Physical Chemistry Commons^™

Hydrothermal Synthesis Of Pure Li4Ti5O12 And Its Electrochemical Performance, Wen-Jun Xie, Yu-Shi He, Hong Wang, Xiao-Zhen Liao, Zi-Feng Ma

Journal of Electrochemistry

Spinel Li₄Ti₅O₁₂ was prepared by hydrothermal method using commercial anatase (TiO₂) and lithium hydroxide (LiOH) as raw materials. The effects of the LiOH concentration of lithium hydroxide, hydrothermal reaction time and calcination temperature on the structure and electrochemical performance of Li₄Ti₅O₁₂ were investigated. The formation process of Li₄Ti₅O₁₂ was also proposed. The micro-structure and morphology wereas characterized by XRD, SEM, TEM techniques, and the electrochemical performance was analyzed by galvanostatic charge-discharge test. The results show that the pure phase spinel Li₄Ti …

Preparation And Catalytic Properties Of Feco Alloy Nanocatalyst, Ming-Xuan Li, Jie-Lian Ou, Sheng-Pei Chen, Peng Wang, Bin-Bin Xu, Shi-Gang Sun

Journal of Electrochemistry

The FeCo alloy nanoparticles were electrodeposited on glassy carbon electrode by chronoamperometry and were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results showed that the shapes of FeCo nanoparticles were cubes with an average size of 65 nm. The atom ratio of Fe and Co is 1:1. As indicated from the pattern of selected area electron diffraction (SAED), the FeCo cubic nanoparticles were single crystal which belonged to body-centered cubic with an interval of 0.201 nm referring to the (110) facets of FeCo alloy. The FeCo cubic nanoparticles exhibited the enhanced electrocatalytic …

Electrochemical Synthesis Of Hierarchical Dendritic Polyaniline Nanostructures, Shao-Huang Weng, Jian-Zhang Zhou, Zhong-Hua Lin, Xin-Hua Lin

Journal of Electrochemistry

In this work, the p-TSA doped and hierarchical dendritic nanostructured polyanilines (PANI) have been prepared by potentiostatic electropolymerization without using any templates at room temperature. The mechanism of the polymerization has been discussed according to the electrodeposition curves. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were employed to confirm the formation of uniform hierarchical dendritic structure on PANI. UV-Vis spectroscopy (UV-Vis) and infrared spectroscopy (FTIR) proved that the prepared PANI is in the form of emeraldine salt. The templateless electrodeposition method is simple, easy to operate, can be applied to fabricate other nanostructures of conducting polymers.

Electrochemical Performance Of Lifepo4/C Synthesized Via Aqueous Solution-Evaporation Route, Ning-Yu Gu, Xing-Hua He, Yang Li

Journal of Electrochemistry

The LiFePO₄/C samples have been synthesized via an aqueous solution-evaporation route with LiH₂PO₄, FeC₂O₄.2H₂O as raw materials and citric acid as a carbon source. X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) were used to analyze structure and morphology of the samples. The electrochemical performances of the LiFePO₄/C cathodes were characterized by charge/discharge cures and electrochemical impedance spectroscopy (EIS). The results show that the LiFePO₄/C sample, calcined at 700 °C and contained 3.03% (by mass) carbon, exhibited a highly pure …

Preparation And Methanol Electrooxidation Of Pt/Pmo12/Pedot/Gc Electrodes, Jing-Hua Ma, Rui-Xiang Wang, Yi-Liang Tan, Shan-Shan Wang, Yan-Qin Zhang, You-Jun Fan

Journal of Electrochemistry

Modification of phosphomolybdic acid (PMo₁₂) on poly(3,4-ethylenedioxythiophene) (PEDOT) film (PEDOT/GC) obtained through the electrochemical polymerization was performed using adsorption method (PMo₁₂/PEDOT/GC), followed by electrodepositing Pt on PMo₁₂/PEDOT/GC to prepare Pt/PMo₁₂/PEDOT/GC electrode. Effects of PMo₁₂ and PEDOT on the methanol oxidation performance of electrode were investigated. Results showed that PMo₁₂ obviously changed the morphology and structure of Pt loaded on the electrode, leading to the formation of sharp thorns at the edge of Pt nanostructures. Cyclic voltammetry and chronoamperometry data demonstrated that the catalytic activities of methanol electrooxidation on the Pt/PMo …

Synthesis And Electrochemical Performance Of Si/C Composite Modified By Pani, Guang-Hui Zhang, Pei-Kang Shen, Ge Sang, Ren-Jin Xiong

Journal of Electrochemistry

Silicon/carbon (Si/C) composite materials were prepared through high-energy ball milling and high-temperature solid-phase method, and then coated with thin polyaniline (PAni) film by oxidation. The microstructure and component of the composites were characterized by SEM, XRD, IR, TG, and the electrochemical performance was investigated by cyclic voltammetry (CV) and galvanostatic charge-discharge tests. The results showed that the surface of PAni/Si/G/C composite was coating with complete lamellar structure of PAni film. Its reversible capacity was 784 mAh·g^-1 and 690 mAh·g^-1 could be maintained after 50th charge-discharge cycles.

Synthesis Of Lifepo4/C Cathode By Sol-Gel And Calcining Method With Chitosan Monomer, Jia Xu, Yan-Yan Wang, Rui Wang, Bo Wang, Yue Pan, Dian-Xue Cao, Gui-Ling Wang

Journal of Electrochemistry

The LiFePO₄/C cathode materials for Li-ion battery were synthesized by sol-gel and calcining method using chitosan monomer as a carbon source and a gelating agent. The structures and morphologies were characterized by X-ray diffraction spectroscopy (XRD) and scanning electron microscopy (SEM). The electrochemical performance was investigated by the galvanostatic charge–discharge test. When the molar ratios between chitosan monomer and LiFePO₄ were 1:1.2, the LiFePO₄/C cathode calcined at 600 ^oC showed the best performance. The particle sizes ranged 200 ～ 400 nm. The initial discharge capacity of 155 mAh·g-¹ was achieved at room temperature …

Synthesis And Electrocatalysis Of Pdcu Alloy Nanocrystals, Hai-Bin Wu, Rui-Zhong Zhang, Wei Chen

Journal of Electrochemistry

Monodispersed PdCu alloy nanoparticles were synthesized by co-reduction of Cu(acac)2 and Pd(acac)2 with 1, 2-hexadecanediol. The spherical and popcorn-like shapes of PdCu alloy nanoparticles were obtained by changing the ratios of mixed surface protecting ligands of 1-octadecene, and oleylamine or oleic acid. TEM and XRD measurements showed that both PdCu nanoparticles are alloy nanocrystals dominated with (111) planes and the average sizes are 12.7 ± 0.18 and 20.4 ± 0.31 nm for he spherical and popcorn-like PdCu nanoparticles, respectively. The electrocatalytic activities of the PdCu nanocrystals for formic acid oxidation were evaluated by electrochemical cyclic voltammetry (CV). The result showed …

Properties Of Carbon Coated Tin Negative Electrode For Lithium-Ion Battery, Gui-Chang Liu, Xiao-Xiao Shen, Li-Da Wang

Journal of Electrochemistry

Carbon coated tin power was prepared by decomposing glucose applying a hydrothermal method, and was further used as the active material for negative electrode of lithium secondary battery. Charge-discharge tests show that the carbon coated tin electrode with the addition of 5 wt.% acetylene black as a conductive agent could obtain an initial discharge capacity of 967 mAh·g^-1 and a discharge capacity of 362 mAh·g^-1 after 50 cycles, which is much higher than that of tin electrode (166 mAh·g^-1 after 50 cycles). The coated carbon hinders the agglomeration of tin powder, reduces the irreversible capacity loss of …

Electrochemical Performance Of Fe3O4/C Composites As Negative Material For Lithium-Ion Batteries, Jun-Jie Cai, Shu Yao, Ze-Sheng Li, Hui Meng, Pei-Kang Shen

Journal of Electrochemistry

The Fe₃O₄/Carbon composites have been synthesized through coprecipitation pathway and by insitu aniline polymerization as a carbon source. Structural characterization and morphological study of the composites were investigated by using XRD, SEM and TEM techniques. The results showed that the nanosized Fe₃O₄ particles (40 ~ 80 nm) were encapsulated in the amorphous carbon. During the electrochemical tests, the Fe₃O₄/C composites exhibited high capaticity and excellent cycle ability, the retention of capaticity was about 1000 mAh·g^-1 after 30 cycles of charge/discharge tests at 50 mA·g^-1.

An In Situ Ftir Spectroelectrochemical Study On Methanol Oxidation At Pt-Mo2C/Gc Catalyst, Hai-Ping Huang, Xi-Yu Yao, Pei-Kang Shen

Journal of Electrochemistry

A 40% Pt on Mo₂C/GC catalyst has been prepared by ion exchange method. The mechanism of methanol electrooxidation on Pt-Mo₂C/GC and commercial Pt/C catalysts in acidic media was studied by cyclic voltammetry, XRD measurements and in-situ Fourier transform infrared spectroelectrochemistry. The results revealed that the Pt nanoparticles were uniformly dispersed on Mo₂C/GC with an average particle size of 3 nm. The cyclic voltammetric and chronopotentiometric experiments indicated that Pt-Mo₂C/GC catalyst exhibited a better performance for methanol oxidation than that of Pt/C in acid solution. A negative shift over 90 mV of the …

Oxygen Reduction Reaction On Glycin Modified Pt(111) Electrode, Ming-Fang Li, Jing Kang, Ling-Wen Liao, Yan-Xia Chen, Shen Ye

Journal of Electrochemistry

O

xygen reduction reaction (ORR) on glycin (NH₂CH₂COOH) modified Pt(111) electrode has been investigated using hanging meniscus rotating disk electrode system (HMRD) in 0.05 mol•L^-1 H₂SO₄ and 0.1 mol•L^-1 HClO₄ solutions, respectively. Cyclic voltammograms of the glycin modified Pt (111) electrode measured in 0.05 mol•L^-1 H₂SO₄ solution similar to that of CN^- modified Pt(111) electrodes, demonstrating that sulfate adsorption is strongly inhibited at the glycin modified Pt(111). From the polarization curve of ORR recorded in 0.05 mol•L^-1 H₂SO₄ solution, it is …

Effect Of Ti/Pbo2 Electrodes Doped With Different Elements On Electrocatalytic Oxidation Characteristics Of Phenol, Xiao-Lei Liu, Yuan-Yuan Dan, Hai-Yan Lu, Hai-Bo Lin, Ming-Li Ouyang, Chuan-Jun Yun

Journal of Electrochemistry

Three types of electrodes, namely, Ti/PbO₂, F-doped PbO₂ (Ti/PbO₂-F) and nano-Co₃O₄-doped PbO₂ (Ti/PbO₂+Nano-Co₃O₄) electrodes, were prepared by electro-deposition method on the Ti substrate with the interlayer of SnO₂-Sb₂O₅. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to study the compositions, structures and film morphologies of the electrodes. Electrocatalytic oxidation characteristics to phenol on the prepared electrodes were investigated by electrochemical method. The experimental results showed that compared with the Ti/PbO₂ electrode, the potentials of oxygen …

A Dft Calculation Screening Of Pt-Based Bimetallic Catalysts For Oxygen Reduction, Li-Hui Ou, Sheng-Li Chen

Journal of Electrochemistry

Developing Pt-lean catalysts for oxygen reduction reaction (ORR) is the key for large-scale application of proton exchange membrane fuel cell (PEMFC). In this paper, we have proposed a multiple-descriptor strategy for screening efficient and durable ORR alloy catalysts of low Pt content. We argue that an ideal Pt-based bimetallic alloy catalyst for ORR should possess simultaneously negative alloy formation energy, negative surface segregation energy of Pt and a lower oxygen binding ability than pure Pt. By performing detailed DFT calculations on the thermodynamics, surface chemistry and electronic properties of various Pt-M alloys (M refers to non-precious transition metals in the …

Sodium Carbonate Catalyzed Photoelectrochemical Water Splitting Over Tio2 Nanotubes Photoanode, De-Sheng Kong, Jing Wang, Xue-Di Zhang, Xi Zhao, Chao Wang, Yuan-Yuan Feng, Wen-Juan Li

Journal of Electrochemistry

Surface recombination of the photogenerated electron-hole pairs at semiconductor/electrolyte interface is one of the most essential reasons responsible for lowering photoconversion efficiency (Φ) of light to chemical energy for photoelectrochemical (PEC) water splitting reaction. In this paper, the catalytic effect of sodium carbonate on the oxygen evolution reaction (OER) over TiO₂ nanotubes photoanode during PEC water splitting was investigated by performing photocurrent and ac impedance measurements. It was demonstrated that the addiction of 1 mmol•L^-1 Na₂CO₃ in 0.5 mol•L^-1 NaClO₄ electrolyte can effectively improve the charge transfer properties for the photogenerated holes across …

Electrocatalytic Oxidation Of Formic Acid On Pd/Ni Heterostructured Catalyst, Mingjun Ren, Liangliang Zou, Ju Chen, Ting Yuan, Qinghong Huang, Haifeng Zhang, Hui Yang, Songlin Feng

Journal of Electrochemistry

A Pd/Ni bimetallic nanostructured electrocatalyst was fabricated via a two-step reduction route. Owing to an epitaxial growth of Pd atoms on the surface of Ni nanoparticles, heterostructured Pd/Ni nanocomposites were formed and verified by high resolution transmission electron microscopy combined with energy-dispersion X-ray spectroscopy. X-ray diffraction confirmed that the as-prepared Pd/Ni nanocomposites possessed a single face-centered-cubic (fcc) Pd structure, probably due to a weaker diffraction intensity of metallic Ni and/or overlapping by that of Pd. The intrinsic catalytic activity on the Pd/Ni is higher than that on the Pd. Moreover, the durability of formic acid oxidation on the Pd/Ni was …

Electrochemical Performance Of Screen-Printed Composite Coatings Of Conducting Polymers And Carbon Nanotubes On Titanium Bipolar Plates In Aqueous Asymmetrical Supercapacitors, Xiaohang Zhou, George Z. Chen

Journal of Electrochemistry

Composites of conducting polymers (polypyrrole and polyaniline) with acid treated multi-walled carbon nanotubes were formulated into printable aqueous inks, with the aid of functional additives (benzethonium chloride as a surfactant with or without polyvinyl alcohol as a binder). The inks were screen-printed as fairly uniform coatings of various mass loading densities and areas (up to 75 mg cm^-2 and 100 cm²) on thin titanium plates (0.1 mm in thickness). These screen-printed plates were used to fabricate both unit cell and multi-cell stack of asymmetrical supercapacitors with screen-printed negative electrodes of activated carbon (pigment black) in aqueous electrolytes …

Ternary Alloy Electrocatalysts For Oxygen Reduction Reaction, Jin Luo, Lefu Yang, Binghui Chen, Chuanjian Zhong

Journal of Electrochemistry

Proton exchange membrane fuel cell represents an important electrochemical energy conversion device with many attractive features in terms of efficiency of energy conversion and minimization of environmental pollution. However, the large overpotential for oxygen reduction reaction at the cathode and the low activity, poor durability and high cost of platinum-based catalysts in the fuel cells constitute a focal point of major barriers to the commercialization of fuel cells. The development of nanostructured catalysts shows promises to addresses some of the challenging problems. The ability to engineer the composition and nanostructure of nanoalloy catalysts is important for developing active, robust and …

Advances And Challenges Of Intermediate Temperature Solid Oxide Fuel Cells: A Concise Review, Sanping Jiang

Journal of Electrochemistry

Fuel cell is an electrochemical energy conversion device to directly convert the chemical energy of fuels to electricity. Among all types of fuel cells, solid oxide fuel cells (SOFCs) operating at intermediate temperatures of 600~800 ^oC offer an attractive option that is much more fuel flexible than low temperature fuel cells such as proton exchange membrane fuel cells, and is suitable for a wide range of applications. However, two main challenges remain towards the commercial viability and acceptance of the SOFC technologies: the cost and durability. Both are critically dependent on the process, fabrication, performance, chemical and microstructural stability …

Electrocatalytic Activity Of Palladium Nanocatalysts Supported On Carbon Nanoparticles In Formic Acid Oxidation, Jie Huang, Zhiyou Zhou, Yang Song, Xiongwu Kang, Ke Liu, Wancheng Zhou, Shaowei Chen

Journal of Electrochemistry

Palladium nanostructures were deposited onto carbon nanoparticle surface by a chemical reduction method. Transmission electron microscopic studies showed that whereas the resulting metal-carbon (Pd-CNP) nanocomposites exhibited a diameter of 20 to 30 nm, the metal components actually showed a cauliflower-like surface morphology that consisted of numerous smaller Pd nanoparticles (3 to 8 nm). Electrochemical studies showed that the effective surface area of the Pd-CNP nanoparticles was about 40% less than that of Pd black, possibly because the Pd nanoparticles were coated with a layer of carbon nanoparticles; yet, the Pd-CNP nanocomposites exhibited marked enhancement of the electrocatalytic activity in formic …

Adsorption And Electrooxidation Of Carbon Monoxide On Platinum Surfaces Modified With Sulfur, A. Mattox Mathew, W. Henney Matthew, Johnson Adam, Zou Shouzhong

Journal of Electrochemistry

Adsorbed sulfur is commonly considered as a reaction poison. However, small amounts of sulfur on platinum significantly increase the surface reactivity toward carbon monoxide (CO) electrooxidation. For the solution CO oxidation, the onset potential was shifted up to over 300 mV negative to that on S-free surface, and the extent of the negative potential shift increases with the sulfur coverage (X_s) up to about 0.6. The enhanced CO oxidation also depends on the solution pH. For the adsorbed CO, at low sulfur coverages (X_s < 0.3), the oxidation peak potential is about 40 mV negative to that of the corresponding clean Pt. However, at higher coverages, the peak potential is about 30 mV more positive. Surface-enhanced Raman spectra show that the adsorption of sulfur significantly redshifts the Pt-CO stretching frequency. These observations are explained by the weakening of the Pt-CO bond and the hindrance of CO diffusion by Sads.

Kinetic Study Of Photoelectrochemical Oxidation Of Lignin Model Compounds On Tio2 Nanotubes, Min Tian, Daniel Liba, Aicheng Chen

Journal of Electrochemistry

In this study, TiO₂ nanotubes were prepared via the electrochemical oxidation of titanium substrates in a non-aqueous electrolyte and their morphology and microstructures were examined by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The photoelectrochemical oxidation of two lignin model compounds, 1-(3,4-dimethoxyphenoxy)-2-(2-methoxyphenoxy)-1,3-propanediol (DMP) and 3-hydroxy-1-(3,4-dimethoxyphenoxy)-2-(2-methoxyphenoxy)-1,3-propanone (HDM), was investigated. A new band appeared at ~304 nm during the photoelectrochemical oxidation of DMP. The rate of DMP intermediate formation was amplified with the increase of initial concentrations, while it was diminished with increased temperature. Despite the similarity in structure between HDM and DMP, there are only small increases in absorbance …

Electrochemical Synthesis Of Silver-Tetracyanoquinodimethane Nanorods At Agar Supported Water/1,2-Dichloroethane Interface, Li Huang, Yixian Wang, Michael V. Mirkin, Bin Ren, Dongping Zhan

Journal of Electrochemistry

Silver-tetracyanoquinodimethane (AgTCNQ) is an important charge transfer salt due to its high conductivity and other electronic properties. In this communication, we report the synthesis of AgTCNQ at the liquid/liquid interface. Agar was used as a gelling agent to support water/1,2-dichloroethane (DCE) interface. Silver ions were transferred from the hydrogel into DCE phase, where they combined with TCNQ^- to form AgTCNQ nanorods. The developed method can provide a new route for synthesis of functional materials based on the electrochemistry at the liquid/liquid interface.

The Oxidation Of Hydrogen Peroxide On Nanostructured Rhodium Microelectrodes, N. Bartlett Philip, F. Esterle Thomas

Journal of Electrochemistry

Mesoporous Rh films were deposited onto platinum microelectrodes from the H₁ lyotropic liquid crystalline phase of C₁₂EO₈ (octaethyleneglycol monododecyl ether). The electrodes show well defined voltammetry for the oxidation and the reduction of hydrogen peroxide at low concentrations (<10 mmol•L-1) with excellent stability for operation at neutral pH. Based on the hysteresis in the current and the potential dependence the oxidation of hydrogen peroxide occurs through a CEE mechanism involving Rh(OH)₃ on the mesoporous Rh electrode surface. At higher hydrogen peroxide concentrations the current reaches a plateau that is due to either saturation of the binding sites for hydrogen peroxide or limitation of the reaction due to acidification of the solution within the pores. For the thin films (below 200 nm) the hydrogen peroxide calibration curves we …

Poly(Aniline/O-Nitroaniline): A High Capacity Cathode Material For Lithium Ion Batteries, Rui-Rui Zhao, Li-Min Zhu, Jiang-Feng Qian, Han-Xi Yang

Journal of Electrochemistry

Polyaniline can be used as a high capacity cathode material due to the advantages of material abundance and synthetic simplicity. However, its practical application in battery has been hindered by poor electrochemical utilization and cycling instability. To solve these problems, we synthesized the poly(aniline/o-Nitroaniline) (P(AN-oNA)) by introducing the electron-drawing group-nitroaniline onto the polyaniline chains, so as to enhance electrochemical utilization and stability of the polyaniline derivative. The as-prepared Li/P(AN-oNA) copolymer shows a greatly enhanced discharge capacities of 186 mAh·g^-1 at initial cycles, about 37% higher than its parent PAN, and remains 168 mAh·g^-1 after 60th cycle. Also, the …

Influences Of Particle Size And Sulfuric Acid Treatment On The Electrochemical Performance Of Bamboo Charcoal, Yu Yao, Ai-Shui Yu

Journal of Electrochemistry

The bamboo charcoal had been milled and treated by sulfuric acid. The influences of as-prepared material particle size and sulfuric acid treatment on the electrochemical performance had been studied. The result displays that the bamboo charcoal with mean particle size about 5 μm has the best first coulombic efficiency. Sulfuric acid treatment could raise the discharge capacity of bamboo charcoal, and the first discharge capacity of 328.2 mAh·g^-1 was obtained with the bamboo charcoal treated by sulfuric acid for 18 h. Furthermore, the capacity of 302.3 mAh·g^-1 could be maintained for 50 cycles, showing good cycle performance.

Electrochemical Sensing Of Guanine And Adenine Based On The Boron-Doped Carbon Nanotubes Modified Electrode, Ya-Lin Xia, Chun-Yan Deng, Juan Xiang

Journal of Electrochemistry

In this work, the boron-doped carbon nanotubes (BCNTs) modified glassy carbon (GC) electrode was simply fabricated, and the electrochemical oxidation behaviors of guanine and adenine at the BCNTs/GC electrode were investigated. Compared with the bare GC and CNTs/GC electrodes, the BCNTs-modified electrode exhibited extraordinary electrocatalytic activity towards the oxidations of guanine and adenine as indicated by the obvious increase in current responses. Moreover, the peak separation between guanine and adenine was large enough for their potential recognition in mixture without any separation or pretreatment. Therefore, the simultaneous determination of guanine and adenine was successfully achieved. The BCNTs/GC electrode showed high …

Naf-M (M = Fe, Cu) Nanocomposites As Conversion Cathode Materials For Sodium Ion Batteries, Ting Li, Zhong-Xue Chen, Yu-Liang Cao, Han-Xi Yang

Journal of Electrochemistry

The NaF-M (M = Fe, Cu) nanocomposites were prepared by high-energy ball milling using TiN grinding nanoparticles and investigated as cathode materials for sodium ion batteries. The experimental results demonstrated that NaF-Fe and NaF-Cu nanocomposites can go through electrochemical conversion reaction with Na⁺ uptake or removal, delivering a reversible capacity of ~ 150 mAh·g^-1, even through a reversed conversion from initial discharged state to a charged state. These results reveal the possibility to realize a conversion reaction as long as NaF and elemental metal particles are intimately contacted to form active nanocomposites at nanodomain, which suggests a …

Synthesis And Electrochemical Properties Of High-Capacity Cathode Material 0.08lico0.75Al0.25O2-0.92linio2, Ru-Ying Wang, Tian Qiu, Chong Mao, Wen-Sheng Yang

Journal of Electrochemistry

CoAl-LDH or Co(OH)₂ coated spherical Ni(OH)₂ precursors were obtained via a co-precipitation method at a constant pH. The mixtures of the precursors and LiOH·H₂O were annealed at high temperature in O₂ atmosphere, and then the cathode materials of 0.08LiCo_0.75Al_0.25O₂-0.92LiNiO₂, 0.08LiCoO₂-0.92LiNiO₂ and LiNiO₂ were synthesized. Effects of the coating layer were also studied. The results showed that the 0.08LiCo_0.75Al_0.25O₂-0.92LiNiO₂ material possessed the best rate and cycle life performance. The discharging capacities at 0.1C, 0.5C and 3C were …

Preparation And Modification Of Li4Ti5O12 As Anode Materials For Lithium-Ion Batteries, Jin-Long Liu, Zhou-Guang Lu, Yang Ren, Ya-Jie Zhu, Shan-Shan Hu, Zhong Peng, Dong Qian, You-Gen Tang

Journal of Electrochemistry

Anode Material Li₄Ti₅O₁₂ for lithium-ion batteries was successfully prepared using half-solid-state method. Furthermore, carbon coating modification of Li₄Ti₅O₁₂ was also carried out. The phase structure and morphology were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and high resolution transmission electron microscopy (HRTEM). The electrochemical properties were investigated by constant current discharge-charge tests, cyclic voltammetry and electrochemical impedance techniques. The results indicated that the electrochemical performance of Li₄Ti₅O₁₂ without modification declined seriously due to the aggregation of Li₄Ti …