Metallurgy Commons^™

Characterization Of Virgin, Re-Used, And Oxygen-Reduced Copper Powders Processed By The Plasma Spheroidization Process, M. Hossein Sehhat, David Perez-Palomino, Connor Wiedemeier, Tristan Cullom, Joseph William Newkirk

Mathematics and Statistics Faculty Research & Creative Works

Fabrication of parts with high mechanical properties heavily depend on the quality of powder deployed in the fabrication process. Copper powder in three different powder types were spheroidized using radio-frequency inductively coupled plasma (ICP) spheroidization process (TekSphero-15 system). The characterized powders include virgin powder as purchased from the powder manufacturer, powder used in electron beam powder bed fusion (EB-PBF) process, and reconditioned powder, which was used powder that underwent an oxygen-reduction treatment. The goal of spheroidizing these powder types was to evaluate the change in powder morphology, the possibility of enhancing the powder properties back to their as-received conditions, and …

Phenomenological Analysis Of Surface Degradation Of Metallic Materials In Extreme Environment, Simon N. Lekakh, Oleg Neroslavsky

Materials Science and Engineering Faculty Research & Creative Works

The resistance to surface degradation in metallic alloys plays an important role for the lifetime of the components working in harsh environments. The mechanisms involved in degradation of metallic surface in a high-temperature aggressive gaseous atmosphere include the following: forming adherent to the surface multiphase oxide layer, partial spallation, and possible vaporization of formed compounds. The governing equation, which describes a parabolic growth of adherent layer, time-dependent vaporization, and cross-linked to instantaneous thickness of adherent layer spallation rate, was suggested and analyzed. The several relationships between the kinetic constants were defined from analysis of the governing equation. Design of routes …

Microstructure Evolution And Austenitic Grain Refinement Of Ti-Modified High Mn Steels During Solution Annealing Heat Treatment, Abhinav Karanam, Arnab Sarkar, Erik Nenzen, Viraj Ashok Athavale, Mark Watson, Laura Nicole Bartlett, Lukas Bichler

Materials Science and Engineering Faculty Research & Creative Works

Austenitic high manganese (Mn) steels are often used in harsh environments due to their high toughness and wear resistance. Heat treatments are performed to engineer the microstructure of the steels and optimize their performance for the desired service conditions. This study investigated the effect of titanium (Ti) and heat treatment on the microstructure of cast high Mn steel (HMS) alloys. The results reveal that Ti addition contributed to grain refinement in the as cast and heat-treated conditions. In-situ observation of microstructure evolution up to 1125 °C confirmed the stability of precipitated TiC particles, while revealing a new mechanism of grain …

Residual Stress Distribution, Distortion, And Crack Initiation In Conventional And Intensive Quench Practices, Kingsley Tochukwu Amatanweze, Mario F. Buchely, Viraj Ashok Athavale, Laura Bartlett, Ronald J. O'Malley, Toshi Suzuki

Materials Science and Engineering Faculty Research & Creative Works

This study evaluates the effect of two different quench practices on distortion, sensitivity to quench cracking, development and distribution of residual stress, microstructural uniformity, and hardenability of standardized test castings. Navy C-rings made of AISI 4340 were quenched in this experiment. Some rings were quenched in a conventional draft tube immersion quench bath, and others were quenched in an intensive quench spray system to compare with the results from the conventional immersion quench bath. The rings were measured with a coordinate measuring machine, for distortion and flatness, before and after quenching. Hardness profiles of the quenched rings showed through hardness …

Compositional Modifications To Alter And Suppress Laves Phases In Alxcrmotayti Alloys, Austin E. Mann, Joseph William Newkirk

Materials Science and Engineering Faculty Research & Creative Works

Herein, the Development of Refractory Complex Concentrated Alloys in the Al–Cr–Mo–Ta–Ti Alloy System is Reported. Alloys with Modified Al and Ta Concentrations Are Designed using CALPHAD Tools and Produced Via Arc Melting and Characterized in Both As-Cast and Annealed Forms. Properties of the Alloys, Nature of the Microstructures, and Phase Transformation Behavior Are Described Via X-Ray Diffraction, Microstructural Characterization, Microhardness, and Differential Scanning Calorimetry. Two Alloys, Namely, Al0.25CrMoTa0.8Ti and Al0.75CrMoTa0.8Ti, Are Represented by a Body-Centered-Cubic Matrix Phase after Annealing, along with a Secondary Cr–Ta Laves Phase of the C15 and C14 Polytypes, respectively. in As-Cast and Annealed Forms, the Al0.75CrMoTa0.45Ti …

Characterization Of Virgin, Re-Used, And Oxygen-Reduced Copper Powders Processed By The Plasma Spheroidization Process, M. Hossein Sehhat, David Perez-Palomino, Connor Wiedemeier, Tristan Cullom, Joseph William Newkirk

Materials Science and Engineering Faculty Research & Creative Works

Fabrication of parts with high mechanical properties heavily depend on the quality of powder deployed in the fabrication process. Copper powder in three different powder types were spheroidized using radio-frequency inductively coupled plasma (ICP) spheroidization process (TekSphero-15 system). The characterized powders include virgin powder as purchased from the powder manufacturer, powder used in electron beam powder bed fusion (EB-PBF) process, and reconditioned powder, which was used powder that underwent an oxygen-reduction treatment. The goal of spheroidizing these powder types was to evaluate the change in powder morphology, the possibility of enhancing the powder properties back to their as-received conditions, and …

Characterization Of Virgin, Re-Used, And Oxygen-Reduced Copper Powders Processed By The Plasma Spheroidization Process, M. Hossein Sehhat, David Perez-Palomino, Connor Wiedemeier, Tristan Cullom, Joseph William Newkirk

Materials Science and Engineering Faculty Research & Creative Works

Fabrication of parts with high mechanical properties heavily depend on the quality of powder deployed in the fabrication process. Copper powder in three different powder types were spheroidized using radio-frequency inductively coupled plasma (ICP) spheroidization process (TekSphero-15 system). The characterized powders include virgin powder as purchased from the powder manufacturer, powder used in electron beam powder bed fusion (EB-PBF) process, and reconditioned powder, which was used powder that underwent an oxygen-reduction treatment. The goal of spheroidizing these powder types was to evaluate the change in powder morphology, the possibility of enhancing the powder properties back to their as-received conditions, and …

Understanding Charge Effects On Marked Ball Wear Rates – A Corrosion Study, John Bailey Fletcher

Masters Theses

"To measure the wear rates of grinding balls within a ball mill, marked ball wear tests (MBWTs) have been used extensively. Using the wear rates from a MBWT, operators select the most cost-effective media for their grinding application. One factor that a MBWT does not account for is the possible interaction between different media materials which could affect their corrosion rates. Galvanic coupling between dissimilar metals can cause significant changes in their corrosion rates. While galvanic interactions between minerals and grinding media have been studied, the interaction between dissimilar media has not. Corrosion rates and potentials of modern high carbon …

Effect Of Boron In Cast Iron, Suyash Durendra Pawaskar

Masters Theses

"Boron, mostly considered a residual element, has started to cause issues in the cast iron foundries by causing a decrease in the strength of pearlitic gray and ductile iron castings. Because of the increase in the use of boron-added steel scrap from automotive steel and a lack of agreement on the critical levels of boron in cast iron, foundries are facing difficulties in controlling the microstructure of gray iron castings when boron is present. The current investigation was designed to analyze the effects of boron in cast irons and predict a mechanism to understand its effects with a vision of …

Tini-Based Bi-Metallic Shape-Memory Alloy By Laser-Directed Energy Deposition, Yitao Chen, Cesar Ortiz Rios, Braden Mclain, Joseph William Newkirk, Frank W. Liou

Materials Science and Engineering Faculty Research & Creative Works

In this study, laser-directed energy deposition was applied to build a Ti-rich ternary Ti-Ni-Cu shape-memory alloy onto a TiNi shape-memory alloy substrate to realize the joining of the multifunctional bi-metallic shape-memory alloy structure. The cost-effective Ti, Ni, and Cu elemental powder blend was used for raw materials. Various material characterization approaches were applied to reveal different material properties in two sections. The as-fabricated Ti-Ni-Cu alloy microstructure has the TiNi phase as the matrix with Ti₂Ni secondary precipitates. The hardness shows no high values indicating that the major phase is not hard intermetallics. A bonding strength of 569.1 MPa …

Effect Of Micro-Structural Dispersity Of Simo Ductile Iron On High Temperature Performance During Static Oxidation, Semen Naumovich Lekakh, Asebi Bofah, Larry A. Godlewski, Mei Li

Materials Science and Engineering Faculty Research & Creative Works

High silicon and molybdenum (SiMo) ductile iron is commonly used for car exhaust systems, and its micro-structural dispersity depends on intrinsic parameters, which include alloy composition and inoculation efficiency, as well as extrinsic factors, such as casting wall thickness and molding material, which define cooling rate during solidification. Micro-structural dispersity is referred to as the degree of heterogeneity of sizes of structural constituencies within the microstructure. A variation in the micro-structural dispersity could impact the high temperature performance of SiMo ductile iron during static oxidation and transient thermo-mechanical loading conditions. In this study, static high temperature tests were performed on …

Effects Of Carrier, Leveller, And Booster Concentrations On Zinc Plating From Alkaline Zincate Baths, Abdul Jalil Mohammed, Michael S. Moats

Materials Science and Engineering Faculty Research & Creative Works

Organic additives are required for alkaline zincate plating baths to obtain an acceptable coating on steel for corrosion protection. The effects and possible interactions of three commercial additives (Eldiem Carrier, Eldiem Booster, and Bright Enhancer 2x on zinc electrodeposition from a high-concentration alkaline zincate bath were investigated. Visually acceptable deposits were produced within the current density range of 130 to 430 A m^-2 for most additive conditions examined. Over concentration ranges examined, decreasing the booster concentration led to brighter zinc deposits, and an interaction between the carrier and the booster was detected. The additives fostered the formation of compact …

Control Of High-Temperature Static And Transient Thermomechanical Behavior Of Simo Ductile Iron By Al Alloying, Semen Naumovich Lekakh, Catherine E. Johnson, L. Godlewski, Mei Li

Materials Science and Engineering Faculty Research & Creative Works

Silicon and molybdenum (SiMo) ductile iron is commonly used for exhaust manifolds because these components experience thermal cycling in oxidizing environment, which requires resistance to fatigue during transient thermomechanical loads. Previous studies have demonstrated that alloying elements, such as Al, to SiMo ductile iron reduces the amount of surface degradation during static high-temperature exposure. However, deterioration of sphericity of the graphite nodules and a decrease in ductility could affect the tendency of cracking during thermal cycling. In this article, the effect of Al alloying on static and transient thermomechanical behavior of SiMo ductile iron was investigated to optimize the amount …

Zinc Plating From Alkaline Non-Cyanide Bath, Abdul J. Mohammed

Masters Theses

“Alkaline non-cyanide zinc plating baths are preferred when trying to avoid the toxicity of cyanide baths or corrosivity of acid baths. Without additives, alkaline zincate baths produce powdery non-adherent deposits which have no use in commercial plating. Additives must be added at optimum concentrations to produce adherent, bright and uniform zinc deposits. In this study electrochemical tests were used to determine effects of additives on cathodic polarization, throwing power and morphology of deposits. Current density distribution in a unique bath of 37.5 g L^-1 Zn and 210 g L^-1 NaOH was modelled using COMSOL and validated two plating …

Experimental Optimization Of Simulated Ring Rolling Operation For Heavy Rail Industry, Jacob M. Summers

Masters Theses

“Industrially cast AISI 1070 steel wheel pre-forms from Amsted Rail Co. were experimentally hot rolled to simulate the conditions for industrial wheel rolling. Ring rolling of near net shape castings can improve location specific properties by decreasing segregation, closing porosity, and reducing grain size without the use of multiple forging operations in a traditional forging line. As-cast wheel sections were subjected to thermomechanical processing routes using a 2-high rolling mill in a temperature range of 830°C to 1200°C. The goal being to simulate the ring rolling process and optimize benefits of mechanical properties of the as-rolled steel. Charpy V- and …

Controlling Microalloy Interactions On Precipitation, Hot Ductility, And Microstructure -- Mechanical Property Relationships, Madhuri Varadarajan

Masters Theses

“One of the main problems faced in the continuous casting of micro-alloy steels is the formation of transverse cracks. Transverse cracks are surface, or near-surface cracks formed perpendicular to the casting direction. The research focuses on using laboratory hot tensile tests methods to determine the low ductility ranges in high strength steel grades with different micro-alloy additions of titanium, niobium, and vanadium. The hot ductility of commercially produced as-cast slab and beam blank samples was evaluated using two experimental methods: tensile testing utilizing a servo-hydraulic load frame with a resistance furnace and thermomechanical testing using rapid Joule heating. The tests …

Corrosion Protection Mechanisms Of Trivalent Chromium Based Passivations On Γ-Znni Coated Al6061-T6 Alloy, Kevin Foster

Doctoral Dissertations

“The role of cobalt in trivalent chromium passivations (TCPs) to improve corrosion resistance of γ-ZnNi coated steel and aluminum is based on its effect on hexavalent chromium content in the passive layer. Investigations of both a cobalt-containing and cobalt-free TCP on SAE 1008 steel indicated that both passivations protect well for up to 1000 hours in neutral salt spray exposure (SSE). A repetition on Al 6061-T6 alloy indicated that TCP performed much better than cobalt-free TCP implicating the underlying substrate. Optical and electron micrographs indicated physical changes such as crack thickness, crack density, passivation porosity, and passivation thickness existed between …

Scale Formation, Properties And De-Scaling In Steelmaking, Richard Osei

Doctoral Dissertations

During continuous castings, reheating, and hot rolling, slab surfaces are exposed to atmospheres containing oxidizing gases which results in scale formation. Inefficient removal of the formed scale during reheating affects product surface quality. The effect of steel composition and operating parameters on scale formation and scale removal efficiencies were investigated. Experimental investigations were carried out using a thermogravimetric (TGA) apparatus designed to replicate the combustion gas atmosphere and temperature in actual industrial slab reheat furnaces. Report on oxidation kinetics, scale structure and properties, and descaling were conducted on laboratory cast and industrial samples. Different characterization techniques were used to analyze …

Peritectic Behavior Detection And Prediction In Fe-C-Si-Mn-Al System, Damilola Balogun

Doctoral Dissertations

"The non-uniformity of shell growth in the continuous casting of peritectic steels constitutes a major barrier to the commercial production of many steel grades such as Advanced high strength steels (AHSS), transformation induced plasticity (TRIP) steels, abrasion-resistant steels, advanced armor plate steels, and many newly proposed steel grades that contain high levels of silicon, manganese, and aluminum.

The shell growth non-uniformity experienced in the continuous casting of peritectic steels results in the formation of defects in the as-cast slab and therefore increases the operating risk from cast aborts and breakouts. The ability to predict and avoid peritectic behavior at the …

The Effect Of Mass Transport On Deposit Quality In Copper Electrowinning, Joseph Bauer

Doctoral Dissertations

"Roughness and nodulation of copper electrodeposits depend strongly on mass transfer conditions of copper ions to the electrode surface. Mass transfer properties in electrowinning electrolytes were first characterized. The effective diffusivity of cupric ion was measured with a rotating disk electrode in CuSO₄-H₂SO₄ electrolytes at temperatures relevant to electrowinning, with and without additives. Adding 20 mg L^-1 of chloride ion increased the measured diffusion coefficient, but commercial smoothing additives had little effect. An empirical formula to predict cupric diffusivity was generated for later use in mass transport modeling.

Boundary layer thickness information for commercial …

Fabricating Tinicu Ternary Shape Memory Alloy By Directed Energy Deposition Via Elemental Metal Powders, Yitao Chen, Xinchang Zhang, Mohammad Masud Parvez, Joseph William Newkirk, Frank W. Liou

Materials Science and Engineering Faculty Research & Creative Works

In this paper, a TiNiCu shape memory alloy single-wall structure was fabricated by the directed energy deposition technique with a mixture of elemental Ti, Ni, and Cu powders following the atomic percentage of Ti50Ni45Cu5 to fully utilize the material flexibility of the additive manufacturing process to develop ternary shape memory alloys. The chemical composition, phase, and material properties at multiple locations along the build direction were studied, using scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction, Vickers hardness test-ing, tensile testing, and differential scanning calorimetry. The location-dependent compositions of martensitic TiNi and austenitic TiNi phases, mechanical properties, and functional properties …

Absorption Of Nitrogen During Pulsed Wave L-Pbf Of 17-4 Ph Steel, Ben Brown, Joseph William Newkirk, Frank W. Liou

Materials Science and Engineering Faculty Research & Creative Works

In the fabrication of 17-4 PH by laser powder bed fusion (L-PBF) the well-documented occurrence of large amounts of retained austenite can be attributed to an elevated concentration of nitrogen present in the material. While the effects of continuous wave (CW) laser processing on in-situ nitrogen absorption characteristics have been evaluated, power modulated pulsed wave (PW) laser processing effects have not. In this study the effects of PW L-PBF processing of 17-4 PH on nitrogen absorption, phase composition, and mechanical performance are explored using commercially available PW L-PBF equipment and compared to samples produced by CW L-PBF. PW L-PBF samples …

Thermodynamic Prediction And Experimental Verification Of Multiphase Composition Of Scale Formed On Reheated Alloy Steels, Richard Osei, Semen Naumovich Lekakh, Ronald O'Malley

Materials Science and Engineering Faculty Research & Creative Works

The structure, phase, and composition of scale formed on a continuously cast steel slab during reheating depend on intrinsic factors (steel chemistry, microstructure, and as-cast surface condition) and extrinsic parameters (temperature, time, composition, and velocity of combustion gas atmosphere). The scale that forms on a slab normally has several layers with differing compositions and phases and knowledge of this scale structure is important in subsequent descaling and hot rolling processing steps. Formation of multiphase scale structures on steel during high temperature oxidation in reheat furnace proceeds according to a local thermodynamic equilibrium, while thickness of layers depends on kinetic conditions …

Toward Understanding Commercial Additives For Zincate Electrogalvanizing, Margaret Scott

Masters Theses

"Cyanide zinc electrogalvanizing has been used for many years to produce high quality and uniform zinc coatings. Due to toxicity concerns, a significant amount of research has occurred to remove the use of cyanide while still producing a similar deposit. One of the resulting plating chemistries is the alkaline zincate bath.

Alkaline zincate plating has the advantages of low startup cost, low toxicity, and low corrosion rate. Despite these advantages, alkaline bath conditions do not produce acceptable zinc deposits without the use of plating additives, which can promote lustrous, smooth deposits. This research aims to: (1) generate fundamental electrochemical data …

Optimization And Characterization Of Novel Injection Molding Process For Metal Matrix Syntactic Foams, Myranda Spratt, Joseph William Newkirk

Materials Science and Engineering Faculty Research & Creative Works

Metal matrix syntactic foams are particulate composites comprised of hollow or porous particles embedded in a metal matrix. These composites are difficult to manufacture due primarily to the lightweight, relatively fragile filler material. In this work, an injection molding process was developed for metal matrix syntactic foams. First, an aqueous binder was optimized for low-pressure injection molding. A mixture model was used to optimize the composition of the binder to achieve the highest relative density. The model predicted the maximum relative density was at a binder composition (in vol.%) of 7% agar, 4% glycerin, and 89% water. Second, this binder …

Microstructural Influence On Mechanical Properties Of A Lightweight Ultrahigh Strength Fe-18mn-10al-0.9c-5ni (Wt%) Steel, Michael Piston, Laura Bartlett, Krista R. Limmer, Daniel M. Field

Materials Science and Engineering Faculty Research & Creative Works

This study evaluates the role of thermomechanical processing and heat treatment on the microstructure and mechanical properties of a hot rolled, annealed, and aged Fe-18Mn-10Al-0.9C-5Ni (wt%) steel. The steel exhibited rapid age hardening kinetics when aged in the temperature range of 500-600 ⁰C for up to 50 h, which has been shown in other work to be the result of B2 ordering in the ferrite and K-carbide precipitation within the austenite matrix. The ultimate tensile strength increased from 1120 MPa in the annealed condition to 1230 MPa after 2 h of aging at 570 ⁰C. Charpy V-notch toughness was evaluated …

Peritectic Behavior Detection In The Fe-C-Mn-Al-Si Steel System Using Fiber Optic Temperature Mapping, Muhammad Roman, Damilola Balogun, Rex E. Gerald Ii, Laura Bartlett, Jie Huang, Ronald J. O'Malley

Materials Science and Engineering Faculty Research & Creative Works

Peritectic reactions can cause surface defects and breakouts in continuous casting and the peritectic region is often avoided by adjusting the chemical composition of the steel to cast outside of the peritectic sensitivity range. However, the combined effects of C, Mn, Al, and Si on the boundaries that map peritectic region are still disputed for many advanced high strength steel grades. An apparatus for performing controlled solidification experiments is being developed to characterize the effects of chemical composition on the uniformity of shell growth during solidification using a copper chill mold with an embedded fiber-optic temperature sensor that enables high …

A Modified Johnson-Cook Model Incorporating The Effect Of Grain Size On Flow Stress, S. Ganguly, Mario F. Buchely, K. Chandrashekhara, Semen Naumovich Lekakh, Ronald J. O'Malley

Materials Science and Engineering Faculty Research & Creative Works

The mechanical properties of steel are influenced by grain size, which can change through mechanisms such as nucleation and growth at elevated temperatures. However, the classic Johnson-Cook model that is widely used in hot deformation simulations does not consider the effect of grain size on flow stress. In this study, the Johnson-Cook model was modified to incorporate the effects of austenite grain size on flow stress. A finite element model was employed to characterize the effects of grain size on the flow stress for different steel grades over a range of temperatures (900⁰ to 1300⁰). Simulation results show good agreement …

Interactions Between Dry Vibratable Tundish Linings And Steel Melts, Tyler M. Richards, Ronald J. O'Malley, Jeffrey D. Smith, Todd P. Sander

Materials Science and Engineering Faculty Research & Creative Works

Interactions between two tundish working linings and molten steel were investigated using industrial samples and laboratory testing. Periclase-based dry vibe linings from two production facilities were sampled and examined after casting: one containing 30 wt.% olivine and one without olivine. Cathodoluminescence imaging, secondary electron microscopy, energydispersive spectroscopy and x-ray diffraction analysis were performed to characterize the interactions. An experiment was developed to replicate the conditions found in a production tundish on the laboratory scale. Results comparing interactions observed in laboratory lining tests and commercial lining samples for the two lining materials are presented and discussed.

Scale Formation On 430 Stainless Steel In A Simulated Slab Combustion Reheat Furnace Atmosphere, Richard Osei, Semen Naumovich Lekakh, Ronald J. O'Malley

Materials Science and Engineering Faculty Research & Creative Works

Scale formed during slab reheating can be difficult to remove by high-pressure descaling, having a negative impact hot roll surface quality. A large-capacity thermogravimetric apparatus that replicates the combustion atmosphere and temperature in a slab reheat furnace was used to investigate scale formation on 430 stainless steel. Effects of reheating parameters (temperature, time and atmosphere) on oxidation kinetics were investigated. Oxidized samples were characterized by scanning electron microscopy, Raman spectroscopy and x-ray diffraction to document the microstructure and morphology of scale. Mechanisms for the formation of multi-layered oxide structures that complicate oxidation kinetics and scale removal are discussed.