Full-Text Articles in Polymer Science

Preparation Of Styrene Acrylic Copolymer Toner Resin By Solution Polymerization., Neo Su Siang Apr 2010

Preparation Of Styrene Acrylic Copolymer Toner Resin By Solution Polymerization., Neo Su Siang

Student Works (2010-2019)

This project has investigated solution polymerization to produce toner resins. There are three stages: (i) synthesis of low molecular weight styrene acrylic copolymer; (ii) synthesis of high molecular weight styrene acrylic copolymer; (iii) mixing high and low molecular weight copolymers. Gel Permeation Chromatography (GPC) was used to study molecular weight distributions, Melt Flow Index (MFI) Instrument to study the flowability of resin, Differential Scanning Calorimetry (DSC) to study the thermal properties of resin, and acid number to quantitate the amount of acidic group in the resin. A comparison of properties between the experimental samples, patent’s claims, and commercial resins had …

Go to article

Synthesis Of Urethane Acrylate Macromer From Palm Oil-Based Polyol And Its Application As A Resin For Dental Composite., Fadhel A. A. Alsanabani Jan 2010

Synthesis Of Urethane Acrylate Macromer From Palm Oil-Based Polyol And Its Application As A Resin For Dental Composite., Fadhel A. A. Alsanabani

Student Works (2010-2019)

A slightly branched urethane acrylate macromer (UAM) was synthesized by reacting palm oil-based polyol with excess amounts of polymeric methylene diphenyl diisocyanate (MDI) to form urethane prepolymer, then reacted with 2-hydroxyethyl methacrylate (HEMA) and FT-IR spectroscopy confirmed the urethane and grafted acrylate groups. 0.2% by weight of camphoroquinone (CQ) and 0.8% by weight of ethyl-4-N,N-dimethylamino-benzoate (4EDMAB) by weight were added to render the experimental resins light-curable. Their viscosity, percentage of degree of conversion (%DC) and cross-linking density (CLD), percentage of volumetric polymerization shrinkage (%VPS), water sorption and solubility, flexural strength, modulus of elasticity and toughness were determined and compared to …

Go to article

Thermo-Electrical And Mechanical Studies On Polymer-Organically Modified Montmorillonite Composite., Norhana Abdul Halim Jan 2010

Thermo-Electrical And Mechanical Studies On Polymer-Organically Modified Montmorillonite Composite., Norhana Abdul Halim

Student Works (2010-2019)

The field of polymer-nanoclay composite has attracted a lot of attention in materials studies due to the dramatic improvement on polymers characteristics. For example mechanical and thermal properties, chemical resistance as well as the reduced gas permeability. However, structural changes and the mechanisms that may contribute to these improvements are not fully understood. In this work, the study on polymer nanoclay composite concentrates on the effects of OMON inclusion within different polymer matrix systems. The matrixes are a series of natural rubbers (Standard Malaysia Rubber – Latex grade (SMRL); Deproteinized Natural Rubber (DPNR) and Epoxidized Natural Rubber (ENR-50)), plasticized Polyvinyl …

Go to article

Characteristics Of Proton Conducting Pva-Chitosan Polymer Blend Electrolytes., Mohd Fakhrul Zamani Abdul Kadir Jan 2010

Characteristics Of Proton Conducting Pva-Chitosan Polymer Blend Electrolytes., Mohd Fakhrul Zamani Abdul Kadir

Student Works (2010-2019)

The main focus of this present work is to build a good conducting solid polymer electrolyte (SPE) based on chitosan and poly(vinyl alcohol)(PVA) blend. Solution cast technique has been employed to produce sample films in this work. From the scanning electron micrographs (SEM) the surface morphology of the blend containing 40 wt.% chitosan and 60 wt.% PVA (C4P6) is homogenous and miscible in one and another. The C4P6 film is the most amorphous and is the best candidate for the polymer host in the electrolyte systems studied in the present work. Ammonium Nitrate (NH4NO3) is the doping salt that provides …

Go to article

Synthesis Of Chromium-Based Ziegler-Natta Catalysts And Thier Application In Ethylene Polymerization And Copolymerization., Wong Jun Xuan Jan 2010

Synthesis Of Chromium-Based Ziegler-Natta Catalysts And Thier Application In Ethylene Polymerization And Copolymerization., Wong Jun Xuan

Student Works (2010-2019)

Four chromium-based oxo-trinuclear carboxylate complexes were prepared by reacting Cr(NO3).9H2O with acetic acid and substituted carboxylic acids to produce [Cr3O(CH3COO)6.3H2O]NO3.7H2O,[Cr3O(ClCH2COO)6.3H2O]NO3.3H2O, [Cr3O(Cl2CHCOO)6.3H2O]NO3.H2O and [Cr3O(Cl3CCOO)6.3H2O]NO3.2H2O, which alysis (TGA).Chromium content in each complex was determined by titrimetry method and the result was in good agreement with that from TGA. Chromium(III)monochloroacetate complex[Cr3O(ClCH2COO)6.3H2O]NO3.3H2O in combination with diethylaluminium chloride formed heterogeneous catalyst system for ethylene polymerization and ethylene-propylene copolymerization. Both Al/Cr ratio and temperature influenced the catalytic activity. The maximum activity of ethylene polymerization was 1768 gPE/gCr/hr/atm, achieved by polymerizing ethylene at 29°C with Al/Cr ratio 30.8. Effect of chloro-substituent groups on carboxylic ligand was studied …

Go to article

Electrical And Structural Studies Of Polyacrylonitrile (Pan) Complexed With Inorganic Salts., Khairul Bahiyah Md Isa Jan 2010

Electrical And Structural Studies Of Polyacrylonitrile (Pan) Complexed With Inorganic Salts., Khairul Bahiyah Md Isa

Student Works (2010-2019)

In the present study, polymer electrolyte films composed of polyacrylonitrile (PAN) as a host polymer, ethylene carbonate (EC) as the plasticizer and lithium triflate (LiCF3SO3) and sodium triflate (NaCF3SO3) as dopant salts were prepared by the solution cast technique. Five systems of polymer electrolytes films have been prepared; these systems are the plasticized-PAN system i.e. PAN-EC system, two salted-PAN systems i.e. PAN-LiCF3SO3 and PAN-NaCF3SO3, and two plasticized-salted PAN systems i.e. PAN-EC-LiCF3SO3 and PAN-EC-NaCF3SO3. The pure PAN film was prepared as a reference. The ionic conductivity for each system is characterized using impedance spectroscopy. The room temperature conductivity of the pure …