Polymer and Organic Materials Commons^™

Bond Strength Characterization Of Su-8 To Su-8 For Fabricating Microchannels Of An Electrokinetic Microfluidic Pump, Nash Anderson

Materials Engineering

Photosensitive negative resist polymer layers of SU-8 2050 were adhered to 100 mm n-type silicon and Pyrex wafers via spin coating. These wafers were then bonded together at various temperatures of 100 ͦC, 120 ͦC, 140 ͦC, 150 ͦC, 160 ͦC, and 180 ͦC. The target thickness of each SU-8 layer was 100 µm. Photolithography was used to create microfluidic channels within the SU-8. An n-type silicon wafer and a Pyrex wafer, each with an SU-8 layer, were brought together on the “hard bake” or final step of SU-8 polymerization. A pressure of ~300 KPa was applied during the hard …

Effects Of Abrasive Particles On The Projected Fatigue Life Of Nylon Climbing Rope, Casey Johnson, Charlie Klonowski

Materials Engineering

When climbing rope is used outdoors, it is exposed to foreign particles such as sand and silt. These particles can potentially work their way through a rope’s sheath and damage the load bearing core decreasing the rope’s strength without exhibiting obvious wear. This project quantified the effect of abrasive particles on the fatigue life of nylon climbing rope. The experimental design involved 18 pieces of static nylon rope of kernmantle construction. 9 of these samples were heavy agitated in a slurry of water, silt, sand and soil, and left to sit for 24 hours. The remaining 9 samples were submerged …

Determining A Method For Rendering Low Cost Cdse(Zns) Core(Shell) Quantum Dots Aqueous Soluble Via Amphiphilic Polymer Wrapping, Patrick Mcbride

Materials Engineering

Herein is described the procedure of two amphiphilic polymer wrapping techniques that may be employed for obtaining aqueous soluble quantum dots (QDs) for use in biological fluorescent imaging applications. The advent of QDs has led to new nanoscale fluorescent materials that exhibit unparalleled quantum yields (QYs), high resistance to photobleaching, tunable emissions, and
absorption over a large optical range. However, the QD synthesis employed here at Cal Poly to obtain bright, photostable CdSe(ZnS) core(shell) QDs involves the use of organic solvents and surfactants, leading to hydrophobic QDs. Since all of biology relies on aqueous solubility, this hydrophobicity creates a major …

Artificial Muscle Project: Process Development Of Polydimethyl Siloxane Thin Films For Use In Dielectric Electroactive Polymer Artificial Muscle Actuators, Vincent J. Gayotin, Richard W. Morrison, Paul A. Preisser

Materials Engineering

An artificial muscle design was created founded on the principles of a dielectric electroactive polymer (DEAP), which is fundamentally similar to a capacitor. A polydimethyl siloxane (PDMS)-based elastomer, Sylgard 184 from Dow Corning, was chosen for the design and spun coat onto polystyrene (PS) Petri dishes at varying speeds to create a thin film, using speeds of 2000 rpm, 3000 rpm, 4000 rpm, 5000 rpm, and 6000 rpm. The film thicknesses were measured optically through use of a microscope with coupled computer imaging software to generate a characteristic curve of film thickness to spin speed, achieving a minimum film thickness …

Processing Pdms Gecko Tape Using Isopore Filters And Silicon Wafer Templates, Boris Luu

Materials Engineering

Gecko tape was processed through nanomolding involving two types of templates. One template was a Millapore Isopore polycarbonate membrane filter and the other template was an n-type silicon wafer processed to include four different pore diameters. These pore diameters were 20, 40, 80, and 160 microns. AutoCAD was used to design to a mask to be used later during photolithography. Two n-type wafers were sputtered with aluminum, underwent photolithography, and then etched using reactive ion etching. A template was placed into a Petri dish and Sylgard 184 polydimethylsiloxane (PDMS) was poured on the template. Once the PDMS cured,   the 1 …

Migration Models - Comparison Of Pvc, Pet And Pla Diffusivity, Combined With A Production Cost Model For Westridge Laboratories, Shelley Cooke, Sarina Surrette

Materials Engineering

This project has two parts: [1] a migration and diffusivity model for candidate plastics used in containers, and [2] a product cost model for Westridge Laboratories (Santa Ana, CA).

Diffusion modeling is a useful tool to predict migration of polymer constituents into exposed liquids.  Polyvinyl chloride (PVC), polyethylene terephthalate (PET) and polylactic acid (PLA) were studied to estimate production costs, and component migration into water-based liquids from plastic containers.  Bis (2-ethylhexyl) phthalate (DEHP), antimony trioxide, and stannous octoate, are components of concern in the three candidate polymers, respectively.  Normal detection limits for these constituents are about 1 - 10 ppb, …

Validation Of A Secondary Fabric Supplier And Characterization Of Alternate Cores For Use In The Aptera 2e Sandwich Core Composite, Bryan Rogers

Materials Engineering

Polymer matrix composites’ high strength to weight ratio has made them an ideal material choice for use in lightweight transportation vehicles. Aptera Motors, a company based out of Oceanside, CA, is currently developing a next-generation high efficiency passenger vehicle called the Aptera 2e. The 2e’s body is composed of a sandwich core composite containing laminates of E-glass fibers embedded within an epoxy matrix sandwiched between a polyester hexagonal core. This project looked to validate a secondary fabric supplier for use in Aptera’s composite and characterize the core shear properties of two alternate core materials for future iterations of Aptera’s vehicle. …