Chitosan/Nonahydrate Gel Derived Fe-N-Doped Porous Carbon Sheet As High-Efficient Orr Electrocatalyst, Fan-Lu Meng, Xin-Bo Zhang, Jun-Min Yan

Journal of Electrochemistry

The chitosan/nonahydrate gel was used as a precursor to realize the uniform mixture of N-polymer and metal salt. After lyophilization treatment, the gel went through heat treatment and acid etch. Accordingly, the Fe-N-doped porous carbon sheet with homogenous composition and microstructure was prepared. Compared with the commercial Pt/C catalyst, the Fe-N-doped porous carbon sheet exhibited more positive onset potential and half-wave potential, higher current density, and especially, excellent durability. The power density of 318 mW·cm^-2 was obtained in alkaline fuel cell with the Fe-N-doped porous carbon sheet as a cathode catalyst, which is higher than 267 mW·cm^-2 with …

Synthesis Of Ultrathin Co3O4 Nanoflakes Film Material For Electrochemical Sensing, Hui-Juan Wang

Journal of Electrochemistry

Ultrathin cobalt oxide (Co₃O₄) nanoflakes film material was synthesized by using an electro-deposited cobalt layer as a raw material through a simple oxidation method and followed by a heat treatment at 350 ^oC. The physical characterizations of the Co₃O₄ nanoflakes film were performed by scanning electron microscopy (SEM), X-ray diffraction (XRD) and transmission electron microscopy (TEM) technologies, and the electrochemical activity was measured by cyclic voltammetry (CV). As a promising material for electrochemical sensing, the as-synthesized ultrathin Co₃O₄ nanoflakes film material exhibited excellent electrochemical activity for H₂O …

Syntheses Of Ag@Pd@Pt Nanoparticles With Tunable Shell Thickness For Electrochemical Oxidation Of Formic Acid, Xiao-Dong Lin, Du-Hong Chen, Zhong-Qun Tian

Journal of Electrochemistry

In an effort to lower cost of a catalyst, the silver (Ag) core with palladium (Pd) layer then platinum (Pt) island (Ag@Pd@Pt) nanoparticles were synthesized and the electrocatalytic activity of Ag@Pd@Pt nanoparticles on formic acid was compared with that of Au@Pd@Pt nanoparticles reported previously. The results showed that the existence of a small amount of Pt could significantly improve the activity of the catalyst. When the surface coverage of Pt approached 0.5 monolayers, the activity of Ag@Pd@Pt nanoparticles reached the maximum. Though the onset potential of the electro-oxidation was slightly more positive (about 50 mV), the overall electrocatalytic activity of …

Investigation On Laser Induced Deposition Of Cu-Based Materials At [Bmim]Bf4/Pt Electrode Interface, Min-Min Xu, Jin-Hua Mei, Jian-Lin Yao, Ren-Ao Gu

Journal of Electrochemistry

By controlling the negative potential, Cu-based materials were deposited at the [BMIm]BF₄/Pt electrode interface under the laser irradiation. The effects of laser power and irradiation time on the yield of deposition products were studied by using different laser powers and different irradiation time. The product yield could be directly determined by the size of deposition point through the observation from the optical microscope. Further mechanism study combined with the formula deduced that the thermal effect of the laser could make the electrode surface temperature rise 110 degrees, which can promote the occurrence of electrodeposition. By SEM characterization, the …

Intrinsic Interfacial Property Between High-Voltage Lini0.5Mn1.5O4 Cathode And Electrolyte, Li Li, Jing-Jing Xu, Shao-Jie Han, Wei Lu, Li-Wei Chen

Journal of Electrochemistry

To obtain high energy density, developing high-voltage cathode materials is an effective approach. The cathode/electrolyte interface stability is the key factor for the cycle performance and safety performance of high-voltage lithium ion batteries. It is, therefore, of significant importance to study the stability of cathode/electrolyte interface. However, many reports have shown that at the cathode/electrolyte interface the cathodes were prepared by coating the mixture of active materials with a conductive additive and a binder on an Al current collector. The introduction of additives will interfere the surface morphology and component analyses, resulting in difficulty to acquire the intrinsic information at …

An Stm Study On The Structure Of Pt(100)/Ionic Liquid Omipf6 Interface, Jin Peng, Mian-Gang Li, Li-Qiang Xie, Jia-Wei Yan, Bing-Wei Mao

Journal of Electrochemistry

Potential-dependent structures of Pt(100)/ionic liquid 1-methyl-3-octylimidazolium hexafluorophosphate (OMIPF₆) interface have been studied by electrochemical scanning tunneling microscopy (ECSTM). The cation OMI⁺ forms ordered structure on Pt(100) surface, which exists in a potential region of about 1.2 V. When the potential is more negative than -0.6 V, it can be seen that the ordered structure transforms to disordered structure. When the potential shifts positively to +0.6 V, the desorption of cations OMI⁺ occurs, which indicates that strong electrostatic repulsion is needed to overcome chemical interaction between OMIPF6 and Pt(100) surface, leading to the desorption. The above results …

Lithium Plating Identification From Degradation Behaviors Of Lithium-Ion Cells, Jian-Bo Zhang, Lai-Suo Su, Xin-Yu Li, Hao Ge, Ya-Kun Zhang, Zhe Li

Journal of Electrochemistry

Lithium plating has huge impact on the lifetime and safety of lithium-ion cells. It is, therefore, necessary to identify lithium plating. In this study, the accelerated stress tests of lithium-ion cells were conducted under different conditions with multi-stress loads. Based on the different effects of the two major aging mechanisms, namely, SEI (Solid Electrolyte Interface) layer growth and lithium plating, on the degradation behaviors, two lithium plating identification methods of resistance-capacity plot and Arrhenius plot were employed. The experimental results revealed that the two identification methods are highly consistent with each other. Furthermore, the origins of capacity loss were distinguished …

Design And Synthesis Of Dynamic Covalent Polymer Scaffolds With Controlled Architectures, Emily Annette Hoff

Dissertations

The design and synthesis of functional, controlled polymer architectures is essential to the development of new materials with precise and tailorable properties or applications. The work described in this dissertation focuses on the development of controlled polymer architectures with dynamic linkages for the design of multifunctional materials and surfaces via robust, efficient, and stimuli-responsive strategies.

In Chapter III, a post-polymerization modification strategy based on ambient temperature nucleophilic chemical deblocking of polymer scaffolds bearing N-heterocycle blocked isocyanate moieties is reported. Room temperature RAFT polymerization of three azole-N-carboxamide methacrylates, including 3,5-dimethyl pyrazole, imidazole, and 1,2,4-triazole derivatives, afforded reactive polymer scaffolds …

Role Of The Inner Shell Architecture On The Various Blinking States And Decay Dynamics Of Core-Shell And Core-Multishell Quantum Dots, Pooja Bajwa

Graduate Theses and Dissertations

Colloidal semiconductor nanocrystals (quantum dots, QDs) have received much attention in recent years due to their uniquely size-tunable properties leading to a number of promising applications. Some of their most popular applications include their use as fluorescent probes in biology, as electro-optical components and in photovoltaic devices. CdSe-based QDs are particularly important because of their ease of synthesis, high photoluminescence quantum yields (PL QYs) across the whole visible spectrum and their photostabilty. Shelling of core QDs is usually carried out to improve their optical properties, minimize outer environmental effects on their properties, and avoid toxic element exposure to the environment. …

Micro/Nano-Structured Electrode Materials For Sodium-Ion Batteries, Shuang Yuan, Yun-Hai Zhu, Sai Wang, Tao Sun, Xin-Bo Zhang, Qiang Wang

Journal of Electrochemistry

Sodium has similar physics and chemical properties to lithium, alternatively, sodium (Na)-ion batteries have again aroused a great deal of interest recently, particularly for large-scale stationary energy storage applications due to the practically infinite sodium resources and low cost. However, the technics and materials for Na-ion batteries are immature. Therefore, development of advanced anode and cathode materials for Na-ion batteries is urgently desired but remains a great challenge. This paper briefly reviews some recent progresses in this field, addressing the morphology effects, as well as functions of carbon composite materials toward Na-ion batteries. Several electrode materials with micro/nano-structures based on …

Research Progress In Cycle Stability Of Silicon Based Li-Ion Battery Anodes, Ze-Liang Guo, Hui Wu

Journal of Electrochemistry

Silicon(Si), with the highest specific capacity currently known, is a promising anode material for Li-ion battery. However, in the charging and discharging process, with Li atoms inserting into and breaking out of the Si crystal lattices, the Si anode undergoes enormous volume expansion and contraction, ending in pulverization. The fact that the specific capacity of bulk Si anodes drop quickly is a challenging problem. In this review, we summarize recent progresses in Si anode. We concern about the nanostructure of silicon, cooperation of silicon with other additives and macrostructure design of anodes. We discuss strengths and shortcomings of different methods, …

Electrochemical Performance Of Crystalline Li12Si7 As Anode Material For Lithium Ion Battery, Ya-Xiong Yang, Rui-Jun Ma, Ming-Xia Gao, Hong-Ge Pan, Yong-Feng Liu

Journal of Electrochemistry

Crystalline Li₁₂Si₇ is successfully synthesized by heating the mixture of LiH and Si with a molar ratio of 12:7, which avoids the huge difference of the melting points between Li and Si. The electrochemical performance and lithium storage mechanism of the as-prepared Li12Si7 are studied in this work. It is found that only a change in cell volume takes place without a phase change during the lithiation/delithiation of Li₁₂Si₇ at a voltage range of 0.02 ~ 0.6 V, exhibiting a solid-solution lithium storage mechanism. Such a lithium storage process effectively retards the volume effect …

Continuous Synthesis And Condition Exploration Of Precursor Ni1/3Co1/3Mn1/3(Oh)2 Ternary Cathode Material, Zhi-Jun Jiang, Ya-Li Zhang, Qian Wang, Hui Zhang

Journal of Electrochemistry

Commercial LiNi_1/3Co_1/3Mn_1/3(OH)₂ ternary material is generally prepared by a combination of co-precipitation and solid state reaction method. The particle size distribution and morphology of Ni_1/3Co_1/3Mn_1/3(OH)₂ precursor have a great impact on the electrochemical performance of LiNi_1/3Co_1/3Mn_1/3O₂. In this work, the precursor Ni_1/3Co_1/3Mn_1/3(OH)₂ ternary cathode material was prepared by co-precipitation method with MnSO₄, NiSO₄, and CoSO₄ as raw materials, NaOH as a precipitating agent and NH_{3 …}

Research And Application Of Key Materials For Sodium-Ion Batteries, Yong-Chang Liu, Cheng-Cheng Chen, Ning Zhang, Liu-Bin Wang, Xing-De Xiang, Jun Chen

Journal of Electrochemistry

Sodium-ion batteries (SIBs) have been considered as a potential large-scale energy storage technology owing to the abundance, wide distribution, and low price of sodium resources. However, the larger and heavier sodium ion as compared to lithium ion makes it difficult to identify appropriate electrode materials with the capability for fast and stable sodium-ion insertion/extraction. Furthermore, the optimization of electrolyte, the matching of cathode and anode materials, and the construction of sodium-ion full batteries with high-performance, high-safety, and low-cost are urgently needed in order to make SIBs commercially available. This review summarizes the up-to-date research progresses in key materials (including cathode, …

Advances And Prospects Of Lithium-Sulfur Batteries, Shou-Yi Yuan, Ying Pang, Li-Na Wang, Yong-Gang Wang, Yong-Yao Xia

Journal of Electrochemistry

Lithium-sulfur batteries have recently attracted worldwide attention due to the high specific theoretical energy density of sulfur cathode (2600 Wh⋅kg^-1), low cost and wide availability of sulfur. However, the practical application of lithium-sulfur batteries has been hindered by several challenges, such as the shuttling of polysulfide intermediates, the large volume expansion of sulfur during charge/discharge and the dendrites formation on lithium anode. Foremost among these is the shuttling effect arising from the dissolution of lithium polysulfides intermediate into the electrolyte from the cathode reaction and their diffusion to the anode where they react with metal lithium to form …

Research Progress Of Si-Based Anode Materials For Lithium-Ion Batteries, Ding-Qiong Chen, Yang Yang, Qiu-Li Li, Jin-Bao Zhao

Journal of Electrochemistry

Owing to its high theoretical specific capacity (4200 mAh·g^-1), silicon is a promising candidate to replace graphite as the anode in lithium ion batteries (LIBs). However, low intrinsic electric conductivity and dramatic volume change (~ 300%) during the process of lithiation and delithiation result in electrode pulverization and capacity loss with cycling, accordingly, the application of silicon as an anode in LIBs has been severely hindered. We will discuss the structure of silicon electrode including synthesis of Si-based composites,the selection of binder for silicon and the fabrication of binder-free Si-based electrode, as well as the electrolyte additive to …

Template-Assisted Hydrothermal Synthesis Of Nio@Co3O4 Hollow Spheres With Hierarchical Porous Surfaces For Supercapacitor Applications, Wen Zhou, Xue-Feng Lu, Ming-Mei Wu, Gao-Ren Li

Journal of Electrochemistry

Hollow structures have shown great potentials in a variety of important applications, such as energy conversion and storage. In order to further enhance the performance, the rational design of hollow structures with higher complexity in terms of composition and structure is highly desirable and still remains a great challenge. In this work, an efficient strategy was established for the fabrication of novel NiO@Co₃O₄ hollow spheres (HSs) with hierarchical porous surfaces by silica spheres template-assisted hydrothermal synthesis. The as-fabricated NiO@Co₃O₄ HSs showed high specific surface area of 219.68 m²·g^-1, and significant …

Effects Of Lithium Salts On The Properties Of Hyperbrandched/Comb-Like Composite Polymer Electrolytes, Xian-Lei Hu, Xiao-Xu Liang, Ming-Qiu Zhang, Ruo-Xin Zhang, Li-Ping Zhang, Wen-Hong Ruan

Journal of Electrochemistry

Based on the chemical characteristics of the hydroxyl group of PVA side-chain, the hyperbrandched poly(amine-ester) (HBPAE) was used to hypergraftingly pretreated nano-silica (SiO₂) and polyving akohol (PVA). And different lithium salts were added to fabricate the SiO₂-g-HBPAE/PVA-g-HBPAE hyperbrandched/comb-like composite polymer electrolytes (CPEs). The dispersion of nanoparticles in matrix was observed by SEM. The effects of different lithium salts on the properties of CPEs were studied by DSC, tensile test and dielectric spectra. The results showed that the hypergrafting method improved the interphase compatibility between SiO₂ and matrix. Sulfonic acid type lithium salts accelerated self-plasticizing with …

The Study Of Dynamical Electrochemical Impedance Spectroscopy For Oxygen Reduction Reaction On Pt/C Catalyst, Kun-Ming Shi, Jian-Wei Guo, Jia Wang

Journal of Electrochemistry

With joint techniques of rotating disc electrode(RDE) and electrochemical impedance spectroscopy(EIS), and further establishment on equivalent circuit model, this paper studied oxygen reduction reaction(ORR) on commercial Pt/C catalyst in acid medium. Our results found that the dynamical interface on Pt/C consists of two independent processes: 1) the PtO reduction from Pt surface, 2) the new PtO formation from ORR, thus providing key clues for catalyst stability and activity. This also implied that the dynamical interface facilitates reconstruction for porous electrode, and matches with mass transfer. One important issue is discovered that at high overpotential, the high reaction rate for ORR …

Effect Of Surface Treatment On Liquid Adhesion Inside 3-D Structures, Madani A. Khan, Jeffrey Alston, Andrew Guenthner, Jacob Zavala

STAR Program Research Presentations

This study explores the relationship between chemical surface treatments on the interior of glass tubes and their resistance to fluid flow. By treating the interior of the tubes with functional silanes we can decrease or increase the interaction of the tube walls with the fluid column, which translates to changes in fluid column height for a given pressure differential. Resistance to fluid flow is quantified by using the tubes as integral parts of a barometric pressure column and measuring the changes in column height as the fluid is pulled into the tube by a set pressure differential. The barometric pressure …

Metal-Organic Hybrid Nanocomposites For Energy Harvesting Applications, Thulitha Madawa Abeywickrama

Masters Theses & Specialist Projects

Various synthetic methods have been developed to produce metal nanostructures including copper and iron nanostructures. Modification of nanoparticle surface to enhance their characteristic properties through surface functionalization with organic ligands ranging from small molecules to polymeric materials including organic semiconducting polymers is a key interest in nanoscience. However, most of the synthetic methods developed in the past depend widely on non-aqueous solvents, toxic reducing agents, and high temperature and high-pressure conditions. Therefore, to produce metal nanostructures and their nanocomposites with a simpler and greener method is indeed necessary and desirable for their nano-scale applications. Hence the objective of this thesis …

Prospects Of D-Π-A Structured Porphyrins And Their Photoelectrochemical Application, Shuang-Shuang Liu, Jian-Feng Lu, Ming-Kui Wang

Journal of Electrochemistry

Porphyrins and their metalloderivatives are a class of compounds exhibiting a wide variety of interesting and highly useful properties, such as chlorophyll. Porphyrins are particularly interesting in photoelectrochemical applications due to their structural similarity to chlorophylls in natural photosynthetic systems, as well as their strong and tunable absorption properties. Recently, various porphyrins have been extensively studied for their applications in solar cells, photocatalytic hydrogen production, optical information storage and others. This review will focus on the unique physical and chemical properties of D-π-A structured porphyrins, and their photovoltaic performances in dye-sensitized solar cells. A brief discussion in the future development …

Activation Effect Of Nano-Carbon Derived From Co2 On Lead Electrode In Sulfuric Aqueous Solution, Yu-Qiao Song, Hua Zhu, Guang-Jin Zhao, Wen-Long Wu, Shou-Bin Zhou, Di-Hua Wang

Journal of Electrochemistry

Serious sulfation of the negative plate is one of the most popular reasons of the early failure of lead-acid battery. Addition of nano-carbon was proved to be effective for recovering the sulfated electrode and the property of the carbon material always plays an important role. In this work, a new kind of nano-carbon material with high electrical conductivity and good adsorption capability for heavy metal cations, which is electrochemically prepared from CO₂ in molten carbonates, was tested as activation additive for the sulfated lead electrode by cyclic voltammetry and SEM measurements. The results showed that the as-prepared carbon can …

WoX/Pedot:Pss Double-Layered Hole-Transport Layers For Efficient And Stable Planar Heterojunction Perovskite Solar Cells, Wen-Yuan Qiao, Qiang Guo, Cong Li, Shuang Ma, Fu-Zhi Wang, Song-Yuan Dai, Zhan-Ao Tan

Journal of Electrochemistry

Poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) is a commonly used hole-transport material in the perovskite solar cells (PerSCs) structure of perovskite/fullerene planer heterojunction, but it also has a negative effect on the stability of device because of its acidity which will corrode metal oxide transparent electrodes. In this work, a WO_x hole-transport layer with high work function was inserted into the PEDOT: PSS and FTO to enhance the stability and photovoltaic performance. The inserted WO_x layer not only can avoid direct contact between PEDOT:PSS and FTO, but also can further reduce the contact barrier between the electrode interface. We studied the effect …

A Novel Flexible Dye-Sensitized Solar Cell Based On Pt Networks Counter Electrode, Zi-Jie Xu, Fa-Yin Zhang, Xiao-Dan Hong, Wen-Xi Guo, Xiang-Yang Liu, Chang-Jian Lin

Journal of Electrochemistry

Flexible dye-sensitized solar cells (DSSCs) have received widespread attentions in recent years because of their ease of fabrication, low production cost, relatively high chemical stability and flexibility. We report the fabrication of ZnO DSSCs based on the highly flexible, conducting, catalytic and transparent Pt networks counter electrode, and the performance of this solar cell was characterized by SEM, XRD, polarized fluorescence microscope, motor, I-V test station and electrochemical workstation. Compared to Pt nanofiber arrays (NFs), Pt networks not only show a better conductivity, but also exhibit superior transparency and catalytic activity. Furthermore, Pt networks electrode could be constructed on arbitrary …

Fabrications Of Three Copper Sulfide Counter Electrodes And Their Influences On Photovoltaic Properties In Qdsscs, Xiao-Dan Hong, Zi-Jie Xu, Fa-Yin Zhang, Yu-Peng Li, Mei-Dan Ye, Chang-Jian Lin, Wen-Xi Guo

Journal of Electrochemistry

Quantum dot-sensitized solar cells (QDSSCs) have attracted intensive attention in scientific and industrial fields due to their high molar extinction coefficient, spectral tunability by particle size, ease of fabrication, and low cost. In the past years, semiconductor metal sulfides have attracted extensive attention because of their attractive physical and chemical properties for potential applications in many fields,such as PbS, CuS, CoS and CdS. In particular, copper sulfides have become a promising candidate for counter electrode materials in QDSSCs for their outstanding electrochemical and catalytic properties. In order to explore more stable and efficient copper sulfide counter electrode materials, in this …

Hydrothermal One-Step Synthesis Of Layered Nickel/Cobalt Double Hydroxide With Using Shape-Directing Agent And Homogeneous Precipitating Agent, Li-Wei Zhu, Yun-Hai Yan, Hui Jia, Run-Fen Liang

Journal of Electrochemistry

Nickel/cobalt double hydroxide (Ni/Co-DH) has been prepared by facile hydrothermal one-step synthesis method using hexamethylene tetramine (HMT) as a homogeneous precipitating agent and cetyltrimethylammonium bromide (CTAB) as a shape-directing agent. With the hydrolysis of HMT and the use of CTAB, the Ni/Co-DH could be synthesized without additional alkali source, and in the meantime, the Ni/Co-DH exhibited a controlled mesopore size of 13.4 nm and a large BET surface area of 93.6 m² •g^-1 . The X-ray diffraction (XRD) pattern displays that the Ni/Co-DH existed as a mixture of α-Ni(OH)₂-β-Co(OH)₂. The scanning electron microscope (SEM) …

Special Issue: Photoelectrochemistry And New Types Of Solar Cells, Chang-Jian Lin, Yong-Fang Li

Journal of Electrochemistry

/

Theoretical Study Of Photoelectrochemical Reactions And Ec-Sers On Spr Metallic Electrodes Of Silver And Gold, Yuan-Fei Wu, Ran Pang, Meng Zhang, Jian-Zhang Zhou, Bin Ren, Zhong-Qun Tian, De-Yin Wu

Journal of Electrochemistry

At present photoelectrochemistry has received much concern back to nanostructures of noble metals from semiconductor electrodes. This is due to the surface plasmon resonance (SPR) effect of metallic nanostructures, which can effectively convert the far-field light to the near-field light and concentrate the photonic energy to the local surface area with high energy density. Thus, the different enhancement mechanisms, such as the local optical field enhancement, the formation of light generated hot carriers (hot electron-hole pairs), or the photothermal effect, have been proposed in literatures. On the basis of the SPR enhancement effect, the surface-enhanced Raman spectroscopy (SERS) can be …

Photoelectrochemical Water Splitting Cells: Methods For Improving Performance Of Electrodes And Recent Progress On Photocathodes, Kai-Jian Zhu, Wen-Jun Luo, Zhong-Jie Guan, Xin Wen, Zhi-Gang Zou, Wei Huang

Journal of Electrochemistry

Photoelectrochemical water splitting can convert solar energy into hydrogen which is an ideal way to utilize and store solar energy. A p-n tandem cell is considered as the most promising solar water splitting cell due to its high theory conversion efficiency, low cost and photoelectrode material flexibility. However, solar conversion efficiency of a tandem cell is still low in the experiment because of poor performance in a single photoelectrode. In this review, we have introduced some effective approaches to improve the performances of photoelectrodes by reducing recombination of photogenerated carriers in the bulk or on the surface, and suppressing back …