The Effect Of Precursors On Performance Of Lini0.5Co0.2Mn0.3O2 Cathode Material, Dong-Ge Hu, Zhang-Zhi Wang, Jia-Li Liu, Tao Huang, Ai-Shui Yu

Journal of Electrochemistry

Commercial LiNi_0.5Co_0.2Mn_0.3O₂ material is generally prepared by a combination of co-precipitation and solid state reaction method. The particle size distribution and morphology of Ni_0.5Co_0.2Mn_0.3(OH)₂ precursor have a great impact on the electrochemical performance of LiNi_0.5Co_0.2Mn_0.3O₂. In this work, the crystal structure and surface morphology of LiNi_0.5Co_0.2Mn_0.3O₂ prepared by three different precursors were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Particle size distribution, tap density and electrochemical performance were …

Preparation And Electrochemical Performance Of Hollow Carbon Spheres/Sulfur Composite, Jun Zang, Hang Qian, Er-Man Zeng, Juan-Ni Fu, Ming-Sen Zheng, Quan-Feng Dong

Journal of Electrochemistry

Hollow carbon spheres were prepared by the PMMA template. Hollow carbon spheres/sulfur composite was made from sulfur and hollow carbon spheres as a conducting framework. The results of SEM and TEM showed that sulfur was uniformly filled in both of the shell and hollow core of hollow carbon spheres. The electrochemical performance of hollow carbon spheres/sulfur composite was characterized by the charge/discharge method. The results showed the excellent rate and cycle performance of hollow carbon spheres/sulfur composite. The reversible capacities of hollow carbon spheres/sulfur composite are 1145 mAh·g^-1, 824 mAh·g^-1, 702 mAh·g^-1, 586 mAh·g …

Polypyrrole-Transition Metal-Oxygen Coordination Complexes As High Performance Lithium Storage Material, Ya Mao, Qingyu Kong, Bingkun Guo, Zhaoxiang Wang, Liquan Chen

Journal of Electrochemistry

No abstract provided.

Influence Of Electrode Hydrophobicity On Performance Of Alkaline Polymer Electrolyte Fuel Cells, Li-Sheng Tan, Jing Pan, Yao Li, Lin Zhuang, Jun-Tao Lu

Journal of Electrochemistry

In the present work, we study the influence of the electrode hydrophobicity on the performance of alkaline polymer electrolyte fuel cells (APEFCs). QAPS or xQAPS is employed as the membrane and the ionomer, while PTFE is used as a hydrophobic additive in order to adjust the electrode hydrophobicity. We find that enhancing the hydrophobicity of anode can promote the performance of APEFCs, while a moderate hydrophobicity of cathode is required to achieve optimal performance. By using xQAPS as the electrolyte and adding some PTFE in the anode, a peak power density of 132 mW·cm^-2 can be obtained at a …

Progress Of Lithium Rich Cathode Materials For Li-Ion Batteries, Jie Zhang, Jiu-Lin Wang, Jun Yang

Journal of Electrochemistry

Lithium rich materials xLi₂MnO₃·(1-x)LiMO₂ (0-1 and low cost. However, the large irreversible capacity during the first cycle, low rate capability and structure collapse during cycling remain impediments in developing these cathodes for applications. The structure analyses and charge/discharge mechanisms for lithium rich materials are currently main research contents. Although whether the lithium rich materials are solid solutions or composite is still controversial, oxygen release mechanism on the first charge 4.5 V plateau of lithium rich materials has come to consistency. Several modifications, such as bulk doping, surface coating and microstructure control, demonstrate promising strategies to …

Electrochemical Performance Of Al-Doped Spinel Limn2O4 Cathode Material For Li-Ion Batteries, Yong-Long Wang, Wen-Ge Wang, Qian Zhang, Xin Wang, Jian-Sheng Cao, Shi-Hai Ye

Journal of Electrochemistry

Spinel LiMn₂O₄, a cathode material for Li-ion batteries, is featured as good high-rate performance, low cost and environmental friendly. The pristine and Al-doped LiMn₂O₄ samples were prepared by sol-gel method. The structure and micromorphology of the as-prepared samples were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results demonstrated that the as-prepared LiMn₂O₄ samples had a typical cubic spinel structure and were composed of sphere-like particles with a diameter range of 300 ~ 500 nm. Galvanostatic charge-discharge tests showed that the LiMn₂O₄ samples doped …

Electrocatalytic Mechanism And Porous Electrode Mass Transfer Process In Membrane Electrode Assembly For Direct Methanol Fuel Cells, Xin-Dong Wang, Yi-Tuo Wang, Gui-Cheng Liu, Meng Wang, Zhe Tian

Journal of Electrochemistry

Direct methanol fuel cell (DMFC) is considered to be a promising commercial energy conversion device for portable electronics due to its many advantages. In order to improve the performance of DMFC, many companies and research institutes have been launching the deep research and obtaining a lot of conspicuous achievements. In this paper, the electrocatalytic mechanism and porous electrode mass transfer process in membrane electrode assembly (MEA) are analyzed. In addition, combined with the preparation process of MEA, multilayer ordered structures and internal transfer process of the cell, recent progresses of MEA in DMFC are discussed.

Fabrication And Performance Of Lani0.6Fe0.4O3-δCathode Modified By Coating With Gd0.2Ce0.8O2 For Intermediate Temperature Solid Oxide Fuel Cell, Rui-Xuan Ren, Bo Huang, Xin-Jian Zhu, Yi-Xing Hu, Xiao-Yi Ding, Zong-Yao Liu, Ye-Bin Liu

Journal of Electrochemistry

The symmetric cell of LaNi_0.6Fe_0.4O_3-δ/Sc_0.1Zr_0.9O_1.95/LaNi_0.6Fe_0.4O _3-δ was fabricated with screen printing method. A LaNi_0.6Fe_0.4O_3-δ (LNF) cathode was modified by coating with nano-sized gadolinium-doped ceria (GDC, Gd_0.2Ce_0.8O₂) prepared using a simple combustion process within the pores of the cathode. According to the electrochemical impedance spectra (EIS), the polarization resistance of the pure LNF was 0.70 W·cm² at 750 ºC, while 0.13 W·cm² for the 21.3% GDC (by mass)-coated LNF cathode at the …

A Comparative Study Of Ce3+/Ce4+ Redox Couple On Pt Electrode In Sulfuric Acid And Methanesulfonic Acid, Zhao-Hua Li, You-Qun Chu, Chun-An Ma

Journal of Electrochemistry

The electrochemical oxidations of Ce³⁺ to Ce⁴⁺ on Pt rotating disk electrode (RDE) in both sulfuric acid and methanesulfonic acid (MSA) solutions were studied by using cyclic voltammetry and linear sweep voltammetry. The complexing behaviors of Ce³⁺/Ce⁴⁺ were preliminarily probed and the exchange current density, diffusion coefficient, as well as reaction rate constant were obtained from Butler-Volmer equation. The activation energies of Ce³⁺ oxidation on Pt electrode in two types of acidic media, obtained from Arrhenius equation, were also compared. The results indicate that Ce³⁺ can be oxidized to Ce4+ much easier in …

Electrochemical Activities Of Oxygen-Doped Carbon Surface For V(Iv)/V(V) Redox Couple, Huan Zhang, Lin-Lin Qin, Yi-Ning Shi, Ming-Sen Zheng, Quan-Feng Dong, Zhao-Wu Tian

Journal of Electrochemistry

Graphite plate electrodes were treated with oxygen plasma and doped with oxygen as well as oxygen functional groups. With the treatment, the activities of graphite plate electrodes toward VO²⁺/VO₂⁺ redox reactions were improved. FT-IR and EDS analysis results indicated that oxygen functional groups were introduced to the surface of graphite plates after oxygen plasma treatment. In this paper, the graphite plate treated for 20 min showed the highest activity. The average charge efficiency reached 91%, suggesting an increase of 19%, compared with that of the untreated graphite plate under a current density of 8 mA·cm^{-2 …}

Hydrothermal Synthesis Of Pure Li4Ti5O12 And Its Electrochemical Performance, Wen-Jun Xie, Yu-Shi He, Hong Wang, Xiao-Zhen Liao, Zi-Feng Ma

Journal of Electrochemistry

Spinel Li₄Ti₅O₁₂ was prepared by hydrothermal method using commercial anatase (TiO₂) and lithium hydroxide (LiOH) as raw materials. The effects of the LiOH concentration of lithium hydroxide, hydrothermal reaction time and calcination temperature on the structure and electrochemical performance of Li₄Ti₅O₁₂ were investigated. The formation process of Li₄Ti₅O₁₂ was also proposed. The micro-structure and morphology wereas characterized by XRD, SEM, TEM techniques, and the electrochemical performance was analyzed by galvanostatic charge-discharge test. The results show that the pure phase spinel Li₄Ti …

Preparation And Catalytic Properties Of Feco Alloy Nanocatalyst, Ming-Xuan Li, Jie-Lian Ou, Sheng-Pei Chen, Peng Wang, Bin-Bin Xu, Shi-Gang Sun

Journal of Electrochemistry

The FeCo alloy nanoparticles were electrodeposited on glassy carbon electrode by chronoamperometry and were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results showed that the shapes of FeCo nanoparticles were cubes with an average size of 65 nm. The atom ratio of Fe and Co is 1:1. As indicated from the pattern of selected area electron diffraction (SAED), the FeCo cubic nanoparticles were single crystal which belonged to body-centered cubic with an interval of 0.201 nm referring to the (110) facets of FeCo alloy. The FeCo cubic nanoparticles exhibited the enhanced electrocatalytic …

Electrochemical Synthesis Of Hierarchical Dendritic Polyaniline Nanostructures, Shao-Huang Weng, Jian-Zhang Zhou, Zhong-Hua Lin, Xin-Hua Lin

Journal of Electrochemistry

In this work, the p-TSA doped and hierarchical dendritic nanostructured polyanilines (PANI) have been prepared by potentiostatic electropolymerization without using any templates at room temperature. The mechanism of the polymerization has been discussed according to the electrodeposition curves. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were employed to confirm the formation of uniform hierarchical dendritic structure on PANI. UV-Vis spectroscopy (UV-Vis) and infrared spectroscopy (FTIR) proved that the prepared PANI is in the form of emeraldine salt. The templateless electrodeposition method is simple, easy to operate, can be applied to fabricate other nanostructures of conducting polymers.

Performance Of Vn As Negative Electrode Materials In Electrochemical Capacitors, Zhao-Hui Gao, Hao Zhang, Gao-Ping Cao, Min-Fang Han, Yu-Sheng Yang

Journal of Electrochemistry

Nanocrystalline vanadium nitride (VN) materials were synthesized by high temperature ammonia (NH₃) reduction of vanadium oxide (V₂O₅). The structure and morphology of VN materials were characterized by XRD, SEM and TEM, while the specific surface area, pore size distribution and supercapacitive behavior by N₂ absorption, cyclic voltammetry (CV) and constant current charge-discharge measurements in 1 mol·L-1 KOH electrolyte. The results showed that the VN sample belonged to the cubic crystal system (Fm3m [225]), and had homogeneous surface and appeared nearly spherical with uniform size. As the reaction time was extended to 12 h, …

Electrochemical Performance Of Lifepo4/C Synthesized Via Aqueous Solution-Evaporation Route, Ning-Yu Gu, Xing-Hua He, Yang Li

Journal of Electrochemistry

The LiFePO₄/C samples have been synthesized via an aqueous solution-evaporation route with LiH₂PO₄, FeC₂O₄.2H₂O as raw materials and citric acid as a carbon source. X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) were used to analyze structure and morphology of the samples. The electrochemical performances of the LiFePO₄/C cathodes were characterized by charge/discharge cures and electrochemical impedance spectroscopy (EIS). The results show that the LiFePO₄/C sample, calcined at 700 °C and contained 3.03% (by mass) carbon, exhibited a highly pure …

Preparation And Methanol Electrooxidation Of Pt/Pmo12/Pedot/Gc Electrodes, Jing-Hua Ma, Rui-Xiang Wang, Yi-Liang Tan, Shan-Shan Wang, Yan-Qin Zhang, You-Jun Fan

Journal of Electrochemistry

Modification of phosphomolybdic acid (PMo₁₂) on poly(3,4-ethylenedioxythiophene) (PEDOT) film (PEDOT/GC) obtained through the electrochemical polymerization was performed using adsorption method (PMo₁₂/PEDOT/GC), followed by electrodepositing Pt on PMo₁₂/PEDOT/GC to prepare Pt/PMo₁₂/PEDOT/GC electrode. Effects of PMo₁₂ and PEDOT on the methanol oxidation performance of electrode were investigated. Results showed that PMo₁₂ obviously changed the morphology and structure of Pt loaded on the electrode, leading to the formation of sharp thorns at the edge of Pt nanostructures. Cyclic voltammetry and chronoamperometry data demonstrated that the catalytic activities of methanol electrooxidation on the Pt/PMo …

Synthesis And Electrochemical Performance Of Si/C Composite Modified By Pani, Guang-Hui Zhang, Pei-Kang Shen, Ge Sang, Ren-Jin Xiong

Journal of Electrochemistry

Silicon/carbon (Si/C) composite materials were prepared through high-energy ball milling and high-temperature solid-phase method, and then coated with thin polyaniline (PAni) film by oxidation. The microstructure and component of the composites were characterized by SEM, XRD, IR, TG, and the electrochemical performance was investigated by cyclic voltammetry (CV) and galvanostatic charge-discharge tests. The results showed that the surface of PAni/Si/G/C composite was coating with complete lamellar structure of PAni film. Its reversible capacity was 784 mAh·g^-1 and 690 mAh·g^-1 could be maintained after 50th charge-discharge cycles.

Synthesis Of Lifepo4/C Cathode By Sol-Gel And Calcining Method With Chitosan Monomer, Jia Xu, Yan-Yan Wang, Rui Wang, Bo Wang, Yue Pan, Dian-Xue Cao, Gui-Ling Wang

Journal of Electrochemistry

The LiFePO₄/C cathode materials for Li-ion battery were synthesized by sol-gel and calcining method using chitosan monomer as a carbon source and a gelating agent. The structures and morphologies were characterized by X-ray diffraction spectroscopy (XRD) and scanning electron microscopy (SEM). The electrochemical performance was investigated by the galvanostatic charge–discharge test. When the molar ratios between chitosan monomer and LiFePO₄ were 1:1.2, the LiFePO₄/C cathode calcined at 600 ^oC showed the best performance. The particle sizes ranged 200 ～ 400 nm. The initial discharge capacity of 155 mAh·g-¹ was achieved at room temperature …

Current Development Of Quantum Dots Based Electrochemiluminescence Immunosensors, Ling-Ling Li, Qian Lu, Jun-Jie Zhu

Journal of Electrochemistry

Electrochemiluminescence exhibits the merits of both luminescence and electrochemistry analysis, and has been extensively employed in biosensors. Quantum dots are considered one of the three main kinds of electrochemiluminescence luminophores due to their unique properties. This paper briefly reviews the classification and signal amplification technology of quantum dots based electrochemiluminescence immunosensors. Future research trends are also suggested.

Synthesis And Electrocatalysis Of Pdcu Alloy Nanocrystals, Hai-Bin Wu, Rui-Zhong Zhang, Wei Chen

Journal of Electrochemistry

Monodispersed PdCu alloy nanoparticles were synthesized by co-reduction of Cu(acac)2 and Pd(acac)2 with 1, 2-hexadecanediol. The spherical and popcorn-like shapes of PdCu alloy nanoparticles were obtained by changing the ratios of mixed surface protecting ligands of 1-octadecene, and oleylamine or oleic acid. TEM and XRD measurements showed that both PdCu nanoparticles are alloy nanocrystals dominated with (111) planes and the average sizes are 12.7 ± 0.18 and 20.4 ± 0.31 nm for he spherical and popcorn-like PdCu nanoparticles, respectively. The electrocatalytic activities of the PdCu nanocrystals for formic acid oxidation were evaluated by electrochemical cyclic voltammetry (CV). The result showed …

Properties Of Carbon Coated Tin Negative Electrode For Lithium-Ion Battery, Gui-Chang Liu, Xiao-Xiao Shen, Li-Da Wang

Journal of Electrochemistry

Carbon coated tin power was prepared by decomposing glucose applying a hydrothermal method, and was further used as the active material for negative electrode of lithium secondary battery. Charge-discharge tests show that the carbon coated tin electrode with the addition of 5 wt.% acetylene black as a conductive agent could obtain an initial discharge capacity of 967 mAh·g^-1 and a discharge capacity of 362 mAh·g^-1 after 50 cycles, which is much higher than that of tin electrode (166 mAh·g^-1 after 50 cycles). The coated carbon hinders the agglomeration of tin powder, reduces the irreversible capacity loss of …

High Performance Membrane Electrode Assembly With Low Platinum Loadings Prepared By Atomic Layer Deposition For Pemfc Application, Ting Shu, Shi-Jun Liao, Chien-Te Hsieh, Ay Su

Journal of Electrochemistry

A high performance membrane electrode assembly (MEA) with low platinum loadings was successfully prepared with atomic layer deposition (ALD) technique. The anode of the MEA was prepared by depositing platinum on the carbon paper substrate, which was prepared by coating the slurry of carbon black (XC-72R) and Teflon, followed by drying and calcining at 350 °C. The MEAs consisted of the ALD anode or commercial catalyst anode, pretreated Nafion membrane (Nafion-117) and commercial cathode. Performances of MEAs were measured by single cell testing, and the anodes and MEAs were characterized by CV, SEM, TEM and XRD. The results revealed that …

Electrochemical Performance Of Fe3O4/C Composites As Negative Material For Lithium-Ion Batteries, Jun-Jie Cai, Shu Yao, Ze-Sheng Li, Hui Meng, Pei-Kang Shen

Journal of Electrochemistry

The Fe₃O₄/Carbon composites have been synthesized through coprecipitation pathway and by insitu aniline polymerization as a carbon source. Structural characterization and morphological study of the composites were investigated by using XRD, SEM and TEM techniques. The results showed that the nanosized Fe₃O₄ particles (40 ~ 80 nm) were encapsulated in the amorphous carbon. During the electrochemical tests, the Fe₃O₄/C composites exhibited high capaticity and excellent cycle ability, the retention of capaticity was about 1000 mAh·g^-1 after 30 cycles of charge/discharge tests at 50 mA·g^-1.

A Comparative Study Of Charge-Discharge Behaviors Of α-Pbo2 And β-Pbo2 Cathodes, Cong-Ying Cui, Xue-Mei Ma, De-Long Kong, Hou-Yi Ma

Journal of Electrochemistry

The α-PbO₂ and β-PbO₂ powders were prepared using simple chemical synthetic methods, and their crystalline structures and surface morphologies were characterized with X-ray powder diffraction spectroscopy and scanning electron microscopy. Using the as-synthesized α-PbO₂ and β-PbO₂ powders as positive active materials, the electrochemical performance of the two PbO₂ materials was investigated by means of cyclic voltammetry, galvanostatic charge-discharge tests, and electrochemical impedance spectroscopy. The results indicate that the discharge capacity of α-PbO₂ electrode is larger than that of β-PbO₂; moreover, the composite electrodes made by α-PbO₂ and β-PbO₂ mixtures with …

An In Situ Ftir Spectroelectrochemical Study On Methanol Oxidation At Pt-Mo2C/Gc Catalyst, Hai-Ping Huang, Xi-Yu Yao, Pei-Kang Shen

Journal of Electrochemistry

A 40% Pt on Mo₂C/GC catalyst has been prepared by ion exchange method. The mechanism of methanol electrooxidation on Pt-Mo₂C/GC and commercial Pt/C catalysts in acidic media was studied by cyclic voltammetry, XRD measurements and in-situ Fourier transform infrared spectroelectrochemistry. The results revealed that the Pt nanoparticles were uniformly dispersed on Mo₂C/GC with an average particle size of 3 nm. The cyclic voltammetric and chronopotentiometric experiments indicated that Pt-Mo₂C/GC catalyst exhibited a better performance for methanol oxidation than that of Pt/C in acid solution. A negative shift over 90 mV of the …

Applications Of Ellipsometry In The Investigations Of Electrode-Solution Interface, Jing-Lei Lei, Liang-Liu Wu, Ling-Jie Li, Sheng-Mao Wu, Sheng-Tao Zhang

Journal of Electrochemistry

Ellipsometry is an optical technique with high-sensitivity to quantitatively obtain surface/interface properties such as thickness andrefractive index by analyzing the changes in polarized light reflected from the surface/interface. Its noncontacting and nondestructivenature makes it possible to acquire thein situreal-time information of the change at the surface/interface. Therefore, ellipsometry has been used widely in the electrochemical investigations. In this paper, based on the brief introduction of the measurementprinciple of ellipsometry, the current progress and the future trends of ellipsometry in electrochemistry arediscussed. The applications of ellipsometry in the fields of conversion and storage of electrochemical energy, electrochemistry ofmaterials science,electroanalysisand bioelectrochemistry are …

Oxygen Reduction Reaction On Glycin Modified Pt(111) Electrode, Ming-Fang Li, Jing Kang, Ling-Wen Liao, Yan-Xia Chen, Shen Ye

Journal of Electrochemistry

O

xygen reduction reaction (ORR) on glycin (NH₂CH₂COOH) modified Pt(111) electrode has been investigated using hanging meniscus rotating disk electrode system (HMRD) in 0.05 mol•L^-1 H₂SO₄ and 0.1 mol•L^-1 HClO₄ solutions, respectively. Cyclic voltammograms of the glycin modified Pt (111) electrode measured in 0.05 mol•L^-1 H₂SO₄ solution similar to that of CN^- modified Pt(111) electrodes, demonstrating that sulfate adsorption is strongly inhibited at the glycin modified Pt(111). From the polarization curve of ORR recorded in 0.05 mol•L^-1 H₂SO₄ solution, it is …

Porous Electrodes With High Pt Utilization Obtained By Ion-Exchange/Electrodeposition, Si-Guo Chen, Wei Ding, Xue-Qiang Qi, Li Li, Zi-Hua Deng, Zi-Dong Wei

Journal of Electrochemistry

We report a novel method based on ion-exchange/electrodeposition (IEE) for constructing high Pt utilization porous electrodes. The electrode prepared using IEE was assessed by linear sweep voltammetry (LSV), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and single cell test. The preliminary results show that the undesired ion-exchange between Pt anion and surface functional group in carbon black can be eliminated through the electrode preparation process, and every Pt particle prepared by IEE is expected to be deposited on the three-phase reaction zone and thus can be fully utilized in fuel cell reactions. The Pt particle size, shape and distribution …

Effect Of Ti/Pbo2 Electrodes Doped With Different Elements On Electrocatalytic Oxidation Characteristics Of Phenol, Xiao-Lei Liu, Yuan-Yuan Dan, Hai-Yan Lu, Hai-Bo Lin, Ming-Li Ouyang, Chuan-Jun Yun

Journal of Electrochemistry

Three types of electrodes, namely, Ti/PbO₂, F-doped PbO₂ (Ti/PbO₂-F) and nano-Co₃O₄-doped PbO₂ (Ti/PbO₂+Nano-Co₃O₄) electrodes, were prepared by electro-deposition method on the Ti substrate with the interlayer of SnO₂-Sb₂O₅. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to study the compositions, structures and film morphologies of the electrodes. Electrocatalytic oxidation characteristics to phenol on the prepared electrodes were investigated by electrochemical method. The experimental results showed that compared with the Ti/PbO₂ electrode, the potentials of oxygen …

A Dft Calculation Screening Of Pt-Based Bimetallic Catalysts For Oxygen Reduction, Li-Hui Ou, Sheng-Li Chen

Journal of Electrochemistry

Developing Pt-lean catalysts for oxygen reduction reaction (ORR) is the key for large-scale application of proton exchange membrane fuel cell (PEMFC). In this paper, we have proposed a multiple-descriptor strategy for screening efficient and durable ORR alloy catalysts of low Pt content. We argue that an ideal Pt-based bimetallic alloy catalyst for ORR should possess simultaneously negative alloy formation energy, negative surface segregation energy of Pt and a lower oxygen binding ability than pure Pt. By performing detailed DFT calculations on the thermodynamics, surface chemistry and electronic properties of various Pt-M alloys (M refers to non-precious transition metals in the …