Ordering Degree Regulation Of Pt2Nico Intermetallics For Efficient Oxygen Reduction Reaction, Chen-Hao Zhang, Han-Yu Hua, Jun-Hao Yang, Qian Zhang, Chang Yang, De-Li Wang

Journal of Electrochemistry

Alloying transition metals with Pt is an effective strategy for optimizing Pt-based catalysts toward the oxygen reduction reaction (ORR). Atomic ordered intermetallic compounds (IMC) provide unique electronic and geometrical effects as well as stronger intermetallic interactions due to the ordered arrangement of metal atoms, thus exhibiting superior electrocatalytic activity and durability. However, quantitatively analyzing the ordering degree of IMC and exploring the correlation between the ordering degree and ORR activity remains extremely challenging. Herein, a series of ternary Pt₂NiCo intermetallic catalysts (o-Pt₂NiCo) with different ordering degree were synthesized by annealing temperature modulation. Among them, the o-Pt …

Performance Of Co2/H2O Co-Electrolysis In A Flat-Tube Solid Oxide Electrolysis Cell Stack Under Air-Free Environment, Xiao-Hui Zhong, Fei Wang, An-Qi Wu, Bei-Bei Han, Jian-Xin Wang, Wan-Bing Guan

Journal of Electrochemistry

This work investigates the transient performance and stability of CO₂/H₂O co-electrolysis in an air-free environment using a flat-tube solid oxide electrolysis cell (SOEC) stack. The results show that the transient behavior of the stack with and without blowing gas in the air electrode is almost the same. With a current density of 0.67 A·cm⁻²@750 °C, the stack operated for over 200 h under co-electrolysis conditions with no air blowing, and the voltage drop rate of the stack was approximately 0.203%/100 hours. Microstructure analysis reveals significant loss of Ni particles and formation of an insulating …

Additive Manufacturing Of Thermoplastic Composites, Matik Heskin, K. Chandrashekhara, Richard Billo, Ming-Chuan Leu, Thomas P. Schuman

Miners Solving for Tomorrow Research Conference

No abstract provided.

Polymerization Methods For Vinyl Phosphonate Monomers: Challenges And Perspectives, Sara Mccauley

Miners Solving for Tomorrow Research Conference

No abstract provided.

Preliminary Assessment Of Non-Volatile Particulate Matter And Gaseous Emissions From A Premixed Pre-Vaporized Combustor Designed For Civil Supersonic Transport, Ugochukwu Ewuzie, Godwin Ifeanyi Ogbuehi, Steven Achterberg, Monday Uchenna Okoronkwo, Philip D. Whitefield

Miners Solving for Tomorrow Research Conference

No abstract provided.

Study On Dopamine Electrochemical Sensing Based On Au@Mos2, Ning An, Ni Su, Xin-Ran Li, Jian-Yu Liu, Qi-Yan Wang

Journal of Electrochemistry

Dopamine (DA) is a vital neurotransmitter, and accurate detection of its concentration is critical for both clinical diagnostics and neuroscience research. Due to its electrochemical activity, DA is commonly detected using electrochemical methods, which are favored for their simplicity, fast response time, and suitability for in vivo analysis. In this work, a highly sensitive DA electrochemical sensor was developed using an Au@MoS₂ composite, created by modifying molybdenum disulfide (MoS₂) nanosheets with gold nanoparticles through HAuCl₄ reduction, and it was aimed at enhancing DA adsorption and improving detection performance. Scanning Electron Microscopy (SEM), transmission electron microscopy (TEM), …

Recent Advances In Non-Enzymatic Electrochemical Sensors For Theophylline Detection, Gustria Ernis, Yulia M T A Putri, Muhammad Iqbal Syauqi, Prastika Krisma Jiwanti, Yeni Wahyuni Hartati, Takeshi Kondo, Qonita Kurnia Anjani, Jarnuzi Gunlazuardi

Journal of Electrochemistry

Detection of target analytes at low concentrations is significant in various fields, including pharmaceuticals, healthcare, and environmental protection. Theophylline (TP), a natural alkaloid used as a bronchodilator to treat respiratory disorders such as asthma, bronchitis, and emphysema, has a narrow therapeutic window with a safe plasma concentration ranging from 55.5–111.0 μmol·L^–1 in adults. Accurate monitoring of TP levels is essential because too low or too high can cause serious side effects. In this regard, non-enzymatic electrochemical sensors offer a practical solution with rapidity, portability, and high sensitivity. This article aims to provide a comprehensive review of the recent developments …

In-Situ Electrodeposition Of Feco-Mof On Au Ultramicroelectrode For Highly Sensitive Detection Of Epinephrine, Yan Chen, Shang Jian, Si-Yu Wan, Xiao-Tong Cui, Zhong-Gang Liu, Zheng Guo

Journal of Electrochemistry

Metal-organic framework (MOF) nanostructures have emerged as a prominent class of materials in the advancement of electrochemical sensors. The rational design of bimetallic MOF-functionalized microelectrode is of importance for improving the electrochemical performance but still in great challenge. In this work, the bimetallic FeCo-MOF nanostructures were assembled onto a gold disk ultramicroelectrode (Au UME, 5.2 μm in diameter) via an in-situ electrodeposition method, which enhanced the sensitive detection of epinephrine (EP). The in-situ electrodeposited FeCo-MOF exhibited a characteristic nanoflower-like morphology and was uniformly dispersed on the Au UME. The FeCo-MOF/Au UME demonstrated excellent electrochemical performance on the detection of EP …

Effect Of Niobium Dopant On Zno Thin Films Prepared Via The Sol–Gel Spin Coating Method, Kevin Alvin Eswar, Nur Fairuz Rostan, Maryam Mohamad, Rabiatuladawiyah Md Akhir, Rosfayanti Rasmidi, Muliyadi Guliling, Najwa Ezira Azhar, Irmaizatussyehdany Buniyamin, Mohd Firdaus Malek, Mohamad Rusop Mahmood, Husairi Fadzilah Suhaimi, Saifollah Abdullah

Makara Journal of Science

Thin films of zinc oxide (ZnO) and niobium (Nb)-doped ZnO were deposited on a glass substrate using the sol–gel spin coating method. Diethanolamine, isopropyl alcohol, and zinc acetate served as the stabilizers, solvent, and starting ma-terial, respectively. Niobium pentachloride was employed as the dopant source. Energy-dispersive X-ray analysis con-firmed Nb incorporation. Field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), and ultravio-let–visible spectroscopy (UV–Vis) analyses characterized the morphology, structure, and optics of the films, respective-ly. Both films, comprising nanoparticles, were visible in FESEM. Nb doping reduced the particle size from 44.2 nm to 35.8 nm. The XRD peaks at 31.23°, …

Metal Nitrides As Cathode Hosts For Lithium-Sulfur Batteries, Hai-Ji Xiong, Cheng-Wei Zhu, Ding-Rong Deng, Qi-Hui Wu

Journal of Electrochemistry

Lithium-sulfur batteries are considered as one of the potential solutions as integrating renewable energy systems for large-scale energy storage because of their high theoretical energy density (2600 Wh·kg^–1) and specific capacity (1675 mAh·g^–1). Currently, various strategies have been proposed to overcome the technical barriers, e.g., “shuttle effect”, capacity decay and volumetric change, which impede the successful commercialization of lithium-sulfur batteries. This paper reviews the applications of metal nitrides as the cathode hosts for high-performance lithium-sulfur batteries, summarizes the design strategies of different host materials, and discusses the relationship between the properties of metal nitrides and their …

Enhancing Cycle Life Of Graphite ‖ Lifepo4 Batteries Via Copper Substituted Li2Ni1-XCuXO2 Cathode Prelithiation Additive, Jian-Ming Zheng, Jing-Wen Zhang, Tian-Peng Jiao

Journal of Electrochemistry

Lithium nickel oxide (Li₂NiO₂), as a sacrificial cathode prelithiation additive, has been used to compensate for the lithium loss for improving the lifespan of lithium-ion batteries (LIBs). However, high-cost Li₂NiO₂ suffers from inferior delithiation kinetics during the first cycle. Herein, we investigate the effects of the cost-effective Cu substitution of Li₂Ni_1-xCu_xO₂ (x = 0, 0.2, 0.3, 0.5, 0.7) synthesized by high-temperature solid-phase method on the structure, morphology, electrochemical performance of graphite‖LiFePO₄ battery. The X-ray Diffraction (XRD) refinement result demonstrates that Cu substitution strategy is favorable …

Sno2 Particles Embedded Into Carbon Coated Mesoporous SioX Rod As High Volumetric Capacity Anode For Lithium-Ion Batteries, Jia-Lin Guo, Ni-Ni Li, Peng Zheng

Journal of Electrochemistry

Due to the high capacity and moderate volume expansion of silicon protoxide SiO_x (160%) compared with that of Si (300%), reducing silicon dioxide SiO₂ into SiO_x while maintaining its special nano-morphology makes it attractive as an anode of Li-ion batteries. Herein, through a one-pot facile high-temperature annealing route, using SBA15 as the silicon source, and embedding tin dioxide SnO₂ particles into carbon coated SiO_x, the mesoporous SiO_x-SnO₂@C rod composite was prepared and tested as the anode material. The results revealed that the SnO₂ particles were distributed uniformly in the …

New Insights Into Controlling The Functional Properties Of Tin Oxide-Based Materials, Alexandra Kuriganova, Nina Smirnova

Journal of Electrochemistry

Development of methodologies for fabrications of nanostructured materials that provide control over their microstructural features and compositions represents a fundamental step in the advancement of technologies for productions of materials with well-defined functional properties. Pulse electrolysis, a top-down electrochemical approach, has been demonstrated to be a viable method for producing nanostructured materials with a particular efficacy in the synthesis of tin oxides. This method allows for significant control over the composition and shape of the resulting tin oxides particles by modifying the anionic composition of the aqueous electrolyte, obviating the need for additional capping agents in the synthesis process and …

A Cnt Intercalated Co Porphyrin-Based Metal Organic Framework Catalyst For Oxygen Reduction Reaction, Pei-Pei He, Jin-Hua Shi, Xiao-Yu Li, Ming-Jie Liu, Zhou Fang, Jing He, Zhong-Jian Li, Xin-Sheng Peng, Qing-Gang He

Journal of Electrochemistry

The poor electronic conductivity of metal-organic framework (MOF) materials hinders their direct application in the field of electrocatalysis in fuel cells. Herein, we proposed a strategy of embedding carbon nanotubes (CNTs) during the growth process of MOF crystals, synthesizing a metalloporphyrin-based MOF catalyst TCPPCo-MOF-CNT with a unique CNT-intercalated MOF structure. Physical characterization revealed that the CNTs enhance the overall conductivity while retaining the original characteristics of the MOF and metalloporphyrin. Simultaneously, the insertion of CNTs generated adequate mesopores and created a hierarchical porous structure that enhances mass transfer efficiency. X-ray photoelectron spectroscopic analysis confirmed that the C atom in CNT …

Nanostructured Graphitic Carbon Nitride For Photocatalytic And Electrochemical Applications, Muhammad Abdul Qadeer, Iqra Fareed, Asif Hussaine, Muhammad Asim Farid, Sadia Nazir, Faheem K. Butt, Ji-Jun Zou, Muhammad Tahir, Shang-Feng Du

Journal of Electrochemistry

Graphitic carbon nitride (g-C₃N₄) exhibits great mechanical as well as thermal characteristics, making it a valuable material for use in photoelectric conversion devices, an accelerator for synthesis of organic compounds, an electrolyte for fuel cell applications or power sources, and a hydrogen storage substance and a fluorescence detector. It is fabricated using different methods, and there is a variety of morphologies and nanostructures such as zero to three dimensions that have been designed for different purposes. There are many reports about g-C₃N₄ in recent years, but a comprehensive review which covers nanostructure dimensions …

Reducing Friction In Machine Oil Via Cesium-Hybridized Graphene Oxide Quantum Dot Additives, Islam Gomaa, Sherief Elsoudy, Maryam Galal, Ahmed Azim

Nanotechnology Research Centre

Friction and wear are among the most common causes of energy loss and component failure in mechanical systems, accounting for around 20–30% of total global energy consumption. Conventional lubricants fail to provide consistent performance in harsh conditions due to inadequate additive dispersion, agglomeration, and restricted surface reactivity. Recent advances in nanomaterial-based lubricants have shown promise, but it remains difficult to achieve significant friction and wear reduction at low additive concentrations while preserving stability. In this study, we synthesized and tested cesium-hybridized graphene oxide quantum dots (Cs-GOQDs) as novel lubricant additives. When incorporated into machine oil at 0.1 wt%, Cs-GOQDs reduced …

Mechanical And Thermal Characterization Of Additively Manufactured Carbon/Nylon 12 And Carbon/Peek Composites, Matik Heskin, Bradley Deuser, Thomas P. Schuman, K. Chandrashekhara, John Bayldon, Jeff Degrange, Steven Patterson, Neiko Levenhagen

Chemistry Faculty Research & Creative Works

This study explores additive manufacturing of carbon fiber-reinforced thermoplastic composites using the Composite-Based Additive Manufacturing (CBAM) process. Carbon/Nylon 12 and Carbon/PEEK composites were fabricated and evaluated through mechanical (compression, tensile, flexural, and impact) and thermal (DSC and TGA) tests. Carbon/PEEK exhibited superior mechanical performance, with 97.5% higher tensile strength, 79.8% higher elastic modulus, and 59.6% higher flexural strength compared to Carbon/Nylon 12. Thermal testing showed that Carbon/PEEK had higher thermal stability, beginning degradation at 350 °C versus 298 °C for Carbon/Nylon. These results indicate that CBAM-fabricated Carbon/PEEK composites are suitable for applications requiring high strength and temperature resistance.

Thermo-Rheological And Tribological Properties Of Low- And High-Oleic Vegetable Oils As Sustainable Bio-Based Lubricants, Abiodun Saka, Tobechukwu K. Abor, Anthony C. Okafor, Monday U. Okoronkwo

Mechanical and Aerospace Engineering Faculty Research & Creative Works

Vegetable oil-based lubricants have attracted increased research attention in recent decades as sustainable alternatives to conventional petroleum-based lubricants in metal machining. However, more studies are required to fully elucidate the thermo-rheological and tribological properties. This study presents an investigation of the thermo-rheological and tribological properties of different vegetable oils, including low- and high-oleic soybean oil, high-oleic sunflower, safflower, and canola oils. The lubricity, and evolution of viscosity and thermodynamic properties as a function of temperature were investigated to obtain important parameters including the viscosity index, flow behavior index, flow activation energy, specific heat capacity, thermal conductivity, coefficient of friction, contact …

Synthesis Of Bio-Orthogonal Hydrogels For 3d Cell Culture Via Penicillamine Β-Thiolactone-Mediated Native Chemical Ligation, Kaelin E. Marshall, Matthew E. Currier, Nathan J. Oldenhuis

Honors Theses and Capstones

Many hydrogel systems designed to mimic the extracellular matrix (ECM) employ thiol-based chemistries with undesirable functional groups, including vinyl sulfones and methacrylates. In downstream applications, any unreacted functional groups are problematic and render hydrogels non-viable for human use. Here, we introduce modifications to the Native Chemical Ligation (NCL) mechanism, exploring the elimination of cytotoxic byproducts and increased reaction rate by using a β-thiolactone. The inclusion of the β-thiolactone results in retention of the thiol within the gel, as well as enhanced kinetics due to the thermodynamic favorability of the ring opening and amide formation. We achieved this by functionalizing 4-arm …

Explorations Of Dna-Single-Walled Carbon Nanotube Interactions To Develop Multiplexed Molecularly Specific Biosensors For Inflammation, Amelia K. Ryan

Dissertations and Theses

Inflammatory cytokines such as interleukin-6 (IL-6) and interleukin-12 (IL-12) are central regulators of immune signaling and key biomarkers of disease, yet existing assays for their detection remain slow, invasive, and lack multiplexing ability. This dissertation advances the development of single-walled carbon nanotube (SWCNT) optical nanosensors capable of real-time, multiplexed, and molecularly specific cytokine detection through innovative use of single-stranded DNA (ssDNA) interfaces.

First, an IL-6-specific DNA aptamer was employed as both a dispersing agent and recognition probe for SWCNT fluorescence sensing. Sequence modifications, including anchor domains, truncations, and thermally induced refolding, were systematically tested to optimize sensitivity and selectivity. The …

Development, Synthesis And Characterization Of Advanced Low- Cobalt And High-Nickel Cathode Materials For Lithium-Ion Batteries, Arjun Patel

Theses and Dissertations

This dissertation focuses on the improvement of structural and electrochemical stability of active materials for lithium-ion batteries. It explores the modification strategies to mitigate the issues related to Ni-rich cathode materials, along with the continuous production of cathode precursors using a slug flow reactor to improve the quality of the product.

The First part of the dissertation examines the effect of substitution of cobalt with aluminum and iron on the electrochemical stability of Ni-rich lithium nickel cobalt manganese oxide (NCM) materials. This study investigates how Al and Fe doping work and how they impact the performance and stability of these …

Catalytic Deoxygenation Of Oleaginous Biomass To Renewable Diesel And Sustainable Aviation Fuel Via Decarboxylation/Decarbonylation, Chukwudalu Great Umenweke

Theses and Dissertations--Chemistry

Several technologies have been developed to produce hydrocarbon biofuels – renewable diesel (RD) and sustainable aviation fuel (SAF) – from fats, oils, and greases (FOG), with the hydroprocessing of esters and fatty acids (HEFA) representing one of the most mature pathways. In its current form, HEFA is mainly reliant on the hydrodeoxygenation (HDO) reaction, which has several drawbacks since HDO requires large amounts and pressures of hydrogen, feedstocks of high purity and cost, as well as problematic sulfided catalysts that risk contaminating the biofuel product with sulfur. A process based on decarboxylation/decarbonylation (deCO_x) offers an attractive alternative to …

Characterization And Optimization Of Sand And Tung Oil-Based Resins For Binder-Jet 3d Printing, Daniel I. Ajiola

College of Graduate Studies: Theses & Dissertations

Binder-jet 3D printing as a transformative technology in additive manufacturing, offers the ability to fabricate complex structures with diverse materials. This thesis investigates the use of a sustainable tung oil-based resin to create composites, exploring the potential for an eco-friendly alternative to synthetic binders.

The aim of this research is to develop and characterize a bio-based resin formulation, using tung oil as the primary binder, for application in binder-jet 3D printing with sand as the reinforcement. The resin formulation was prepared by combining tung oil, n-butyl methacrylate, divinylbenzene, and di-tert-butyl peroxide in precise proportions, ensuring a balanced mixture that supports …

Single-Step Synthesis Of Activated Carbon From Arabica Spent Coffee Ground Using K2co3 As Activator Agent, Ghina Ivana Mieldan, Yuliusman Yuliusman

Journal of Materials Exploration and Findings

Activated carbon is a nanomaterial that is often used as an effective adsorbent. Activated carbon raw materials can use biomass, such as coffee grounds, which can be found along with the growth of public interest in coffee drinks. Chemical activators are used for activation to increase biomass carbon's adsorption capacity. Using K₂CO₃ activator to increase the specific surface area of activated carbon is more harmless than KOH. The use of spent coffee grounds as carbon source and food additive K₂CO₃ as an activator can make food-grade activated carbon that can be used for food. …

Effect Of Alkyd And Polyester Resin Compositions On Corrosion Resistance, Blistering, And Adhesion In Utilization Of Oily Sludge As Anti-Rust Coating Material, Gerets Land Kakalang, Yohanes David Kristianto, Johny Wahyuadi Mudaryoto

Journal of Materials Exploration and Findings

Oil sludge is a waste derived from upstream and downstream activities of the oil and gas industry which is estimated at 10,000 tonnes generated from all PERTAMINA downstream activities spread across various fields, processing units and depots throughout Indonesia. Oil sludge has the same characteristics as asphalt, where asphalt in previous studies can be used as an anti-rust coating, so that the handling of oily sludge can be topped up by reusing and having its own added value. The purpose of this research is to utilise waste oily sludge as an alternative anti-rust coating material and compare alkyd resin and …

Dendrite-Free Strategies For Aqueous Zinc-Ion Batteries: Structure, Electrolyte, And Separator, Gang Wu, Wu-Hai Yang, Yang Yang, Hui-Jun Yang

Journal of Electrochemistry

Continued growth in energy demand and increased environmental pollution constitute major challenges that need to be addressed urgently. The development and utilization of renewable, sustainable, and clean energy sources, such as wind and solar, are crucial. However, the instability of these intermittent energy sources makes the need for energy storage systems increasingly urgent. Aqueous zinc-ion batteries (AZIBs) have received widespread attention due to their unique advantages, such as high energy density, cost-effectiveness, environmental friendliness, and safety. However, AZIBs face significant challenges, mainly the formation of zinc dendrites that seriously affect the stability and lifetime of the batteries, leading to battery …

All-Solid-State Sodium-Ion Batteries: A Leading Contender In The Next-Generation Battery Race, Rui-Jie Zhu, Ze-Chen Li, Wei Zhang, Akira Nasu, Hiroaki Kobayashi, Masaki Matsui

Journal of Electrochemistry

All-solid-state lithium-ion batteries (LIBs) using ceramic electrolytes are considered the ideal form of rechargeable batteries due to their high energy density and safety. However, in the pursuit of all-solid-state LIBs, the issue of lithium resource availability is selectively overlooked. Considering that the amount of lithium required for all-solid-state LIBs is not sustainable with current lithium resources, another system that also offers the dual advantages of high energy density and safety— all-solid-state sodium-ion batteries (SIBs) —holds significant sustainable advantages and is likely to be the strong contender in the competition for developing next-generation high-energy-density batteries. This article briefly introduces the research …

Contributions To Journal Of Electrochemistry, The Flagship Journal Of Chinese Chemical Society Electrochemical Committee, Will Be Listed As A New Recommendation Policy For China Youth Awards Of Electrochemist, Editorial Office Of J.Electrochem.

Journal of Electrochemistry

No abstract provided.

Electrochemical-Method-Induced Strong Metal-Support Interaction In Pt-Cnt@Sno2 For Co-Tolerant Hydrogen Oxidation Reaction, Shen-Zhou Li, Zi-Jie Lin, Qi-An Chen, Zhao Cai, Qing Li

Journal of Electrochemistry

Inducing the classic strong metal-support interaction (SMSI) is an effective approach to enhance the performance of supported metal catalysts by encapsulating the metal nanoparticles (NPs) with supports. Conventional thermal reduction method for inducing SMSI processes is often accompanied by undesirable structural evolution of metal NPs. In this study, a mild electrochemical method has been developed as a new approach to induce SMSI, using the cable structured core@shell CNT@SnO₂ loaded Pt NPs as a proof of concept. The induced SnO_x encapsulation layer on the surface of Pt NPs can protect Pt NPs from the poisoned of CO impurity in …

Thermal Conductivity Characterization Of High Oleic Vegetable Oils Based Hybrid Nanofluids Formulated Using Gnp, Tio2, Mos2, Al2o3 Nanoparticles For Mql Machining, Anthony Chukwujekwu Okafor, Tobechukwu Kingsley Abor, Saidanvar Esanjonovich Valiev, Ignatius Echezona Ekengwu, Abiodun Saka, Monday Uchenna Okoronkwo

Chemical and Biochemical Engineering Faculty Research & Creative Works

This paper presents the results of thermal conductivity characterization of six high oleic soybean oil (HOSO) and four high oleic canola oil (HOCO)-Based hybrid nanofluids formulated with four types of nanoparticles (Graphene nanoplatelet (xGnP), TiO₂, MoS₂, and Al₂O₃) at nanoparticles wt.% concentration from 1 % to 7 % in 1 % increment using the two-step method for use in MQL machining of difficult-to-cut metals. Thermal conductivity of the formulated hybrid nanofluids were measured using Thermtest Transient Hot Wire Liquid Thermal Conductivity Meter at temperatures from 25 °C to 75 °C in increment …