Biology and Biomimetic Materials Commons^™

Optimization Of Conditions For Production Of Mechanically Strong Suckerin Protein Hydrogels, Autumn Furniss

Williams Honors College, Honors Research Projects

Hydrogels are polymer networks with a large water content. Uses include biomedical applications like drug delivery, wound dressing, and more. Current natural hydrogels lack mechanical robustness. Squid ringed teeth (completely protein) have a modulus comparable to thermoplastics; adding this to hydrogels could improve modulus while maintaining biocompatibility.

Three experiments were performed: Hofmeister solubility study, SRT powder additive, and SRT aqueous solution. The first showed that LiCl solution without acetic acid dissolved the most SRT; overall LiCl dissolved more than all others. SRT as a powder additive increased the modulus of the hydrogels, however the error in the measurements make it …

Developing Strategies To Toughen Bio-Inspired Adhesives, Narelli P. Narciso, Samuel Lee Huntington, Jonathan J. Wilker

The Summer Undergraduate Research Fellowship (SURF) Symposium

Mussels and other marine creatures adhere very well in underwater environments, having the ability to withstand the force of the sea. These animals have inspired synthetic biomimetic adhesives for wet systems, presenting potential for biomedical applications. However, most current commercial adhesives tend to be brittle, not resisting repetitive movements. This study assesses toughening strategies to improve the mussel-inspired adhesives’ ductility while maintaining its strength. The strategies included altering the polymer’s chemical structure by changing the percentage of polyethylene glycol (PEG) in the molecule and by adding fillers, such as calcium carbonate, silica and nacre - a calcium carbonate compound found …

Synthesis Of Zinc Oxide Nanorods And Use In Biosensor Applications, Anishkumar Manoharan

Graduate Theses and Dissertations

The main aim of this research was to develop a nanorod based biosensor for biomedical applications. In this project I use zinc oxide nanorods as the bio-material for biosensor. I fabricated these nanorods using a solution-based technique. Initially I coated a zinc oxide seed layer as the base. This seed layer was then annealed at 350 degrees for almost 1 hour. As a next step, interdigitated electrodes were fabricated on the top of the seed layer using a lift off process. The zinc oxide nanorods were then grown at 90 degrees for almost 4 hours along the electrodes. In this …