Monte Carlo Simulation Of Kinetics Of Phenol Degradation On Titanium Based Anode, Xing-Fang Zhang, Zhen-Hai Liang, Wen-Ping Shi, Cai-Mei Fan
Monte Carlo Simulation Of Kinetics Of Phenol Degradation On Titanium Based Anode, Xing-Fang Zhang, Zhen-Hai Liang, Wen-Ping Shi, Cai-Mei Fan
Journal of Electrochemistry
According to Monte Carlo mechanism and random process theory,the mechanism of phenol degradation on titanium electrode was simulated. The effects of degradation time,initial concentration of phenol,electrode performance and intermediates on the process of degradation were determined. The results indicated that the phenol concentration is decreasing and becoming steady during the degradation process,if increase the initial concentration,the degradation rate is also increased at the beginning of reaction process,the electrodes with high performance strongly affect the first step of degradation by reducing the residence time of intermediates,the whole process and the productions of second step are primarily controlled by the first step …
The Accelerated Test Of Simulated Atmospheric Corrosion And The Rust Evolution Of Low Carbon Steel, Jun-Hua Dong, Wei Ke
The Accelerated Test Of Simulated Atmospheric Corrosion And The Rust Evolution Of Low Carbon Steel, Jun-Hua Dong, Wei Ke
Journal of Electrochemistry
It has been set up an accelerated method of simulating to atmospheric corrosion by using wet/dry alternate test.The rust evolution rule of mass change vs time(in logarithmic coordinate) of low carbon steel under this test shows two linear sections with different slopes,in which the rust evolution transition in weight change corresponds to the compactness transition and crystallization transition during the rust layer growth.It has found that the rust evolution rule of low carbon steel in Wanning exposure site correlates to the rust evolution rule obtained by simulating the coastal atmospheric corrosion test,and the rust evolution rule of low carbon steel …