Static And Fatigue Failure Response Of Woven Carbon Fiber Specimens With Double Edge Notches, Ahmad J. Amini

Master's Theses

Carbon fiber composites are continually seeing increased use in aerospace applications. It is necessary to understand their failure modes in order to properly design and perform analysis on structures constructed primarily from them. This thesis studies woven carbon fiber composites with and without double-edge notches in a series of static and fatigue tests performed on an Instron 8801 servo-hydraulic testing system.

Specimens were constructed of Advanced Composites Group product # LTM45EL woven carbon fiber pre-preg/epoxy and were cut to approximately 9-inch in length and 1-inch in width. Notches were cut into some of the specimens using a slitting saw blade …

The Effectiveness Of Damage Arrestment Devices In Delaying Fastener-Hole Interaction Failures In Carbon Fiber Polyurethane Foam Composite Sandwich Panels Subjected To Static And Dynamic Loading Under Increased Temperatures, Dominic E. Surano

Master's Theses

A study was conducted to investigate simple, cost-effective manufacturing techniques to delay skin-core delamination, micro-buckling and bearing stress failures resulting from fastener-hole interactions. Composite sandwich panels, with and without damage arrestment devices (DADs), were subjected to monotonic compression at a rate of 5mm per second, and compression-compression fatigue at 50% yield at an amplitude of 65%, under temperatures of 75, 100, 125, 150, 175, and 200 °F.

The sandwiches tested were composed of two-layer cross-weave carbon fiber facesheets, a polyurethane foam core, and an epoxy film adhesive to join the two materials. The most successful method to delay the aforementioned …

An Investigation Of Damage Arrestment Devices Application With Fastener/Hole Interaction, Richard Vincent S. Balatbat

Master's Theses

This thesis presents a parametric study on the effects of how damage arrestment devices application interacts with a fastener in a composite sandwich panel. The primary objective of the damage arrestment device was to prevent the failure of the composite face sheet, such as crack propagation, around the hole/fastener joint. The damage arrestment devices are made of composite strips that are inserted under the face sheet to increase the overall structural strength of the panel and to prevent the propagation of failure along the hole. This was supposed to be a quicker and stronger alternative to potted inserts for composite …

Effects Of Delamination On Composite Sandwich Structures Under Static And Fatigue Loading, Eugene Everett Eswonia

Master's Theses

This thesis will present the experimental and numerical analysis of composite sandwich structures under monotonic and fatigue loading. The sandwich skins were made of fiberglass and the core used was a closed cell PVC foam. Initial delaminations were introduced into the sandwich structures during manufacturing to see the effect of delamination size on the ultimate strength and monotonic fracture. Fiberglass rods, called shear keys, added to the foam core to determine whether or not they increased the strength of the test specimens. Furthermore, shear key locations were also varied and their effects noted. The fixed rate static behavior for all …

Multidisciplinary Design Optimization Of An Extreme Aspect Ratio Hale Uav, Bryan J. Morrisey

Master's Theses

ABSTRACT

Multidisciplinary Design Optimization of an Extreme Aspect Ratio HALE UAV

Bryan J. Morrisey

Development of High Altitude Long Endurance (HALE) aircraft systems is part of a vision for a low cost communications/surveillance capability. Applications of a multi payload aircraft operating for extended periods at stratospheric altitudes span military and civil genres and support battlefield operations, communications, atmospheric or agricultural monitoring, surveillance, and other disciplines that may currently require satellite-based infrastructure. Presently, several development efforts are underway in this field, including a project sponsored by DARPA that aims at producing an aircraft that can sustain flight for multiple years and …

An Investigation Of E-Glass Structure With Different Filler Material Under Vibration And Bending Loading, John R. Parra

Master's Theses

Although fiberglass reinforced polyester manholes and wetwalls have been proven by the American Society for Testing Materials (ASTM) and are currently being used in some parts of the world, there still exists a lack of investigation for testing manhole covers made with different inorganic fillers under static and dynamic behavior. The filler would not only improve the mechanical properties of fiber-reinforced polymer matrix composite not otherwise achieved by the resin ingredients alone but also lower the overall manufacturing costs by decreasing the amount of fiber content without adversely affecting the composite’s mechanical properties. The main objective involved the development of …

The Effect Of The Fastener Of Different Configuration Composite Panels On Failure Analysis, Robert Austin

Master's Theses

This study presents the effect of the stacking sequence and fiber orientation on a composite sandwich panel subjected to static in-plane bolt loading. Six plates were constructed with laminates of unidirectional carbon fiber and cross ply weaves of fiberglass. The orientations that were examined included 0, +/- 45, and 90 degrees. Half of the plates had fiberglass lamina on the outside of the laminate while the other three plates had the carbon fiber on the outside. Experimental and analytical tests were performed to determine the best orientations and stacking sequence.

For the numerical analysis, plates with fibers oriented at +/- …