Full-Text Articles in Mechanics of Materials
Viscoplastic Characterization And Fatigue Modeling Of Titanium Based Metal Matrix Composites, Mark A. Foringer
Viscoplastic Characterization And Fatigue Modeling Of Titanium Based Metal Matrix Composites, Mark A. Foringer
Theses and Dissertations
Viscoplastic characterization and fatigue modeling of titanium-based metal matrix composites was accomplished by combining a unified viscoplastic theory, a nonlinear micromechanics model, and a linear damage accumulation model. First. Ti 15-3 was characterized using the Bodner-Partom viscoplastic theory. A micromechanics model was then employed in a linear damage accumulation fatigue model to predict the fatigue behavior of titanium based composites. The viscoplastic behavior predictions of the micromechanics model were used to eliminate separately defined time dependent terms in the fatigue model. Also, a new linear damage accumulation model was developed from the fatigue behavior of the composite constituents. Finally, it …
Fatigue Behavior Of A Cross-Ply Metal Matrix Composite At Elevated Temperature Under Strain Controlled Mode, Leon B. Dennis
Fatigue Behavior Of A Cross-Ply Metal Matrix Composite At Elevated Temperature Under Strain Controlled Mode, Leon B. Dennis
Theses and Dissertations
This research extends the existing knowledge of cross-ply metal matrix composites (MMC) to include fatigue behavior under strain-controlled fully reversed loading. This study investigated fatigue life, failure modes and damage mechanisms of the SCS-6-Ti-15-3, [O-9O]2s, MMC. The laminate was subjected to fully reversed fatigue at elevated temperature (427° C) at various strain levels. Stress, strain and modulus data were analyzed to characterize the macro-mechanical behavior of the composite. Microscopy and fractography were accomplished to identify and characterize the damage mechanisms at the microscopic level. Failure modes varied according to the maximum applied strain level showing either mixed mode …
Investigation Of Tension-Compression Fatigue Behavior Of A Notched Cross-Ply Metal Matrix Composite At Elevated Temperature, Matthew W. Yocum
Investigation Of Tension-Compression Fatigue Behavior Of A Notched Cross-Ply Metal Matrix Composite At Elevated Temperature, Matthew W. Yocum
Theses and Dissertations
This research extends the existing knowledge of MMC fatigue damage mechanisms by studying the tension-compression fatigue behavior of a notched cross-ply laminate MMC at elevated temperature. A [0-90]2S SCS-6-Ti-15-3 laminate with a center hole was subjected to tension-compression fatigue at 427 °C (800 °F). Stress and strain data was taken to evaluate macro-mechanic behavior of the material. Microscopy and fractography were performed to characterize the damage on a micro-mechanical level. Crack initiation and progression was monitored using acetate face replicas. Four cracks were found to develop around the periphery of the hole, two of which became dominant and proceeded …
Investigation Of Tension-Compression Fatigue Behavior Of A Cross-Ply Metal Matrix Composite At Room And Elevated Temperatures, Elizabeth A. Boyum
Investigation Of Tension-Compression Fatigue Behavior Of A Cross-Ply Metal Matrix Composite At Room And Elevated Temperatures, Elizabeth A. Boyum
Theses and Dissertations
This research, the first load-controlled tension-compression fatigue testing to be performed on a MMC, extends the existing knowledge of MMC fatigue damage mechanisms to include the tension compression loading condition. To accomplish this, a (0/90)2, SCS-6/Ti-15-3 laminate was subjected to tension- tension fatigue at room temperature, and tension-compression fatigue at both room temperature and 427°C. Stress and strain data was taken to evaluate the macro-mechanic behavior of the material. Microscopy and fractography were performed to characterize the damage on a micro-mechanic level. On a maximum applied stress basis, the room temperature tension-tension specimens had longer fatigue lives than the room …
Characterization Of Fatigue Damage In A Metal Matrix Composite (Scs-6/ Ti-15-3) At Elevated Temperature, Brian P. Sanders
Characterization Of Fatigue Damage In A Metal Matrix Composite (Scs-6/ Ti-15-3) At Elevated Temperature, Brian P. Sanders
Theses and Dissertations
The fatigue characteristics of a unidirectional titanium based metal matrix composite (MMC) were investigated at elevated temperature (427°C). A hybrid strain controlled loading mode was used to subject the 0° and 90° laminas to fatigue. Along with the fatigue tests, microscopy and analytical modeling ware also conducted. This combination of activities led to defining the initiation and progression of damage and deformation in the MMC. Hen loading was parallel to the fiber on, the fatigue behavior was initially dominated by creep deformation of the matrix. Then, depending on the maximum strain, specimen failure was the result either fiber fractures or …
Failure Characteristics Of Scs-6/Ti-24al-11nb Composite With A Circular Hole At Room And Elevated Temperatures, Joseph E. Overbeck
Failure Characteristics Of Scs-6/Ti-24al-11nb Composite With A Circular Hole At Room And Elevated Temperatures, Joseph E. Overbeck
Theses and Dissertations
Off-axis loading of eight ply, unidirectional specimens with and without a circular hole determined the ultimate tensile strength of SCS-6/Ti- 24A1-11Nb composite at temperatures of 25°C and 650°C and fiber orientations of 0 degrees, 15 degrees, 45 degrees. Longitudinal moduli of the tested orientations compared closely to the rule of mixtures calculated values, and strengths compared closely to those predicted by the Tsai-Wu failure theory. The small diameter hole does not act as a stress concentrator, but merely reduces the material's strength in proportion to area loss. This result differs from those predicted by linear finite element analysis and orthotropic …
Investigation Of Fatigue Damage Mechanisms In A Metal Matrix Composite Under Elevated Temperature, Barry D. Portner
Investigation Of Fatigue Damage Mechanisms In A Metal Matrix Composite Under Elevated Temperature, Barry D. Portner
Theses and Dissertations
This study investigated the fatigue damage initiation and progression in SCS-6/Ti-15-3 under an environment of fatigue loading at isothermal temperature. This program included two parts. First, an 808 Ultimate Tensile Strength system was set up to accommodate testing at two frequencies of 2.0 and 0.0208 cps at a constant temperature of 427° C. Second, at intervals during the load cycle process, the test specimens were characterized by establishing damage parameters based on changing modulus of elasticity, average strain, strain range, and ultimate tensile strength. Damage progression was documented in the form of failure of the fiber-matrix interface, matrix cracking, fiber …
Investigation Of Damage Mechanisms In A Cross-Ply Metal Matrix Composite Under Thermo-Mechanical Loading, Joel J. Schubbe
Investigation Of Damage Mechanisms In A Cross-Ply Metal Matrix Composite Under Thermo-Mechanical Loading, Joel J. Schubbe
Theses and Dissertations
Metal matrix composites (MMCs) are rapidly becoming strong candidates for high temperature and high stiffness structural applications such as the Advanced Tactical Fighter (ATF). This study systematically investigated the failure modes and associated damage in a cross-ply, [0/90]2s SCS6/Ti-15-3 metal matrix composite under in-phase and out-of-phase thermomechanic fatigue. Initiation and progression of fatigue damage were recorded and correlated to changes in Young's Modulus of the composite material. Experimental results show an internal stabilization of reaction zone size but degradation and separation from constituent materials under extended cyclic thermal loading. Critical to damage were transverse cracks initiating in the 90° …