Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials, Ajit K. Roy, Brendan O'Toole, Zhiyong Wang, David W. Hatchett

Transmutation Sciences Materials (TRP)

The primary objective of this task is to evaluate the potential for the environmentally-assisted cracking of candidate target materials for applications in spallation-neutron-target systems, such as accelerator-driven system for the transmutation of waste. The materials selected for evaluation and characterization are martensitic stainless steels (SS) including Alloys HT- 9, EP 823 and Type 422 stainless steel.

More recently, this experimental program has been expanded to evaluate the effect of molten lead-bismuth eutectic (LBE) on the corrosion behavior of target materials in the presence of oxygen. Since the materials performance laboratory (MPL) at UNLV currently cannot accommodate this type of testing, …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The corrosion of structural materials is a major concern for the use of lead-bismuth eutectic (LBE) systems for nuclear applications such as in transmuter targets or fast reactors. Corrosion in liquid metal systems can occur through various processes, including, for example, dissolution, formation of inter-metallic compounds at the interface, and penetration of liquid metal along grain boundaries. Predicting the rate of these processes depends on numerous system operational factors: temperature, system geometry, thermal gradients, solid and liquid compositions, and velocity of the liquid metal, to name a few. Corrosion, along with mechanical and/or hydraulic factors, often contributes to component failure. …

Modeling Of Corrosion In Oxygen Controlled Lead Bismuth Eutectic Systems With The Coupling Of Chemical Kinetics And Hydrodynamics, Samir Moujaes, Yitung Chen, Kanthi Kiran Dasika, Chao Wu

Transmutation Sciences Materials (TRP)

Objectives:

• To simulate a 2-D model of the Materials Test Loop by approximating it to be a toroid with a pie cross section for the purpose of comparing the simulated results with the analytical results.
• The temperature and concentration profiles on the wall boundaries imposed are similar to the actual test model.
• Geometry effects have great influence on local corrosion rate.
• A 2-D benchmark problem and a sudden expansion case are studied which show good consistency to analytical solution.
• Results from 2-D sudden expansion problem are similar to experimental data obtained by other researchers.

Development Of A Mechanistic Understanding Of High-Temperature Deformation Of Alloy Ep-823, Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The purpose of this task is to evaluate the mechanical properties of Alloy EP-823 at temperatures relevant to the transmutation processes. Testing has been initiated to evaluate the tensile properties of martensitic Alloy EP-823 stainless steel at temperatures ranging from ambient (25 °C) to 600°C. The test materials were thermally treated prior to the evaluation of their tensile properties. The deformation characteristics of these tensile specimens, upon completion of testing, will be evaluated by surface analytical techniques such as scanning electron microscopy (SEM) and transmission electron microscopy (TEM).

Use Of Positron Annihilation Spectroscopy For Stress-Strain Measurements, Ajit K. Roy

Transmutation Sciences Materials (TRP)

One of the greatest challenges in evaluating the performance of materials in the real world is the determination of residual stresses, or the stresses induced in a material. Plastic deformation of metals and alloys produces an increase in the number of lattice imperfections known as dislocations, which by virtue of their interaction results in higher state of internal stress and reduces ductility. These stresses, if not properly annealed (released) can significantly degrade the long-term performance of the materials.

Due to the high temperatures and radiation fields typically encountered in most nuclear systems, such as accelerator-driven transmutation systems (ADS) and nuclear …

Fundamental And Applied Experimental Investigations Of Corrosion Of Steel By Lbe Under Controlled Conditions: Kinetics, Chemistry, Morphology, And Surface Preparation, Allen L. Johnson, John Farley, Dale L. Perry

Transmutation Sciences Materials (TRP)

An innovative research program is proposed to investigate the corrosion of steel by lead alloys, and in particular lead-bismuth eutectic (LBE). In our previous work, some steels were found to be far more resistant to corrosion by LBE than others depending on surface preparation (cold working). This program would allow testing of crucial hypotheses about the causes of the observed increased corrosion resistance. We propose to build a new test facility at UNLV to expose steel samples to LBE as well as facilities to prepare steel samples as indicated by our work.

The unique capabilities of the test system will …

Effects Of Environmental Variables And Stress Concentration On Target Materials, Sudheer Sama

Transmutation Sciences Materials (TRP)

This paper presents a brief summary on stress corrosion cracking (SCC) behavior of alloy HT 9. The susceptibility of this alloy to SCC was evaluated by using constant load and slow strain rate test techniques in neutral and acidic solutions at ambient temperature and 90°C. A proof ring was used to apply tensile load to the smooth specimen for 30 days in constant load testing. In slow strain rate testing, the specimen was continuously strained in tension at a rate of 3.3 × 10^-6 sec^-1 until fracture.

Effects Of Environmental Variables And Stress Concentration On Cracking Of Spallation Target Materials, Ajit K. Roy, Ramprashad Prabhakaran, Mohammad K. Hossain

Transmutation Sciences Materials (TRP)

This paper presents the results of stress corrosion cracking (SCC) studies of two martensitic target materials, namely Alloy EP-823 and Type 422 stainless steel. The susceptibility to SCC was evaluated by using constantload and slow-strain-rate (SSR) test techniques in neutral (pH: 6-7) and acidic (pH: 2-3) aqueous solutions at ambient temperature and 90^oC. A proof ring was used to apply tensile load to the smooth cylindrical specimen for 30 days in constant-load testing. For SSR testing, the specimen was strained in tension until fracture at a strain rate of 3.3 x 10^-6 sec^-1.

Stress Corrosion Cracking Of Type 422 Stainless Steel, Ramprashad Prabhakaran

Transmutation Sciences Materials (TRP)

This paper presents the results of SCC tests of quenched and tempered martensitic Type 422 SS in neutral and acidic aqueous environments at ambient temperature and 90^oC.The susceptibility of smooth and notched tensile specimens to SCC was evaluated by using constant load (CL) and slow strain rate (SSR) test methods. During CL testing, a calibrated proof ring was used to apply a constant load to the test specimen. The magnitude of the applied stress was based on ambient temperature yield strength of the material. On the contrary, the test specimen during SSR testing was continuously strained in tension …

Investigation Of The Corrosion Of Steel By Lead-Bismuth Eutectic (Lbe) Using Scanning Electron Microscopy And X-Ray Photoelectron Spectroscopy, Daniel Koury

UNLV Theses, Dissertations, Professional Papers, and Capstones

Lead Bismuth Eutectic (LBE) has been proposed for use in programs for accelerator transmutation of waste. LBE is the leading candidate material as a spallation target and an option for the sub-critical blanket coolant. The corrosion of 316 and 316L stainless steels by LBE has been studied using UNLV's facilities for Scanning Electron Microscopy (SEM) and X-ray Photoelectron Spectroscopy (XPS). We have compared exposed and unexposed samples and studied the differences. Some amount of surface contamination is present on the samples and has been removed by ionbeam etching. The unexposed samples reveal typical stainless steel characteristics: a chromium oxide passivation …

Corrosion Of Steel By Lead Bismuth Eutectic: Quarterly Report August September October 2002, John Farley

Transmutation Sciences Materials (TRP)

We continued with sputter depth profiling of 316 and 316L steel samples that have been exposed to LBE. We also calibrated the sputter depth profiling using a sample of SiO₂ on Si, and the SEM. This is a valuable independent determination of the thickness of oxide layers.

In the laboratory, progress continues using the XPS machine. Experiments have been performed on steel samples using Argon ions to mill away the surface of the sample, thereby making measurements as a function of depth. This "ion beam milling" proceeds slowly through the oxide layer that covers the steel sample. We are …

Development Of A Mechanistic Understanding Of High-Temperature Deformation Of Alloy Ep-823 For Transmutation Applications: Annual Progress Report (September 2001 – August 2002), Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The purpose of this project is to evaluate the elevated temperature tensile properties of Alloy EP-823, a leading target material for accelerator-driven waste transmutation applications. This alloy has been proven to be an excellent structural material to contain the lead-bismuth-eutectic (LBE) nuclear coolant needed for fast spectrum operations. Very little data exist in the open literature on the tensile properties of this alloy. The test material will be thermally treated prior to the evaluation of its tensile properties at temperatures relevant to the transmutation applications. The deformation characteristics of tensile specimens, upon completion of testing, will be evaluated by surface …

Hydrogen-Induced Embrittlement Of Candidate Target Materials For Applications In Spallation-Neutron-Target Systems: Quarterly Progress Report (June 01 – August 31, 2002), Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The primary objective of this task is to evaluate the effect of hydrogen on environment-assisted cracking of candidate target materials for applications in spallation-neutron-target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization are martensitic stainless steels including Alloy HT-9, Alloy EP 823 and Type 422 stainless steel. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of these materials are being evaluated in environments of interest using tensile specimens under constant load and slow-strain-rate (SSR) conditions. Further, the localized corrosion behavior of these alloys …

Use Of Positron Annihilation Spectroscopy For Stress-Strain Measurements: Quarterly Progress Report (June 1 – August 31, 2002), Ajit K. Roy

Transmutation Sciences Materials (TRP)

The purpose of this collaborative research project involving the University of Nevada Las Vegas (UNLV), the Idaho State University (ISU), and the Los Alamos National Laboratory (LANL) is to evaluate the feasibility of determining residual stresses in cold-worked, plastically-deformed, and welded materials using a nondestructive method based on positron annihilation spectroscopy. This technique uses γ-rays from a small MeV electron Linac to generate positrons inside the sample via pair production. This method is known to have capabilities of characterizing defects in thick specimens, that could not be accomplished by conventional positron technique or other nondestructive methods. The generated data will …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics-Task V: Final Report -Phase I 09/01/2001-08/30/2002, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The Lead-Bismuth eutectic (LBE) has been determined from previous experimental studies by the Russians and the European scientific community to be a potential material that can be used as a spallation target and coolant for the AAA proposed application. Properly controlling the oxygen content in LBE can drastically reduce the LBE corrosion to structural steels. However, existing knowledge of material corrosion performance was obtained from point-wise testing with only very sparse experimental data. Scientists have noticed that the concentration of oxygen dissolved in the liquid alloy could control the corrosion rate of steels exposed to Pb or Pb-Bi. At high …

Design And Analysis For Melt Casting Metallic Fuel Pins Incorporating Volatile Actinides: Quarterly Progress Report 5/16/02- 8/15/02, Yitung Chen, Randy Clarksean, Darrell Pepper

Fuels Campaign (TRP)

An important aspect of the Advanced Accelerator Applications (AAA) program is the development of a casting process by which volatile actinide element (i.e., americium) can be incorporated into metallic alloy fuel pins. The traditional metal fuel casting process uses an inductively heated crucible.

This process works well for the fabrication of metal fuel pins traditionally composed of alloys of uranium and plutonium, but does not work well when highly volatile actinides are included in the melt. The problem occurs both during the extended time period required to superheat the alloy melt as well as when the chamber must be evacuated. …

Corrosion Of Steel By Lead Bismuth Eutectic: Quarterly Report For May-June-July 2002, John Farley

Transmutation Sciences Materials (TRP)

The goal of this project is to understand the basic science of corrosion in the steel/LBE system.

We are taking more data, typically using the newly installed X-ray Photoelectron Spectrometry (XPS) apparatus, and analyzing our existing data. Undergraduate students Denise Parsons and Julia Manzerova have helped a great deal in the analysis of the data. We can obtain the elemental composition as a function of position within the sample. This gives clues to the migration of materials, the composition of the protective oxide layer, and the basic science of the corrosion process. We found dramatic differences between the exposed and …

Design And Analysis For Melt Casting Metallic Fuel Pins Incorporating Volatile Actinides, Xiaolong Wu

UNLV Theses, Dissertations, Professional Papers, and Capstones

Fundamental issues related to the selection of a metallic fuel casting furnace design are presented and discussed including heating mechanisms, casting issues, crucible design, and issues related to the mass transport of americium. The process of evaluating all of these different criteria is undertaken to select a concept that would have the greatest chance of success for casting americium in a metallic fuel rod. Based on this evaluation process, a concept for the casting of metallic fuel pins containing high vapor pressure materials is selected and discussed. The important physics of this concept include mass transport of americium from the …

Hydrogen-Induced Embrittlement Of Candidate Target Materials For Applications In Spallation-Neutron-Target Systems: Annual Progress Report (May 2001 – May 2002), Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The primary objective of this task is to evaluate the effect of hydrogen on environment-assisted cracking of candidate target materials for applications in spallation-neutron-target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization are martensitic stainless steels including Alloy HT-9, Alloy EP 823 and Type 422 stainless steel. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of these materials are being evaluated in environments of interest using tensile specimens under constant load and slow-strain-rate (SSR) conditions. Further, the localized corrosion behavior of these alloys …

Development Of A Mechanistic Understanding Of High-Temperature Deformation Of Alloy Ep-823: Aaa Task-10 Quarterly (03/01, 2002 –05/31, 2002) Report, Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The objective of this task is to evaluate the elevated temperature tensile properties of Alloy EP-823, a leading target material for accelerator-driven waste transmutation applications. The test material will be thermally treated prior to evaluation of its tensile properties at temperatures relevant to the transmutation applications. The deformation characteristics of tensile specimens, upon completion of testing, will be evaluated by surface analytical techniques including scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The overall results are expected to provide a mechanistic understanding of high-temperature deformation behavior of Alloy EP-823 as a function of heat treatment.

Highlights of Accomplishment

• …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics: Quarterly Progress Report 03/16/02- 06/15/02, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The Lead-Bismuth eutectic (LBE) has been determined from previous experimental studies by the Russians and the European scientific community to be a potential material that can be used as a spallation target and coolant for the AAA proposed application. Properly controlling the oxygen content in LBE can drastically reduce the LBE corrosion to structural steels. However, existing knowledge of material corrosion performance was obtained from point-wise testing with very limited density. Scientists have noticed that the concentration of oxygen dissolved in the liquid alloy could control the corrosion rate of steels exposed to Pb or Pb-Bi. At high oxygen concentration, …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics-Phase Two, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The proposed work will combine chemical kinetics and hydrodynamics in target and test-loop lead-bismuth eutectic (LBE) systems to model system corrosion effects. This approach will result in a predicative tool that can be validated with corrosion test data, used to systematically design tests and interpret the results, and provide guidance for optimization in LBE system designs. The task includes two subtasks. The first subtask is to try to develop the necessary predictive tools to be able to predict the levels of oxygen and corrosion products close to the boundary layer through the use of Computational Fluid Dynamics (CFD) modeling. The …

Development Of A Mechanistic Understanding Of High-Temperature Deformation Of Alloy Ep-823 For Transmutation Applications, Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The purpose of this project is to evaluate the elevated temperature tensile properties of Alloy EP-823, a leading target material for accelerator-driven waste transmutation applications. This alloy has been proven to be an excellent structural material to contain the lead-bismuth-eutectic (LBE) nuclear coolant needed for fast spectrum operations. However, very little data exist in the open literature on the tensile properties of this alloy. The selection of Alloy EP-823 as the test material in the proposed task is based on the recommendation of our collaborator at the Los Alamos National Laboratory (LANL). The test material will be thermally treated prior …

Humidity And Temperature Boundaries For Biofilm Formation In Yucca Mountain, Terry Ann Else, Penny S. Amy, James Jay, Amy J. Smiecinski

Publications (YM)

To determine the long-term success of the recommended Yucca Mountain high-level nuclear waste repository, studies of bacterial colonization and biofilm development are needed. Bacteria involved in microbially-influenced corrosion and degradation are known to form biofilms with the potential to impact the integrity of repository packaging and structural materials. Temperature and humidity are environmental factors that can greatly affect biofilm formation. Therefore, it is necessary to determine the temperature and humidity conditions that affect biofilm formation. Microcosms, which simulated the repository environment of Yucca Mountain, were placed at temperatures ranging from 30° C to 70° C and in relative humidities ranging …

Design And Analysis Of A Process For Melt Casting Metallic Fuel Pins Incorporating Volatile Actinides, Yitung Chen, Darrell Pepper, Randy Clarksean

Fuels Campaign (TRP)

UNLV has developed and will continue to develop process models for the analysis of melt casting processes. This work will continue to be performed under the guidance of Argonne National Laboratory (ANL) engineers to ensure that their knowledge and experience benefits the project. The research to be conducted during the second year will center on performing detailed analyses on a conceptual design of an inductively heated skull-crucible casting furnace. Processing conditions will be analyzed, basic models utilized, and detailed heat and mass transfer models will be developed to analyze the most promising processes. The goal of this second year is …

Use Of Positron Annihilation Spectroscopy For Stress-Strain Measurements, Ajit K. Roy

Transmutation Sciences Materials (TRP)

The purpose of this collaborative research project involving the University of Nevada, Las Vegas (UNLV) and Idaho State University (ISU) is to evaluate the feasibility of determining residual stresses of welded (after pre-straining) engineering materials using a new nondestructive technique based on positron annihilation spectroscopy. The proposed technique is to use γ-rays 2 from a small MeV electron Linac to generate positrons inside the sample via pair production. This method can be used for materials characterization and investigation of defects in thick samples that could not be accomplished by conventional positron techniques or other nondestructive methods. The data generated will …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials: Aaa Task-4 Quarterly (December 1, 2001 – February 28, 2002) Report, Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The primary objective of this task is to evaluate the effect of hydrogen on environment-assisted cracking of candidate materials for applications in spallation-neutron-target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization are martensitic stainless steels including HT- 9, EP 823 and 422. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of these alloys will be evaluated in environments of interest using tensile specimens under constant load and slow-strain-rate (SSR) conditions. The extent and morphology of cracking of these alloys will further be evaluated …

Development Of A Mechanistic Understanding Of High-Temperature Deformation Of Alloy Ep-823: Aaa Task-10 Quarterly (12/1, 2001 –02/28, 2002) Report, Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The objective of this task is to evaluate the elevated temperature tensile properties of Alloy EP-823, a leading target material for accelerator-driven waste transmutation applications. The test material will be thermally treated prior to evaluation of its tensile properties at temperatures relevant to the transmutation applications. The deformation characteristics of tensile specimens, upon completion of testing, will be evaluated by surface analytical techniques including scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The overall results are expected to provide a mechanistic understanding of high-temperature deformation behavior of Alloy EP-823 as a function of heat treatment.

Highlights of Accomplishment

• …

Third Quarter Report, Covering January Through March 2002, John Farley

Transmutation Sciences Materials (TRP)

Progress from June 2001-November 2001 was presented at the winter meeting of the American Nuclear Society in Reno (November 12-15, 2001), and incorporated into a refereed conference proceeding. A copy of the refereed conference proceeding has been provided to Tony Hechanova. In brief, the paper described the new program to examine the corrosive effects of lead-bismuth eutectic (LBE) on steels. We employed various types of surface studies (Scanning Electron Microscope [SEM], and X-ray Photoelectron Spectrometry [XPS]) to examine steel samples that had been exposed to LBE for various lengths of time at various temperatures. The goal is to understand the …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics: Quarterly Progress Report 11/16/01- 2/15/02, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The Lead-Bismuth eutectic (LBE) has been determined from previous experimental studies by the Russians and the European scientific community to be a potential material that can be used as a spallation target and coolant for the AAA proposed application.

Properly controlling the oxygen content in LBE can drastically reduce the LBE corrosion to structural steels. However, existing knowledge of material corrosion performance was obtained from point-wise testing with very limited density. The transport of oxygen and corrosion products, their interaction and variation of corrosion/precipitation along the flow are not well understood.

The first subtask of this project involves using a …