Femtosecond Laser Induced Structural Dynamics And Melting Of Cu (111) Single Crystal. An Ultrafast Time-Resolved X-Ray Diffraction Study, Runze Li, Omar A. Ashour, Jie Chen, H. E. Elsayed-Ali, Peter M. Rentzepis
Femtosecond Laser Induced Structural Dynamics And Melting Of Cu (111) Single Crystal. An Ultrafast Time-Resolved X-Ray Diffraction Study, Runze Li, Omar A. Ashour, Jie Chen, H. E. Elsayed-Ali, Peter M. Rentzepis
Electrical & Computer Engineering Faculty Publications
Femtosecond, 8.04 keV x-ray pulses are used to probe the lattice dynamics of a 150 nm Cu (111) single crystal on a mica substrate irradiated with 400 nm, 100 fs laser pulses. For pump fluences below the damage and melting thresholds, we observed lattice contraction due to the formation of a blast force and coherent acoustic phonons with a period of ∼69 ps. At larger pump fluence, solid to liquid phase transition, annealing, and recrystallization were measured in real time by monitoring the intensity evolution of the probing fs x-ray rocking curves, which agreed well with theoretical simulation results. The …
Time-Resolved Reflection High-Energy Electron Diffraction Study Of The Ge(111)-C(2×8)-(1×1) Phase Transition, Xinglin Zeng, Bo Lin, Ibrahim El-Kholy, Hani E. Elsayed-Ali
Time-Resolved Reflection High-Energy Electron Diffraction Study Of The Ge(111)-C(2×8)-(1×1) Phase Transition, Xinglin Zeng, Bo Lin, Ibrahim El-Kholy, Hani E. Elsayed-Ali
Electrical & Computer Engineering Faculty Publications
The dynamics of the Ge(111)-c(2×8)-(1×1) phase transition is investigated by 100-ps time-resolved reflection high-energy electron diffraction. A laser pulse heats the surface while a synchronized electron pulse is used to obtain the surface diffraction pattern. Slow heating shows that the adatoms in Ge(111)-c(2×8) start to disorder at ∼510 K and are converted to a disordered adatom arrangement at 573 K. For heating with 100-ps laser pulses, the Ge(111)-c(2×8) reconstructed adatom arrangement starts to disorder at 584±16K, well above the onset temperature of ∼510 K for the disordering of Ge(111)-c(2×8) observed for slow …
Temperature Dependence Of Step Density On Vicinal Pb(111), Z. H. Zhang, H. E. Elsayed-Ali
Temperature Dependence Of Step Density On Vicinal Pb(111), Z. H. Zhang, H. E. Elsayed-Ali
Electrical & Computer Engineering Faculty Publications
The temperature dependence of step density on the vicinal Pb(111) surface is investigated using reflection high-energy electron diffraction. When the temperature is increased from 323 to 590 K. the average terrace width and the average string length at the step edge decrease from 85±25 to 37±16 Å and from 220±33 to 25±8 Å, respectively. Thermal step collapse on the Pb(111) surface near its bulk melting temperature is not observed. Above 530±7 K, the change in the string length at the step edge with temperature becomes small, and the intensity of the (00) beam is significantly decreased. We conclude that partial …
Surface Morphology Of Laser-Superheated Pb(111) And Pb(100), Z. H. Zhang, Bo Lin, X. L. Zeng, H. E. Elsayed-Ali
Surface Morphology Of Laser-Superheated Pb(111) And Pb(100), Z. H. Zhang, Bo Lin, X. L. Zeng, H. E. Elsayed-Ali
Electrical & Computer Engineering Faculty Publications
The surface step density on the vicinal Pb(111) and the surface vacancy density on Pb(100) after laser superheating and melting are investigated using reflection high-energy electron diffraction. With ∼100-ps laser pulses, Pb(111) surface superheating does not significantly change the density of the steps and step-edge roughness. However, after laser surface melting, the average terrace width and the string length at the step edge become as large as those at room temperature. The average terrace width at 573 K changes from 38±15 to 64±19 Å after laser surface melting, while the average string length at the step edge changes from 90±14 …