Corrosion Characteristics Of Ti And Al2o3/Ti Thin Films Sputtered On 316lss, Iman El-Mahallawi, Hanan ِ Abd El-Fattah Dr., Lamiaa Mohamed Dr., Aliaa Abdelfattah

Mechanical Engineering

In this work, two thin films (Ti and Al2O3/Ti) were deposited on 316LSS substrates by the physical vapor deposition (PVD) sputtering technique. Heat treatment was applied for thin films at 400 °C for 2 h. Thin films were divided into two groups, The First group cooled in the air (normalized), and the second cooled in the furnace (annealed). The electrochemical characteristics were investigated by potentiodynamic polarization (POT) and impedance spectroscopy (EIS) tests. The corrosion resistance (CRST) for all thin films before and after heat treatment was determined in 3.5% NaCl at room temperature (RT). Scanning electron microscope (SEM), and surface …

Machine Learning-Assisted Multiscale Simulation And Design Optimization Of Composite Jackets Under Low-Velocity Impacts, Masoud Mohammadi

Graduate Theses, Dissertations, and Problem Reports (ETD)

This research presents the development of a data-driven machine learning-assisted approach to simulate and optimize the design of composite materials subjected to low-velocity impacts. It focuses on a specific type of hybrid composite comprised of fiberglass and Kevlar fabrics stitched with Kevlar threads. The study begins by creating a multiscale finite element simulation for the composite under a low-velocity impact, which operates across three scales: microscale, mesoscale, and macroscale. This simulation accepts various inputs, such as different layer configurations and orientations, and provides impact outputs including maximum load and energy absorption capacity and displacement at failure.

Python and MATLAB scripts …

Direct Measurement Of Microwave Loss In Nb Films For Superconducting Qubits, B. Abdisatarov, D. Bafia, A. Murthy, G. Eremeev, H. E. Elsayed-Ali, J. Lee, A. Netepenko, C. P. A. Carlos, S. Leith, G. J. Rosaz, A. Romanenko, A. Grassellino

Electrical & Computer Engineering Faculty Publications

Niobium films are a key component in modern two-dimensional superconducting qubits, yet their contribution to the total qubit decay rate is not fully understood. The presence of different layers of materials and interfaces makes it difficult to identify the dominant loss channels in present two-dimensional qubit designs. In this paper, we present the study that directly correlates measurements of RF losses in such films to material parameters by investigating a high-power impulse magnetron sputtered (HiPIMS) film atop a three-dimensional niobium superconducting radio frequency (SRF) resonator. By using a 3D SRF structure, we are able to isolate the niobium film loss …

Underlying Substrate Effect On Electrochemical Activity For Hydrogen Evolution Reaction With Low-Platinum-Loaded Catalysts, Baleeswaraiah Muchharla, Peter V. Sushko, Kishor K. Sadasivuni, Wei Cao, Akash Tomar, Hani Elsayed-Ali, Adetayo Adedeji, Abdennaceur Karoui, Joshua M. Spurgeon, Bijandra Kumar

Electrical & Computer Engineering Faculty Publications

Platinum is known as the best catalyst for the hydrogen evolution reaction (HER) but the scarcity and high cost of Pt limit its widespread applicability. Herein, the role of the underlying substrate on the HER activity of dispersed Pt atoms is uncovered. A direct current magnetron sputtering technique is utilized to deposit transition metal (TM) thin films of W, Ti, and Ta as underlying substrates for extremely low loading of Pt (

Thermal Diffusivity And Acoustic Properties Of Nb Thin Films Studied By Time-Domain Thermoreflectance, Md. Obidul Islam, Hani Elsayed-Ali

Electrical & Computer Engineering Faculty Publications

The thermal diffusion and acoustic properties of Nb impacts the thermal management of devices incorporating Nb thin films such as superconducting radiofrequency (SRF) cavities and superconducting high-speed electronic devices. The diffusion and acoustic properties of 200-800 nm thick Nb films deposited on Cu substrates were investigated using time-domain thermoreflectance (TDTR). The films were examined by X-ray diffraction, scanning electron microscopy, and atomic force microscopy. The grain size and thermal diffusivity increase with film thickness. The thermal diffusivity increased from 0.100± 0.002 cm²s^-1 to 0.237± 0.002 cm²s^-1 with the increase in film thickness from 200 …

Real-Time Spectroscopic Ellipsometry For Flux Calibrations In Multi-Source Co-Evaporation Of Thin Films: Application To Rate Variations In Cuinse₂ Deposition, Dhurba R. Sapkota, Balaji Ramanujam, Puja Pradhan, Mohammed A. Razooqi Alaani, Ambalanath Shan, Michael J. Heben, Sylvain Marsillac, Nikolas J. Podraza, Robert W. Collins

Electrical & Computer Engineering Faculty Publications

Flux calibrations in multi-source thermal co-evaporation of thin films have been developed based on real-time spectroscopic ellipsometry (RTSE) measurements. This methodology has been applied to fabricate CuInSe₂ (CIS) thin film photovoltaic (PV) absorbers, as an illustrative example, and their properties as functions of deposition rate have been studied. In this example, multiple Cu layers are deposited step-wise onto the same Si wafer substrate at different Cu evaporation source temperatures (TCu). Multiple In₂Se₃ layers are deposited similarly at different In source temperatures (TIn). Using RTSE, the Cu and In₂Se₃ deposition rates are determined as …

Predictions Of Lattice Parameters In Niti High-Entropy Shape-Memory Alloys Using Different Machine Learning Models, Tu-Ngoc Lam, Jiajun Jiang, Min-Cheng Hsu, Shr-Ruei Tsai, Mao-Yuan Luo, Shuo-Ting Hsu, Wen-Jay Lee, Chung-Hao Chen, E-Wen Huang

Electrical & Computer Engineering Faculty Publications

This work applied three machine learning (ML) models—linear regression (LR), random forest (RF), and support vector regression (SVR)—to predict the lattice parameters of the monoclinic B19′ phase in two distinct training datasets: previously published ZrO₂-based shape-memory ceramics (SMCs) and NiTi-based high-entropy shape-memory alloys (HESMAs). Our findings showed that LR provided the most accurate predictions for a_c, a_m, b_m, and c_m in NiTi-based HESMAs, while RF excelled in computing βm for both datasets. SVR disclosed the largest deviation between the predicted and actual values of lattice parameters for both training datasets. A combination approach …

Liquid Metal Printing Of Ultrathin Conductive Metal Oxides, Andrew B. Hamlin

Dartmouth College Ph.D Dissertations

Widegap metal oxides are critical semiconducting materials in solar power generation, transparent electronics and displays. Ultrathin versions of these materials are poised to be at the forefront of next generation technology due to their high transparency, flexibility, and the capacity to advantageously use backchannel sensitivity and quantum confinement. Liquid metal printing is a novel deposition technique that fundamentally yields ultrathin oxide materials by exfoliating the self-limited oxide that exists on molten metals at low temperatures. Our work involves the invention of novel liquid metal printing techniques to deposit semiconducting 2D metal oxides with precise electrostatic properties. We investigate the electronic …

The Impacts Of Impurities And Stress State On Polycrystalline Ice Deformation And Investigations Into The Densification Of Polar Firn, Ayobami Oladapo Ogunmolasuyi

Dartmouth College Ph.D Dissertations

Glacier ice cores are unparalleled natural archives of past climate, containing ancient air and impurities. Understanding glacier and ice sheet behavior and their impact on impurity records is crucial for interpreting ice core records. H₂SO₄ is particularly significant, as it provides the strongest evidence for the diffusion of chemical signals and decreases the strength of single crystals and polycrystals of ice. However, its effects on recrystallization, grain growth, and fabric development mechanisms, as well as the effects of grain boundaries on its post-depositional diffusion remain unclear.

This thesis investigates the effects of the microstructural location of H …

Matrix Stiffness Sensing By Nascent Adhesions And The Role Of Riam In Adhesion Assembly, Nikhil Mittal

Dissertations, Master's Theses and Master's Reports

Mechanical stiffness of the extracellular matrix (ECM) impacts many cellular functions such as proliferation, migration, and differentiation. ECM stiffness is sensed by a cell via integrin-based focal adhesions (FAs) by changing conformation and biochemical activities of molecules within FAs by the exchange of the force between the ECM and filamentous actin (F-actin). Cells in turn respond to this stiffness by generating traction force that plays an important role in many biological events such as tissue morphogenesis, stem cell differentiation, wound healing, and cancer cell metastasis. The stiffness of the extracellular matrix induces differential tension within integrin-based adhesions. Understanding stiffness sensing …

Inherently Porous Metal Structures With Sufficient Mechanical Properties Through Direct Writing Of Bio-Based Inks, Havva Eda Aysal

Graduate Theses, Dissertations, and Problem Reports (ETD)

There is currently a burgeoning interest in developing 3D printed metal structures with inherent porosity and sufficient mechanical properties for mass customization in the biomedical field. Current approaches for 3D printing of biocompatible metals rely on powder-bed fusion methods which are energy intensive and utilize large amounts of metal powder that is challenging to recycle. In addition, such methods aim on producing dense parts and porosity generation, within the printed part, is challenging due to the complex physics of the melting pool. Here, a relatively new and promising approach is undertaken to study the 3D printing of inherently porous structures …

Influence Of Nanofiller Surface Treatment On Mechanical Properties Of Pyrolyzed Ceramic Nanocomposites, Laxmi Sai Viswanadha, Chenglin Wu, Jeremy Watts, Mohammad Naraghi

Civil, Architectural and Environmental Engineering Faculty Research & Creative Works

The brittleness and limited plastic deformation of ceramics restrict their applications. In this work, the effects of pristine (CNTP), functionalized (CNTOH, CNTCOOH) and silanized MWCNTs on the mechanical properties of Silicon Carbide obtained by pyrolyzing polycarbosilane SMP-10 were studied. Functionalization with 3-glycidoxypropyltrimethoxy was analyzed through dispersion stability, zeta potential, and EDS analyses, revealing increased silicon content and colloidal stability in silanized MWCNTs. However, silanized MWCNTs led to reduced mechanical properties in composites, while untreated MWCNTs (CNTP, CNTOH, CNTCOOH), showed a substantial increase in modulus by 74.2 %, 86.9 %, and 30.5 %, respectively. The observed enhancement in mechanical properties exceeded …

Ultra-Fast Annealing Improves Snr And Long-Term Stability Of A Highly Multiplexed Line-By-Line Fbg Array Inscribed By Femtosecond Laser In A Coreless Fiber For Extreme-Temperature Applications, Farhan Mumtaz, Bohong Zhang, Jeffrey D. Smith, Ronald J. O'Malley, Rex E. Gerald, Jie Huang

Electrical and Computer Engineering Faculty Research & Creative Works

This study reports the fabrication of an 4th-order line-by-line Fiber Bragg Gratings (FBG) array using femtosecond laser inscription within a highly multimode coreless optical fiber, with a particular focus on achieving substantial multiplexing capabilities. An ultra-fast annealing procedure is employed, resulting in an impressive enhancement of the FBG sensor's fringe visibility by approximately 13 dB, signifying a notable improvement of approximately ~4 dB. This substantial enhancement contributes to the long-term stability and performance of the multiplexed FBG array in extreme temperature conditions. The systematic fabrication approach employed for the multiplexed FBG array guarantees a high signal-to-noise ratio (SNR) for each …

Desirable Candidates For High-Performance Lead-Free Organic–Inorganic Halide Perovskite Solar Cells, Sajid Sajid, Salem Alzahmi, Imen Ben Salem, Nouar Tabet, Yousef Haik, Ihab M. Obaidat

All Works

Perovskite solar cells (PSCs) are currently demonstrating tremendous potential in terms of straightforward processing, a plentiful supply of materials, and easy architectural integration, as well as high power conversion efficiency (PCE). However, the elemental composition of the widely utilized organic–inorganic halide perovskites (OIHPs) contains the hazardous lead (Pb). The presence of Pb in the PSCs is problematic because of its toxicity which may slow down or even impede the pace of commercialization. As a backup option, the scientific community has been looking for non-toxic/less-toxic elements that can replace Pb in OIHPs. Despite not yet matching the impressive results of Pb-containing …

Processing & Properties Of Zirconium Carbide Manufactured By Ceramic On-Demand Extrusion, Clare Sabata

Masters Theses

"This research focuses on the development of a zirconium carbide (ZrC) paste for use in material extrusion direct ink write additive manufacturing (AM) followed by the pressure less densification of ZrC and the mechanical and thermal characterization of the resulting ceramics. A highly loaded, aqueous paste was developed using commercial ZrC powder ball milled to ~1 μm. Optimal dispersant, binder, and solids loading were found by rheological characterization. The paste composition consisted of 46-47 vol% ZrC, 43.5 vol% distilled water, 8.1 vol% dispersant, and 1.6 vol% binder. A yield stress of ~8 Pa allowed for shape retention upon removal of …

Sub-Critical Crack Growth And Fatigue Behaviour Of Alkali Silicate Glass, Noah Weyrauch

Masters Theses

"Delayed failure in silicate glasses can be linked to subcritical crack growth (SCCG) where surface defects grow over time until catastrophic failure. This phenomenon originates from stress-enhanced chemical interactions between the environment (e.g. water) and the strained silicate bonds at the crack tip. SCCG must be accounted for to predict the long-term survivability of silicate-glass components. This study compares two methods to measure SCCG parameters for a commercial alkali silicate sealing glass and for a series of binary xNa₂O-(1-x)SiO₂ glasses, where 0.15 ≤ x ≤ 0.35. A constant moment double cantilever beam (DCB) technique was used to …

Theoretical Modeling And Experimental Investigation Of Phase Selection During Rapid Solidification Of Alloys, Azeez Aremu Akinbo

Masters Theses

"A novel model, rooted in time-dependent nucleation theory, has been created to explore how rapid solidification affects the extended solubility in metal alloys. This model was used to forecast solubility concerning undercooling in multiple binary aluminum (Al) alloys, and its predictions for both eutectic and peritectic systems closely match experimental data. It was demonstrated that this developed model surpasses the T0 line method, which does not consider the kinetic aspects of nucleation. Furthermore, the model can be extended to ternary and multicomponent phases by assuming that the scarcest element or the slowest diffusing component restricts nucleation. Al-Cu and Al-Cr, vital …

Investigating The Role Of Tesserae In Energy Absorption In Shark Cartilage, Molly Dobrow

UNF Graduate Theses and Dissertations

Unlike mammals, shark endoskeletons are composed of cartilage, which is less stiff compared to bone. Despite this structural disadvantage, sharks have risen to become apex predators, with reported maximum posterior bite force estimates approximating 5914 N in bull sharks. Shark jaws are estimated to undergo high cycle loading within the organism’s lifecycle without evidence of failure. Fatigue resistance may relate to mineral distribution within a component of the endoskeletal system – tesserae. Tesserae are thin, roughly hexagonal tiles composed of calcium phosphate hydroxyapatite (HA) crystals and grow by accretion to eventually surround the hyaline cartilage core. Though tesserae dimensions are …

Process, Structure, & Property Investigation Of Gallium-Based Metallic Alloys Processed At Room Temperature, Jennifer E. Ruliffson

UNF Graduate Theses and Dissertations

Metallic and intermetallic alloys are important in engineering, necessitating a thorough comprehension of their structure, processing, and properties. Amalgams are a class of alloy which are synthesized by various methods to produce diverse properties. Gallium-based amalgams, particularly gallium eutectic alloys, have low melting points, which allow for applications in dentistry and temperature sensitive electronics. This thesis investigates the process-structure-property relationships of gallium-based amalgams mixed with copper. Phases, microstructure, and diffusion processes are investigated using XRD and SEM. Adhesion strength and thermal properties are then correlated to these as well as process steps. This study contributes to advancing the understanding and …

Processing Of Niti Sma For High Reflectivity Applications, Nicholas Dean Asbury

UNF Graduate Theses and Dissertations

Nickel Titanium (NiTi) is a shape memory alloy (SMA) that is capable of being deformed and subsequently returned to the original shape through heating. This unique property makes NiTi a prime material for potential applications in the aerospace industry. As manufacturing capabilities advance, the ability to produce and implement advanced materials, such as shape memory alloys like NiTi, becomes more feasible. One such application being studied is deployable mirrors for imaging satellites. Reflector and mirror surfaces for imaging in the visible and infra-red range of the light spectrum require low surface roughness across the largest allowable area for the collection …

Influence Of Heat Treatment And Shielding Gas Environment On The Very High Cycle Fatigue Behavior Of 17-4 Precipitation Hardened Stainless Steel, Jade Welsh

UNF Graduate Theses and Dissertations

Additive manufacturing (AM) for stainless steel components has proved useful in a variety of industries ranging from aerospace to biomedical engineering. Many of these components are subject to very high cycle fatigue (VHCF) loading and must have tailored mechanical properties to ensure failures do not occur before a service life is reached. Testing the fatigue strength AM materials exposed to VHCF loading is paramount to compare with the expected life cycles of their wrought counterparts. In this thesis, AM 17-4 precipitation hardened (PH) stainless steel (SS) were fabricated using laser powder bed fusion (L-PBF) technique, while the wrought 17-4 PH …

Development And Characterization Of Ceramic Devices For Capillary Action In Microgravity For The Purpose Of Growing Vegetables In Space, Lucas S. Mougeot

UNF Graduate Theses and Dissertations

The future of humanity is often rendered in spectacular visions of a multiplanetary civilization with a booming space economy. Reaching this reality requires addressing one of the core needs of survival: food. Porous ceramics used for Passive Porous Tube Nutrient Delivery Systems (PPTNDS) offer a promising solution. In microgravity environments such as the International Space Station (ISS), fluid dynamics and liquid coagulation do not support conventional agricultural practices. Porous ceramic materials present a solution that enables nutrient solution diffusion via capillary action.

In this research, it was determined that extruding a wadding ceramic tube and sintering it at 1900 °F …

Improving Cast Steel Rail Coupler Fatigue Resistance Through Local Wire-Arc Additive Manufacturing, Andrew M. Bunge

Dissertations, Master's Theses and Master's Reports

Every year, thousands of cast-steel railcar couplers suffer from corrosion-initiated fatigue cracking in similar areas of the coupler’s knuckle; between 2015 and 2018 about 90,000 knuckles were replaced, otherwise these couplers would have been at risk for unexpected failures. These types of couplers have been common in industrial use as early as 1932, hence it is desirable for a countermeasure to the fatigue cracking that does not involve significantly altering the geometry or casting process. Wire arc additive manufacturing (WAM) is a developing technology which boasts the ability to produce complex near-net-shape components; however, less attention has been paid to …

High Temperature Strength Reduces Soldering In Aluminum High Pressure Die Casting, Jacob A. Belke

Dissertations, Master's Theses and Master's Reports

Die soldering, an adhesion defect in high pressure die casting (HPDC), is a symptom of localized sticking where a localized portion of the cast material is adhered to the tooling surface causing build up over time. This requires the tooling to be serviced which incurs additional costs to the process that gets passed on to the parts. Historically, soldering has been mitigated using lubricants, coatings, and alloy chemistry modifications but solder persists.

The Tresca friction thermomechanical model suggests soldering occurs when the local interfacial shear stress between the casting and die surface exceeds the local shear strength of the casting. …

Sustainable Materials For Environment − Multifunctional Material Made From Dead Leaves And Nanostructured Materials For Antibiotic Degradation, Siyuan Fang

Dissertations, Master's Theses and Master's Reports

As environmental pollution from industrial processes and human activities continues to rise, finding efficient approaches to recycle waste materials and degrade persistent contaminants becomes increasingly critical. Dead leaves, an abundant but underutilized biomass, present an opportunity for creating value-added materials if their biocomponents can be preserved and transformed. Simultaneously, antibiotics such as tetracycline are widely found in water bodies but pose serious ecological and health risks, necessitating effective degradation methods. This dissertation addresses these challenges by leveraging natural and nanostructured materials to develop multifunctional products and advanced photocatalytic processes.

Chapter 3 of this dissertation addresses the challenge of converting waste …

Molecular Modeling Of Phenolic Resin For Carbon-Carbon Composites, Ivan Gallegos

Dissertations, Master's Theses and Master's Reports

One of the most difficult challenges associated with space exploration is terrestrial atmospheric reentry due to the high thermal loads generated. Carbon carbon (C/C) composites have been used as heat shielding materials due to their high strengthto- weight ratio and thermal properties and their applications include heat shielding for various high temperature environments. C/C composites are manufactured by polymer-infiltration pyrolysis (PIP) via cycles of curing and pyrolysis of a prepreg which can be costly and take up to several days. Thus, C/C composites ideal candidates for computationally-driven optimization techniques, such as a multiscale Integrated Computational Materials Engineering (ICME) approach, by …

Development And Testing Of High Strength Scalable High Entropy Alloys, Hans Jakob Pommerenke

Doctoral Dissertations

"High entropy alloys have shown promise through their ability to be tailored to specific scenarios. From highly corrosive environments to precipitation strengthened alloys to radiation environments high entropy alloys allow tailor made alloys for every solution. New compositions are developed and tested but little work focuses on the processing effect choosing rather than using processing as a steppingstone to achieve properties without investigating the processing effects. This work focuses on single phase face-centered cubic alloys strengthened by processing and precipitation strengthening. In conjunction with the development of these alloys, the ability to scale production will be investigated and characterized to …

The Development Of Hard Materials And Fibrous Monolith Composites For Friction Stir Welding, Paul Michael Brune

Doctoral Dissertations

"This research focuses on the development of hard materials and fibrous monolith composites for the purpose of adding to current friction stir welding tool technology. Well studied hard material systems, such as WC-Co, were incorporated and evaluated as cell materials for fibrous monolith composites with ductile cell boundaries of Co, W, and Mo. The indentation behavior of the WC-Co and WC-Co-cBN composites indicated possible crack deflection at the cell/cell boundary interface. Cylindrical pin friction stir welding tools were developed for each of the three fibrous monolith material systems. Welding was achieved on AA1100 aluminum, 260 brass, and AISI 1018 steel …

Processing-Microstructure-Properties Relationships In Additively Manufactured Zrb2-Sic Ceramics, Marharyta Lakusta

Doctoral Dissertations

"The study explores the pressure less sintering (PS) and chemical compatibility of ZrB₂-30 vol.%SiC produced by additive manufacturing (AM) with CO₂. The oxidation kinetics and scale microstructures were compared for ZrB₂-SiC made by hot pressing (HP) and by AM coupled with PS. All specimens exhibited parabolic oxidation kinetics. The difference in oxidation behavior becomes evident at temperatures of 1100-1400°C (200-900h). Oxidation rates increased as grain size increased. Similar oxide scale morphologies were observed in both CO₂ and air, with an outer borosilicate layer and an inner porous ZrO₂ layer containing partially oxidized …

In-Depth Characterization Of The Selective Oxidation Products Of Hafnium Carbide, Jonathan Allen Scott

Doctoral Dissertations

"Materials capable of withstanding oxidative environments at temperatures >2000°C are necessary for hypersonic applications. Hafnium carbide (HfC) shows a combination of properties that lends itself toward these applications; however, its oxidation behavior is poorly understood. At 1300°C, HfC was found to oxidize via the following mechanism: 1) Initial oxidation of both C and Hf present in the system, 2) Formation of an interconnected pore network, whose size is related to the volume of gases being generated during the oxidation process, 3) Growth of the oxide scale to become sufficiently protective, 4) Formation of an initially amorphous “HfO₂C” at …