigation Of Tension-Compression Fatigue Behavior Of A Cross-Ply Metal Matrix Composite At Room And Elevated Temperatures, Elizabeth A. Boyum

Theses and Dissertations

This research, the first load-controlled tension-compression fatigue testing to be performed on a MMC, extends the existing knowledge of MMC fatigue damage mechanisms to include the tension compression loading condition. To accomplish this, a (0/90)2, SCS-6/Ti-15-3 laminate was subjected to tension- tension fatigue at room temperature, and tension-compression fatigue at both room temperature and 427°C. Stress and strain data was taken to evaluate the macro-mechanic behavior of the material. Microscopy and fractography were performed to characterize the damage on a micro-mechanic level. On a maximum applied stress basis, the room temperature tension-tension specimens had longer fatigue lives than the room …

Influence Of Embedded Optical Fibers On Compressive Strength Of Advanced Composites, Stefan B. Dosedel

Theses and Dissertations

This study investigated the effects of embedding optical fibers into advanced composite materials. This combination was meant to simulate 'smart structures' that have been shown to sense several different variables in the composite including strain, temperature, and damage. A laminate orientation taken from an existing aircraft structure was used to fabricate sixteen groups of specimens which were subjected to compression testing in an IITRI fixture to determine the ultimate compressive strength and modulus of elasticity. Ten of these groups were fabricated with optical fibers while the other six were control groups and contained no optical fibers. This study showed that …

Fatigue Behavior Of A Cross-Ply Ceramic Matrix Composite Under Strain Controlled Tension-Tension And Tension-Compression Loading, James J. Gudaitis

Theses and Dissertations

This stuidy investigates the fatigue response of a cross-ply [0/90]_2s Nicalon/Calcium Aluminosillicate (Nicalcc/CAS) ceramic matrix composite at room temperature under strain controlled tension-tension and tension-compression fatigue loading. The primary objectives were to determine strain fatigue limits for both loading cases and to complete a fatigue life diagram (Δe-N) for all tests. Failure mechanisms were also studied. The average initial modulus value for this lay-up was 120 GPa. The ultimate tensile strain was 0.00988 mn/mm (285 MPa). Eight tests were conducted with maximum strains that ranged from 0.00300 mm/mm to 0.00722 mm/mm. The tension-tension fatigue limit was found to be …

Investigation Of Compressive Behavior For Metal Matrix Composites With A Circular Hole, Janet L. Gooder

Theses and Dissertations

This study investigated the notched and unnotched macromechanical response due to micromechanical behavior of [0/±45/90]_S SCS-6/β 21 S and [0/90] _2S Sigma/β 21S subjected to static compressive loads at room temperature. The stress-strain behavior and mechanical response in the presence of a circular hole was examined. A clear description of the progressive nature of damage, which ultimately resulted in failure, was provided. The effect of elevated temperature was shown for SCS-6/β 21S. The ultimate compressive strength and elastic modulus were reported for both MMCs. Sigma/β 21S and SCS-6/β 21S were mildly notch sensitive at room temperature. Notch sensitivity of …

Fatigue Behavior Of A Cross-Ply Ceramic Matrix Composite At Elevated Temperatures Under Tension-Tension Loading, Richard J. Tuznik

Theses and Dissertations

A study was conducted which investigated the behavior of a Nicalon/ Calcium-Aluminosilicate (Nicalon/CAS) cross-ply [0/90]_2S ceramic matrix composite at elevated temperatures under tension-tension fatigue loading. Tension-tension fatigue tests were performed with a load ratio of R = 0.10 and a frequency of 10 Hertz at 700°C and 850°C. These results were compared to results from a previous study conducted at room temperature. Material behavior and damage was recorded by fatigue life curves, elastic modulus' maximum and minimum strain, acetate replication techniques, and post-mortem fractography. Analysis of these results showed identical matrix dominated damage behavior at RT and 700°C. Ultimate …

Characterization Of Fatigue Damage In A Metal Matrix Composite (Scs-6/ Ti-15-3) At Elevated Temperature, Brian P. Sanders

Theses and Dissertations

The fatigue characteristics of a unidirectional titanium based metal matrix composite (MMC) were investigated at elevated temperature (427°C). A hybrid strain controlled loading mode was used to subject the 0° and 90° laminas to fatigue. Along with the fatigue tests, microscopy and analytical modeling ware also conducted. This combination of activities led to defining the initiation and progression of damage and deformation in the MMC. Hen loading was parallel to the fiber on, the fatigue behavior was initially dominated by creep deformation of the matrix. Then, depending on the maximum strain, specimen failure was the result either fiber fractures or …

An Investigation Of Graphite Peek Composite Under Compression With A Centrally Located Circular Discontinuity, Benjamin Wham Ii

Theses and Dissertations

The purpose of this thesis was to determine (both experimentally and analytically) the initiation and progression of failure, stress-strain response, and the failure loads of Graphite/Polyetheretherketone (Gr/PEEK) laminates, incorporating a centrally located circular discontinuity, loading in axial compression at room temperature. The laminates studied were (0°)₁₆,(90°)₁₆, (0°/90°)_4S, (± 45°)_4S, and (0°/±45°/90°)_2S. The specimens were loaded within a Boeing Open Hole Compression Fixture. The micromechanical failure modes were identified using a Scanning Electron Microscope. The analytical progression of failure was predicted using a nonlinear finite element code developed by Dr. R.S. …

Computational And Experimental Investigation Into Fracture Of Brittle Fiber - Brittle Matrix Composite Systems, James P. Solti

Theses and Dissertations

Experimental and computational analyses provided an improved understanding of quasi-static fracture in model composite systems. Constant displacement compression tests using borosilicate glass double cleavage drilled compression test templates provided qualitative assessments of localized toughening for crack growth near cylindrical inclusions. Large crack-tip stress fields induced interfacial slip and separation prior to arrival of the main crack. Debonding and the proliferation of secondary matrix cracks characterized the role of bridging fibers along weak interfaces. Strong residual normal compressive interfacial stresses diminished the influence of crack-tip stresses; however, slip was still observed. VHS tape and computer enhanced photos record a history of …

Investigation Of Fatigue Behavior In Notched Cross-Ply Titanium Metal Matrix Composite At Elevated Temperature, Robert P. Baker

Theses and Dissertations

The objective of this research was to investigate the initiation and progression of damage which develops in notched (0/90)_2S SCS-6/Ti-15-3 at elevated temperature. Testing consisted of a monotonic tensile test at 427°C followed by fatigue testing performed under load control with a stress ratio of 0.1 at a frequency of 10 Hz. A crack was defined to have initiated when it had attained a length greater than or equal to 0.124 mm. Crack initiation and progression was monitored by strain and modulus observations and visual inspection via telemicroscope. The cracks were recorded with edge and face replicas. Metallographic and …

Behavior Of A Titanium Matrix Composite Under Quasi-Static Tensile And Compressive Loading, Keith L. Bearden

Theses and Dissertations

Quasi-Static tensile and compressive testing was performed on a unidirectional titanium matrix composite. The specific material was SCS-9/β 21S. The initial tensile and compressive modulus for both laminates was the same. The ninety degree laminate had a tensile and compressive modulus of 115.89 GPa. The zero degree laminate had a tensile and compressive modulus of 197.51 GPa. The ninety degree laminate exhibited a three stage stress/strain response in tension. The first stage is completely linearly elastic, however, partial debonding of the fiber from the matrix was observed. This partial debased did not effect the stress/strain response. The second stage is …