Open Access. Powered by Scholars. Published by Universities.®
Biomedical Engineering and Bioengineering Commons™
Open Access. Powered by Scholars. Published by Universities.®
- Discipline
- Keyword
-
- Drug delivery (14)
- Electrospun fibers (12)
- Biomaterials (8)
- Astrocyte (6)
- Spinal cord injury (6)
-
- Nanomedicine (5)
- Silica nanoparticles (5)
- Astrocytes (4)
- Dendrimer (4)
- Dorsal root ganglia (4)
- Hydrogel (4)
- Inflammation (4)
- Iron oxide nanoparticles (4)
- Scaffold (4)
- Biodegradation (3)
- Chitosan (3)
- Coating (3)
- Curcumin (3)
- Electrospinning (3)
- Electrospun fiber (3)
- Glaucoma (3)
- Hydrogels (3)
- Macrophage (3)
- Magnesium (3)
- Nanoparticle (3)
- Neuroprotection (3)
- Poly- l -lactic acid (3)
- Poly-l-lactic acid (3)
- Tissue engineering (3)
- Aligned microfibers (2)
Articles 151 - 180 of 247
Full-Text Articles in Biomedical Engineering and Bioengineering
Relating Ph And Ion Release From Ga2o3-Na 2o-Cao-Zno-Sio2 Bioactive Glasses, T. J. Keenan, A. W. Wren, A. Coughlan, Mark R. Towler, M. M. Hall
Relating Ph And Ion Release From Ga2o3-Na 2o-Cao-Zno-Sio2 Bioactive Glasses, T. J. Keenan, A. W. Wren, A. Coughlan, Mark R. Towler, M. M. Hall
Chemical and Biochemical Engineering Faculty Research & Creative Works
Three glasses were designed for this study, including one Ga-free glass (Control), and two Ga-containing glasses (TGa-1, TGa-2). In the Ga-containing glasses, Ga2O3 is included at the expense of ZnO. This study focuses on the relation between pH and ion concentration present in solution in which these bioactive glasses have been submerged for periods of 1, 7, and 14 days. © 2013 IEEE.
Biocompatibility Of Cao-Na2o-Sio2/Tio2 Glass Ceramic Scaffolds For Orthopaedic Applications, A. W. Wren, A. Coughlan, K. E. Smale, S. T. Misture, B. P. Mahon, O. M. Clarkin, Mark R. Towler
Biocompatibility Of Cao-Na2o-Sio2/Tio2 Glass Ceramic Scaffolds For Orthopaedic Applications, A. W. Wren, A. Coughlan, K. E. Smale, S. T. Misture, B. P. Mahon, O. M. Clarkin, Mark R. Towler
Chemical and Biochemical Engineering Faculty Research & Creative Works
This work aims to determine the effect of substituting TiO2 for SiO2 in a 0.62SiO2-Na2O-0.24CaO based glass-ceramic scaffold. High temperature X-ray Diffraction (HT-XRD) was used to determine the sintering temperature (700oC). Both optical microscopy and x-ray micotomography was used to determine the average pore size (540-680ìm) of each scaffold. Cytocompatibility of each scaffold was conducted using murine mesenchymal stem cells. © 2013 IEEE.
An Investigation Into The Structure And Properties Of Cao-Zno-Sio 2-Tio2-Na2o Bioactive Glass/Hydroxyapatite Composite, Chokchai Yatongchai, Mark R. Towler, Anthony W. Wren
An Investigation Into The Structure And Properties Of Cao-Zno-Sio 2-Tio2-Na2o Bioactive Glass/Hydroxyapatite Composite, Chokchai Yatongchai, Mark R. Towler, Anthony W. Wren
Chemical and Biochemical Engineering Faculty Research & Creative Works
Effect of the addition of CaO-ZnO-SiO2-TiO2-Na2O glass as a reinforcing phase on properties of hydroxyapatite/glass composites was investigated. The addition of the glass caused the decomposition of HA phase to tricalcium phosphate, inhibiting densification in the HA/glass composites. However, depending on the glass concentration, some of the glass can act as a sintering aid enhancing the densification in the composites. © 2013 IEEE.
Gallium Containing Glass Polyalkenoate Bone Cements: Ion Release And E. Coli Inhibition, L. Placek, A. W. Wren, A. Coughlan, Mark R. Towler
Gallium Containing Glass Polyalkenoate Bone Cements: Ion Release And E. Coli Inhibition, L. Placek, A. W. Wren, A. Coughlan, Mark R. Towler
Chemical and Biochemical Engineering Faculty Research & Creative Works
The Glass Polyalkenoate Cement (GPC) series (LCon., LGa-1 and LGa-2) containing gallium (Ga) and a 50 wt% addition of E11 polyacrylic acid (PAA), previously developed, was evaluated for ion release, specifically Si, Ca, Zn and Ga, and E. coli inhibition. The maximum inhibition was observed in the t = 0 samples and was 0.35 mm for LCon. and 0.65 mm for LGa-1 and LGa-2. © 2013 IEEE.
Engineered Nanotopography On Electrospun Plla Microfibers Modifies Raw 264.7 Cell Response, Nicholas J. Schaub, Tara Britton, Rupak Rajachar, Ryan J. Gilbert
Engineered Nanotopography On Electrospun Plla Microfibers Modifies Raw 264.7 Cell Response, Nicholas J. Schaub, Tara Britton, Rupak Rajachar, Ryan J. Gilbert
Chemical and Biochemical Engineering Faculty Research & Creative Works
In this study, we created a new method of electrospinning capable of controlling the surface structure of individual fibers (fiber nano topography). The nano topographical features were created by a phase separation in the fibers as they formed. To control the phase separation, a nonsolvent (a chemical insoluble with the polymer) was added to an electrospinning solution containing poly-l-lactic acid (PLLA) and chloroform. The nano topography of electro spun fibers in the PLLA/chloroform solution was smooth. However, adding a small weight (< 2% of total solution) of a single nonsolvent (water, ethanol, or dimethyl sulfoxide) generated nanoscale depressions on the surface of the fibers unique to the nonsolvent added. Additionally, nanoscale depressions on electro spun fibers were observed to change with dimethyl sulfoxide (DMSO) concentration in the PLLA/chloroform solution. A nonlinear relationship was found between the concentration of DMSO and the number and size of nano topographical features. The surface depressions did not alter the hydrophobicity of the scaffold or degradation of the scaffold over a two-day period. To determine if fiber nano topography altered cell behavior, macrophages (RAW 264.7 cells) were cultured on fibers with a smooth nano topography or fibers with nanoscale depressions. RAW 264.7 cells spread less on fibers with nanoscale depressions than fibers with a smooth topography (p < 0.05), but there were no differences between groups with regard to cell metabolism or the number of adherent cells. The results of this study demonstrate the necessity to consider the nano topography of individual fibers as these features may affect cellular behavior. More importantly, we demonstrate a versatile method of controlling electro spun fiber nano topography. © 2013 American Chemical Society.
Synthesis And Characterization Of Encapsulated Nanosilica Particles With An Acrylic Copolymer By In Situ Emulsion Polymerization Using Thermoresponsive Nonionic Surfactant, Mostafa Yazdimamaghani, Tannaz Pourvala, Elaheh Motamedi, Babak Fathi, Daryoosh Vashaee, Lobat Tayebi
Synthesis And Characterization Of Encapsulated Nanosilica Particles With An Acrylic Copolymer By In Situ Emulsion Polymerization Using Thermoresponsive Nonionic Surfactant, Mostafa Yazdimamaghani, Tannaz Pourvala, Elaheh Motamedi, Babak Fathi, Daryoosh Vashaee, Lobat Tayebi
Chemical and Biochemical Engineering Faculty Research & Creative Works
Nanocomposites of encapsulated silica nanoparticles were prepared by in situ emulsion polymerization of acrylate monomers. The synthesized material showed good uniformity and dispersion of the inorganic components in the base polymer, which enhances the properties of the nanocomposite material. A nonionic surfactant with lower critical solution temperature (LCST) was used to encapsulate the silica nanoparticles in the acrylic copolymer matrix. This in situ method combined the surface modification and the encapsulation in a single pot, which greatly simplified the process compared with other conventional methods requiring separate processing steps. The morphology of the encapsulated nano silica particles was investigated by …
Comparison Of A Sio2-Cao-Zno-Sro Glass Polyalkenoate Cement To Commercial Dental Materials: Ion Release, Biocompatibility And Antibacterial Properties, A. W. Wren, A. Coughlan, M. M. Hall, M. J. German, Mark R. Towler
Comparison Of A Sio2-Cao-Zno-Sro Glass Polyalkenoate Cement To Commercial Dental Materials: Ion Release, Biocompatibility And Antibacterial Properties, A. W. Wren, A. Coughlan, M. M. Hall, M. J. German, Mark R. Towler
Chemical and Biochemical Engineering Faculty Research & Creative Works
Ion Release and biocompatibility of a CaO-SrO-ZnO-SiO2 (BT 101) based glass polyalkenoate cement (GPC) was compared against commercial GPCs, Fuji IX and Ketac Molar. The radiopacity (R) was similar for each material, 2.0-2.8. Ion release was evaluated on each material over 1, 7, 30 and 90 days. BT 101 release included Ca (23 mg/L), Sr (23 mg/L) Zn (13 mg/L), Si (203 mg/L). Fuji IX release includes Ca (0.7 mg/L), Al (3 mg/L) Si (26 mg/L), Na (60 mg/L) and P (0.5 mg/L) while Ketac Molar release includes Ca (1 mg/L), Al (0.6 mg/L) Si (23 mg/L), Na (76 …
Automated Methods To Determine Electrospun Fiber Alignment And Diameter Using The Radon Transform, Nicholas J. Schaub, Sean J. Kirkpatrick, Ryan J. Gilbert
Automated Methods To Determine Electrospun Fiber Alignment And Diameter Using The Radon Transform, Nicholas J. Schaub, Sean J. Kirkpatrick, Ryan J. Gilbert
Chemical and Biochemical Engineering Faculty Research & Creative Works
Recent evidence demonstrates the ability to change cell function by altering the physical properties of electro spun scaffolds, but many studies still do not characterize electro spun fiber alignment and diameter. To aid in the reporting of these crucial properties, we demonstrate two methods of quantifying electro spun fiber alignment with one method capable of determining electro spun fiber diameter. The first method assesses fiber alignment in a scanning electron microscopy image using the Radon Transform (RT) to calculate the entropy of the fibers in the image. The RT entropy method was more sensitive than a commonly used Fast Fourier …
Characterisation Of Ga2o3-Na2o-Cao-Zno- Sio2 Bioactive Glasses, A. W. Wren, T. Keenan, A. Coughlan, F. R. Laffir, D. Boyd, Mark R. Towler, M. M. Hall
Characterisation Of Ga2o3-Na2o-Cao-Zno- Sio2 Bioactive Glasses, A. W. Wren, T. Keenan, A. Coughlan, F. R. Laffir, D. Boyd, Mark R. Towler, M. M. Hall
Chemical and Biochemical Engineering Faculty Research & Creative Works
The structural role of Gallium (Ga) is investigated when substituted for Zinc (Zn) in a 0.42SiO2-0.40-xZnO-0.10Na2O-0.08CaO glass series, (where x = 0.08). Each starting material was amorphous, and the network connectivity (NC) was calculated assuming Ga acts as both a network modifier (1.23), and also as a network former. Assuming a network forming role for Ga the NC increased with increasing Ga concentration throughout the glass series (Control 1.23, TGa-1 2.32 and TGa-2 3.00). X-ray photoelectron spectroscopy confirmed both composition and correlated NC predictions. Raman spectroscopy was employed to investigate Q-structure and found that a shift …
Multilayer Bioactive Glass/Zirconium Titanate Thin Films In Bone Tissue Engineering And Regenerative Dentistry, Masoud Mozafari, Erfan Salahinejad, Vahid Shabafrooz, Mostafa Yazdimamaghani, Daryoosh Vashaee, Lobat Tayebi
Multilayer Bioactive Glass/Zirconium Titanate Thin Films In Bone Tissue Engineering And Regenerative Dentistry, Masoud Mozafari, Erfan Salahinejad, Vahid Shabafrooz, Mostafa Yazdimamaghani, Daryoosh Vashaee, Lobat Tayebi
Chemical and Biochemical Engineering Faculty Research & Creative Works
Surface modification, particularly coatings deposition, is beneficial to tissue-engineering applications. In this work, bioactive glass/zirconium titanate composite thin films were prepared by a sol-gel spin-coating method. The surface features of the coatings were studied by scanning electron microscopy, atomic force microscopy, and spectroscopic reflection analyses. The results show that uniform and sound multilayer thin films were successfully prepared through the optimization of the process variables and the application of carboxymethyl cellulose as a dispersing agent. Also, it was found that the thickness and roughness of the multilayer coatings increase nonlinearly with increasing the number of the layers. This new class …
Aluminium-Free Glass Polyalkenoate Cements: Ion Release And In Vitro Antibacterial Efficacy, A. W. Wren, J. P. Hansen, S. Hayakawa, Mark R. Towler
Aluminium-Free Glass Polyalkenoate Cements: Ion Release And In Vitro Antibacterial Efficacy, A. W. Wren, J. P. Hansen, S. Hayakawa, Mark R. Towler
Chemical and Biochemical Engineering Faculty Research & Creative Works
Glass polyalkenoate cements (GPCs) have exhibited potential as bone cements. This study investigates the effect of substituting TiO2 for SiO2 in the glass phase and the subsequent effect on cement rheology, mechanical properties, ion release and antibacterial properties. Glass characterization revealed a reduction in glass transition temperature (Tg) from 685 to 669 C with the addition of 6 mol % TiO2 (AT-2). Magic angle spinning nuclear magnetic resonance (MAS-NMR) revealed a shift from -81 ppm to -76pmm when comparing a Control glass to AT-2, indicating de-polymerization of the Si network. The incorporation of TiO2 …
Comparison Of A Sio2-Cao-Zno-Sro Glass Polyalkenoate Cement To Commercial Dental Materials: Glass Structure And Physical Properties, A. W. Wren, A. Coughlan, F. R. Laffir, Mark R. Towler
Comparison Of A Sio2-Cao-Zno-Sro Glass Polyalkenoate Cement To Commercial Dental Materials: Glass Structure And Physical Properties, A. W. Wren, A. Coughlan, F. R. Laffir, Mark R. Towler
Chemical and Biochemical Engineering Faculty Research & Creative Works
Glass polyalkenoate cements (GPCs) have previously been considered for orthopedic applications. A Zn-GPC (BT 101) was compared to commercial GPCs (Fuji IX and Ketac Molar) which have a setting chemistry analogous to BT 101. Handling properties (working, Tw and setting, Ts times) for BT 101 were shorter than the commercial GPCs. BT 101 also had a higher setting exotherm (Sx - 34 °C) than the commercial GPCs (29 °C). The maximum strengths for BT 101, Fuji IX, and Ketac Molar were 75, 238, and 216 MPa (compressive, σc), and 34, 54, and 62 MPa (biaxial …
Fabrication Of Cao-Nao-Sio2/Tio2 Scaffolds For Surgical Applications, A. W. Wren, A. Coughlan, K. E. Smale, S. T. Misture, B. P. Mahon, O. M. Clarkin, Mark R. Towler
Fabrication Of Cao-Nao-Sio2/Tio2 Scaffolds For Surgical Applications, A. W. Wren, A. Coughlan, K. E. Smale, S. T. Misture, B. P. Mahon, O. M. Clarkin, Mark R. Towler
Chemical and Biochemical Engineering Faculty Research & Creative Works
A series of titanium (Ti) based glasses were formulated (0.62 SiO2-0.14 Na2O-0.24 CaO, with 0.05 mol% TiO2 substitutions for SiO2) to develop glass/ceramic scaffolds for bone augmentation. Glasses were initially characterised using X-ray diffraction (XRD) and particle size analysis, where the starting materials were amorphous with 4.5 μm particles. Hot stage microscopy and high temperature XRD were used to determine the sintering temperature (̃700 °C) and any crystalline phases present in this region (Na2Ca3Si6O16, combeite and quartz). Hardness testing revealed that the Ti-free control (ScC- …
Developing Novel Prognostic Biomarkers For Multivariate Fracture Risk Prediction Algorithms, Ernest K. Poku, Mark R. Towler, Niamh M. Cummins, Jeff D. Newman
Developing Novel Prognostic Biomarkers For Multivariate Fracture Risk Prediction Algorithms, Ernest K. Poku, Mark R. Towler, Niamh M. Cummins, Jeff D. Newman
Chemical and Biochemical Engineering Faculty Research & Creative Works
Multivariate prediction algorithms such as FRAX® and QFracture Scores provide an opportunity for new prognostic biomarkers to be developed and incorporated, potentially leading to better fracture prediction. As more research is conducted into these novel biomarkers, a number of factors need to be considered for their successful development for inclusion in these algorithms. In this review, we describe two well-known multivariate prediction algorithms for osteoporosis fracture risk applicable to the UK population, FRAX and QFracture Scores, and comment on the current prognostic tools available for fracture risk; dual X-ray assessment, quantitative ultrasonography, and genomic/biochemical markers. We also highlight the factors …
Mineralization Potential Of Electrospun Pdo-Hydroxyapatite-Fibrinogen Blended Scaffolds, Isaac A. Rodriguez, Parthasarathy A. Madurantakam, Jennifer M. Mccool, Scott A. Sell, Hu Yang, Peter C. Moon, Gary L. Bowlin
Mineralization Potential Of Electrospun Pdo-Hydroxyapatite-Fibrinogen Blended Scaffolds, Isaac A. Rodriguez, Parthasarathy A. Madurantakam, Jennifer M. Mccool, Scott A. Sell, Hu Yang, Peter C. Moon, Gary L. Bowlin
Chemical and Biochemical Engineering Faculty Research & Creative Works
The current bone autograft procedure for cleft palate repair presents several disadvantages such as limited availability, additional invasive surgery, and donor site morbidity. The present preliminary study evaluates the mineralization potential of electrospun polydioxanone:nano-hydroxyapatite: fibrinogen (PDO: nHA: Fg) blended scaffolds in different simulated body fluids (SBF). Scaffolds were fabricated by blending PDO: nHA: Fg in the following percent by weight ratios: 100: 0: 0, 50: 25: 25, 50: 50: 0, 50: 0: 50, 0: 0: 100, and 0: 50: 50. Samples were immersed in (conventional (c), revised (r), ionic (i), and modified (m)) SBF for 5 and 14 days to …
Experimental Composite Guidance Conduits For Peripheral Nerve Repair: An Evaluation Of Ion Release, X. F. Zhang, A. Coughlan, H. O'Shea, Mark R. Towler, S. Kehoe, D. Boyd
Experimental Composite Guidance Conduits For Peripheral Nerve Repair: An Evaluation Of Ion Release, X. F. Zhang, A. Coughlan, H. O'Shea, Mark R. Towler, S. Kehoe, D. Boyd
Chemical and Biochemical Engineering Faculty Research & Creative Works
Poly (lactide-co-glycolide) (PLGA) - Pluronic F127 - glass composites have demonstrated excellent potential, from the perspective of controlled mechanical properties and cytocompatibility, for peripheral nerve regeneration. In addition to controlling the mechanical properties and cytotoxicity for such composite devices, the glass component may mediate specific responses upon implantation via degradation in the physiological environment and release of constituent elements. However, research focused on quantifying the release levels of such therapeutic ions from these experimental medical devices has been limited. To redress the balance, this paper explores the ion release profiles for Si4+, Ca2+, Na+, …
Gallium Containing Glass Polyalkenoate Anti-Cancerous Bone Cements: Glass Characterization And Physical Properties, A. W. Wren, A. Coughlan, L. Placek, Mark R. Towler
Gallium Containing Glass Polyalkenoate Anti-Cancerous Bone Cements: Glass Characterization And Physical Properties, A. W. Wren, A. Coughlan, L. Placek, Mark R. Towler
Chemical and Biochemical Engineering Faculty Research & Creative Works
A gallium (Ga) glass series (0.48SiO2-0.40ZnO-0.12CaO, with 0.08 mol% substitution for ZnO) was developed to formulate a Ga-containing Glass Polyalkenoate Cement (GPC) series. Network connectivity (NC) and X-ray Photoelectron Spectroscopy (XPS) was employed to investigate the role of Ga3+ in the glass, where it is assumed to act as a network modifier. Ga-GPC series was formulated with E9 and E11 polyacrylic acid (PAA) at 50, 55 and 60 wt% additions. E11 working times (Tw) ranged from 68 to 96 s (Lcon.) and 106 s for the Ga-GPCs (LGa-1 and LGa-2). Setting times (Ts) …
Examination Of The Migratory Potential Of Patterned Cortical Neurons Using Laser Direct-Write, T. B. Phamduy, C. J. Rivet, D. Kingsley, R. J. Gilbert, D. B. Chrisey
Examination Of The Migratory Potential Of Patterned Cortical Neurons Using Laser Direct-Write, T. B. Phamduy, C. J. Rivet, D. Kingsley, R. J. Gilbert, D. B. Chrisey
Chemical and Biochemical Engineering Faculty Research & Creative Works
We describe the patterning of neuronal cultures by a laser-based printing system. Embryonic chick cortical neurons were transferred into predetermined array positions with micron accuracy, enabling detailed study of neuronal migration, aggregation, and neurite outgrowth regulated by cell-cell interactions on a homogeneous surface. Images of cells were analyzed up to 14 days. Results demonstrated that increasing the spacing between neighboring groups of cells causes intra-group cells to preferentially migrate towards each other and aggregate towards the center of the printed 'spot'. In addition, increasing the printed 'spot' size encouraged migration towards neighboring groups of cells. © 2012 IEEE.
The Structural Characterization Of Ga 2o 3-Na 2o-Cao-Zno-Sio 2 Bioactive Glasses, T. J. Keenan, A. W. Wren, A. Coughlan, M. M. Hall, Mark R. Towler
The Structural Characterization Of Ga 2o 3-Na 2o-Cao-Zno-Sio 2 Bioactive Glasses, T. J. Keenan, A. W. Wren, A. Coughlan, M. M. Hall, Mark R. Towler
Chemical and Biochemical Engineering Faculty Research & Creative Works
The characterization of bioactive glasses in which zinc (Zn) has been incrementally replaced by gallium (Ga). © 2012 IEEE.
Silver Coated Bioactive Glass Particles For Wound Healing Applications, P. Hassanzadeh, A. W. Wren, Mark R. Towler
Silver Coated Bioactive Glass Particles For Wound Healing Applications, P. Hassanzadeh, A. W. Wren, Mark R. Towler
Chemical and Biochemical Engineering Faculty Research & Creative Works
Hench and colleagues discovered that bone could bond chemically to certain glass compositions in 1969 [1]. This group of glasses is known as bioactive glasses [1]. Some special compositions of bioactive glasses will bond to soft tissues as well as bone [1]. One of the important characteristics of bioactive glasses is their ability to release beneficial ions such as Ca2+, Na+, Zn2+, Sr2+, and PO 43- in the body, which promote self-healing [2]. Bioactive glasses generally contain much less glass former (e.g., SiO2, B2O3 etc.) than conventional …
Increasing The Quantity Of Silver In Zinc-Based Glass Polyalkenoate Cement: Is There An Improvement In Antibacterial Efficacy?, A. Coughlan, S. M. Breed, C. Ashraf, J. A. Cardinale, M. M. Hall, Mark R. Towler
Increasing The Quantity Of Silver In Zinc-Based Glass Polyalkenoate Cement: Is There An Improvement In Antibacterial Efficacy?, A. Coughlan, S. M. Breed, C. Ashraf, J. A. Cardinale, M. M. Hall, Mark R. Towler
Chemical and Biochemical Engineering Faculty Research & Creative Works
Bone cements should have the ability to chemically bond to both bone and surgical metals, exhibit no chemical or thermal necrosis, and have no significant shrinkage or exotherm upon setting. Taking these properties into consideration, glass polyalkenoate cements (GPCs) have potential as bone cements. GPCs are formed by the reaction between an ion-leachable glass and an aqueous solution of polyacrylic acid (PAA) [1] and have proven antibacterial and cariostatic properties [2], which are related to their ability to release beneficial amounts of ions over time [3, 4]. The GPCs can be formulated to release ions that can have a therapeutic …
Gallium Containing Glass Polyalkenoate Bone Cements: Glass Characterization And Physical Properties, L. Placek, A. W. Wren, A. Coughlan, Mark R. Towler
Gallium Containing Glass Polyalkenoate Bone Cements: Glass Characterization And Physical Properties, L. Placek, A. W. Wren, A. Coughlan, Mark R. Towler
Chemical and Biochemical Engineering Faculty Research & Creative Works
Gallium (Ga) glasses were developed to formulate a Glass Polyalkenoate Cement (GPC) series with both E9 and E11 polyacrylic acid (PAA) at 50, 55 and 60wt% additions. Working times (T w), setting times (T s), compression (σ c), and biaxial flexural (σ f) strength testing were evaluated to determine the GPCs potential use in orthopedics. © 2012 IEEE.
Silver Coated Bioactive Glass Particles For Wound Healing Applications, A. W. Wren, A. Coughlan, P. Hassanzadeh, Mark R. Towler
Silver Coated Bioactive Glass Particles For Wound Healing Applications, A. W. Wren, A. Coughlan, P. Hassanzadeh, Mark R. Towler
Chemical and Biochemical Engineering Faculty Research & Creative Works
Bioactive glass particles (0.42SiO2-0.15CaO-0.23Na 2O-0.20ZnO) of varying size (<90 >μm and 425-850 μm) were synthesized and coated with silver (Ag) to produce Ag coated particles (PAg). These were compared against the uncoated analogous particles (Pcon.). Surface area analysis determined that Ag coating of the glass particles resulted in increased the surface area from 2.90 to 9.12 m2/g (90 μm) and 1.09-7.71 m2/g (425-850 μm). Scanning electron microscopy determined that the Ag coating remained at the surface and there was little diffusion through the bulk. Antibacterial (Escherichia coli - 13 mm and Staphylococcus epidermidis …
Altering Iron Oxide Nanoparticle Surface Properties Induce Cortical Neuron Cytotoxicity, Christopher J. Rivet, Yuan Yuan, Diana Andra Borca-Tasciuc, Ryan J. Gilbert
Altering Iron Oxide Nanoparticle Surface Properties Induce Cortical Neuron Cytotoxicity, Christopher J. Rivet, Yuan Yuan, Diana Andra Borca-Tasciuc, Ryan J. Gilbert
Chemical and Biochemical Engineering Faculty Research & Creative Works
Superparamagnetic iron oxide nanoparticles, with diameters in the range of a few tens of nanometers, display the ability to cross the blood-brain barrier and are envisioned as diagnostic and therapeutic tools in neuro-medicine. However, despite the numerous applications being explored, insufficient information is available on their potential toxic effect on neurons. While iron oxide has been shown to pose a decreased risk of toxicity, surface functionalization, often employed for targeted delivery, can significantly alter the biological response. This aspect is addressed in the present study, which investigates the response of primary cortical neurons to iron oxide nanoparticles with coatings frequently …
Comparison Of Microwave And Conventionally Sintered Yttria-Doped Zirconia Ceramics, Colin J. Reidy, Thomas J. Fleming, Stuart Hampshire, Mark R. Towler
Comparison Of Microwave And Conventionally Sintered Yttria-Doped Zirconia Ceramics, Colin J. Reidy, Thomas J. Fleming, Stuart Hampshire, Mark R. Towler
Chemical and Biochemical Engineering Faculty Research & Creative Works
This paper reports on improvement of the physical and mechanical properties of Y2O3-ZrO2 ceramics through compositional optimization, the use of nanograined powders and utilization of microwave sintering. ZrO2 with 2-5 mol% Y2O3, prepared from nanopowders, was sintered in both conventional and microwave furnaces under exactly the same heating schedule. It was found that microwave sintering improves physical and mechanical properties of Y2O3-ZrO2 ceramics compared with conventional sintering. Compositions containing 2 mol% Y2O3 exhibit the greatest improvement due to retention of tetragonal ZrO …
Robust Cns Regeneration After Complete Spinal Cord Transection Using Aligned Poly-L-Lactic Acid Microfibers, Andres Hurtado, Jared M. Cregg, Han B. Wang, Dane F. Wendell, Martin Oudega, Ryan J. Gilbert, John W. Mcdonald
Robust Cns Regeneration After Complete Spinal Cord Transection Using Aligned Poly-L-Lactic Acid Microfibers, Andres Hurtado, Jared M. Cregg, Han B. Wang, Dane F. Wendell, Martin Oudega, Ryan J. Gilbert, John W. Mcdonald
Chemical and Biochemical Engineering Faculty Research & Creative Works
Following spinal cord injury, axons fail to regenerate without exogenous intervention. In this study we report that aligned microfiber-based grafts foster robust regeneration of vascularized CNS tissue. Film, random, and aligned microfiber-based conduits were grafted into a 3 mm thoracic rat spinal cord gap created by complete transection. Over the course of 4 weeks, microtopography presented by aligned or random poly- l-lactic acid microfibers facilitated infiltration of host tissue, and the initial 3 mm gap was closed by endogenous cell populations. This bulk tissue response was composed of regenerating axons accompanied by morphologically aligned astrocytes. Aligned fibers promoted long distance …
Sol-Gel Derived Silver-Incorporated Titania Thin Films On Glass: Bactericidal And Photocatalytic Activity, Betul Akkopru Akgun, Anthony W. Wren, Caner Durucan, Mark R. Towler, Nathan P. Mellott
Sol-Gel Derived Silver-Incorporated Titania Thin Films On Glass: Bactericidal And Photocatalytic Activity, Betul Akkopru Akgun, Anthony W. Wren, Caner Durucan, Mark R. Towler, Nathan P. Mellott
Chemical and Biochemical Engineering Faculty Research & Creative Works
Titanium dioxide (TiO2) and silver-containing TiO2 (Ag-TiO2) thin films were prepared on silica pre-coated float glass substrates by a sol-gel spin coating method. The bactericidal activity of the films was determined against Staphylococcus epidermidis under natural and ultraviolet (UV) illumination by four complementary methods; (1) the disk diffusion assay, (2) UV-induced bactericidal test, (3) qualitative Ag ion release in bacteria inoculated agar media and (4) surface topographical examination by laserscan profilometry. Photocatalytic activity of the films was measured through the degradation of stearic acid under UV, solar and visible light conditions. The chemical state and …
Clinical Risk Factors For Osteoporosis In Ireland And The Uk: A Comparison Of Frax And Qfracturescores, N. M. Cummins, E. K. Poku, Mark R. Towler, O. M. O'Driscoll, S. H. Ralston
Clinical Risk Factors For Osteoporosis In Ireland And The Uk: A Comparison Of Frax And Qfracturescores, N. M. Cummins, E. K. Poku, Mark R. Towler, O. M. O'Driscoll, S. H. Ralston
Chemical and Biochemical Engineering Faculty Research & Creative Works
Recently two algorithms have become available to estimate the 10-year probability of fracture in patients suspected to have osteoporosis on the basis of clinical risk factors: the FRAX algorithm and QFractureScores algorithm (QFracture). The aim of this study was to compare the performance of these algorithms in a study of fracture patients and controls recruited from six centers in the United Kingdom and Ireland. A total of 246 postmenopausal women aged 50-85 years who had recently suffered a low-trauma fracture were enrolled and their characteristics were compared with 338 female controls who had never suffered a fracture. Femoral bone mineral …
Controlled Release Of 6-Aminonicotinamide From Aligned, Electrospun Fibers Alters Astrocyte Metabolism And Dorsal Root Ganglia Neurite Outgrowth, Nicholas J. Schaub, Ryan J. Gilbert
Controlled Release Of 6-Aminonicotinamide From Aligned, Electrospun Fibers Alters Astrocyte Metabolism And Dorsal Root Ganglia Neurite Outgrowth, Nicholas J. Schaub, Ryan J. Gilbert
Chemical and Biochemical Engineering Faculty Research & Creative Works
Following central nervous system (CNS) injury, activated astrocytes form a glial scar that inhibits the migration of axons ultimately leading to regeneration failure. Biomaterials developed for CNS repair can provide local delivery of therapeutics and/or guidance mechanisms to encourage cell migration into damaged regions of the brain or spinal cord. Electro spun fibers are a promising type of biomaterial for CNS injury since these fibers can direct cellular and axonal migration while slowly delivering therapy to the injury site. In this study, it was hypothesized that inclusion of an anti-metabolite, 6-aminonicotinamide (6AN), within poly-l-lactic acid electro spun fibers could attenuate …
An Argument For The Importance Of Material Property Characterization Of Hydrogels, J. M. Zuidema, R. J. Gilbert
An Argument For The Importance Of Material Property Characterization Of Hydrogels, J. M. Zuidema, R. J. Gilbert
Chemical and Biochemical Engineering Faculty Research & Creative Works
Hydrogels are being fabricated for use in many tissue engineering applications. In order to advance the field, material properties must be characterized to determine the most desirable attributes. The data presented shows the importance of both surface charge and mechanical properties on dorsal root ganglia neurite extension. © 2011 IEEE.