Studies Of The Black Molybdate Conversion Film On Stainless Steel, Jingli Fang, Liuqin Liuqin, Keping Han, Yaohui Chen

Journal of Electrochemistry

A black conversion film was formed on stainless steel with cathodic electrode position method from a molybdate-phosphate solution. This film displayed good themcotability. The results of XPS and AES analysis showed that the thickness of the film was 820 nm and that Mo existed as Mo(Ⅵ) in the surface of the film, while existed as Mo(Ⅵ) and Mo(Ⅳ) in the internal layer of the film. The relative atomic percent content (A.C.% of the film obtained from the elemental composition constant region of the depth profile curves by AES was O 50.9%, Mo 29.4%, P 12.6% and Fe 7.1% respectively. The …

Studies On Low Temperature Performance Of Rechargeable Mh-Ni Batteries, Wenkuan Zhang, Jingxian Shi, Yuwan Lou, Qiusheng Duan

Journal of Electrochemistry

The Dependence of low temperature performance on the alloy composition and electrolyte component for rechargeable MH-Ni batteries is studied, the suitable composition of alloy and electrofyte are founds.

An Indirect Electrochemical Oxidation Of Toluene──Anodic Oxidation Of Mn(Ⅱ) On The Lead Electrode, Zhonghua Wang, Qingmin Hua, Guacai Chen, Zhongquan Wang, Yunan Qiu, Xingguo Yan

Journal of Electrochemistry

The electrochemical oxidation of Mn(Ⅱ) to Mn(Ⅱ) in concentrated H₂SO₄ (2 ~ 8 mol⋅L^-1) at lead electrode has been studied. It is found that the electrode surface is oxidized to PbO₂ in a direct electrochemical reaction, then PbO₂ formed reacts with Mn(Ⅱ) in a chemical reaction. Some effects involves current density, concentration of H₂SO₄, temperature and conversionwere evaluated. The rule of electrogenerated Mn(Ⅲ) in flow electrolysis cell were determined at several conditions. The current efficiency at greater than 90% is obtained in general.

Electrochemically Modified Glassy Carbon Electrode And Determination Of Copper By Anodic Stripping Voltammetry, Jinrui Xu, Yie Liu, Xiurun Zhuang, Tomoo Miwa, Toyohide Takeuchi

Journal of Electrochemistry

This paper reported the glassy carbon electrode modified by cyclic voltammetrybetween -0.1 and +1.5 V (vs. SCE) in an aqueous solution containing catechol, for maldehyde and talium hydroxide. The modified electrode can be applied to the determination of copper(Ⅱ) in water, and its sensitivity is about 35 times higher than that of unmedified glassy carbon electrode, The quantitative limit with this modified electrode is 0.1 ng/ml.

The Reduction Of Oxygen To Hydrogen Peroxide At The Poly(O-Phenylenediamine)-Filmed Electrode, Zhaoe Lu, Tiangeng Zhong, Guanyong Zhang

Journal of Electrochemistry

The poly(o-phenylenediamine) (PPD) filmed graphite electrode was formed by electro-polymerization of o-phenylenediamine in acidified (pH=1) 0.2 mol·L^-1 Na₂SO₄ solution using the cyclic voltammetric methed. The catalytic effect of the electrcareduction of oxygen in acid olution was demonstrated by the voltammogram of the electrode in the oxygen saturated acid solutionof Na₂SO₄. The current efficiency of the reduction of oxygen to hydrogen peroxide was determined by the electrolysis in a divided cell under the condition of constant current. The various effectsinfluencing the accmulation of H₂O₂ in the catholyte were discussed.

Studies On Coordination Behavior Of Dimethyl Sulfoxide In Complex Of Rare Earth With Cryptand, Shichang Liu, Tianpei Zhu

Journal of Electrochemistry

Electrochemical reduction reaction in the course of the titration of Eu(2.2.2) and Eu(2.2) using strong bonding solvent, DMSO, in C₂H₄Cl₂ has been investigated by cyclic voltammetry. The greater the concentration of strong bonding solvent, the more negative the half-wave potentials for the reduction reaction are. The coordination number of Eu(2.2.2) and Eu(2.2) which are 2 and 3 respectively, with DMSO can be calculated, according to the relations between half-wave potentials and the variety of concentration of DMSO.

The Effect Of Some Ions On Cr2O72- Anodic Formation Process At Pt And Pbo2 Electrodes, Shixiong Jin, Zhigang Zhou, Lan Wang

Journal of Electrochemistry

The influence of Ag₂SO₄, Li₂SO₄, Na₂SO₄, K₂SO₄, (NH₄)₂SO₄,MgSO₄ and KF on the evolution of O₂ and the formation of Cr₂O at Pt and PbO₂ anodes was investigated in mixed H₂SO₄-Cr₂(SO₂)₃ solutions. The kinetic data related respectively to Cr₂O formation and O₂ evolution at Pt and PbO₂ anodes were measured by method of resolving the steady-state polarization curve. The Tafel slope …

The Study Of The Growth Processes Of The Oxides On Lead Electrodes In Sulfuric Acid Solution, Hesheng Zhai, Xuguang Chen, Jinkua You, Yong Yang, Zugeng Lin

Journal of Electrochemistry

The growth processes of PbO and PbO₂ on lead electrodes have been investigatedby using in-situ methods that are combined with temporary AC resistance measurment technique and in-situ laser scanning photoelectrochemical microscopy. It is found that a linear relationship existsbetween the electrode resistance(R) and^1/2 after the electrode is oxidized at +0.6 V(vs.Hg/H₂SO₄/35% H₂SO₄) for more than 5 min. This result suggests that the growth of PbO is well distributed during the early stage of oxidation. The study by using laser scanning photoelectrochemical microscopy has further proved this point. The results also …

The Catalytic Behavior For Ni-W Electrode Modified By Carbon Ion Beam Implantion, Jishuang Zhang, Yaojiao Lv, Qinglian Li, Baoen Shen

Journal of Electrochemistry

The hydrogen evolution activity in acidic and basic mediums for Ni-W electrodemodified by carbon ion bean implantation was investigated. The experimental results show thiselectrode has superior catalytic activity for the hydrogen evolution reaction than that of the unmodified Ni-electrode. Long period testing of electrolysis under high current density show that this electrode hasalonger useful life hence it is a practical electrode material. The temperature effect of electrocatalytic property was also inverstigated. The experimental regularities are explained on the basis of the formation of surface multialloys of Ni-W-WC.

Studies Of Elecctrochcmical Oscillation Of Au/Hcl In Presence Of ″Positive Feedback″Of Substrate Electrodes, Bin Ren, Bingwei Mao, Xiongwei Cai, Tao Jiang, Jiqian Mu

Journal of Electrochemistry

/

Transient Photocurrent Behavior Of Multiple Quantum Well Gaas/AlXGa(1-X)As Electrode, Liu Yao, Xurui Xiao, Yuan Lin, Yiping Zeng, Dianzhao Sun, Haiqun Zheng

Journal of Electrochemistry

Transient photocurrents induced by short light pulses at lattice-matched multiplequantum well (MQW)GaAs/Al_0.3)Ga_0.7 As electrodes were studied in the 1 ×10^-2 mol·dm^-3 ferrocene([Fc⁰]/[Fc⁺]=9/1)-0.1 mol·dm^-3 tetrabutylammonium tetrafluoroborate acetonitrile solutionin order to examine the relaxation photoprocesses and to evaluate kinetic parameters of superlattice electrodes.

GaAs/Al_0.3Ca_0.7 As MQW electrode consisting of 10 periods with each of GaAs well (5.3 nm) and Al_0.3Ga_0.7. As barrier (10 nm) showed two pronounced and well-resolved peak structures located at 1.503 eV and 1.699 eV in the photocurrent spectrum, corresponding to the …

Self Assembly Via Layer By Layer Surface Reaction On Gold Electrodes And The Electrochcmical Characterization, Xiandui Dong, Juntao Lu, Chuanxin Cha

Journal of Electrochemistry

The self-assembled monolayers,which were built by spontaneous adsorption of ω-carboxylic acid thiols on gold surface,were used as substrate for further modification through later bylayer amide surface reactions. At each stage of modification,the gold surface was characterizedelectochemieally. The results demonstrated that the strategies of layer by layer self assembly is ofsignificant potential for fabrieating functionalized ultrathin layers.

A Photoelectrochemical Investigation Of Zirconium Oxide Film, Maizhi Yang, Ping Wei, Di Quarto F., Piazza S., Sunseri C.

Journal of Electrochemistry

A photoelectrochemical investigation has been carried out on zirconium initialoxide film and its oxide film grownanodically at constant rate up to different thickness. Both anodicand cathedic photocurrents on the photocurrent spectrum depended on the potential, but had littlerelation with the forming anedic films or measuring solutions. Photocurrent spectrum and photocurrenttransients suggested that the oxide films on zirconium were duplex layers structure. The internal layerwas ZrO₂ and the external layer ZrO₂·(H₂O)_n. The photocurrent included photogenerated carrier ininternal and external oxide films, as well as internal photoinjection process for electrons from thesubstrate metal into the …

Electroreduction Of The Nittobenzene On Titanium Electrode Implanted With Palladium, Zhongda Wu, Xianjun Zhu, Hongsen Wang

Journal of Electrochemistry

The titanium substrates were bombarded with 1×10¹⁷～5×10¹⁷ ions·cm^-2 ofpalladium at the room temperature. The surface composition of implanted electrode and concentration-depth profiles of various elements were measured by AES. The electrored uction processes ofnitrobenzene (NB) in 0.1 mol/L NaOH solution at Pd/Ti electrodes have been investigated by cyclicvoltaivimetry. The results show that the palladium implanted titanium electrodes exhibit a high catalyticactivity in the electroreduction of NB. The NB radical anion, which is the product of one-electronelectroreduction of NB, was detected by ESR in-situ in conjunction with electrochemical methods. Aniline was also detected as a product of …

Electroreduction Of Holmium Ion On Iron Electrde In Molten Cholorides, Qiqin Yang, Guankun Liu, Yuzhi Su

Journal of Electrochemistry

The cyclic voltammetry, open circuit potential-time curve after poteritiostatic electrolysis, current-time curve at potential step, X-ray diffraction and electron probe microanalysiswere used to investigate the electrode process of Ho(Ⅲ) reduced on iron electrode in molten chloridesand the phases of surface alloy layer. The Ho-Fe alloys are formed at first, and then the metallic holmium is deposited when Ho(Ⅲ) is reduced on iron electrode. The charge transfer is reversible. The free energies of formation for the four inter metallic compounds of Ho-Fe system, the diffusion coefficients and diffusion activation energy of Ho in alloyed cathode are determined.

Electrocatalytic Oxidation Of Formaidehyde And Formic Acid On A Pt/SbAd Electrode, Hong Li, Lincai Jiang, Xiong Jiang

Journal of Electrochemistry

The electrocatalytic activity for the oxidation of formaldehyde and formic acid ona Sb-modified platinum (Pt/Sb_ad) was investigated. Results showed that the Pt/Sb_ad electrode was electrocatalytically more active than a Pt electrode in the anodic oxidation of formaldehyde and formicacid. In the case of formaldehyde, an oxidation peak appeared at a potential of ca. 0.7V. During the oxidation of formic acid, a 4-fold increase in the 1st peak current was observed. The Sb-modified platinum electrode was found to be most electrocatalytically active at a coverage of 0.75±0.05. The electrocatalytic activity of the Pt/Sb_ad electrode can be best …

Synthesis Of LiXCoo2 And Its Behaviour In Rechargeable Lithium Battery, Mingfeng Guo, Ruimin Yang, Zebo Zhang, Jincao Ye

Journal of Electrochemistry

The Variations of crystal lattice parameters of Li_xCoO₂ during charge anddischarge have been st ud ied by XRD and AAR spectroscopy. It was found that the Li_xCoO₂ crystalvolume expanded during charge and contracted during discharge. The crystal lattice structure was broken because of the formation of Co₃O₄ when deeply charge.The variation of lattice parameter C₀ value in cycling process was similar to that in charge process.The variation of 006 peak was the mostsensitive in every case. In case of preheating for 20 hours at 700℃ before operating high temperature, the …

Application Of Inhibitor To Improve The Anticorrosion Performance Of Electrophoretic Coating, Changshou Cai, Fangteng Su, Bihuan Liu, Guomou Wen, Jingdong Guo, Renxin Liu, Weidong Tian

Journal of Electrochemistry

To improve the anti-corrosion performance of electrocoating, organic andinorganic inhibitors are applied in an anodic electrophoretic-coating. The results show that the deposition of polymer with zinc phospate exhibits a high inbihition efficiency. The inhibition mechanism of the inhibitor in electrocoating has been studied.

The Electrode Process Of Y(Ⅲ) On Copper Electrode And Its Surface Metallizing, Chungen Zhou, Shuzhen Duan

Journal of Electrochemistry

The reduction of yttrium ion on copper electrode in NaCl-KCl-YCl₃ molten saltshas been investigated. The results indicate that the formation of intermetallic compounds is occuredbefore the metallic yttrium to be formed. The formation of intermetallic compounds is controlled bythe process of which yttrium atoms are diffusing into copper electrode. The kinetic characters todiffusion of yttrium atoms were also discussed.

A Investigation Of Hydrogen-Storage Alloy As Catalytic Electrode For Hydrogenation Of Nitrobenzene, Shigang Lu, Hanxi Yang, Changfa Wan

Journal of Electrochemistry

Since hydrogen-storage alloy ean not only absorb hydrogen atoms to form highlyreactive metal hydride as hydrogen source by electrolysis but also possesses a certain catalytic activityfor hydrogenation,it is thus feasible to utilize the allov as a novel electrode for electrolvtichydrogenation in organic electroreduction. This work employed misch metal AB₅ type alloy as acatalytic electrode and studied the electrochemical hydrogenation of nitrobenzene.

The hydrogen-storage electrode (MH) was a plastic bonded electrode sheet made from a paste of Mm(NiCoMnAl)₅ alloy powder and teflon emulsion. The electrolysis was performed at constantcurrent and controlled potential in a three electrode cell of H-type …

Thermal Characterization Of Carbon Monoxide Oxidation Catalysts Using Thermogravimetric Analysts And Differential Scanning Calorimetry, Rene A. Bartgis

Chemistry & Biochemistry Theses & Dissertations

Catalysts composed of platinum and/or palladium on tin (IV) oxide supports, with and without silica gel, as well as catalysts composed of gold on manganese oxide, have been developed for the recombination of carbon monoxide and oxygen to form carbon dioxide for use in carbon dioxide lasers. A thermogravimetric method and a differential scanning calorimetric method have been developed for the thermal characterization of these catalysts. The mass loss data and the enthalpy changes determined as the catalysts lost water were then related to existing activity data for these catalysts. No relationship was found between the thermal data and the …

The Use Of Thermal Analysis In The Identification And Characterization Of Fibers Of Forensic Interest, Ronald J. Coffey

All-Inclusive List of Electronic Theses and Dissertations

This study investigates the use of thermal analysis for the identification and characterization of fibers for forensic purposes. Fibers such as polyesters, polyacrylics, polypropylenes and nylon were investigated by Differential Thermal Analysis (D.T.A.) and Thermogravimetric Analysis (T.G.A.) to see if their resulting thermograms were characteristic of each fiber. Also, infrared analysis was performed on each fiber. In addition, such factors as heating rate and sample size along with fiber blends were studied as to their effect on thermograms. As a result of this study several important conclusions may be drawn. Although it was found that for the most part D.T.A. …