The Effect Of Silicon Content On Impact Toughness Of T91 Grade Steels, Ajit K. Roy, Pankaj Kumar, Debajyoti Maitra

Mechanical Engineering Faculty Research

The impact resistance of silicon (Si)-containing modified 9Cr-1Mo steels has been investigated within a temperature regime of -40 to 440°C using the Charpy method. The results indicate that the energies absorbed in fracturing the tested specimens were substantially lower at temperatures of -40, 25, and 75°C compared to those at elevated temperatures. Lower impact energies and higher ductile-to-brittle-transition-temperatures (DBTTs) were observed with the steels containing 1.5 and 1.9 wt.% Si. The steels containing higher Si levels exhibited both ductile and brittle failures at elevated temperatures. However, at lower temperatures, brittle failures characterized by cleavage and intergranular cracking were observed for …

Corrosion Research On Rock Bolts And Steel Sets For Sub-Surface Reinforcement Of The Yucca Mountain Repository, Dhanesh Chandra, Jaak J.K. Daemen

Publications (YM)

Underground nuclear waste storage repositories generally use steels and super alloys for various structural members and storage containers. These materials are susceptible to corrosion due to seepage of water. We studied rock bolt materials for reinforcing tunnels and containment materials for storing nuclear waste materials. In general, the design of underground support materials for tunnels are mainly based on mechanical behavior of the materials, but not much was known about the interaction of the seepage YM waters with the structural members under various conditions in the tunnels. The sources of water in the Yucca Mountain (YM) repository are due to …

Metal Induced Crystallization Of Silicon Thin Films, Sandeep Kumar Raju Sangaraju

UNLV Theses, Dissertations, Professional Papers, and Capstones

Low temperature crystallization of thin film silicon is important for many industrial applications including flat panel displays and silicon thin film solar cells. Unfortunately this remains a major challenge since crystallization temperature of silicon is above 1,000 degrees Celsius, thus limiting to substrates that can tolerate high temperatures. The inability to deposit crystalline thin films on glass substrates is the reason why flat panel display industry uses amorphous silicon for LCD active matrix displays. Thus the ability to deposit crystallized thin film silicon at low temperatures will have significant impact on thin film silicon applications. It has been observed that …

Yttrium And Hydrogen Superstructure And Correlation Of Lattice Expansion And Proton Conductivity In The Bazr0.9y0.1o2.95 Proton Conductor, A. Braun, A. Ovalle, V. Pomjakushin, A. Cervellino, S. Erat, Wayne C. Stolte, T. Graule

Chemistry and Biochemistry Faculty Research

Bragg reflections in Y-resonant x-ray diffractograms of BaZr_0.9Y_0.1O_2.95 (BZY10) reveal that Y is organized in a superstructure. Comparison with neutron diffraction superstructure reflections in protonated/deuterated BZY10 suggests that both superstructures are linked, and that protons move in the landscape imposed by the Y. The thermal lattice expansion decreases abruptly for protonated BZY10 at T≥648±20 K, coinciding with the onset of lateral proton diffusion and suggesting a correlation of structural changes and proton conductivity. The chemical shift in the Y L₁-shell x-ray absorption spectra reveals a reduction from Y³⁺ toward Y²⁺ upon …

Fracture Toughness, Crack-Growth-Rate And Creep Studies Of Alloy 276, Joydepp Pal

UNLV Theses, Dissertations, Professional Papers, and Capstones

Austenitic nickel-base Alloy 276 had been proposed to be a candidate structural material within the purview of the nuclear hydrogen initiative program. A mechanistic understanding of high temperature tensile deformation of this alloy has already been presented in an earlier investigation. The current investigation has been focused on the evaluation of crack-growth behavior, fracture toughness, stress-corrosion-cracking and creep deformation of this alloy as functions of different metallurgical and mechanical variables. The results of crack-growth study under cyclic loading indicate that this alloy exhibited greater cracking tendency with increasing temperature at a constant load ratio (R). However, the effect of temperature …

Spectroscopic Investigation Of Palladium-Copper Bimetallic Systems For Pem Fuel Cell Catalysts, Timo Hofmann

UNLV Theses, Dissertations, Professional Papers, and Capstones

One of the main barriers to commercialization of polymer electrolyte membrane fuel cells systems is cost, which is largely due to the need of platinum (Pt)-containing catalysts. In this thesis we investigate bimetallic systems consisting of a base metal (copper) and a noble metal (palladium) that, as an alloy on the nanoscale, mimic the electronic properties that make Pt desirable as a catalyst.

We present a detailed investigation of the electronic structure of carbon-supported Pd/Cu nanoparticle catalysts, model bilayer thin film systems, alloys, and various metal reference samples. We have investigated the valence band structure of the catalysts using a …

Damage Characterization Of Beam-Column Joints Reinforced With Gfrp Under Reversed Cyclic Loading, Aly M. Said

Civil and Environmental Engineering and Construction Faculty Research

The use of fiber reinforced polymer (FRP) reinforcement in concrete structures has been on the rise due to its advantages over conventional steel reinforcement such as corrosion. Reinforcing steel corrosion has been the primary cause of deterioration of reinforced concrete (RC) structures, resulting in tremendous annual repair costs. One application of FRP reinforcement to be further explored is its use in RC frames. Nonetheless, due to FRP's inherently elastic behavior, FRP-reinforced (FRP-RC) members exhibit low ductility and energy dissipation as well as different damage mechanisms. Furthermore, current design standards for FRP-RC structures do not address seismic design in which the …

Oxidation Modeling By Means Of Molecular Dynamics, Chaiyod Soontrapa

UNLV Theses, Dissertations, Professional Papers, and Capstones

Oxidation modeling is normally engineered to study systems at macroscopic scales, mostly in analytical forms based on diffusion theories. The associated time scale is usually in months, days, or minutes, and the length scale is in the order of microns. In this dissertation, oxidation modeling is performed at atomistic scale with the time and length scales in picoseconds and angstroms, respectively, using molecular dynamics. Molecular dynamics simulations generate trajectories of each atom or particle in a system according to the laws of physics. Studying oxidations under the atomistic point of view can offer new insights on atomic behaviors and influencing …

Tensile Strength And Failure Criterion Of Analog Lithophysal Rock, James A. Nott

UNLV Theses, Dissertations, Professional Papers, and Capstones

This project determines the tensile strength of lithophysal analog rock and presents failure criteria that can be used by geotechnical engineers to evaluate underground structures in rock. The physical and mechanical properties that are related to the failure criterion, such as porosity, compressive strength and modulus of elasticity, are also discussed. Experimental tensile tests were made using direct uniaxial and indirect Brazilian tests. Three 4-inch specimens were fabricated and tested in direct uniaxial tensile tests using Hydro-Stone TB. The results showed that the elastic tensile modulus of elasticity was within two percent of existing data for the compressive modulus of …

Study Of Corrosion Of Materials In The Sulfur-Iodine Hydrogen Production Cycle, Thao Trung Ho

UNLV Theses, Dissertations, Professional Papers, and Capstones

Hydrogen is of great interest since the availability of traditional fossil fuels is in decline. Strictly speaking, hydrogen is not a primary source of energy but is an energy carrier, since energy typically must be used from another source (electricity, natural gas, coal, etc.) to produce it. Of hydrogen production techniques, the Sulfur-Iodine thermochemical water splitting process (S-I cycle), which was proposed by General Atomics (GA), is promising with its simplicity and high efficiency. Most of the chemicals are recycled except water. However, the S-I cycle operates in a harsh, corrosive environment in the presence of a mixture of iodine …

Effects Of Mechanical And Metallurgical Variables On Creep, Fracture Toughness And Crack Growth Behavior Of Alloy 617, Muhammad Hasibul Hasan

UNLV Theses, Dissertations, Professional Papers, and Capstones

Nickel base Alloy 617 has been identified to be a suitable structural material for heat exchanger applications in both hydrogen and electricity generation using nuclear heat. A maximum operating temperature of 950°C has been specified by department of energy (DOE) for both applications to achieve a maximum possible efficiency. Therefore, an extensive investigation has been pursued to evaluate time-dependent-deformation (Creep) of this alloy as functions of temperature and applied load. The results indicate that this alloy exhibited severe creep deformation, characterized by development of an instantaneous tertiary creep region at 850 and 950°C under applied stresses corresponding to its 35% …

Model For Alumina Nanopore-Based Optical Filter, Nathan Lehman, Rama Venkat, Robert A. Schill

Electrical & Computer Engineering Faculty Research

Alumina nanopore structures find applications in magnetic sensors, optical filters, and various biological devices. In this work, we present a ray-optics model for the optical filter. We present a detailed simulation and a simplified analytical expression for the reflectance as a function of the alumina parameters such as pore diameter, pore density, alumina thickness, and a function of the wavelength and angle of incidence of the illuminating plane electromagnetic wave. The reflectance vs wavelength in the range of 400–800nm obtained from the simulation and the analytical expression are compared with that of the experiments for thin and thick alumina. All …

High Temperature Heat Exchanger Annual Report, Anthony Hechanova

Publications (NSTD)

Objectives

• Identify candidate materials for heat exchanger components.

• Test candidate materials for heat exchanger components.

• Design critical components in the interface between the reactor and hydrogen production plant and within the sulfur iodine thermochemical process.

• Fabricate prototypical components.

• Test prototypical components.

Environmental Effects On Corrosion Properties Of Alloy 22, Mano Misra

Publications (YM)

This document presents detailed technical report for four Subtasks that were conducted independently. All four Subtasks investigated environmental effects on corrosion properties of Alloy 22. The four Subtasks that were investigated are as follows: Subtask 1: Experimental Determination of Parameters for the General Corrosion Model. Subtask 2: Corrosion under Dust Deposits Containing Hygroscopic Salts. Subtask 3: Heated Electrode Approach for the Study of Corrosion Under Aggressive Conditions. Subtask 4: Effect of Hydrogen Permeation on the Stability of the Passive Film of Alloy 22.

Raman Studies Of 1,3,5,7 Cyclooctatetraene At High Pressure, Martin Galley, Ed Romano, Sergey Tkachev, Michael Pravica

Undergraduate Research Opportunities Program (UROP)

We performed Raman spectroscopic studies of 1,3,5,7-cyclooctatetraene at elevated pressures up to 10 GPa with the aim of examining possible planarization of the molecule and further studying two prior-discovered phases of the solid with pressure. The Raman excitation source was a Krypton-ion laser operating at 674.1 nm (give wavelength).

1,3,5,7 Cyclooctatetraene has an octagonal formation however it is not aromatic or anti-aromatic (not a subject to the 4n+2 Huckel’s rule) [1]. As a result, its adopts a somewhat reactive tub shape. Upon the addition or removal of one to two electrons under ambient conditions, the molecule planarizes and becomes aromatic …

Structural Studies Of Crsi2 At High Pressures And Temperatures, Weldu Gabrimicael, Ravhi S. Kumar, Andrew Cornelius

Undergraduate Research Opportunities Program (UROP)

It is of extreme importance to develop new potential energy sources to reduce dependence on fossil fuels. As a result of this, the study of thermoelectric materials, capable of changing heat into electrical energy, has become a field of great interest regarding fundamental properties. To help better understand these materials, facilities for the measurement of relevant properties at high pressure have been developed, but lack the ability to characterize the materials at high temperature and pressure. Therefore, this project has the goal of developing a heater arrangement to be used in conjunction with the high pressure capabilities already developed to …

The Role Of Silicon Content On Environmental Degradations Of T91 Steels, Ajit K. Roy, D. Maitra, Pankaj Kumar

Mechanical Engineering Faculty Research

T91 grade steels showed a gradual enhancement in tensile ductility at ambient temperature due to an increase in Si content from 0.5 to 2.0 weight percent (wt.%). However, the ultimate tensile strength was reduced only above 1.5 wt.% Si. The corrosion potential became more active in an acidic solution with increasing temperature. The cracking susceptibility in a similar environment under a slow-strain-rate (SSR) condition was enhanced at higher temperatures showing reduced ductility, time to failure, and true failure stress. Cathodic potentials applied to the test specimens in SSR testing caused an enhanced cracking tendency at 30 and 60°C, suggesting hydrogen …

Tensile Deformation Of A Nickel-Base Alloy At Elevated Temperatures, Ajit K. Roy, Anand Venkatesh, Vikram Marthandam

Mechanical Engineering Faculty Research

The results of tensile testing involving Waspaloy indicate that the failure strain was gradually reduced at temperatures ranging between ambient and 300 °C. Further, serrations were observed in the engineering stress versus strain diagrams in the temperature range of 300-600 °C. The reduced failure strain and the formation of serrations in these temperature regimes could be the result of dynamic strain aging of this alloy. The extent of work hardening due to plastic deformation was reduced at temperatures above 300 °C. A combination of ductile and intergranular brittle failures was seen at temperatures above 600 °C. γ′ was detected at …

An Ultrahigh Vacuum Complementary Metal Oxide Silicon Compatible Nonlithographic System To Fabricate Nanoparticle-Based Devices, Arghya Banerjee, Biswajit Das

Electrical & Computer Engineering Faculty Research

Nanoparticles of metals and semiconductors are promising for the implementation of a variety of photonic and electronic devices with superior performances and new functionalities. However, their successful implementation has been limited due to the lack of appropriate fabrication processes that are suitable for volume manufacturing. The current techniques for the fabrication of nanoparticles either are solution based, thus requiring complex surface passivation, or have severe constraints over the choice of particle size and material. We have developed an ultrahigh vacuum system for the implementation of a complex nanosystem that is flexible and compatible with the silicon integrated circuit process, thus …

Sub-Surface Corrosion Research On Rock Bolt System, Perforated Ss Sheets And Steel Sets For The Yucca Mountain Repository — Quarterly Technical Report No. 14, Dhanesh Chandra, Jaak J.K. Daemen

Publications (YM)

This report shows the work done for this period in accordance to cooperative agreement of University of Nevada system for the Task 019 “Subsurface Corrosion Research on Rock Bolt System, Perforated SS Sheets and Steel Sets for the Yucca Mountain Repository”, the overall objective of which is to conduct corrosion research and predict the durability of rock-bolts and other underground metallic roof supports. We are performing oxidation tests using Thermogravimetric Analyzer (TGA), and Potentiodynamic and immersion tests to determine the corrosion rates of rock bolts. In this quarter specifically we have accomplished the following: Potentiodynamic tests were performed to determine …

A New Method Of Synthesizing Black Birnessite Nanoparticles: From Brown To Black Birnessite With Nanostructures, Shizhi Qian, Marcos A. Cheney, Pradip K. Bhowmik, Sang W. Joo, Wensheng Hou, Joseph M. Okoh

Mechanical Engineering Faculty Research

A new method for preparing black birnessite nanoparticles is introduced. The initial synthesis process resembles the classical McKenzie method of preparing brown birnessite except for slower cooling and closing the system from the ambient air. Subsequent process, including wet-aging at 7◦C for 48 hours, overnight freezing, and lyophilization, is shown to convert the brown birnessite into black birnessite with complex nanomorphology with folded sheets and spirals. Characterization of the product is performed by X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), thermogravimetric analysis (TGA), and N2 adsorption (BET) techniques. Wet-aging and lyophilization times are shown to …

Fundamental And Applied Experimental Investigations Of Corrosion Of Steel By Lbe Under Controlled Conditions: Kinetics, Chemistry Morphology, And Surface Preparation, John Farley, Allen L. Johnson

Transmutation Sciences Materials (TRP)

Advanced nuclear processes and facilities (e.g., transmutation of nuclear waste, fast reactors, and spallation neutron sources) impose special demands on materials, which must withstand high temperatures, high radiation fields, and chemical corrosion. Proposed schemes for transmuting nuclear waste require a nonmoderating coolant such as lead-bismuth eutectic (LBE) or liquid sodium. While LBE corrodes most steels, small amounts of oxygen in the LBE greatly reduces the corrosion rate, and could ideally re-grow a damaged oxide layer in situ. The protective oxide layer would thus be self-healing. However, a fundamental understanding of the role of oxygen and passivating oxide layers is presently …

Effect Of Silicon Content On The Corrosion Resistance And Radiation-Induced Embrittlement Of Materials For Advanced Heavy Liquid Metal Nuclear Systems, Ajit K. Roy

Transmutation Sciences Materials (TRP)

The beneficial effects of Si on both the metallurgical and corrosion properties of Cr-Mo steels have previously been demonstrated at UNLV. Therefore, additions of Si ranging from 0.5-2.0 weight percent (wt%) was attempted in this investigation to explore Si effect on both the high temperature tensile properties and corrosion behavior of T91 grade steel. Corrosion studies in the presence of molten LBE could not be performed due to a lack of proper experimental facilities at UNLV. Therefore, detailed corrosion studies involving Si-containing T91 grade steels were performed in an aggressive aqueous solution of acidic pH. Further, significant efforts have been …

Theoretical Modeling Of Protective Oxide Layer Growth In Non-Isothermal Lead Alloy Coolant Systems, Yitung Chen, Taide Tan, Jinsuo Zhang, Jichun Li

Transmutation Sciences Materials (TRP)

In advanced nuclear energy systems, lead alloys emerge as strong candidates for transmutation and advanced reactor systems as nuclear coolants and spallation neutron targets. However, it is widely recognized that corrosion of materials caused by lead alloys presents a critical barrier to their industrial use. A few experimental research and development projects have been set up by different groups such as at Los Alamos National Laboratory to study the corrosion phenomena in their test facilities and to develop mitigation techniques and materials. One of the central or main techniques under development is to use active control of oxygen thermodynamic activity …

Development Of Nanostructure Based Corrosion-Barrier Coatings On Steel For Transmutation Applications, Biswajit Das

Transmutation Sciences Materials (TRP)

Advanced transmutation systems require structural materials that are able to withstand high neutron fluxes, high thermal cycling, and high resistance to chemical corrosion. The current candidate materials for such structures are ferritic and ferritic-martensitic steels due to their strong resistance to swelling, good microstructural stability under irradiation, and the retention of adequate ductility at typical reactor operating temperatures.

In parallel, lead-bismuth eutectic (LBE) has emerged as a potential spallation target material for efficient production of neutrons, as well as a coolant in the accelerator system. While LBE has excellent properties as a nuclear coolant, it is also highly corrosive to …

Final Report: Phase Stability And Segregation In Alloy 22 Base Metal And Weldments, Jeffrey Lacombe

Publications (YM)

At the outset of this project, the design of the waste disposal containers relied heavily on encasement in a multi-layered container, featuring a corrosion barrier of Alloy 22, a Ni-Cr- Mo-W based alloy with excellent corrosion resistance over a wide range of conditions. The fundamental concern from the perspective of the Yucca Mountain Project, however, was the inherent uncertainty in the (very) long-term stability of the base metal and welds. Should the properties of the selected materials change over the long service life of the waste packages, it was conceivable that the desired performance characteristics (such as corrosion resistance) would …

Interaction Between Metal Fission Products And Triso Coating Materials, Clemens Heske

Fuels Campaign (TRP)

This project focuses on the chemical bonding and interface formation of metal fission products with the coating materials used in tri-isotropic (TRISO) fuel particles for gas-cooled reactors. By combining surface- and bulk-sensitive spectroscopic and microscopic methods, intermediate chemical phases at the interface, intermixing/diffusion behavior, and the electronic interface structure for different coating materials and metals are examined.

In detail, the project studies the interface formation of Pd, Cs, and Ag with SiC and pyrolytic carbon. Using SiC single crystals and highly-ordered pyrolytic carbon (HOPG) as substrates, interfaces are prepared under controlled conditions in an ultra-high vacuum environment and are studied …

Dissolution, Reactor, And Environmental Behavior Of Zro2-Mgo Inert Fuel Matrix, Kenneth Czerwinski

Fuels Campaign (TRP)

This project will examine inert fuels containing ZrO₂ and MgO as the inert matrix. Ceramics with this inert matrix, Ce, U and eventually Pu will be synthesized and examined. While the Advanced Fuel Cycle Initiative focus is on inert fuels with Pu as the fissile component, this task will perform initial laboratory experiments with Ce and U. The initial work with Ce will be performed early in the project with results used as a basis for U studies. Reactor physics calculations will be used to examine suitable quantities of burnable poisons from the candidate elements Gd, Er, or Hf. …

College Of Engineering Senior Design Competition Fall 2007, University Of Nevada, Las Vegas

Fred and Harriet Cox Senior Design Competition Projects

Part of every UNLV engineering student’s academic experience, the senior design project stimulates engineering innovation and entrepreneurship. Each student in their senior year chooses, plans, designs, and prototypes a product in this required element of the curriculum. A capstone to the student’s educational career, the senior design project encourages the student to use everything learned in the engineering program to create a practical, real world solution to an engineering challenge.

The senior design competition helps to focus the senior students in increasing the quality and potential for commercial application for their design projects. Judges from local industry evaluate the projects …

High Temperature Heat Exchanger Project: Quarterly Progress Report July 1, 2007 Through September 30, 2007, Anthony Hechanova

Publications (NSTD)

• Ceramatec Sulfuric Acid Decomposer. The numerical model of a SiC ceramic coupon with two layers of microchannels was developed. Calculations of the factor of safety and probability of failure for the case of a straight channel were performed. Results for a pressure of 7.5 MPa were performed. The thermal and mechanical stress analyses of the Ceramatec HTHX and decomposer were completed.

• Bayonet Heat Exchanger. The thermal and mechanical stress analyses of the bayonet type HTHX and decomposer (Sandia design) were completed. Temperature profiles obtained from thermocouples measured from the Sandia experiments have been applied to the whole packed …