Biomedical Devices and Instrumentation Commons^™

Effect Of Nitrogen On Properties Of Na2o-Cao-Sro-Zno-Sio2 Glasses, Ahmed Bachar, Cyrille Mercier, Arnaud Tricoteaux, Jean Christophe Hornez, Anne Leriche, Claudine Follet, Bertrand Revel, Stuart Hampshire, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

Glasses in the Na₂O-CaO-SrO-ZnO-SiO₂ system have previously been investigated for suitability as a reagent in Al-free glass polyalkenoate cements (GPCs). These materials have many properties that offer potential in orthopedics. However, their applicability has been limited, to date, because of their poor strength. This study was undertaken with the aim of increasing the mechanical properties of a series of these Zn-based GPC glasses by doping with nitrogen to give overall compositions of: 10Na₂O-10CaO-20SrO-20ZnO-(40-3x)SiO₂-xSi₃N₄ (x is the no. of moles of Si₃N₄). The density, glass-transition temperature, hardness, …

Processing And Mechanical Testing Of Strontium-Substituted Hydroxyapatite/Glass Composites, Chokchai Yatongchai, Mark R. Towler, Anthony W. Wren

Chemical and Biochemical Engineering Faculty Research & Creative Works

Sr-HA/Glass composites were produced. Phase composition of composites was evaluated. Their physical and mechanical properties were determined. Sintered composites mainly consisted of Sr-HA/β-TCP, or β-TCP/Ca₂ZnSi₂O₇. The composites had porosity up to 4 times those of undoped Sr-HA. Compared to undoped Sr-HA, the Sr-HA/Glass composites had lower biaxial flexural strength and hardness. The Weibull modulus for the composites ranged from 2.77 to 18.74.

Investigating The Effect Of Sio2-Tio2-Cao-Na 2o-Zno Bioactive Glass Doped Hydroxyapatite: Characterisation And Structural Evaluation, Chokchai Yatongchai, Anthony W. Wren, Declan J. Curran, Stuart Hampshire, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

The effects of increasing bioactive glass additions,

SiO₂-TiO₂-CaO-Na₂O-ZnO up to 25 wt% in increments of 5 wt%, on the physical and mechanical properties of hydroxyapatite (HA) sintered at 900, 1000, 1100 and 1200°C for 2 h was investigated. Increasing both the glass content and the temperature resulted in increased HA decomposition. This resulted in the formation of a number of bioactive phases. However the presence of the liquidus glass phase did not result in increased densification levels. At 1000 and 1100°C the additions of 5 wt% glass resulted in a decrease in density which …

Degradable Borate Glass Polyalkenoate Cements, L. Shen, A. Coughlan, Mark R. Towler, M. Hall

Chemical and Biochemical Engineering Faculty Research & Creative Works

Glass polyalkenoate cements (GPCs) containing aluminum-free borate glasses having the general composition Ag₂O-Na₂O-CaO-SrO-ZnO- TiO₂-B₂O₃ were evaluated in this work. An initial screening study of sixteen compositions was used to identify regions of glass formation and cement compositions with promising rheological properties. The results of the screening study were used to develop four model borate glass compositions for further study. A second round of rheological experiments was used to identify a preferred GPC formulation for each model glass composition. The model borate glasses containing higher levels of TiO₂ (7.5 mol %) …

Characteristics Of Glass Ionomer Cements Composed Of Glass Powders In Cao-Sro-Zno-Sio2 System Prepared By Two Different Synthetic Routes, Ill Yong Kim, Chikara Ohtsuki, Aisling Coughlan, Lana Placek, Anthony W. Wren, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

Glass ionomer cements (GICs) are composed of an acid degradable glass, polyacrylic acid and water. Sol-gel processing to prepare the glass phase has certain advantages, such as the ability to employ lower synthesis temperatures than melt quenching and glasses that are reported to have higher purity. A previous study reported the effects of glass synthesis route on GIC fabrication. However, in that study, the sol-gel derived glass exhibited a reduced concentration of cations. This study investigates increasing the cation content of a sol-gel derived glass, 12CaO·4SrO·36ZnO·48SiO₂ (molar ratio) by heating before aging to reduce dissolution of cations. This glass …

Biocompatibility Of Cao-Na2o-Sio2/Tio2 Glass Ceramic Scaffolds For Orthopaedic Applications, A. W. Wren, A. Coughlan, K. E. Smale, S. T. Misture, B. P. Mahon, O. M. Clarkin, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

This work aims to determine the effect of substituting TiO₂ for SiO₂ in a 0.62SiO₂-Na₂O-0.24CaO based glass-ceramic scaffold. High temperature X-ray Diffraction (HT-XRD) was used to determine the sintering temperature (700oC). Both optical microscopy and x-ray micotomography was used to determine the average pore size (540-680ìm) of each scaffold. Cytocompatibility of each scaffold was conducted using murine mesenchymal stem cells. © 2013 IEEE.

Gallium Containing Glass Polyalkenoate Bone Cements: Ion Release And E. Coli Inhibition, L. Placek, A. W. Wren, A. Coughlan, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

The Glass Polyalkenoate Cement (GPC) series (LCon., LGa-1 and LGa-2) containing gallium (Ga) and a 50 wt% addition of E11 polyacrylic acid (PAA), previously developed, was evaluated for ion release, specifically Si, Ca, Zn and Ga, and E. coli inhibition. The maximum inhibition was observed in the t = 0 samples and was 0.35 mm for LCon. and 0.65 mm for LGa-1 and LGa-2. © 2013 IEEE.

An Investigation Into The Structure And Properties Of Cao-Zno-Sio 2-Tio2-Na2o Bioactive Glass/Hydroxyapatite Composite, Chokchai Yatongchai, Mark R. Towler, Anthony W. Wren

Chemical and Biochemical Engineering Faculty Research & Creative Works

Effect of the addition of CaO-ZnO-SiO₂-TiO₂-Na₂O glass as a reinforcing phase on properties of hydroxyapatite/glass composites was investigated. The addition of the glass caused the decomposition of HA phase to tricalcium phosphate, inhibiting densification in the HA/glass composites. However, depending on the glass concentration, some of the glass can act as a sintering aid enhancing the densification in the composites. © 2013 IEEE.

Relating Ph And Ion Release From Ga2o3-Na 2o-Cao-Zno-Sio2 Bioactive Glasses, T. J. Keenan, A. W. Wren, A. Coughlan, Mark R. Towler, M. M. Hall

Chemical and Biochemical Engineering Faculty Research & Creative Works

Three glasses were designed for this study, including one Ga-free glass (Control), and two Ga-containing glasses (TGa-1, TGa-2). In the Ga-containing glasses, Ga₂O₃ is included at the expense of ZnO. This study focuses on the relation between pH and ion concentration present in solution in which these bioactive glasses have been submerged for periods of 1, 7, and 14 days. © 2013 IEEE.

Comparison Of A Sio2-Cao-Zno-Sro Glass Polyalkenoate Cement To Commercial Dental Materials: Ion Release, Biocompatibility And Antibacterial Properties, A. W. Wren, A. Coughlan, M. M. Hall, M. J. German, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

Ion Release and biocompatibility of a CaO-SrO-ZnO-SiO₂ (BT 101) based glass polyalkenoate cement (GPC) was compared against commercial GPCs, Fuji IX and Ketac Molar. The radiopacity (R) was similar for each material, 2.0-2.8. Ion release was evaluated on each material over 1, 7, 30 and 90 days. BT 101 release included Ca (23 mg/L), Sr (23 mg/L) Zn (13 mg/L), Si (203 mg/L). Fuji IX release includes Ca (0.7 mg/L), Al (3 mg/L) Si (26 mg/L), Na (60 mg/L) and P (0.5 mg/L) while Ketac Molar release includes Ca (1 mg/L), Al (0.6 mg/L) Si (23 mg/L), Na (76 …

Materials Education And Research In Art And Design: A New Role For Libraries (Survey Stats), Mark Pompelia

Materials Education and Research in Art and Design: A New Role for Libraries

No abstract provided.

Materials Education And Research In Art And Design: A New Role For Libraries (Program Sheet), Mark Pompelia

Materials Education and Research in Art and Design: A New Role for Libraries

No abstract provided.

Materials Education And Research In Art And Design: A New Role For Libraries (Program Booklet), Mark Pompelia

Materials Education and Research in Art and Design: A New Role for Libraries

No abstract provided.

Materials Education And Research In Art And Design: A New Role For Libraries (Website), Mark Pompelia

Materials Education and Research in Art and Design: A New Role for Libraries

No abstract provided.

Materials Collection Creation And Administration: A New Role For Libraries (White Paper), Mark Pompelia

Materials Education and Research in Art and Design: A New Role for Libraries

The Problem/Opportunity: To define, identify, and guide design-based materials collections in academic settings and foster community among those with existing collections and/or those considering creating and supporting one.

Contents and topics:

1. What is a materials collection?
2. Why have a materials collection?
3. Acquisition strategies
4. Organizational approaches
5. Programming possibilities
6. Symposium summary
7. Resources

Characterisation Of Ga2o3-Na2o-Cao-Zno- Sio2 Bioactive Glasses, A. W. Wren, T. Keenan, A. Coughlan, F. R. Laffir, D. Boyd, Mark R. Towler, M. M. Hall

Chemical and Biochemical Engineering Faculty Research & Creative Works

The structural role of Gallium (Ga) is investigated when substituted for Zinc (Zn) in a 0.42SiO₂-0.40-xZnO-0.10Na₂O-0.08CaO glass series, (where x = 0.08). Each starting material was amorphous, and the network connectivity (NC) was calculated assuming Ga acts as both a network modifier (1.23), and also as a network former. Assuming a network forming role for Ga the NC increased with increasing Ga concentration throughout the glass series (Control 1.23, TGa-1 2.32 and TGa-2 3.00). X-ray photoelectron spectroscopy confirmed both composition and correlated NC predictions. Raman spectroscopy was employed to investigate Q-structure and found that a shift …

Aluminium-Free Glass Polyalkenoate Cements: Ion Release And In Vitro Antibacterial Efficacy, A. W. Wren, J. P. Hansen, S. Hayakawa, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

Glass polyalkenoate cements (GPCs) have exhibited potential as bone cements. This study investigates the effect of substituting TiO₂ for SiO₂ in the glass phase and the subsequent effect on cement rheology, mechanical properties, ion release and antibacterial properties. Glass characterization revealed a reduction in glass transition temperature (T_g) from 685 to 669 C with the addition of 6 mol % TiO₂ (AT-2). Magic angle spinning nuclear magnetic resonance (MAS-NMR) revealed a shift from -81 ppm to -76pmm when comparing a Control glass to AT-2, indicating de-polymerization of the Si network. The incorporation of TiO_{2 …}

Comparison Of A Sio2-Cao-Zno-Sro Glass Polyalkenoate Cement To Commercial Dental Materials: Glass Structure And Physical Properties, A. W. Wren, A. Coughlan, F. R. Laffir, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

Glass polyalkenoate cements (GPCs) have previously been considered for orthopedic applications. A Zn-GPC (BT 101) was compared to commercial GPCs (Fuji IX and Ketac Molar) which have a setting chemistry analogous to BT 101. Handling properties (working, T_w and setting, T_s times) for BT 101 were shorter than the commercial GPCs. BT 101 also had a higher setting exotherm (S_x - 34 °C) than the commercial GPCs (29 °C). The maximum strengths for BT 101, Fuji IX, and Ketac Molar were 75, 238, and 216 MPa (compressive, σ_c), and 34, 54, and 62 MPa (biaxial …

Fabrication Of Cao-Nao-Sio2/Tio2 Scaffolds For Surgical Applications, A. W. Wren, A. Coughlan, K. E. Smale, S. T. Misture, B. P. Mahon, O. M. Clarkin, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

A series of titanium (Ti) based glasses were formulated (0.62 SiO₂-0.14 Na₂O-0.24 CaO, with 0.05 mol% TiO₂ substitutions for SiO₂) to develop glass/ceramic scaffolds for bone augmentation. Glasses were initially characterised using X-ray diffraction (XRD) and particle size analysis, where the starting materials were amorphous with 4.5 μm particles. Hot stage microscopy and high temperature XRD were used to determine the sintering temperature (̃700 °C) and any crystalline phases present in this region (Na₂Ca₃Si₆O₁₆, combeite and quartz). Hardness testing revealed that the Ti-free control (ScC- …

Developing Novel Prognostic Biomarkers For Multivariate Fracture Risk Prediction Algorithms, Ernest K. Poku, Mark R. Towler, Niamh M. Cummins, Jeff D. Newman

Chemical and Biochemical Engineering Faculty Research & Creative Works

Multivariate prediction algorithms such as FRAX® and QFracture Scores provide an opportunity for new prognostic biomarkers to be developed and incorporated, potentially leading to better fracture prediction. As more research is conducted into these novel biomarkers, a number of factors need to be considered for their successful development for inclusion in these algorithms. In this review, we describe two well-known multivariate prediction algorithms for osteoporosis fracture risk applicable to the UK population, FRAX and QFracture Scores, and comment on the current prognostic tools available for fracture risk; dual X-ray assessment, quantitative ultrasonography, and genomic/biochemical markers. We also highlight the factors …

Gallium Containing Glass Polyalkenoate Anti-Cancerous Bone Cements: Glass Characterization And Physical Properties, A. W. Wren, A. Coughlan, L. Placek, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

A gallium (Ga) glass series (0.48SiO₂-0.40ZnO-0.12CaO, with 0.08 mol% substitution for ZnO) was developed to formulate a Ga-containing Glass Polyalkenoate Cement (GPC) series. Network connectivity (NC) and X-ray Photoelectron Spectroscopy (XPS) was employed to investigate the role of Ga³⁺ in the glass, where it is assumed to act as a network modifier. Ga-GPC series was formulated with E9 and E11 polyacrylic acid (PAA) at 50, 55 and 60 wt% additions. E11 working times (T_w) ranged from 68 to 96 s (Lcon.) and 106 s for the Ga-GPCs (LGa-1 and LGa-2). Setting times (T_s) …

Experimental Composite Guidance Conduits For Peripheral Nerve Repair: An Evaluation Of Ion Release, X. F. Zhang, A. Coughlan, H. O'Shea, Mark R. Towler, S. Kehoe, D. Boyd

Chemical and Biochemical Engineering Faculty Research & Creative Works

Poly (lactide-co-glycolide) (PLGA) - Pluronic F127 - glass composites have demonstrated excellent potential, from the perspective of controlled mechanical properties and cytocompatibility, for peripheral nerve regeneration. In addition to controlling the mechanical properties and cytotoxicity for such composite devices, the glass component may mediate specific responses upon implantation via degradation in the physiological environment and release of constituent elements. However, research focused on quantifying the release levels of such therapeutic ions from these experimental medical devices has been limited. To redress the balance, this paper explores the ion release profiles for Si⁴⁺, Ca²⁺, Na⁺, …

The Structural Characterization Of Ga 2o 3-Na 2o-Cao-Zno-Sio 2 Bioactive Glasses, T. J. Keenan, A. W. Wren, A. Coughlan, M. M. Hall, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

The characterization of bioactive glasses in which zinc (Zn) has been incrementally replaced by gallium (Ga). © 2012 IEEE.

Silver Coated Bioactive Glass Particles For Wound Healing Applications, P. Hassanzadeh, A. W. Wren, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

Hench and colleagues discovered that bone could bond chemically to certain glass compositions in 1969 [1]. This group of glasses is known as bioactive glasses [1]. Some special compositions of bioactive glasses will bond to soft tissues as well as bone [1]. One of the important characteristics of bioactive glasses is their ability to release beneficial ions such as Ca²⁺, Na⁺, Zn²⁺, Sr²⁺, and PO 43- in the body, which promote self-healing [2]. Bioactive glasses generally contain much less glass former (e.g., SiO₂, B₂O₃ etc.) than conventional …

Increasing The Quantity Of Silver In Zinc-Based Glass Polyalkenoate Cement: Is There An Improvement In Antibacterial Efficacy?, A. Coughlan, S. M. Breed, C. Ashraf, J. A. Cardinale, M. M. Hall, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

Bone cements should have the ability to chemically bond to both bone and surgical metals, exhibit no chemical or thermal necrosis, and have no significant shrinkage or exotherm upon setting. Taking these properties into consideration, glass polyalkenoate cements (GPCs) have potential as bone cements. GPCs are formed by the reaction between an ion-leachable glass and an aqueous solution of polyacrylic acid (PAA) [1] and have proven antibacterial and cariostatic properties [2], which are related to their ability to release beneficial amounts of ions over time [3, 4]. The GPCs can be formulated to release ions that can have a therapeutic …

Gallium Containing Glass Polyalkenoate Bone Cements: Glass Characterization And Physical Properties, L. Placek, A. W. Wren, A. Coughlan, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

Gallium (Ga) glasses were developed to formulate a Glass Polyalkenoate Cement (GPC) series with both E9 and E11 polyacrylic acid (PAA) at 50, 55 and 60wt% additions. Working times (T w), setting times (T s), compression (σ c), and biaxial flexural (σ f) strength testing were evaluated to determine the GPCs potential use in orthopedics. © 2012 IEEE.

Silver Coated Bioactive Glass Particles For Wound Healing Applications, A. W. Wren, A. Coughlan, P. Hassanzadeh, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

Bioactive glass particles (0.42SiO₂-0.15CaO-0.23Na ₂O-0.20ZnO) of varying size (<90 >μm and 425-850 μm) were synthesized and coated with silver (Ag) to produce Ag coated particles (PAg). These were compared against the uncoated analogous particles (Pcon.). Surface area analysis determined that Ag coating of the glass particles resulted in increased the surface area from 2.90 to 9.12 m²/g (90 μm) and 1.09-7.71 m²/g (425-850 μm). Scanning electron microscopy determined that the Ag coating remained at the surface and there was little diffusion through the bulk. Antibacterial (Escherichia coli - 13 mm and Staphylococcus epidermidis …

Comparison Of Microwave And Conventionally Sintered Yttria-Doped Zirconia Ceramics, Colin J. Reidy, Thomas J. Fleming, Stuart Hampshire, Mark R. Towler

Chemical and Biochemical Engineering Faculty Research & Creative Works

This paper reports on improvement of the physical and mechanical properties of Y₂O₃-ZrO₂ ceramics through compositional optimization, the use of nanograined powders and utilization of microwave sintering. ZrO₂ with 2-5 mol% Y₂O₃, prepared from nanopowders, was sintered in both conventional and microwave furnaces under exactly the same heating schedule. It was found that microwave sintering improves physical and mechanical properties of Y₂O₃-ZrO₂ ceramics compared with conventional sintering. Compositions containing 2 mol% Y₂O₃ exhibit the greatest improvement due to retention of tetragonal ZrO …

Sol-Gel Derived Silver-Incorporated Titania Thin Films On Glass: Bactericidal And Photocatalytic Activity, Betul Akkopru Akgun, Anthony W. Wren, Caner Durucan, Mark R. Towler, Nathan P. Mellott

Chemical and Biochemical Engineering Faculty Research & Creative Works

Titanium dioxide (TiO₂) and silver-containing TiO₂ (Ag-TiO₂) thin films were prepared on silica pre-coated float glass substrates by a sol-gel spin coating method. The bactericidal activity of the films was determined against Staphylococcus epidermidis under natural and ultraviolet (UV) illumination by four complementary methods; (1) the disk diffusion assay, (2) UV-induced bactericidal test, (3) qualitative Ag ion release in bacteria inoculated agar media and (4) surface topographical examination by laserscan profilometry. Photocatalytic activity of the films was measured through the degradation of stearic acid under UV, solar and visible light conditions. The chemical state and …

Clinical Risk Factors For Osteoporosis In Ireland And The Uk: A Comparison Of Frax And Qfracturescores, N. M. Cummins, E. K. Poku, Mark R. Towler, O. M. O'Driscoll, S. H. Ralston

Chemical and Biochemical Engineering Faculty Research & Creative Works

Recently two algorithms have become available to estimate the 10-year probability of fracture in patients suspected to have osteoporosis on the basis of clinical risk factors: the FRAX algorithm and QFractureScores algorithm (QFracture). The aim of this study was to compare the performance of these algorithms in a study of fracture patients and controls recruited from six centers in the United Kingdom and Ireland. A total of 246 postmenopausal women aged 50-85 years who had recently suffered a low-trauma fracture were enrolled and their characteristics were compared with 338 female controls who had never suffered a fracture. Femoral bone mineral …