Damage Initiation Of 15v38 Steel Bar During Square-To-Round Hot Rolling Process, Siva Sai Krishna Dasari, Henry Adekola Haffner, K. Chandrashekhara, Mario F. Buchley, Simon N. Lekakh, Ronald J. O'Malley

Mechanical and Aerospace Engineering Faculty Research & Creative Works

Hot rolling processes have been extensively used to produce round bars by reducing the cross-sectional area of continuously cast steel. The current trend toward increasing productivity often requires a more aggressive reduction per pass. Establishing safe and optimized hot rolling parameters must be determined to avoid damage while deforming the specific steel composition. Understanding the damage mechanism during the metal forming process is vital for product quality. Herein, a combined experimental and simulation approach is developed to track the evolution potential damage during hot bar rolling. Hot tension tests are conducted on as-cast vanadium micro alloyed 15V38 steel at different …

Oxidation Of Additively Manufactured Zrb2–Sic In Air And In Co2 At 700–1000 °C, Marharyta Lakusta, Nicholas M. Timme, Abid H. Rafi, Jeremy Lee Watts, M. (Ming) C. (Chuan) Leu, Gregory E. Hilmas, William G. Fahrenholtz, David W. Lipke

Materials Science and Engineering Faculty Research & Creative Works

Oxidation behavior of additively manufactured zrb2–sic in air and in co2 is reported in the temperature range of 700–1000 °c. Observed scale morphologies in air and in co2 were similar, featuring an outer borosilicate layer and an inner porous zirconia layer containing partially oxidized silicon carbide particles and remnant borosilicate products. Oxide scale thicknesses and parabolic scaling constants in air were approximately twice those observed in co2 across all studied temperatures. Activation energies for oxidation of 140 ± 20 kj/mol in air and 110 ± 20 kj/mol in co2 were determined, indicating similar diffusion processes that appear to be rate-limiting. …

Impact Of Quenching Intensity Conditions On Using A Finite Element Model To Investigate The Microstructure And Hardenability Of Low-Alloy Steel, J. S. Alabi, E. Heidari, M. F. Buchely, K. Chandrashekhara, S. N. Lekakh, R. J. O'Malley, V. Athavale, A. Kumar

Materials Science and Engineering Faculty Research & Creative Works

Quenching is one of the primary processes to improve mechanical properties in steels, particularly hardness. Quenching is well established for different geometries of individually treated steel components; while in-steam quenching of large diameter continuously cast steel bar has several specific features which are difficult and costly to experimentally optimize. The end-quench Jominy test has been used extensively to study the hardenability of different steel grades. Different numerical, analytical, and empirical models have been developed to simulate the Jominy process and to understand quenching of steels. However, it is not straight forward to translate experimental data from Jominy test on instream …

Kinetic Modeling Of Electrostatic Sieving For Lunar Regolith Beneficiation: Case Studies, Easton Ingram, Emmanuela Amen Eze, Jeffrey Smith, Fateme Rezaei, David Bayless, William Schonberg, Daoru Han

Materials Science and Engineering Faculty Research & Creative Works

A new kinetic particle modeling framework was developed to investigate electrostatic transport of lunar regolith particles with applications to the concept of electrostatic sieving. the new approach is based on kinetic particle dynamics and includes major modules of sampling the particle size distribution, solving electric fields, and tracking motion of charged dust grains. Case studies for a concept of electrostatic sieving were chosen to validate the new model. the simulation achieved similar yields reported in previous works, which served as validation of the model. the new model is computationally efficient and could serve as a design, analysis, and optimization tool.

Impact Of Quenching Intensity Conditions On Using A Finite Element Model To Investigate The Microstructure And Hardenability Of Low-Alloy Steel, J. S. Alabi, E. Heidari, M. F. Buchely, K. Chandrashekhara, S. N. Lekakh, R. J. O'Malley, V. Athavale, A. Kumar

Materials Science and Engineering Faculty Research & Creative Works

Quenching is one of the primary processes to improve mechanical properties in steels, particularly hardness. Quenching is well established for different geometries of individually treated steel components; while in-steam quenching of large diameter continuously cast steel bar has several specific features which are difficult and costly to experimentally optimize. the end-quench Jominy test has been used extensively to study the hardenability of different steel grades. Different numerical, analytical, and empirical models have been developed to simulate the Jominy process and to understand quenching of steels. However, it is not straight forward to translate experimental data from Jominy test on instream …

Machine Learning-Assisted Multiscale Simulation And Design Optimization Of Composite Jackets Under Low-Velocity Impacts, Masoud Mohammadi

Graduate Theses, Dissertations, and Problem Reports (ETD)

This research presents the development of a data-driven machine learning-assisted approach to simulate and optimize the design of composite materials subjected to low-velocity impacts. It focuses on a specific type of hybrid composite comprised of fiberglass and Kevlar fabrics stitched with Kevlar threads. The study begins by creating a multiscale finite element simulation for the composite under a low-velocity impact, which operates across three scales: microscale, mesoscale, and macroscale. This simulation accepts various inputs, such as different layer configurations and orientations, and provides impact outputs including maximum load and energy absorption capacity and displacement at failure.

Python and MATLAB scripts …

Molecular Modeling Of Phenolic Resin For Carbon-Carbon Composites, Ivan Gallegos

Dissertations, Master's Theses and Master's Reports

One of the most difficult challenges associated with space exploration is terrestrial atmospheric reentry due to the high thermal loads generated. Carbon carbon (C/C) composites have been used as heat shielding materials due to their high strengthto- weight ratio and thermal properties and their applications include heat shielding for various high temperature environments. C/C composites are manufactured by polymer-infiltration pyrolysis (PIP) via cycles of curing and pyrolysis of a prepreg which can be costly and take up to several days. Thus, C/C composites ideal candidates for computationally-driven optimization techniques, such as a multiscale Integrated Computational Materials Engineering (ICME) approach, by …

Cfrp Delamination Density Propagation Analysis By Magnetostriction Theory, Brandon Eugene Williams

All Dissertations

While Carbon Fiber Reinforced Polymers (CFRPs) have exceptional mechanical properties concerning their overall weight, their failure profile in demanding high-stress environments raises reliability concerns in structural applications. Two crucial limiting factors in CFRP reliability are low-strain material degradation and low fracture toughness. Due to CFRP’s low strain degradation characteristics, a wide variety of interlaminar damage can be sustained without any appreciable change to the physical structure itself. This damage suffered by the energy transfer from high- stress levels appears in the form of microporosity, crazes, microcracks, and delamination in the matrix material before any severe laminate damage is observed. This …

Implementation Of Experimental Static Recrystallization Of High Strength Steel Into Computational Simulation Of Multi-Pass Slab Hot Rolling, S. K. Dasari, S. Ganguly, A. Abutunis, K. Chandrashekhara, M. F. Buchely, S. N. Lekakh, R. J. O'Malley, T. Natarajan

Mechanical and Aerospace Engineering Faculty Research & Creative Works

Microstructural changes and softening due to static recrystallization have a critical influence on thermo-mechanical behavior of high strength steels during industrial multi-pass hot rolling. Numerical simulation using finite element analysis (FEA) can be used to accurately predict the softening behavior during the hot rolling process. Therefore, the implementation of an experimentally defined static recrystallization model into FEA is necessary to get realistic simulation prediction. in this study, the extent of softening during static recrystallization in Si and Mn alloyed high strength steel was measured using double hit tests. a Gleeble™ thermo-mechanical simulator was used to perform the double hit tests …

Interfacial Thermomechanical Behavior Of Hybrid Carbon Fibers, Sriraj Srihari

Doctoral Dissertations and Master's Theses

The carbon fiber/epoxy interface is of great importance in composite design due to its load transfer mechanisms from the weak epoxy to the stronger fiber. Improving the strength of the interface reduces the risk of failure at the interface and improves the load transfer to the fiber. In this study, two types of nano-species ZnO nanowires and nickel-based metal organic frameworks were grown on carbon fibers to improve the interfaces. The interfacial mechanics of the enhanced fibers are evaluated using nanoindentation studies. Composite samples with Aeropoxy matrix and vertically aligned fibers are fabricated for this purpose. A Bruker TI-980 TriboIndenter …

The Effect Of Through Thickness Reinforcement Angle On The Disbonding Behavior In Skin-Stringer Configuration, Christopher John Morris

Mechanical & Aerospace Engineering Theses & Dissertations

Post-cure through thickness reinforcement is a method used to increase the mechanical properties of composite laminates in the transverse direction. This study conducted a test on skin-stringer structures bonded together in three configurations using an epoxy or thermoplastic adhesive at the interface with reinforcing pins inserted through the laminate thickness located at the edge of the stringer at differing angles between -30º and 30º. The fabrication of these samples in configurations B and C consisted of the use of carbon fiber prepeg laminate at a ply orientation of [0₂90₂]_2s for the skin and [0 90] …

The Plastics Collection Reference Packet, Special Collections Research Center

Special Collections Research Center

This reference packet is an informational tool to support further research into the history of plastics—whether interested in companies, individuals within the plastics industry's history, historical plastics materials, essays, and more. All content featured within this packet was previously published on the former plastics.syr.edu website as part of a Syracuse University Libraries and Special Collections Research Center (SCRC) partnership established in 2007 with the Plastics Pioneers Association (PPA)—an association of plastics industry professionals interested in preserving the plastics industry's past.

Improving The Tensile Mechanical Properties Of Direct Energy Deposited (Ded) Inconel 718 Aircraft Components Using A Standard Heat Treatment, Spencer Vincent Flynn

Materials Engineering

This project aimed to improve the mechanical properties of as-printed additively manufactured Inconel 718 samples using a heat treatment usually used for cast and wrought Inconel 718. The mechanical properties sought to be optimized were yield strength, ultimate tensile strength, elongation, and reduction in area. The property goals were to match or exceed those of cast and heat treated Inconel 718. Wire-fed electron beam direct energy deposition (DED) was used to manufacture the samples, which were then heat treated using the AMS 5663 standard in an inert atmosphere. The samples were then tested in tension to obtain data on their …

Morphology And Hemodynamics Of Cerebral Arteries And Aneurysms In A Rare Pair Of Monozygotic Twins, Hang Yi, Zifeng Yang, Luke C. Bramlage, Bryan R. Ludwig

Mechanical and Materials Engineering Faculty Publications

In this preliminary study, the underlying pathophysiology mechanisms of cerebral aneurysms (CAs) in monozygotic twins (MTs) were investigated via a rare pair of MTs (twin A and twin B) involving four reconstructed arterial models using preclinical information. First, dimensions and configurated outlines of three-perspective geometries were compared. Adopting an in-vitro validated numerical CA model, hemodynamic characteristics were investigated in the MTs, respectively. Despite expected genetic similarities, morphological comparisons show that configurations of cerebral arteries exhibit significant differences between the twins. The ICA size of twin A is larger than that in twin B (2.23~25.86%), varying with specific locations, attributing to …

3d Printed Aircraft, Matthew Nagy, Charles D'Amico, Alexis Salgado Medina

Mechanical Engineering

This project is to design, build, and test a 3D-printable aircraft. The goal is to create a final design that will be able to fly for the longest duration possible, around 20 seconds. To determine the correct preliminary design and manufacturing process for a 3D printed RC aircraft, an analysis of multiple design options and manufacturing materials was performed. This allowed for a variety of choices for aircraft type, airfoil design, structure, among other topics to be narrowed down to the most promising option. It has been found that the aircraft will follow a design similar to industry motor-gliders, with …

Study Of A Carbon Fiber Reinforced Polymer Composite Using A Biobased Polyurethane As A Thermosetting Resin, Teddy Mageto

Electronic Theses & Dissertations

Carbon Fiber Reinforced Polymer composites (CFRP) have garnered increasing interest in recent years especially in the aerospace and automobile industries where they are gradually replacing metals as structural materials. This is owing to their light weight, high strength, high modulus, and excellent strength-to-weight ratio. Polymers are typically used as thermosetting resins in these composites. However, the synthesis of polymers currently is conducted via petrochemical processes which leads to adverse effects on the environment. To this end, in this work a biobased Polyurethane (PU) was used as a thermosetting resin in a CFRP. The biobased PU was synthesized by the reaction …

Classification Of Electrical Current Used In Electroplastic Forming, Tyler Grimm

All Dissertations

Electrically assisted manufacturing (EAM) is the direct application of an electric current to a workpiece during manufacturing. This advanced manufacturing process has been shown to produce anomalous effects which extend beyond the current state of modeling of thermal influences. These purported non-thermal effects have collectively been termed electroplastic effects (EPEs).

While there is a distinct difference in results between steady-state (ideal DC) testing and pulsed current testing, the very definition of these two EAM methods has not been well established. A "long" pulse may be considered DC current; a "short" pulse may produce electroplastic effects; and even "steady-state" current shapes …

Lunar In-Situ Aluminum Production Through Molten Salt Electrolysis (Lisap-Mse), Jacob Ortega, Jeffrey D. Smith, Fateme Rezaei, David Bayless, William P. Schonberg, Daniel S. Stutts, Daoru Frank Han

NASA-Missouri Space Grant Consortium

The goal of Artemis is to establish a sustained presence on the Moon. To achieve so, numerous resources are necessary. The Moon contains several essential elements needed to sustain human presence. Most of those elements are trapped in the form of minerals. To refine those minerals into useful materials, reduction methods are needed. Most reduction methods on Earth require large amounts of mass and power which is unrealistic for early stages of building a lunar base. To solve this problem, we are developing a concept of Lunar In-Situ Aluminum Production through Molten Salt Electrolysis (LISAP-MSE).

The LISAP-MSE project, if successful, …

Effects Of Tempering Temperature On Gas Turbine Fan Cases, Seth Utter

Honors Scholar Theses

The project aimed to investigate the effects of tempering temperature on metals used for gas turbine engine fan cases as a major relevant concern is containing blades in during blade-out events. There are three ways to accomplish this: using a thicker metal, incorporating different materials into the case, or heat treating the metal. This project focused on the third solution: reviewing the impact toughness and hardness of fractured samples and their equivalent ductile-to-brittle transition shear faces. Given its availability, 1045 steel, as opposed to aerospace grade metals, was used for in-house testing. The data obtained from these experiments were then …

Impact Resistance Of Hybrid Metal-Organic Frameworks/Carbon Fibers Composites, Derek Isaac Espinosa Ramirez

Doctoral Dissertations and Master's Theses

The increase in the use of carbon fiber-reinforced polymers (CFRPs) composites in the aerospace industry generated the need of improving the properties and capabilities of these composites by adding nano-reinforcements to the carbon fibers, also called hybrid fiber reinforced polymer composites. In this study, the energy absorption due to impact at low speed will be tested and simulated in four configurations of CFRPs utilizing the same [0/90]_S layout throughout them.

The carbon fiber configurations used during this study are de-sized, acid-activated, metal-organic frameworks (MOF), and carbon nanotubes (CNTs). Nickel (II) Nitrate, Methylimidazole, and Methanol were used to grow the …

Experimental And Computational Bearing Strength Of Fiber Metal Laminate With And Without Film Adhesive, Christopher L. Bellanova Jr.

Theses and Dissertations

This research characterized the performance of a fiber metal laminate composed of carbon fiber and stainless steel without film adhesive and compared it to a similar, previously tested, fiber metal laminate including film adhesive. Removal of the adhesive layers reduced the localized thickness, simplified manufacturing, and allowed for a 20% increase in foil thickness. Quasi-static testing was conducted in double shear, single shear protruding, and single shear countersunk configurations. The results were compared to adhesive hybrid and control samples. To study the affects of bolt tension, samples at low torque in double shear were also tested. Progressive failure samples revealed …

Development Of Novel Turbomachinery Manufacturing Methods, Timothy P. Winkler

Theses and Dissertations

Compact turbine engines are of increasing interest as a means of propulsion for small, lightweight, low cost, unmanned aerial systems. This study looks to leverage advancements in novel manufacturing technology to produce turbomachinery components while simultaneously reducing costs and manufacturing time. To determine the feasibility of drop-in replacements for stock components this study focused on several research areas. This included materials research on both polymer-reinforced and ceramic materials, specimen tensile testing to determine temperature-dependent material properties, finite element analysis of multiple candidate materials, design and fabrication of a spin test rig, and physical spin testing of manufactured components to predict …

Hemodynamic Investigations In Intracranial Aneurysms: A Commentary, Hang Yi, Mark Johnson, Luke Bramlage, Zifeng Yang, Bryan Ludwig

Mechanical and Materials Engineering Faculty Publications

Intracranial aneurysms (IAs) are abnormal bulges in a blood vessel in the brain that have a potential to rupture and even causing a stroke, which can lead to lasting brain damage, long-term disability, or even loss of life. It has been widely acknowledged that hemodynamic factors, e.g., instantaneous wall shear stress, time-averaged wall shear stress, wall shear stress gradient, gradient oscillatory number, oscillatory shear index, pulsatile blood flow waveform (flow rate magnitude and shape, physical flow period), relative residence time/turnover time, blood pressure, and vortex (i.e., size, location, and numbers), have a close relationship with the pathobiology (i.e., initiation, growth, …

Synthesizing Ti–Ni Alloy Composite Coating On Ti–6al–4v Surface From Laser Surface Modification, Yitao Chen, Joseph William Newkirk, Frank W. Liou

Materials Science and Engineering Faculty Research & Creative Works

In This Work, a Ni-Alloy Deloro-22 Was Laser-Deposited on a Ti–6Al–4V Bar Substrate with Multiple Sets of Laser Processing Parameters. the Purpose Was to Apply Laser Surface Modification to Synthesize Different Combinations of Ductile TiNi and Hard Ti₂Ni Intermetallic Phases on the Surface of Ti–6Al–4V in Order to Obtain Adjustable Surface Properties. Scanning Electron Microscopy, Energy Dispersion Spectroscopy, and X-Ray Diffraction Were Applied to Reveal the Deposited Surface Microstructure and Phase. the Effect of Processing Parameters on the Resultant Compositions of TiNi and Ti₂Ni Was Discussed. the Hardness of the Deposition Was Evaluated, and Comparisons with …

Application Of Multi-Scale Computational Techniques To Complex Materials Systems, Mujan N. Seif

Theses and Dissertations--Chemical and Materials Engineering

The applications of computational materials science are ever-increasing, connecting fields far beyond traditional subfields in materials science. This dissertation demonstrates the broad scope of multi-scale computational techniques by investigating multiple unrelated complex material systems, namely scandate thermionic cathodes and the metallic foam component of micrometeoroid and orbital debris (MMOD) shielding. Sc-containing "scandate" cathodes have been widely reported to exhibit superior properties compared to previous thermionic cathodes; however, knowledge of their precise operating mechanism remains elusive. Here, quantum mechanical calculations were utilized to map the phase space of stable, highly-faceted and chemically-complex W nanoparticles, accounting for both finite temperature and chemical …

Microstructure, Mechanical Properties And Oxidation Behavior Of Refractory Multi-Principal Element Alloys By Laser Remelting And Conventional Manufacturing, Visharad Jalan, Seth Crawford, Sung Heng Wu, Frank W. Liou, Haiming Wen

Mechanical and Aerospace Engineering Faculty Research & Creative Works

Refractory Multi-Principal Element Alloys (RMPEAs), HfNbTaTiZr, (HfNbTaTiZr)₉Cr, and (HfNbTaTiZr)₉Al, Were Manufactured using Vacuum Arc Melting Followed by Laser Remelting to Mimic Additive Manufacturing. the Microhardness of the As-Cast HfNbTaTiZr, (HfNbTaTiZr)₉Cr, and (HfNbTaTiZr)₉Al Samples after Arc Melting Was Measured as 6.20, 7.63, and 6.89 Gpa, respectively. after Laser Remelting and Re-Solidification, the Hardness Increased by ~ 30% for Each Composition; the Hardest Was (HfNbTaTiZr)₉Cr Measured at 9.60 GPa, While the Softest Was HfNbTaTiZr with a Hardness of 8.42 GPa, Which Was Still Harder Compared to All the Other Samples. the Addition …

Comparison Of The Thermal Stability In Equal-Channel-Angular-Pressed And High-Pressure-Torsion-Processed Fe–21cr–5al Alloy, Maalavan Arivu, Andrew Hoffman, Jiaqi Duan, Jonathan Poplawsky, Xinchang Zhang, Frank W. Liou, Rinat Islamgaliev, Ruslan Valiev, Haiming Wen

Mechanical and Aerospace Engineering Faculty Research & Creative Works

Nanostructured Steels Are Expected to Have Enhanced Irradiation Tolerance and Improved Strength. However, They Suffer from Poor Microstructural Stability at Elevated Temperatures. in This Study, Fe–21Cr–5Al–0.026C (Wt%) Kanthal D (KD) Alloy Belonging to a Class of (FeCrAl) Alloys Considered for Accident-Tolerant Fuel Cladding in Light-Water Reactors is Nanostructured using Two Severe Plastic Deformation Techniques of Equal-Channel Angular Pressing (ECAP) and High-Pressure Torsion (HPT), and their Thermal Stability between 500–700 °C is Studied and Compared. ECAP KD is Found to Be Thermally Stable Up to 500 °C, Whereas HPT KD is Unstable at 500 °C. Microstructural Characterization Reveals that ECAP KD …

Performance Evaluation Of Composite Sandwich Structures With Additively Manufactured Aluminum Honeycomb Cores With Increased Bonding Surface Area, M. Rangapuram, S. K. Dasari, Joseph William Newkirk, K. Chandrashekhara, H. Misak, P. R. Toivonen, D. Klenosky, T. Unruh, J. Sam

Materials Science and Engineering Faculty Research & Creative Works

Modern aerostructures, including wings and fuselages, increasingly feature sandwich structures due to their high-energy absorption, low weight, and high flexural stiffness. The face sheet of these sandwich structures are typically thin composite laminates with interior honeycombs made of Nomex or aluminum. Standard cores are structurally efficient, but their design cannot be varied throughout the structure. With additive manufacturing (AM) technology, these core geometries can be altered to meet the design requirements that are not met in standard honeycomb cores. This study used a modified aluminum honeycomb core, with increased surface area on the top and bottom, as the core material …

Molecular Dynamics Modeling Of Polymers For Aerospace Composites, Swapnil Sambhaji Bamane

Dissertations, Master's Theses and Master's Reports

Polymer matrix composite materials are widely used as structural materials in aerospace and aeronautical vehicles. Resin/reinforcement wetting and the effect of polymerization on the thermo-mechanical properties of the resin are key parameters in the manufacturing of aerospace composite materials. Determining the contact angle between combinations of liquid resin and reinforcement surfaces is a common method for quantifying wettability. It is challenging to determine contact angle values experimentally of high-performance resins on CNT materials such as CNT, graphene, bundles or yarns, and BNNT surfaces. It is also experimentally difficult to determine the effect of polymerization reaction on material properties of a …

Study Of Nanocomposite Materials Using Molecular Dynamics, Prashik Sunil Gaikwad

Dissertations, Master's Theses and Master's Reports

There is an increase in demand for new lightweight structural materials in the aerospace industry for more efficient and affordable human space travel. Polymer matrix composites (PMCs) with reinforcement material as carbon nanotubes (CNTs) have shown exceptional increase in the mechanical properties. Flattened carbon nanotubes (flCNTs) are a primary component of many carbon nanotube (CNT) yarn and sheet materials, which are promising reinforcements for the next generation of ultra-strong composites for aerospace applications. These flCNT/polymer materials are subjected to extreme pressure and temperature during curing process. Therefore there is a need to investigate the evolution of properties during the curing …