Polymer and Organic Materials Commons^™

Predicting Long-Term Creep Behavior Using Short-Term Stress Relaxation Data In Expanded Polyethylene Foam, Andrew M. Seelig

All Theses

Closed cell expanded polyethylene (EPE) foams are widely used for protective packaging due to their high energy absorption properties and recyclability. However, these foams can be subjected to sustained compressive stresses (13.78 - 36.20 kPa), depending on density and application, leading to time-dependent deformation (creep). Creep reduces cushioning performance, making its understanding critical for effective protective packaging. Two standards, ASTM D3575 and ASTM D2221, define methods for conducting compressive creep tests on foam materials, with test durations extending up to 1000 hours. Accelerated methods such as Time Temperature Superposition (TTS) and the Stepped Isostress Method (SSM) have been explored for …

Effect Of Polymer Contaminants Sourced From Coated Paper On The Performance Of The Resulting Recycled Paper, Ezekiel J. Guevarra

All Theses

The growing demand for sustainable packaging has accelerated the use of paper-based materials as alternatives to plastics. To provide barrier and functional properties, these materials are often modified with polymer coatings. While beneficial during use, such coatings can persist as contaminants during recycling, potentially disrupting fiber bonding and reducing the quality of recycled paper. This study examined the impact of extrusion-coated low-density polyethylene (LDPE) films and two aqueous dispersions (Vapor/Water-Barrier, Acrylic Film (VWAF) and Oil & Grease Barrier (OGBF)) on contaminant distribution and mechanical performance of recycled handsheets. Kraft paper coated at varying levels was repulped and formed into handsheets, …

Mechanistic Insights Into Polymer-Assisted Graphene Exfoliation: The Roles Of Velocity, Adhesion, Cohesion, Temperature, Peeling Mode, And Edge Defect Via Coarse-Grained Molecular Dynamics, Linjiale Dai

All Theses

Graphene exfoliation is a critical step in the fabrication of high-quality graphene

layers. However, the underlying fracture mechanisms remain poorly understood. In this

work, I employed coarse-grained (CG) molecular dynamics (MD) simulations to

investigate how factors such as interfacial binding energy, substrate cohesion, temperature,

peeling mode, and edge defects influence the outcome of the exfoliation process. To model

polymer-assisted mechanical exfoliation, I used a finite-size system in which multilayer

graphene (MLG) is sandwiched between two thin polymer films. Leveraging the

spatiotemporal efficiency of the CG model, I performed fifty simulation iterations per

parameter set and analyzed the results from a …

Investigation Of Domain Formation During Phase Separation In A Mixture Of Flexible And Rigid Biopolymers, Steven Huntley

All Theses

Complex fluids and heterogenous mixtures composed of multiple types of polymers are found throughout industrial and biological fluid systems. For example, extrusion based additive manufacturing systems pass dense mixtures of polymers through the extrusion heads to deposit composite polymeric materials. In cells, active and complex mixtures of biopolymers self-organize into assemblies that perform critical physiological functions.

Polymers in dense solutions undergo phase separation as a result of differences in physiochemical properties. A few examples of these properties include charge, structure, rigidity, and hydrophobicity. We observe the formation of polymer domains composed of rigid and a flexible biopolymer species that phase …

Carbon Fibers From Athabasca Oil-Sand Asphaltenes, Blake Reardon

All Theses

Carbon fibers possess ultra-high specific strength and modulus. Therefore, the material is popular in aerospace, automotive, and sports industries. Approximately 95% of all carbon fibers are spun from a high-cost precursor, polyacrylonitrile (PAN). There is a need for a cheaper grade of carbon fiber for low-cost applications because about half of carbon fiber cost is associated with precursor cost. A promising alternative to the high-cost PAN precursor is petroleum-based asphaltene. Asphaltenes are highly aromatic and have a high carbon content but lack the purity of the PAN precursor. Processes like the molten- sodium desulfurization upgrading have been used to harvest …

Life Cycle Energy Assesment Of Advanced Fiber Reinforced Composite Design And Manufacturing Methodologies, Urjit Lad

All Theses

Automotive industry at large is focused on vehicle light-weighting since a 6%-8% increase in fuel efficiency can be achieved with a 10% reduction in vehicle weight [1]. With the growing demand for cost-effective and sustainable light weighting of automobile structures, interest has increased in the application of fiber reinforced plastic (FRP) composites for use in the Body-in-White (BiW), which can account for up to 40% of the total vehicle weight. Traditional FRP composite manufacturing processes like vacuum assisted resin transfer molding, autoclave consolidation or use of automated fiber placement have been successfully used for marine and aerospace applications. However, these …

Characterization Of Mechanically Recycled Polylactic Acid (Pla) Filament For 3d-Printing By Evaluating Mechanical, Thermal, And Chemical Properties And Process Performance, Mahsa Shabani Samghabady

All Theses

Polylactic acid (PLA) is a biopolymer made from renewable resources such as sugar and corn. PLA filament is a popular material used in Fused Deposition Modeling (FDM) 3D-printing. While this material has many advantages, all the failed parts, support structures, rafts, nozzle tests, and the many prototype iterations during the 3D-printing process contribute to the plastic pollution and release of greenhouse gases. Although PLA is biodegradable, it can take years to degrade in landfills. Instead of throwing away PLA waste and buying new filaments, PLA can be recycled. Amongst the different recycling technologies, mechanical recycling is the most environmentally friendly. …

Characterization Of Thermal Gelation Properties In Bioresorbable Thermally Activated Hydrogel Polymers For Hernia Surgery Applications, Alexander Mayfield

All Theses

Hydrogel adhesives are a new class of materials with excellent biocompatibility, which makes them very attractive for biomaterial applications. It has been previously shown that Tetronic T1107, a four-arm poly (propylene oxide)-poly (ethylene oxide) (PPO-PEO) block copolymer, is useful as a chemical crosslinking thermo-responsive hydrogel for bioadhesive applications. The end groups of this polymer are modified with acrylate and N-hydroxysuccinimide (NHS) functional groups. The acrylate end group gives the polymer cohesive properties with long-range chemical crosslinking using dithiothreitol (DTT), while the NHS end group gives the polymer adhesive properties through bonding with amines found in organic tissue. It was found …

Insect Antennae As Bioinspirational Superstrong Fiber-Based Microfluidics, Griffin J. Donley

All Theses

Nature is frequently turned to for inspiration for the creation of new materials. Insect antennae are hollow, blood-filled fibers with complex shape, and are cantilevered at the head. The antenna is muscle-free, but the insect can controllably flex, twist, and maneuver it laterally. To explain this behavior, a comparative study of structural and tensile properties of the antennae of Periplaneta americana (American cockroach), Manduca sexta (Carolina hawkmoth), and Vanessa cardui (painted lady butterfly) was performed. These antennae demonstrate a range of distinguishable tensile properties, responding either as brittle fibers (Manduca sexta) or strain-adaptive fibers that stiffen when stretched (Vanessa cardui …

Mechanochromic Tunable Emissions Of Hydrogel Encapsulated Radioluminescent Crystalline Colloidal Arrays, Sarah Mell

All Theses

Crystalline colloidal arrays (CCAs) are periodic dielectric arrays composed of monodisperse, negatively charged nanoparticles with unique optical characteristics. Poly(styrene-co-propargyl acrylate) (PS-PA) based copolymer nanoparticles synthesized via an emulsion polymerization form the basis of the CCAs in this work. The negatively charged surfaces result in the colloidal nanoparticles self-assembling into a face-centered cubic (fcc) crystal-like structure. The long-range order and spatial periodicity of the array result in a rejection wavelength, characteristic of CCAs, in which a specific wavelength of light is forbidden from propagating throughout the optical system. The CCAs exhibit mechanochromism through a rejection wavelength shift corresponding to a change …