The Effect Of Annealed Temperature On Properties Of Ru-Ir-Sn Oxide Anode Coatings, Lei Ji, Jun-Tao Wang, Li-Kun Xu, Wen-Bin Liu, Gui-Lin Xue

Journal of Electrochemistry

The anode coatings of Ru-Ir-Sn oxide were prepared by sol-gel method with different annealed temperatures.The influences of annealed temperature in properties of anode coatings were characterized by scanning electron microscope(SEM),energy dispersive X-ray detector(EDX),X-ray diffraction(XRD),potential of chlorine evolution,accelerated life,cyclic voltammetry and electrochemical impedance spectroscopy(EIS) tests.The results showed that the annealed temperature affected the morphology of coatings,while the electric quantities of cyclic voltammetry and double layer capacitances of anode coatings had a tendency to fall down and the potential of chlorine evolution and accelerated life had a tendency to increase as the annealed temperature increased.

Preparation And Photoelectrochemical Properties Of Fe-Doped Tio2 Nanotube Arrays, Jing Li, Lan Sun, Hui-Fang Zhuang, Cheng-Lin Wang, Rong-Gui Du, Chang-Jian Lin

Journal of Electrochemistry

The Fe-doped TiO₂ nanotube arrays were fabricated in Fe(NO₃)₃-HF mixing solutions by electrochemical anodic oxidation method,and characterized by FESEM,Raman,XPS and DRS.The effect of Fe concentratiions on photoelectrochemical property of the arrays was also investigated.The diameters and lengths of Fe-doped TiO₂ nanotube arrays were 50~90 nm and about 200 nm,respectively.Compared with the undoped TiO₂ nanotube arrays,the absorption edge of Fe-doped TiO₂ nanotube arrays appeared red shifting.The more Fe content,the larger red shifting,in addition,the photocurrent of Fe-doped TiO₂ nanotube arrays increased obviously.

Cyclic Voltammetry And In Situ Ftir Studies Of Cyanide Adsorption On Nanostructured Au Film Electrode In Alkaline Solutions, Chun-Hua Zhen, Chun-Jie Fan, Shi-Gang Sun

Journal of Electrochemistry

The adsorption of cyanide(CN^-) on electrodes of nanometer scale thin film of gold supported on glassy carbon(nm-Au/GC) in alkaline solutions were investigated using cyclic voltammetry and in situ FTIR spectroscopy.It has revealed that the electrodeposited nanostructured Au thin film exhibited AIREs(abnormal infrared effects) for CN^-adsorption,which manifested 3 nonlinear IR spectral features: inversion of the direction of CN^-band,enhancement of IR absorption of adsorbed CN-species(about 39.2 folds) and increase in the FWHM(full width at half maximum) of CN^-band.

Quick Tester With Usb Interface For The Corrosion Protection Properties Of Organic Coating, Xiang-Dong Zhuo, Chang-Jian Lin

Journal of Electrochemistry

According to the principle of multiple dynamic potential scaning polarization,a quick tester with USB interface for the fast study of corrosion resistance properties of organic coating/ metal system has been developed.This tester is portable,facile,practical,and has a strong function for data collection and data treatment.It is not only suitable for the accelerated test in laboratory,but also for the quick test and evaluation to the corrosion resistance of the organic coating/metal system in industrial spots.

Broadband Dielectric Spectroscopy Studies Of Nafion, David Walter Rhoades

Dissertations

In light of available literature regarding Nafion® materials, it is apparent that an information gap exists between the current state of understanding of Nafion relaxations and the dielectric behavior of these materials. Although the currently available dielectric relaxation data is accurate it is very limited in its scope—specifically in-depth broadband analyses are not available. As a result, very little information is available regarding the dependence of the relaxation processes on frequency and temperature. This presents an important opportunity for the exploration of the dielectric broadband relaxation behavior of Nafion® materials. The primary intent of this research is to quantify the …

Preparation Of Halogenated Derivatives Of Thiazolo[5,4-D]Thiazole Via Direct Electrophilic Aromatic Substitution, Vladimir Benin, Alan T. Yeates, Douglas Dudis

Chemistry Faculty Publications

Chlorination and bromination reactions of thiazolo[5,4-d]thiazole led to the generation of its mono- and dihalogenated derivatives. These are the first instances of successful direct electrophilic aromatic substitution in the thiazolo[5,4-d]thiazole ring system. X-ray analysis demonstrates that both 2-bromothiazolo[5,4-d]-thiazole and 2,5-dibromothiazolo[5,4-d]thiazole are planar structures, with strongly manifested π-stacking in the solid state. Theoretical analysis of the pyridine-catalyzed halogenation (MP2/6-31+G(d) and B3LYP/6-31+G(d)calculations) reveals that introduction of one halogen actually leads to a slightly enhanced reactivity towards further halogenation. Several halogenation mechanisms have been investigated: 1) The direct C-halogenation with N-halopyridine as electrophile; …

Synthesis And Characterization Of Polymeric Materials Derived From Multifunctional Alkyl A-Hydroxymethylacrylates, Jean-Francois Morizur

Dissertations

The research presented in this dissertation covers the investigation of new materials derived from alkyl a-hydroxymethylacrylates (RHMA). The first project exposed in Chapter II involves the synthesis, characterization of RHMA-based reactive surfactants and their successful incorporation in acrylic latexes. The amphiphilic monomers testify of a good copolymerization behavior with other acrylic monomers such as methyl methacrylate and butyl acrylate although their extensive bulkiness. They led to the formation of well-defined polymeric particles via a seeded emulsion polymerization process and permitted decreasing significantly the water sensitivity of the resulting films as compared to film incorporating conventional emulsifier such as sodium dodecyl …

Photopolymerization And Characterization Of Crosslinked Thiol-Ene Networks And Poss/Thiol-Ene Nanocomposites, Tolecia Sharonda Shaunee Clark

Dissertations

Interests in the area of thiol-ene photopolymerization are rapidly expanding due to the numerous advantages over the polymers produced by traditional solvent based polymerizations. Although current research of photoinitiated thiol-ene polymerization is diverse, numerous opportunities are available for investigating structure/property and structure/reactivity relationships and novel material applications. This research in this dissertation includes a fundamental study of the effect of monomelic thiol functionality on thiol-ene polymerization kinetics and formation of the thiol-ene network structure, and an investigation of the development of novel silicate based thiol-ene nanocomposites. The first fundamental study investigates the effect of thiol functionality on the kinetics and …

Stability And Equation Of State Of A Nanocrystalline Ga-Ge Mullite In A Vitroceramic Composite: A Synchrotron X-Ray Iffraction Study, Kristina E. Lipinska-Kalita, Patricia Kalita, Cedric Gobin, Oliver Hemmers, Thomas Hartmann, Gino Mariotto

Environmental Studies Faculty Publications

Synchrotron x-ray diffraction and diamond anvil cell techniques were used to characterize the phase transformations and to evaluate the structural stability at elevated pressures of a developed nanocrystalline composite. The optically transparent material was built of a germanium oxide-based amorphous host matrix with homogeneously dispersed 13±3 nm Ga-Ge mullite-type nanocrystals, which had a structure similar to the conventional Al₂O₃-SiO₂ mullite. The equation of state of the nanocrystals and the overall structural integrity of the nanocomposite were investigated in quasihydrostatic conditions on compression to 36 GPa and on the following decompression to ambient conditions. The overall …

Equation Of State Of Gallium Oxide To 70 Gpa: Comparison Of Quasihydrostatic And Nonhydrostatic Compression, Kristina E. Lipinska-Kalita, Patricia Kalita, Oliver Hemmers, Thomas Hartmann

Environmental Studies Faculty Publications

Synchrotron x-ray diffraction and diamond-anvil cell techniques were used to characterize pressure induced structural modifications in gallium oxide. Gallium oxide was studied on compression up to 70 GPa and on the following decompression. The effect of the pressure-transmitting medium on the structural transformations was investigated in two sets of compression and decompression runs, one with nitrogen as a quasihydrostatic pressure-transmitting medium and the other in nonhydrostatic pressure conditions. The x-ray diffraction data showed gradual phase transition from a low-density, monoclinic β-Ga₂O₃ to a high-density, rhombohedral α-Ga₂O₃. With the use of nitrogen as a …

Cu Doping Lifepo4 And Its Electrochemical Performance, Ming-Sen Zheng, Shan-Ke Liu, Shi-Gang Sun, Quan-Feng Dong

Journal of Electrochemistry

LiFePO₄ and LiFePO₄ doped with Cu²⁺ ions were synthesized by solid-state reactions.The structure of LiFePO₄ and the Fe valence were analyzed by the XRD(X-ray diffraction) and XPS(X-ray photoelectron spectroscopy) respectively.The Cu doping position in LiFePO₄ is discussed.It has found that the volume of LiFePO₄ by doping Cu²⁺ ions is reduced.The minim Cu²⁺ ions doping does not almost change the binding energy of Fe₂p_1/2 in LiFePO_4.According to the experiment results,we conclude that most of the Cu²⁺ ions substitute the Fe²⁺ ions in LiFePO₄ when a …

In Situ Measurement Of Chloride Concentration And Ph Distribution In The Crevice During The Crevice Corrosion Of Copper Electronic Board, Min Zhang, Xiang-Dong Zhuo, Chang-Jian Lin

Journal of Electrochemistry

Although the crevice corrosion of metals had been extensively studied in the past years,it remained lack of direct experimental information of the micro chemical environments and electrochemical conditions inside the corroding crevice.The distribution of chloride concentration and local pH in the occluded area are the most crucial factors in development of crevice corrosion.The array probes in one dimension of Ag/AgCl and IrO₂ array were developed in this work to in situ follow the distribution of chloride concentration and local pH in the occluded area during the crevice corrosion propagation.Based on a designed simulated crevice corrosion system in 0.5mol/L NaCl …

A Study On Supercapacitor Based On Aligned Carbon Nanotubes, Xiao-Yan Ye, Yan-Zhi Wang, Hai-Yan Song, Zhuo Sun, Pin-Gang He, Yu-Zhi Fang

Journal of Electrochemistry

Large scale vertically aligned carbon nanotubes(ACNTs) with uniform length and diameter were prepared by the pyrolysis of iron(Ⅱ) phthalocyanine at low pressure.The ACNTs were activated by electrolyte-activation,acid-activation or electrochemical activation.The performance of the capacitor based on activated ACNTs was characterized by cyclic voltammograms which was of rectangular shape,impedence spectroscopy in which the phase is above 80° and the result specific capacitance was 16～32 F/g,which suggest that the ACNTs are the promising material for the supercapacitor.

Preparation And Electrochemical Performance Of Ordered Mesoporous Titanium Phosphate As Cathode Material For Li-Ion Battery, Qiong Wang, Attia Adel, Zhi-Cong Shi, Yong Yang

Journal of Electrochemistry

Ordered porous titanium phosphate materials were prepared by using the surfactant template combined with the sol-gel method. The samples were characterized by small angle X-ray diffraction(SA-XRD) method, N₂ adsorption/desorption techniques,high resolution transmission electron microscopy(HRTEM) and element analysis. It is found that the calcination temperature is a big influence on the porous structure, and electrochemical performance of the titanium phosphate materials, and the mesoporous titanium phosphate showed good performance in the electrochemical test, the first discharge capacity is 94 mAh/g at the current density of 150 mA/g. On the other hand, the no porous material with a low capacity of …

Synthesis Of Adipic Acid From Cyclohexanol By Electrochemical Oxidation Using Cr2O72-/Cr3+ As Indirect Oxidant, Zhen-Hai Liang, Yu-Qing Cui, Hong-Yan Sun

Journal of Electrochemistry

Adipic acid was synthesized by electro-oxidation of cyclohexanol taking Cr₂O₇^2-/Cr³⁺ as indirect oxidant.The best technological conditions were optimized by orthogonal experiment.The optimum condition are as follows: the temperature is 35 ℃,ratio of crude material is n(cyclohexanol)∶n(Cr₂O₇^2-)=0.4∶1 and concentration of H₂SO₄ is 4 mol·L^-1.Under these conditions,the yield of adipic acid can reach 70.29%.Moreover,The effects of concentration of Ag₂SO₄,(NH₄)₂SO₄,H₂SO₄and current density on the formation of Cr₂O₇^2-were also …

Mechanism Of The Cathode Reduction Of Ti(Ⅳ) In Molten Na3Alf6-Alf3, Hai-Bin Sun, Xiu-Rong Zuo, Zhi-Guo Zhong, Xue-Hui Hu

Journal of Electrochemistry

The mechanism of TiO₂ electrode process has been investigated by cyclic voltammetry and chronopotentiometry on the tungsten filament in molten Na₃AlF₆-AlF₃ salts at 990 ℃.The experimental results showed that electrochemical reduction of Ti(Ⅳ) precede were two steps,firstly Ti(Ⅳ) was reduced to Ti(Ⅱ),then Ti(Ⅱ) was reduced to Ti,namely: Ti(Ⅳ)→Ti(Ⅱ)→Ti.

Interfacial Electrochemical Behavior Of Fibrinogen On Pt Electrode, Song-Mei Chen, Jian-Zhang Zhou, Zhong-Hua Lin, Dong-Mei Zeng, Nan Huang, Guo-Jiang Wan

Journal of Electrochemistry

The interfacial electrochemical behaviors of fibrinogen on Pt electrode in phosphate buffered solution(PBS) was investigated by using cyclic voltammetry and electrochemical in-situ FTIR spectroscopy.The cyclic voltammetry results demonstrated that the fibrinogen adsorb on Pt electrode and impede the interfacial charge transfer of hydrogen ion reaction process as well as of oxygen reduction process,which is increased with higher scan rate.The cyclic voltammetry spectra of platinum absorbed with fibrinogen in K₃[Fe(CN)₆] and K₄[Fe(CN)₆]·3H₂O solutions shows that the fibrinogen can partly decrease the oxidation and reduction current peaks.There is no specific anodic and …

Effects Of Oxidation Methods On The Stability Of Coooh Conductive Network In Foam Nickel Electrodes, Xiao-Feng Li, Yan-Wei Wei, Hui-Chao Dong

Journal of Electrochemistry

Two kinds of the cobalt oxyhydroxide conductive networks in foam nickel electrodes were prepared by different methods i.e.the electrochemical-oxidation(EO) and chemical-oxidation(CO) and which redox behaviors were studied by using cyclic voltammetry and X-ray diffraction measurements.The results show that the CoOOH(CO) has better redox reversibility than CoOOH(EO) and the structure of the former can be kept when nickel electrodes are subjected to a negative potential.Thus,98.7% capacity retention is demonstrated on nickel/metal-hydride batteries with CoOOH(CO) conductive network after being imposed over-discharge state storage;on the contrary,only 83.3% capacity retention is found on the batteries with CoOOH(EO) conductive network.

The Influence Of The Sputtering Power On The Structural And Electrochemical Properties Of Tin Oxide Films, Min-Zhen Cai, Jie Song, Ming-Sen Zheng, Qi-Hui Wu, Sun-Tao Wu, Quan-Feng Dong

Journal of Electrochemistry

Tin oxide films were deposited on silicon substrates at room temperature using the radio frequency(RF) magnetron sputtering with different sputtering power.The influence of sputtering power upon the crystal structure,surface morphology and electrochemical properties of tin oxide films were then investigated.The XRD and SEM results illustrate that the phase of tin oxide thin films changed from amorphous to crystalline and the grain size augments with the increase of the sputtering power.The constant current charge and discharge cycle tests imply that the initial irreversible capacity loss of Li/tin oxide batteries increase and which capacity decrease as the sputtering power increases.The sputtering power …

Effect Of Au At Different States On Electrocatalytic Performance Of Pd Catalyst For Oxidation Of Formic Acid, Xin Wang, Ya-Wen Tang, Tian-Hong Lu

Journal of Electrochemistry

Using liquid-reduction or complex-redution method,four catalysts,i.e,the Au/C,Pd/C,Pd-Au/C-T and Pd-Au/C-H were preparated and which electroanalytic activities and stabilities for the oxidation of formic acid were compares.It was found that the Au/C catalyst has no electrocatalytic activity,and the Pd/C catalyst possesses the good electrocatalytic performance for the oxidation of formic acid.The addition of Au into the Pd/C catalyst can increase the electrocatalytic activity and stability.Especially,the electrocatalytic activity and stability of the Pd-Au/C-T catalyst with the alloy of Pd and Au are better than that of the of the Pd-Au/C-H catalyst,in which,Pd and Au do not form the alloy.The investigation of its reason …

Molten Salt Treatment Of Mno2 And Investigation On Supercapacitor Properties, Ye Chen, Zun-Bo Zhang, Wei Zhang, Liang Liu, Zhi-Min Liu

Journal of Electrochemistry

The MnO₂ prepared by solid phase method is treated by KCl-NaCl-LiCl molten salt system.The XRD patterns indicated that the crystal structures of MnO₂ sample have had the α-MnO₂ and γ-MnO₂ phase,the crystallinity of sample is increased after treated by molten salt.The electrochemical properties were tested by cyclic voltammetry,constant current charge/discharge and AC impedance.The result shows that the supercapacitor performance of the treated material has improved.The specific discharge capacitance of the treated sample are 129.07 F·g^-1,increased by 27.88% compared to 100.94 F·g^-1 of untreated sample.Long cycle life and high coulombic efficiency were also demonstrated …

Synthesis Of 2,2′-Dichlorohydrazobenzene Using An Ion Exchange Membrane, Chao Zhang, Pei-Jin Li

Journal of Electrochemistry

Using an ion exchange membrane as a separator,the 2,2′-Dichlorohydrazobenzene is synthesized by the electrolytic reduction of o-chloronetrobenzene.The effects of electrode activation condition,current density,electrolyte temperature on electrolytic reduction are discussed.It was found that the optimum reaction temperature is 80 ℃.When the electrolyte concentration was 30% NaOH at the anode and 10% NaOH at the cathode,current density is 4.2A/dm²,the current efficiency reached 73% and yield is 83%.

Potentiometric Response Of Glucose On Mno2-GoX Carbon Paste Electrode, Cai-Juan Wang, Xiao-Ya Hu

Journal of Electrochemistry

A novel carbon paste electrode(CPE) modified with MnO₂ and glucose oxidase(GO_x), is reported. Different factors, such as the effect of supporting electrolyte, pH of solutions,various paste glues, the amount of MnO₂ and temperature, which may influence the determination of H₂O₂ and glucose were tested to optimize. Based on above, potentiometric determination of glucose was achieved in neutral solution and at 35 ℃, the electrode gave a response of 36.12～34.62 mV/pG lucose between 2.0×10^-5 mol·L-1 and 5.2×10^-3 mol·L^-1 with a detection limit of 3.3×10^-6 mol·L^-1. Moreover, this kind …

Square Wave Stripping Voltammetric Behaviors Of Rutin On Glassy Carbon Electrode And Its Application, Jun Hua, Xiao-Ying He, Fang Liao, Qing-Tao Zhu

Journal of Electrochemistry

The electrochemical behaviors of rutin(Rt) at glassy carbon electrode were studied by square wave stripping voltammeter in the presence of 0.1mol·L^-1HAc-NaAc buffer solution(pH=3.0).The sensitive oxidation peak of rutin was observed and which potential peak is 0.46V(vs.SCE).The experimental parameters,such as pH value,deposition potential and deposition time were investigated and selected.The peak currents were proportional to the concentration of rutin in range of 5.0×10^-8 mol·L^-1~1.0×10^-6mol·L^-1,and the linear regression coefficient equaled 0.99799,the detection limit was 1.1×10-8 mol·L^-1.This method was applied to the determination of rutin content in tablet with satisfactory results.

Corrosion Electrochemical Behavior Of Az31 And Az61 Magnesium Alloys In Simulated Sea Water, Ling-Jie Li, Sheng-Hai Yu, Jing-Lei Lei, Chuan-Pu Liu, Sheng-Tao Zhang, Fu-Sheng Pan

Journal of Electrochemistry

Tafel polarization curves and electrochemical impedance spectroscopy(EIS) techniques were employed to investigate the corrosion electrochemical behavior of AZ31 and AZ61 magnesium alloys.Scanning electron microscopy(SEM) was used to observe the alloy microstructure and corrosion morphology.The variation of the bulk corrosive medium pH with immersion time was recorded during the exposure of the alloys to simulated sea water.Results show that AZ61 magnesium alloy exhibits much better anti-corrosion ability than AZ31 magnesium alloy.The different corrosion behavior between the two magnesium alloys is correlated with their different content of Al alloying element.The higher content of Al in AZ61 alloy leads to the homogenerous microstructure …

The Determination Of Vitamin C By Bromophenol Blue Modified Glassy Carbon Electrode, Shu-Lin Zhang, Min-Jiao Li, Yi Luo, Xiao-Bo Wang

Journal of Electrochemistry

The content of ascorbic acid of(vitamin C) was analyzed by using fast cyclic voltamment with bromophenol blue(BPB) modififed GC-electrode,and which experimental conditions were optimiged.The results showed that the BPB modified GC-electrode had the good stability and anti-jamming faculty for analysing the content of ascorbic acid.A linear relationship between the peak current and concentration of vitamin C in the range of 0.0050~0.1500 g·L^-1 was obtained,which related coefficient and the detection limit are-0.9991 and 0.0010 g·L^-1,respeclively.The method has satisfactory results.

Dirubidium Digallium Oxide Bis(Orthoborate), Robert W. Smith, Chunhua Hu, Christopher D. Despain

Chemistry Faculty Publications

The title compound, Rb2Ga2O(BO3)2, is part of the homologous series A2Ga2O(BO3)2 (A = Na, K, Rb and Cs). The structure contains pairs of gallium-centered tetrahedra connected through a shared oxygen vertex. Orthoborate triangles connect the basal vertices of the tetrahedra, forming a three-dimensional network with voids occupied by rubidium ions.

C–N Bond Rotation And E–Z Isomerism In Some N-Benzyl-N-Methylcarbamoyl Chlorides: A Dft Study, Michael Horwath, Vladimir Benin

Chemistry Faculty Publications

The current report presents the first theoretical study of the restricted CN bond rotation in carbamoyl chlorides. Several N-benzyl-N-methylcarbamoyl chlorides were investigated, with varying pattern of substitution in the aromatic ring. Optimizations and frequency calculations were conducted employing DFT at the B3LYP/6-31+G(d) level of theory. Each of the studied structures exhibits a pair of rotamers (s-Z and s-E), generated upon rotation around the C(O)N bond. The s-E isomer is the global minimum in every case, but the preference for it is usually less than 1 kcal/mol. Two possible transition state structures were identified …

Ua66/1/5 Icset - Institute For Combustion Science & Environmental Technology, Wku Ogden College Of Science & Engineering

WKU Administration Documents

History and overview of the work of the WKU Institute for Combustion Science & Environmental Technology through 2008.

Mass Spectrometry Of Dendrimer Metal Complexes, Jason David Batchelor

Theses, Dissertations and Capstones

Dendrimers are hyper-branched macromolecules with unique properties. They form using a “cascade-like” synthesis involving repetitive reaction steps. These steps are controlled, resulting in monodisperse dendrimers. Synthesis is divergent, core to exterior, or convergent, exterior to core. Dendrimers are created from various molecules with numerous functional properties. They are used as catalysts, diagnostic agents, and others.

This thesis studies 1st generation poly(propylene) imine, consisting of a diaminobutane core with 4 propyl amine branches. Fragmentation of protonated and metal (Co, Ni, Cu and Zn) complexed dendrimers was analyzed by ion-trap mass spectrometry. Two isotopically labeled dendrimers were synthesized for neutral loss identification …