Evaluation Of Long Term Durability In Concrete With External Pre-Saturated Cfrp Laminate, Ramya Anandhan

Civil Engineering Theses - Archive

Many studies have investigated the use of carbon fiber reinforced polymer (CFRP) wraps to strengthen structural members, but there is limited literature on the application of presaturated CFRP wraps on reinforced concrete members. The main objective of this research is to study the long-term effectiveness of presaturated CFRP wraps in preventing corrosion of reinforced concrete specimens in severe environments. This paper presents numerical and experimental studies that were conducted to determine whether CFRP presaturated wraps provide a barrier against the ingress of chloride and permeability of water into concrete and thereby decelerate the corrosion process. The results show that the …

Long-Term Durability Of Solar Photovoltaic Modules, Chibuisi Chinasaokwu Okorieimoh, Brian Norton

Conference papers

Solar photovoltaic (PV) panels experience long-term performance degradation resulting in lower like-per-like efficiencies and performance ratios when compared with their initial performance. Manufacturers of solar photovoltaic modules usually guarantee the life span for more than 20 years. It is therefore necessary to track and mitigate degradation of PV modules over this period to satisfy such guarantees and beyond this period to identify maintenance and repair requirements. Degradation of solar PV modules makes them less efficient, less reliable and, ultimately, inoperative. This paper reviews relevant literature to discuss:

• Causes of efficiency reductions in photovoltaic cells

• Ways to achieve long-term durability of …

The Impact Of Conversion On The Durability Of Calcium Aluminate Cement Concrete Systems, Marwa Mohsen Korayem

Dissertations

The deterioration of infrastructure in North America has resulted in a significant need for concrete repair materials that can be used to maintain service life of these structures. Hydraulic cement based rapid repair materials can be used to repair pavement and bridge deterioration with minimal impact on economic activities such as freight handling or public transportation. While there are many options for use in repair situations, calcium aluminate cements have become more popular recently, particularly in situations where repairs must be completed rapidly.

Calcium aluminate cement (CAC) is a cement characterized by its rapid strength gain, even at low temperatures …

About The Influence Of The Organosilicon Hydrophobizer "Gidrofob" On The Properties Of Non-Autoclave Gas Concrete, V.M. Tsoy, S. Hodjayev

Journal of Tashkent Institute of Railway Engineers

The article examines the effect of hydrophobizing additives on the normal density and setting time of the cement paste and the strength of the cement stone. We used an organosilicon additive - "Hydrophobe" as a water-repellent additive. As a result of research, it was found that the introduction of a water repellent agent, depending on its dosage, leads to a significant increase in the setting time and insignificantly affects the strength

Production Of Fire-Resistant Concrete Based On Technogenic Waste, Uzmonjon Turgunaliyevich Yusupov

Journal of Tashkent Institute of Railway Engineers

The article notes that at present, with the development of the construction industry, the need for fire-resistant concrete is also increasing. In increasing the volume of construction, concrete and other components are some of the resources available at the price of finished objects achieved through cost reduction. It is determined that the developed fire- and heat-resistant concrete, prepared according to the technological requirements developed by us and the established standards, will provide the facility with reliable fire safety and longevity

Feasibility Study Of Development Of Ultra-High Performance Concrete (Uhpc) For Highway Bridge Applications In Nebraska, Flavia Ribeiro Furtado De Mendonca, Mostafa Abo El-Khier, George Morcous, Jiong Hu

Nebraska Department of Transportation: Research Reports

Ultra-high performance concrete (UHPC) is a new class of concrete that has superior mechanical, durability, and workability properties that far exceed those of conventional concrete. To achieve these properties, a specific mix design with a very dense internal structure, fiber reinforcement, and low water-to-binder ratio (w/b) is commonly used. The goal of this research is to develop a non-proprietary UHPC mix with constituent materials that are readily available in the state of Nebraska for bridge construction applications. In developing this mix, the particle packing model is used, and an experimental study of the impact of various design parameters on the …

Will Blended-Cement Systems With Similar Chloride Penetration Potentials Resist Similarly To Corrosion?, William Wilson, Vincent Labattaglia, Arezki Tagnit-Hamou, Luca Sorelli

International Conference on Durability of Concrete Structures

The capacity of concrete to prevent chloride ions penetration represents a key durability factor for steelreinforced structures exposed to de-icing salts and/or marine environments. Although blended-cement systems are commonly characterized with accelerated chloride penetration tests developed for Portlandcement concrete (e.g. the ASTM C1202 method), their microstructures and pore solutions are very different. This study aims to illustrate how the full potential of blended-cement systems to resist chloride ingress (and thus, chloride-induced corrosion) may not be justly disclosed by these accelerated tests using electrical current, even when tested after three months of curing. A Portland-cement-only mortar and five binary blended-cement mortars …

An Investigation On Moisture And Water Absorption In Cement Paste With Electrical Resistance Method, Manami Mizoguchi, Tatsuya Kitagawa, Totsawat Daungwilailuk, Yuko Ogawa, Kenji Kawai

International Conference on Durability of Concrete Structures

Moisture in concrete is one of main factors related to degradation and deterioration of concrete structure, and there are various moisture transport phenomena in concrete such as drying and absorbing. There are a lot of previous studies on the drying process of concrete to clarify the mechanisms of creep as well as shrinkage. However, few studies have been reported on the process of water absorption and moisture absorption although carbonation and chloride attack are strongly related to moisture and water absorbing. It is necessary to investigate moisture transfer in concrete in detail. This study investigated the moisture transfer in moisture …

Influence Of Pore Structure On Relative Chloride Diffusion Coefficient In Unsaturated Cementitious Materials, Yong Zhang, Guang Ye

International Conference on Durability of Concrete Structures

Chloride-induced corrosion of reinforcement in concrete structures is a serious issue in engineering practice. This paper investigates the influence of pore structure on the relative chloride diffusion coefficient Drc in unsaturated cementitious materials. The effects of various pore features, including porosity, pore size, and pore connectivity, on the continuity of water-filled pores in unsaturated porous systems are analyzed based on the Kelvin law and water desorption process. In the experimental program, different cementitious materials (OPC, slag, fly ash, and limestone powder) were used to prepare paste and mortar samples. The Drc of the mortar samples (one year old) at various …

Self-Sensing And Self-Healing ‘Smart’ Cement-Based Materials – A Review Of The State Of The Art, Dhanada Mishra Phd, Jing Yu, Christopher Leung Phd

International Conference on Durability of Concrete Structures

The paper reviews recent research on self-sensing and self-healing cement-based materials as part of Smart Civil Engineering Infrastructures. Incorporated in Structural Health Monitoring systems, these materials are likely to play an important role in making future infrastructure robust, resilient and sustainable. Smart or intelligent cement-based materials have attracted extensive attention in the last decade or so with strong implications for improving structural durability and service life. Additions of carbon fibres, carbon nano-tubes and various nano-powders giving cement-based matrix electrical properties used for self-sensing have been known for over a decade and a half. In addition, the strong capacity of Strain-Hardening …

Characterization Of Vibration Effects On The Internal Structure And Strength Of Regular And High Strength Recycled Concrete, Jovanca Smith, Rekha Rampit, R. Parey

International Conference on Durability of Concrete Structures

There is a need for more in depth understanding of the consolidation effect of concrete on its durability, especially in tropical climates. During placement of fresh concrete in molds vibration is required to prevent quality problems such as honeycombs and desegregation. Nevertheless, precise monitoring of concrete vibration time has been avoided by construction professionals. This results in concrete durability reduction of appropriately designed concrete due to variation in aggregate settlement, air void content and change in water to cement ratio. In this study, the effects of vibration time on concrete strength, aggregate segregation, and physical properties were experimentally investigated on …

Using Long-Term Outdoor Exposure Data To Benchmark Accelerated Durability Test Methods, R. Hooton

International Conference on Durability of Concrete Structures

Many performance-based durability test methods adopted in various national and international standards were developed decades ago based on short-term evaluations. Most durability tests use various methods to accelerate reactions in order to obtain results in a reasonably short period of time. Then pass/fail criteria are set for these tests in standard specifications. However, the acceleration techniques used maybe overly severe, and preclude the use of concrete materials and mix designs that perform perfectly well in the field. The inclusion of long-term field tests or outdoor exposure tests can be used to verify the appropriateness of both the test methods and …

Durability Of Cement-Based Materials In Drinking Water Storage, Matthias Schwotzer, Andreas Gerdes

International Conference on Durability of Concrete Structures

In order to provide a hygienic storage drinking water reservoirs have been coated with mineral mortar linings in all epochs of European history. However, modern cement-based materials often show in this special operational environment an inadequate durability. Even though drinking water is commonly not considered particularly harmful to cementitious systems, the chemical degradation of mortar linings in drinking water storage systems can occur very fast compared to other common deterioration reactions. This results in cost intensive repair measures and thus high life-cycle costs as well associated with an ecological burden. Furthermore, an insufficient understanding of degradation mechanisms and their underlying …

Effect Of External Loading On Durability Properties Of Pre-Stressed Concrete Girders With Microcracking, Savitha Sagari Srinivasan, Raissa Douglas Ferron, Michael Rung

International Conference on Durability of Concrete Structures

Over the last fourteen years, very early in the service life of pre-stressed concrete girders, unexplained microcracks have been observed. Their presence led to concerns about the future integrity of the girders, with one of the major concerns being corrosion of pre-stressing strands. As such, a comprehensive study aimed at understanding the effects these microcracks have on the service life of the girders was initiated. Eight in-service girders, under external loads, and five rejected girders, not under external loads, were selected for the study. In this paper, we present work on the temporal evolution of the cracks during a one-year …

Influence Of Surface Retarders On Texture Profile And Durability Of Upper Layer Of Exposed Aggregate Concrete Pavement, Mariusz Dąbrowski, Miachał Antoni Glinicki, Karolina Gibas, Aneta Antolik, Kinga Dziedzic

International Conference on Durability of Concrete Structures

Exposed aggregate concrete (EAC) pavement technology is used in Poland for construction of major highways and expressways. When properly executed, it is an efficient technique to provide desired friction for skid resistance without compromising the noise limitations. Concrete mix uniformity, proper dosing of retarding agent and optimal time to brush with a mechanical broom are supposed to have a major impact on the properties of the upper pavement layer. An experimental investigation was performed on exposed aggregate concrete specimens manufactured in the laboratory in a way to simulate the industrial production of two-layer concrete slab with exposed aggregate. The texture …

Freeze-Thaw Resistance Of Concrete: Insight From Microstructural Properties, Sam Adu-Amankwah, Leon Black Dr, M Zajac, J Skoceck, M Ben Haha

International Conference on Durability of Concrete Structures

Composite cements offer low carbon alternatives to conventional CEM I. These binders also generally tend to perform better than CEM I in aggressive chemical environments. However, their freeze-thaw resistance, evident through surface scaling and internal damage is usually impaired. Postulated theories on freeze-thaw induced damage do not fully explain the origin of this weakness in composite cement concretes.

This paper systematically presents the phase assemblage changes associated with the freeze-thaw of concrete specimen made from composite cements with and without limestone. The freeze-thaw test was performed on concrete according to CIF method based on CEN/TR 15177 and the corresponding cement …

Influence Of Exposure Environments On The Durability Of Slag-Blended Cements, Joseph Onah Ukpata, P. A. M. Basheer, Leon Black

International Conference on Durability of Concrete Structures

Both chlorides and sulphates combine in seawater to affect the durability of reinforced concrete structures located in marine environments. This paper presents the results of an experimental study on slag blended cement systems, cured for 7 days, before exposure to a combined solution of sodium chloride (30 g/L) and sodium sulphate (3 g/L). Two slags of different chemical compositions, designated as slags 1 and 2 were respectively blended with Portland cement CEM I 52.5R at 30 and 70 wt.% replacement levels. Mechanical tests on mortar samples were complemented by microstructural examination and chemical characterisation on paste samples, all using a …

Fib Model Code 2020 – Durability Design And Through Life Management Of New And Existing Structures, Frank Papworth, S Matthews

International Conference on Durability of Concrete Structures

Work has recently started in fib (Fédération Internationale du Béton) on the preparation of a new fib Model Code for Concrete Structures, under the working title of Model Code 2020 (MC2020). This will be a single code dealing with both new and existing concrete structures, that is both the design of new structures and all the activities associated with the assessment, interventions and the through-life management and care of existing concrete structures. Numerous goals relating to durability and service life design have been identified, including that ideally MC2020 should incorporate:

• Better models for deterioration processes addressing issues such as …

Absorption, Porosity, Capillarity And Chloride Diffusion In Ultra High Performance Concretes, José Manuel Gandia-Romero, José Enrique Ramón-Zamora, Isabel Gasch, Manuel Valcuende, Rafael Calabuig, Victor Calvet, Pedro Serna

International Conference on Durability of Concrete Structures

Concrete durability performance can be assessed by a number of parameters, among which permeability properties are key. In this experimental work, the permeability to water and the diffusion of chlorides in Ultra High Performance Concrete (UHPC) are studied. To this end, three types of concrete were made: two Ultra High Performance (one with fibers and one without fibers) and a Conventional Concrete (CC) of w/c ratio equal to 0.5. The compressive strength of Ultra High Performance Concretes was 130 MPa, and that of conventional concrete was 50 MPa. All of them were cured at a temperature of 20°C and RH …

Influence Of Mineralogical Nature Of Aggregates On Acid Resistance Of Mortar, K P. Ramaswamy, Manu Santhanam

International Conference on Durability of Concrete Structures

Cement-based materials being alkaline in nature are often subjected to rapid deterioration on exposure to the aggressive acidic environments. Acids penetrate into the cement matrix causing calcium leaching and deterioration of phases leading to alteration in the microstructure. Currently, there are hardly any codes or standards available for evaluating the durability of materials to acid attack. Moreover, the literature addressing the material resistance is quite inconclusive. This paper aims to evaluate the influence of mineralogical nature of aggregates on the degradation kinetics of cement mortar when exposed to inorganic and organic acid solutions by performing a static accelerated leaching test. …

Performance Of Concrete Made With A Calcined Clay – Limestone-Portland Cement Exposed To Natural Conditions, Fernando Martirena, Ernesto Díaz, Dayran Rocha, Hamed Maraghechi, Karen Louise Scrivener

International Conference on Durability of Concrete Structures

This work presents the results of an investigation carried out to assess durability of concrete made with a calcined clay- limestone-Portland cement with 47% of clinker, hereafter named LC3, produced during an industrial trial in 2013. LC3 was used to cast concrete blocks and later expose them at a natural location at the northern coast of Cuba. Reference concrete was cast with Cuban Portland cement having 88% of clinker. Throughout three years (2015, 2016, 2017) concrete cores were systematically taken and the specimens were subjected to a testing program that included Formation factor, chloride profiling, surface resistivity, air permeability and …

Enhancement Of Durability Characteristics Of Geopolymer Concrete With Manufactured Sand, Abdul Aleem, T Shanmuga Priya

International Conference on Durability of Concrete Structures

Geopolymer Concrete is the concrete made without using any quantity of cement. Instead the waste material from the thermal power station called fly ash is used as the binding material. This fly ash reacts with alkaline solution like sodium hydroxide (NaOH) and sodium silicate (Na2SiO3) and forms a gel which binds the fine and coarse aggregates. Similarly another artificial material called manufactured sand (M-Sand) is also used as the fine aggregate against the normal river sand. The durability of Geopolymer Concrete with M-sand was studied by casting cubes of size 100 x 100 x 100 mm. The cube specimens were …

Strength And Durability Of Hybrid Fibre Reinforced Binary Blend Geopolymer Concrete, Namasivayam Ganesan, P V Indira, R Sahana

International Conference on Durability of Concrete Structures

This paper deals with an investigation on the influence of hybrid fibres on the strength and durability of binary blend geopolymer concrete. Geopolymer concrete was prepared using Fly ash and GGBS as source material and mix design was carried out as per the guidelines of Professor Rangan of Curtin University, Australia. Different fly ash-GGBS proportions namely 50-50%, 60-40%, 70-30%, 80-20% and 90-10% were considered. The tests on Geopolymer concrete reveal that the compressive strength increases as the percentage of GGBS increases up to 30%. Hence the combination of 70% fly ash and 30% GGBS was considered as a base material. …

Impact Of Water Content On The Performance Of Alkali-Activated Slag Concretes, Susan A. Bernal, John L. Provis, Jannie S.J. Van Deventer

International Conference on Durability of Concrete Structures

In this study, we report the effect of varying the water/binder (w/b) ratio on the performance of sodium silicate activated concretes. Compressive strength development and water transport properties of these concretes were assessed, along with their resistance to carbonation. The results demonstrate that varying the water content within a reasonable range induced negligible changes in the compressive strengths of these concretes, when a constant paste content was used. A direct correlation between the w/b ratio and the amount of permeable voids in the concretes was not identified. The carbonation behaviour of these concretes changes prominently depending on the CO2 concentration …

Research Of System Conditions For Formation Of Failure On Mathematical Models By The Results Of The Research Of Reinforced Concrete Bridges, E.T. Yaxshiev, F.Z. Zokirov, A.B. Karimova

Journal of Tashkent Institute of Railway Engineers

Based on the data of field surveys, the results of assessing the state of reinforced concrete span structures of bridges and characteristic defects that occur in the structure during operation are presented. An analysis of the results of inspections and periodic inspections responsible for the operation of artificial structures shows that a significant part of reinforced concrete spans has various types of defects and damage to load-bearing structures. Studies show that defects have a significant impact on the operational properties of reinforced concrete spans, leading both to a limitation of the speed regime of train movements and to the emergence …

Long-Term Performance Of Sustainable Pavements Using Ternary Blended Concrete With Recycled Aggregates, Seth M. Wagner

Theses and Dissertations

The purposes of this study were to (a) design concrete pavement mixtures with recycled concrete aggregates using ternary blends of cementitious materials and a low water-to-binder ratio, (b) measure the fresh and hardened properties of the proposed concrete mixtures and (c) assess the long-term performance of the concrete implementing the use of recycled coarse aggregates. Preliminary investigation into ternary blend combinations via the compressive testing of mortar cubes and isothermal calorimetry was used to predict an optimal blend of cementitious material. Mixes using recycled concrete aggregates at varying replacement rates were tested for fresh and hardened properties using the proposed …

Design And Predicting Performance Of Carbon Nanotube Reinforced Cementitious Materials : Mechanical Properties And Dispersion Characteristics., Mahyar Ramezani

Electronic Theses and Dissertations

Recently, Carbon Nanotubes (CNTs) are drawing considerable attention of researchers for reinforcing cementitious materials due to their excellent mechanical properties and high aspect ratio (length-to-diameter ratio). However, CNTs might not disperse well within the cement matrix, resulting in little improvement or even degradation of concrete properties. The uncertainty in producing the consistent results in different studies might be attributed to multiple interactions between the experimental variables affecting the nanotube dispersion and the final properties of CNT-cement nanocomposites. Therefore, this research mainly focused on proposing equations that can reliably capture these interactions in order to correlate CNT dispersion with the mechanical …

Morphology And Detection Of Corrosion On Stainless Steel Reinforcement In Concrete, Julio J. Saire Yanez

USF Tampa Graduate Theses and Dissertations

Stainless steel (SS) has emerged as an alternative corrosion-resistant reinforcement in concrete instead of the commonly used carbon steel (CS). The biggest advantage of SS is that it takes more time for corrosion to initiate than for CS. An additional benefit from the use of SS in concrete may be derived from the period after the corrosion started until the concrete structure reaches a limit state. This period is called corrosion propagation stage (CPS) and it has been hardly studied in SS reinforced structures. The duration of this period could be related, among other factors, to the morphology of corrosion …

Effect Of Specimen Thicknesses On Water Absorption And Flexural Strength Of Cfrp Laminates Subjected To Water Or Alkaline Solution Immersion, Xue Zhang, Yanlei Wang, Baolin Wan, Gaochuang Cai, Yuan Qu

Civil and Environmental Engineering Faculty Research and Publications

In this paper, an experimental research was undertaken to investigate the effect of specimen thicknesses on water absorptions and flexural strengths of wet lay-up CFRP laminates subjected to distilled water or alkaline solution immersion up to 180 days. Test results showed that the water uptake and flexural strength retention of CFRP laminates were significantly affected by the adopted specimen thickness. For the same aging time, the water uptake of CFRP laminates decreased in the early stage of immersion and increased in the later stage of immersion with the increase of specimen thickness. Meanwhile, the flexural strength retention generally increased as …

Reducing The Porosity And Sealing Cracks By Using Crystalline Admixture In Conventional Concrete, Visar Krelani, Liberato Ferrara

International Journal of Business and Technology

There is a continuous increase of quality on civil engineering materials in developed countries and parallel increase of need for new constructions in developing countries. Professional community should propose solutions for the durability that can resist in different severe environments. The most important factor that can affect concrete durability is represented by the pore distribution. Transport properties can take place through the porous network inside the cementitious composites and the aggregates interface, permitting the ingress of aggressive agents damaging concrete function intrinsically as a material and the wellfunctioning of the entire structure. The use of a crystalline admixture during the …