Investigation Into Contact Resistance And Damage Of Metal Contacts Used In Rf-Mems Switches, Kevin W. Gilbert

Theses and Dissertations

This research examines the physical and electrical processes involved in lifecycle failure of Microelectromechanical (MEMS) Radio-Frequency (RF) cantilever beam ohmic contact switches. Failures of these switches generally occur at the contact, but complete details of performance of microcontacts are difficult to measure and have not been previously reported. This study investigated the mechanics of microcontact behavior by designing and constructing a novel experimental setup. Three representative contact materials of varying microstructure (Au, Au5%Ru, Au4%V₂O₅) were tested and parameters of contact during cycling were measured. The Au4%V₂O₅, a dispersion strengthened material developed at …

Fatigue Behavior Of An Advanced Sic/Sic Composite At Elevated Temperature In Air And In Steam, Devon T. Christensen

Theses and Dissertations

The fatigue behavior of an advanced Silicon Carbide/Silicon Carbide (SiC/SiC) ceramic matrix composite (CMC) was investigated at 1200 ˚C in laboratory air and in steam environments. The composite consisted of a SiC matrix reinforced with Boron Nitride (BN) coated Hi-Nicalon fibers woven into eight-harness-satin (8HS) weave plies. Tensile stress-strain behavior and tensile properties were also evaluated at 1200 ˚C. Tension-tension fatigue tests were conducted in both laboratory air and in steam at 1200 ˚C at frequencies of 0.1 Hz, 1.0 Hz, and 10 Hz. The tension-tension fatigue tests had a ratio of minimum stress to maximum stress of R = …

Effects Of Delamination On Composite Sandwich Structures Under Static And Fatigue Loading, Eugene Everett Eswonia

Master's Theses

This thesis will present the experimental and numerical analysis of composite sandwich structures under monotonic and fatigue loading. The sandwich skins were made of fiberglass and the core used was a closed cell PVC foam. Initial delaminations were introduced into the sandwich structures during manufacturing to see the effect of delamination size on the ultimate strength and monotonic fracture. Fiberglass rods, called shear keys, added to the foam core to determine whether or not they increased the strength of the test specimens. Furthermore, shear key locations were also varied and their effects noted. The fixed rate static behavior for all …

An Analytical Investigation Of Natural Frequency For A Symmetric Composite Box-Beam With Thermal Effects, Lakshmi Narayana Sanjeev Chitikela

Master's Theses - Daytona Beach

The main purpose of the following analysis is to develop an analytical method for determining the natural frequency of a symmetric composite box-beam subjected to temperature gradient. A set of coupled partial differential equations of motion is obtained by means of small defection theory and D'Alembert's method. The Smith and Chopra stiffness matrix is used in the governing equations of motion and an appropriate MATLAB® code has been written to solve for the stiffness matrix elements of the box-beam. The resulting governing equations of motion are solved to obtain the natural frequencies of the box-beam in flap and lag directions …

Compression After Impact Load Prediction In Graphite/Epoxy Laminates Using Acoustic Emission And Artificial Neural Networks, Anthony Michael Gunasekera

Master's Theses - Daytona Beach

The purpose of this research was to investigate the effectiveness of artificial neural networks (ANNs) in predicting the compression after impact (CAI) load of graphite/epoxy laminates from acoustic emission (AE) nondestructive testing (NDT) data. Thirty-four 24-ply bidirectional woven cloth laminate coupons were constructed and impacted at various energy levels ranging from 8 to 20 Joules, generating barely visible impact damage (BVID). Acoustic emission data were acquired as the coupons were compressed to failure. Not having been analyzed by previous experimenters, several noise tests were also performed to determine the impact of external noise on acoustic emission data during testing. Once …

Application Of Systems Engineering To Rapid Prototyping For Close Air Support, John M. Colombi, Richard G. Cobb

Faculty Publications

Twenty-first century military operations have brought forth many new challenges for the Armed Forces of the United States. One such challenge is with new operating environments, where current systems are not always effective. While it is desirable to apply a systems engineering approach to best meet critical user needs, there may be a misconception that systems engineering requires a lengthy and detailed process not nimble enough for a rapid prototyping effort. This article describes how a classic systems engineering methodology was successfully tailored to the rapid development of potential material solutions to meet a critical operational need. Key observations are …

Developing Abrasion Test Standards For Evaluating Lunar Construction Materials, Ryan L. Kobrick, David M. Klaus, Kenneth W. Street

Publications

Operational issues encountered by Apollo astronauts relating to lunar dust were catalogued, including material abrasion that resulted in scratches and wear on spacesuit components, ultimately impacting visibility, joint mobility and pressure retention. Standard methods are being developed to measure abrasive wear on candidate construction materials to be used for spacesuits, spacecraft, and robotics. Calibration tests were conducted using a standard diamond stylus scratch tip on the common spacecraft structure aluminum, Al 6061-T6. Custom tips were fabricated from terrestrial counterparts of lunar minerals for scratching Al 6061-T6 and comparing to standard diamond scratches. Considerations are offered for how to apply standards …

An Intelligible Software (Cfa) Approach For Fiber-Reinforced Laminate Failure Analysis Including A Piecewise Representation Of The Tsai-Wu Failure Criterion Using Excel And Matlab, Ryan C. Schmidt

Master's Theses - Daytona Beach

Present generations rely heavily on the use of petroleum as their primary means of transportation. As the cost of petroleum continues to escalate, the need for lightweight structures for vehicle applications becomes more evident. The ability to engineer materials so that they possess desired application specific properties and characteristics has made tremendous progress in the past century. Consequently, the use of these composite materials for aircraft weight reduction has been investigated for decades.

The aerospace industry often uses composite materials to make a laminated composite structure where each constituent ply of the laminate has its own material properties. This anisotropic …

Multidisciplinary Design Optimization Of An Extreme Aspect Ratio Hale Uav, Bryan J. Morrisey

Master's Theses

ABSTRACT

Multidisciplinary Design Optimization of an Extreme Aspect Ratio HALE UAV

Bryan J. Morrisey

Development of High Altitude Long Endurance (HALE) aircraft systems is part of a vision for a low cost communications/surveillance capability. Applications of a multi payload aircraft operating for extended periods at stratospheric altitudes span military and civil genres and support battlefield operations, communications, atmospheric or agricultural monitoring, surveillance, and other disciplines that may currently require satellite-based infrastructure. Presently, several development efforts are underway in this field, including a project sponsored by DARPA that aims at producing an aircraft that can sustain flight for multiple years and …

An Investigation Of E-Glass Structure With Different Filler Material Under Vibration And Bending Loading, John R. Parra

Master's Theses

Although fiberglass reinforced polyester manholes and wetwalls have been proven by the American Society for Testing Materials (ASTM) and are currently being used in some parts of the world, there still exists a lack of investigation for testing manhole covers made with different inorganic fillers under static and dynamic behavior. The filler would not only improve the mechanical properties of fiber-reinforced polymer matrix composite not otherwise achieved by the resin ingredients alone but also lower the overall manufacturing costs by decreasing the amount of fiber content without adversely affecting the composite’s mechanical properties. The main objective involved the development of …

Design Of A "Figure-8" Spherical Motion Flapping Wing For Miniature Uav's, Zohaib Parvaiz Rehmat

UNLV Theses, Dissertations, Professional Papers, and Capstones

Hummingbirds and some insects exhibit a Figure-8 motion, which allows them to undergo variety of maneuvers including hovering. It is therefore desirable to have flapping wing miniature air vehicles (FWMAV) that can replicate this unique wing motion. In this research, a design of a flapping wing for FWMAV that can mimic Figure-8 motion using a spherical four bar mechanism is presented. To produce Figure-8 motion, the wing is attached to the coupler point of the spherical four bar mechanism and driven by a DC servo motor. For verification of the design, a prototype of the wing and mechanism is fabricated …

Development Of A New Mixed Mode I-Ii-Iii Delamination Toughness Test, Ruben Hortensius

Renée Crown University Honors Thesis Projects - All

Optimal use of laminated composite materials can only be achieved if its most common failure mechanisms are well understood. One of the most common modes of failure in laminates is delamination, or the separation of adjacent material layers. Therefore, there is a need to be able to predict a laminated composite’s resistance to delamination growth due to the complex real-world application loadings that it may experience. These complex loadings are made up of three primary modes of delamination growth, known as modes I, II, and III. Test fixtures for a new mixed mode I-II-III delamination toughness test were designed, built, …

Design And Fabrication Of A Small Prototype Airframe Structure, Kimberly Lynn Clark

UNLV Theses, Dissertations, Professional Papers, and Capstones

This project called for a first-generation prototype aircraft with hovering capabilities that was lightweight. The focus of this study was to design a small low-cost prototype composite airframe that meets specified requirements, analyze structures using finite element analysis and mechanical testing, and construct a prototype using proven composite manufacturing techniques. One fuselage, one wing, and several engine nacelles were designed and fabricated. Several design and fabrication methods and materials were analyzed, with focus given to the nacelles, and recommendations were provided for the manufacture of the first generation airframe based on time, weight, and cost.

The Effect Of The Fastener Of Different Configuration Composite Panels On Failure Analysis, Robert Austin

Master's Theses

This study presents the effect of the stacking sequence and fiber orientation on a composite sandwich panel subjected to static in-plane bolt loading. Six plates were constructed with laminates of unidirectional carbon fiber and cross ply weaves of fiberglass. The orientations that were examined included 0, +/- 45, and 90 degrees. Half of the plates had fiberglass lamina on the outside of the laminate while the other three plates had the carbon fiber on the outside. Experimental and analytical tests were performed to determine the best orientations and stacking sequence.

For the numerical analysis, plates with fibers oriented at +/- …

Multiscale Modeling Of Impact On Heterogeneous Viscoelastic Solids With Evolving Microcracks, Flavio V. Souza

Department of Engineering Mechanics: Dissertations, Theses, and Student Research

Multiscale computational techniques play a major role in solving problems related to viscoelastic composite materials due to the complexities inherent to these materials. In the present work, a numerical procedure for multiscale modeling of impact on heterogeneous viscoelastic solids containing evolving microcracks is proposed in which the (global scale) homogenized viscoelastic incremental constitutive equations have the same form as the local scale viscoelastic incremental constitutive equations, but the homogenized tangent constitutive tensor and the homogenized incremental history dependent stress tensor depend on the amount of damage accumulated at the local scale. Furthermore, the developed technique allows the computation of the …

Effect Of Steam Environment On Creep Behavior Of Nextel720/Alumina-Mullite Ceramic Matrix Composite At Elevated Temperature, Tolga Kutsal

Theses and Dissertations

The tensile creep behavior of an oxide-oxide ceramic matrix composite (CMC) was investigated at 1000 and 1100° C in laboratory air and steam. The oxide-oxide CMC studied in this research was Nextel™ 720/alumina-mullite (N720/AM). The composite consists of N720/fibers with 0°/90° fiber orientation and a porous alumina-mullite matrix. Tensile-strain behavior was investigated and tensile properties measured at 900, 1000 and 1100° C. The effect of loading rate on tensile properties of N720/AM ceramic matrix composite at 1100° C in steam was also examined. Creep-rupture tests were performed at 1100° C in laboratory air and steam, and at 1000° C only …

Predicting Solar Protons: A Statistical Approach, Jonathan C. Spaulding

Theses and Dissertations

A small fraction of solar flares are accompanied by high energy (>10 MeV) protons. These events can cause degradation or failure of satellite systems and can be harmful to humans in space or in high altitude flight. For risk management purposes, the Air Force is interested in predicting these events. Several algorithms exist to do this operationally, but none predict when these events will occur with much accuracy. Here, we analyzed 3610 M1 and greater flares including 106 with proton events from the GOES sensors from 1 Jan 1986 to 31 Dec 2004 to produce new results, including a …

Non-Destructive Evaluation Of Aerospace Composites, Jeremy D. Johnson

Theses and Dissertations

Five methods of non-destructive material evaluation (NDE) were used to inspect various forms of damage commonly found in aerospace fiberglass composites: voids, edge and sub-surface delaminations, surface burning, and cracking. The images produced by X-ray, X-ray Computed Tomography, terahertz (THz) imaging, ultrasound, and flash IR thermography were analyzed for the detection of defects. Test results and analysis of each NDE method's capabilities provide a comparison study of conventional techniques versus the emerging technology of THz imaging for the non-destructive evaluation of aerospace composite materials. A comparison guide to the five methods' damage detection effectiveness for fiberglass composites is provided by …

Fatigue Evaluation Of Nanocomposites As Lightweight Electronic Enclosures For Satellites' Applications, Javier Rodriguez

Theses and Dissertations

Existing nanocomposite materials used for satellite applications don't offer the required conductivity and electromagnetic shielding protection, requiring metal shields in order to survive in space. The AFRL Materials and Manufacturing Directorate in conjunction with the private sector have developed a material that promises to blend the attributes of nanocomposites and metal materials. The M55J/RS3 material consists of carbon fibers combined with a polyisocyanate matrix, in which Nickel nanostrands^TM are added. The research effort investigated the changes in the EMI and ESD of the material after being subjected to cyclic loads. Four configurations of a symmetric layup with fibers oriented …

Creep And Fatigue Interaction Characteristics Of Pwa1484, Christian J. Pierce

Theses and Dissertations

One of the main methods for predicting the service life of jet engine turbine blades is through creep analysis. A sample of the turbine blade material will be mechanically tested to characterize its creep performance. This characterization will be used to determine safe operating conditions for the material. While methods for modeling creep behavior are generally well developed, this constant load creep testing does not fully represent the loading conditions present in a jet engine due to cyclic loading caused by the mission profile and throttle movements. As the industry seeks to become more accurate in physics based modeling of …

Effects Of Environment On Creep Behavior Of Nextel720/Alumina-Mullite Ceramic Composite With ±45º Fiber Orientation At 1200ºc, Muzaffer Ozer

Theses and Dissertations

The present effort will investigate the off-axis creep behavior of the Nexte720/Alumina-Mullite CMC, a material system which relies on a porous alumina/mullite matrix for damage tolerance as compared to the pure alumina matrix in earlier studies. This research evaluated the creep behavior of N720/AM with a ± 45° fiber orientation at 1200°C in: laboratory air, steam, and argon environments. Creep-rupture tests at the creep stress levels of: 32, 30, 26, and 20 MPa were conducted in each environment. Additionally 35 MPa stress level examined in air and 13 MPa stress level examined both in air and steam. The N720/AM with …

Electrostatic Discharge Properties Of Irradiated Nanocomposites, Joshua D. Mcgary

Theses and Dissertations

Modernization in space systems requires employment of new light-weight, high performance composite materials that reduce bulk weight and increase structural integrity. This thesis explored the behavior of one such material prior to and following a 35-year simulated space radiation life-cycle. Select electrical properties of nickel nanostrand^TM-carbon composites in seven configurations were characterized prior to electron irradiation via surface and bulk resistivity measurements and contact electrostatic discharge (ESD) measurements. Following irradiation at a fluence of 10¹⁶ e^-/cm² at an average energy of 500 keV, measurements were repeated and compared against pre-irradiation data. Configuration D is …