Fabrication And Performance Of Lani0.6Fe0.4O3-δCathode Modified By Coating With Gd0.2Ce0.8O2 For Intermediate Temperature Solid Oxide Fuel Cell, Rui-Xuan Ren, Bo Huang, Xin-Jian Zhu, Yi-Xing Hu, Xiao-Yi Ding, Zong-Yao Liu, Ye-Bin Liu

Journal of Electrochemistry

The symmetric cell of LaNi_0.6Fe_0.4O_3-δ/Sc_0.1Zr_0.9O_1.95/LaNi_0.6Fe_0.4O _3-δ was fabricated with screen printing method. A LaNi_0.6Fe_0.4O_3-δ (LNF) cathode was modified by coating with nano-sized gadolinium-doped ceria (GDC, Gd_0.2Ce_0.8O₂) prepared using a simple combustion process within the pores of the cathode. According to the electrochemical impedance spectra (EIS), the polarization resistance of the pure LNF was 0.70 W·cm² at 750 ºC, while 0.13 W·cm² for the 21.3% GDC (by mass)-coated LNF cathode at the …

Optimization Of Electroless Silver Plating Process On Fabric Surface Without Activation And Sensitization, Bo Lian Wang, Ya Ping Zhao, Zai Sheng Cai

Journal of Electrochemistry

Silver was deposited homogeneously on the surface of polyamide fabric by electroless plating without activation and sensitization. The electroless silver plating process was optimized with the orthogonal array testing strategy. It is found that the optimum conditions are the electroless plating time of 50 min with the concentrations of silver nitrate, sodium hydroxide and ammonium hydroxide being 14 g·L^-1, 6 g·L-1 and 130 mL·L^-1, respectively. The surface morphologies, compositions, and phases of fabric samples were characterized by scanning electron microscopy and energy-dispersive X-ray spectrometry (SEM-EDS), X-ray diffraction (XRD). The wear-resisting property was tested by friction fastness …

A Comparative Study Of Ce3+/Ce4+ Redox Couple On Pt Electrode In Sulfuric Acid And Methanesulfonic Acid, Zhao-Hua Li, You-Qun Chu, Chun-An Ma

Journal of Electrochemistry

The electrochemical oxidations of Ce³⁺ to Ce⁴⁺ on Pt rotating disk electrode (RDE) in both sulfuric acid and methanesulfonic acid (MSA) solutions were studied by using cyclic voltammetry and linear sweep voltammetry. The complexing behaviors of Ce³⁺/Ce⁴⁺ were preliminarily probed and the exchange current density, diffusion coefficient, as well as reaction rate constant were obtained from Butler-Volmer equation. The activation energies of Ce³⁺ oxidation on Pt electrode in two types of acidic media, obtained from Arrhenius equation, were also compared. The results indicate that Ce³⁺ can be oxidized to Ce4+ much easier in …

An Electrochemical Impedance Spectroscopic Study Of Cuf2/Moo3/C Cathode Composites, Yue-Li Shi, Nan Wu, Ming-Fang Shen, Jia-Qun Dong, Quang-Chao Zhuang, Li Jiang

Journal of Electrochemistry

Composite electrode of CuF₂/MoO₃/C was fabricated through high energy mechanical milling. The properties of CuF₂/MoO₃/C were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), high resolution transmission electron microscopy (TEM), galvanostatic charge-discharge measurements, cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The results showed that the grain sizes of CuF₂ and MoO₃ after milling were 200 ~ 300 nm, and the initial discharge capacity of CuF₂/MoO₃/C was 647 mAh·g^-1 at room temperature and at a current density of 10 mA·g^-1. However, the …

Analysis Of The Material Factors In The Degradation Of Sofc Performance, Ke-Qing Gao, Xiao-Tian Liu, Qing Zhao, Li-Quan Fan, Yue-Ping Xiong

Journal of Electrochemistry

Based on the cell operating conditions, the material factors which influence the cell performance of SOFC including the chemical stability of materials at solid-gas interface in redox atmosphere, the diffusion and reaction between the interface of solid-solid materials, and degradation caused by the external chemical substances brought into the cells at triple phase boundary are mainly analyzed. Given that under the current state of the research it is urgent to explore the material factors on degradation of cell performance to meet demands in SOFC applications.

Electrochemical Activities Of Oxygen-Doped Carbon Surface For V(Iv)/V(V) Redox Couple, Huan Zhang, Lin-Lin Qin, Yi-Ning Shi, Ming-Sen Zheng, Quan-Feng Dong, Zhao-Wu Tian

Journal of Electrochemistry

Graphite plate electrodes were treated with oxygen plasma and doped with oxygen as well as oxygen functional groups. With the treatment, the activities of graphite plate electrodes toward VO²⁺/VO₂⁺ redox reactions were improved. FT-IR and EDS analysis results indicated that oxygen functional groups were introduced to the surface of graphite plates after oxygen plasma treatment. In this paper, the graphite plate treated for 20 min showed the highest activity. The average charge efficiency reached 91%, suggesting an increase of 19%, compared with that of the untreated graphite plate under a current density of 8 mA·cm^{-2 …}

Hydrothermal Synthesis Of Pure Li4Ti5O12 And Its Electrochemical Performance, Wen-Jun Xie, Yu-Shi He, Hong Wang, Xiao-Zhen Liao, Zi-Feng Ma

Journal of Electrochemistry

Spinel Li₄Ti₅O₁₂ was prepared by hydrothermal method using commercial anatase (TiO₂) and lithium hydroxide (LiOH) as raw materials. The effects of the LiOH concentration of lithium hydroxide, hydrothermal reaction time and calcination temperature on the structure and electrochemical performance of Li₄Ti₅O₁₂ were investigated. The formation process of Li₄Ti₅O₁₂ was also proposed. The micro-structure and morphology wereas characterized by XRD, SEM, TEM techniques, and the electrochemical performance was analyzed by galvanostatic charge-discharge test. The results show that the pure phase spinel Li₄Ti …

Current Statuses And Prospects Of Bioeletrochemical Instruments, Ren Hu, Chun-Hui Piao, Chang-Jian Lin, Dong-Ping Zhan, Bin Ren, Amatore Christian, Zhong-Qun Tian

Journal of Electrochemistry

Charge transfer is one of the essential life processes. In the past decades, the electrochemical methods have been developed to study life science in a unique physicochemical view and have exhibited abundant and precious information beyond conventional biological techniques. As bioelectrochemical research areas evolved from the fundamental studies of biomolecules’ electrochemical behaviours in non-living conditions to the living cells in intro and in vivo, and further to the single molecule in living systems, the role of instruments becomes more and more crucial. The performances of instruments such as sensitivity, resolution (time, spatial and eneygy resolutions) and controllability are more demanding …

Preparation And Catalytic Properties Of Feco Alloy Nanocatalyst, Ming-Xuan Li, Jie-Lian Ou, Sheng-Pei Chen, Peng Wang, Bin-Bin Xu, Shi-Gang Sun

Journal of Electrochemistry

The FeCo alloy nanoparticles were electrodeposited on glassy carbon electrode by chronoamperometry and were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results showed that the shapes of FeCo nanoparticles were cubes with an average size of 65 nm. The atom ratio of Fe and Co is 1:1. As indicated from the pattern of selected area electron diffraction (SAED), the FeCo cubic nanoparticles were single crystal which belonged to body-centered cubic with an interval of 0.201 nm referring to the (110) facets of FeCo alloy. The FeCo cubic nanoparticles exhibited the enhanced electrocatalytic …

Fabrication And Localized Surface Plasmon Resonance Of Ultrathin Nanoporous Gold Films, Shi Feng, Shu Chen, Qing Yang, Juan Xiang

Journal of Electrochemistry

Ultrathin nanoporous gold films (NPGF) with a thickness of approximately 50 nm were fabricated via electrochemical dealloy method. The morphology of NPGF was evaluated with a parameter of surface roughness. SEM results demonstrate that the fabrication of NPGF with different roughness factors can be achieved by controlling the circles of cyclic voltammetry. UV-Vis spectra indicate that the localized surface plasmon resonance (LSPR) of NPGF is affected by the roughness of NPGF. With the optimal roughness factor, NPGF displays a linear relationship between the ethanediol concentration and the absorbance intensity at λ = 450 nm. The LSPR effect of NPGF presents …

Electrochemical Synthesis Of Hierarchical Dendritic Polyaniline Nanostructures, Shao-Huang Weng, Jian-Zhang Zhou, Zhong-Hua Lin, Xin-Hua Lin

Journal of Electrochemistry

In this work, the p-TSA doped and hierarchical dendritic nanostructured polyanilines (PANI) have been prepared by potentiostatic electropolymerization without using any templates at room temperature. The mechanism of the polymerization has been discussed according to the electrodeposition curves. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were employed to confirm the formation of uniform hierarchical dendritic structure on PANI. UV-Vis spectroscopy (UV-Vis) and infrared spectroscopy (FTIR) proved that the prepared PANI is in the form of emeraldine salt. The templateless electrodeposition method is simple, easy to operate, can be applied to fabricate other nanostructures of conducting polymers.

Performance Of Vn As Negative Electrode Materials In Electrochemical Capacitors, Zhao-Hui Gao, Hao Zhang, Gao-Ping Cao, Min-Fang Han, Yu-Sheng Yang

Journal of Electrochemistry

Nanocrystalline vanadium nitride (VN) materials were synthesized by high temperature ammonia (NH₃) reduction of vanadium oxide (V₂O₅). The structure and morphology of VN materials were characterized by XRD, SEM and TEM, while the specific surface area, pore size distribution and supercapacitive behavior by N₂ absorption, cyclic voltammetry (CV) and constant current charge-discharge measurements in 1 mol·L-1 KOH electrolyte. The results showed that the VN sample belonged to the cubic crystal system (Fm3m [225]), and had homogeneous surface and appeared nearly spherical with uniform size. As the reaction time was extended to 12 h, …

Electrochemical Performance Of Lifepo4/C Synthesized Via Aqueous Solution-Evaporation Route, Ning-Yu Gu, Xing-Hua He, Yang Li

Journal of Electrochemistry

The LiFePO₄/C samples have been synthesized via an aqueous solution-evaporation route with LiH₂PO₄, FeC₂O₄.2H₂O as raw materials and citric acid as a carbon source. X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) were used to analyze structure and morphology of the samples. The electrochemical performances of the LiFePO₄/C cathodes were characterized by charge/discharge cures and electrochemical impedance spectroscopy (EIS). The results show that the LiFePO₄/C sample, calcined at 700 °C and contained 3.03% (by mass) carbon, exhibited a highly pure …

Preparation And Methanol Electrooxidation Of Pt/Pmo12/Pedot/Gc Electrodes, Jing-Hua Ma, Rui-Xiang Wang, Yi-Liang Tan, Shan-Shan Wang, Yan-Qin Zhang, You-Jun Fan

Journal of Electrochemistry

Modification of phosphomolybdic acid (PMo₁₂) on poly(3,4-ethylenedioxythiophene) (PEDOT) film (PEDOT/GC) obtained through the electrochemical polymerization was performed using adsorption method (PMo₁₂/PEDOT/GC), followed by electrodepositing Pt on PMo₁₂/PEDOT/GC to prepare Pt/PMo₁₂/PEDOT/GC electrode. Effects of PMo₁₂ and PEDOT on the methanol oxidation performance of electrode were investigated. Results showed that PMo₁₂ obviously changed the morphology and structure of Pt loaded on the electrode, leading to the formation of sharp thorns at the edge of Pt nanostructures. Cyclic voltammetry and chronoamperometry data demonstrated that the catalytic activities of methanol electrooxidation on the Pt/PMo …

The Electrochemical Capacitance Performance Of La1-XSrXCoo3 Perovskites, Yang Xu, Yan-Yan Bao, Long-Fei Du, Dian-Xue Cao, Gui-Ling Wang

Journal of Electrochemistry

In this paper, the La_1-xSr_xCoO₃ (x = 0.2, 0.4, 0.6, 0.8) perovskites powders were synthesized by a sol-gel method. The perovskite phases were characterized by X-ray diffraction (XRD), while the electrochemical capacitance performance of La_1-xSr_xCoO₃ electrodes in alkaline electrolyte was studied by cyclic voltammetry and galvanostatic charge/discharge test. It was found that the La_0.6Sr_0.4CoO₃ electrode exhibited a specific capacitance of 325 F.g^-1 in 6.0 mol.L^-1 KOH electrolyte at a current density of 10 mA.cm^-2, and the specific capacitance of 315 F.g …

Synthesis And Electrochemical Performance Of Si/C Composite Modified By Pani, Guang-Hui Zhang, Pei-Kang Shen, Ge Sang, Ren-Jin Xiong

Journal of Electrochemistry

Silicon/carbon (Si/C) composite materials were prepared through high-energy ball milling and high-temperature solid-phase method, and then coated with thin polyaniline (PAni) film by oxidation. The microstructure and component of the composites were characterized by SEM, XRD, IR, TG, and the electrochemical performance was investigated by cyclic voltammetry (CV) and galvanostatic charge-discharge tests. The results showed that the surface of PAni/Si/G/C composite was coating with complete lamellar structure of PAni film. Its reversible capacity was 784 mAh·g^-1 and 690 mAh·g^-1 could be maintained after 50th charge-discharge cycles.

Synthesis Of Lifepo4/C Cathode By Sol-Gel And Calcining Method With Chitosan Monomer, Jia Xu, Yan-Yan Wang, Rui Wang, Bo Wang, Yue Pan, Dian-Xue Cao, Gui-Ling Wang

Journal of Electrochemistry

The LiFePO₄/C cathode materials for Li-ion battery were synthesized by sol-gel and calcining method using chitosan monomer as a carbon source and a gelating agent. The structures and morphologies were characterized by X-ray diffraction spectroscopy (XRD) and scanning electron microscopy (SEM). The electrochemical performance was investigated by the galvanostatic charge–discharge test. When the molar ratios between chitosan monomer and LiFePO₄ were 1:1.2, the LiFePO₄/C cathode calcined at 600 ^oC showed the best performance. The particle sizes ranged 200 ～ 400 nm. The initial discharge capacity of 155 mAh·g-¹ was achieved at room temperature …

Current Development Of Quantum Dots Based Electrochemiluminescence Immunosensors, Ling-Ling Li, Qian Lu, Jun-Jie Zhu

Journal of Electrochemistry

Electrochemiluminescence exhibits the merits of both luminescence and electrochemistry analysis, and has been extensively employed in biosensors. Quantum dots are considered one of the three main kinds of electrochemiluminescence luminophores due to their unique properties. This paper briefly reviews the classification and signal amplification technology of quantum dots based electrochemiluminescence immunosensors. Future research trends are also suggested.

Synthesis And Electrocatalysis Of Pdcu Alloy Nanocrystals, Hai-Bin Wu, Rui-Zhong Zhang, Wei Chen

Journal of Electrochemistry

Monodispersed PdCu alloy nanoparticles were synthesized by co-reduction of Cu(acac)2 and Pd(acac)2 with 1, 2-hexadecanediol. The spherical and popcorn-like shapes of PdCu alloy nanoparticles were obtained by changing the ratios of mixed surface protecting ligands of 1-octadecene, and oleylamine or oleic acid. TEM and XRD measurements showed that both PdCu nanoparticles are alloy nanocrystals dominated with (111) planes and the average sizes are 12.7 ± 0.18 and 20.4 ± 0.31 nm for he spherical and popcorn-like PdCu nanoparticles, respectively. The electrocatalytic activities of the PdCu nanocrystals for formic acid oxidation were evaluated by electrochemical cyclic voltammetry (CV). The result showed …

Properties Of Carbon Coated Tin Negative Electrode For Lithium-Ion Battery, Gui-Chang Liu, Xiao-Xiao Shen, Li-Da Wang

Journal of Electrochemistry

Carbon coated tin power was prepared by decomposing glucose applying a hydrothermal method, and was further used as the active material for negative electrode of lithium secondary battery. Charge-discharge tests show that the carbon coated tin electrode with the addition of 5 wt.% acetylene black as a conductive agent could obtain an initial discharge capacity of 967 mAh·g^-1 and a discharge capacity of 362 mAh·g^-1 after 50 cycles, which is much higher than that of tin electrode (166 mAh·g^-1 after 50 cycles). The coated carbon hinders the agglomeration of tin powder, reduces the irreversible capacity loss of …

Physical Essentials Of Rotating Complex Impedance Diagram In Some Electrochemical Systems, Bing-Liang Wu

Journal of Electrochemistry

The essential of the rotation of complex impedance diagram in some electrochemical systems is discussed. It is attributing to that the electrochemical capacitance usual is not simple real capacitor but must be complex number capacitance. As the examples: 1, the metal/support electrolyte electrode in the ideal polarization condition, the capacitance must be that of the electrochemical double layer and represents complex number properties. Its complex impedance diagram was not a line parallel to imaginary axis but rotated clockwise α=arctgC"/C'. 2, In the case of insertion/desertion electrodes, the capacitance must be that of the solid electrolyte interphase (SEI). The rotation of …

Combination And Applications Of Time-Resolved Surface Plasmon Resonance Spectroscopy And Electrochemical Methods, Yu Bao, Yan Mao, Wei Wang, Zheng-Gang Li, Li Niu

Journal of Electrochemistry

Electrochemical-surface plasmon resonance (EC-SPR) technique, developed in recent years, is a new technology which combines time-resolved surface plasmon resonance spectroscopy and electrochemical methods. Surface plasmon resonance (SPR) is a physical phenomenon generated by optical coupling using a metallic thin film and is very sensitive to optical analysis. The principles of SPR and EC-SPR are briefly introduced and the applications of the combination of SPR spectroscopy with electrochemical techniques are reviewed in this paper. This new technology has been widely used in such research areas as reaction dynamics, biochemical sensors, electrode/electrolyte interfaces, kinetic parameters and bimolecular interactions.

High Performance Membrane Electrode Assembly With Low Platinum Loadings Prepared By Atomic Layer Deposition For Pemfc Application, Ting Shu, Shi-Jun Liao, Chien-Te Hsieh, Ay Su

Journal of Electrochemistry

A high performance membrane electrode assembly (MEA) with low platinum loadings was successfully prepared with atomic layer deposition (ALD) technique. The anode of the MEA was prepared by depositing platinum on the carbon paper substrate, which was prepared by coating the slurry of carbon black (XC-72R) and Teflon, followed by drying and calcining at 350 °C. The MEAs consisted of the ALD anode or commercial catalyst anode, pretreated Nafion membrane (Nafion-117) and commercial cathode. Performances of MEAs were measured by single cell testing, and the anodes and MEAs were characterized by CV, SEM, TEM and XRD. The results revealed that …

Electrochemical Performance Of Fe3O4/C Composites As Negative Material For Lithium-Ion Batteries, Jun-Jie Cai, Shu Yao, Ze-Sheng Li, Hui Meng, Pei-Kang Shen

Journal of Electrochemistry

The Fe₃O₄/Carbon composites have been synthesized through coprecipitation pathway and by insitu aniline polymerization as a carbon source. Structural characterization and morphological study of the composites were investigated by using XRD, SEM and TEM techniques. The results showed that the nanosized Fe₃O₄ particles (40 ~ 80 nm) were encapsulated in the amorphous carbon. During the electrochemical tests, the Fe₃O₄/C composites exhibited high capaticity and excellent cycle ability, the retention of capaticity was about 1000 mAh·g^-1 after 30 cycles of charge/discharge tests at 50 mA·g^-1.

A Comparative Study Of Charge-Discharge Behaviors Of α-Pbo2 And β-Pbo2 Cathodes, Cong-Ying Cui, Xue-Mei Ma, De-Long Kong, Hou-Yi Ma

Journal of Electrochemistry

The α-PbO₂ and β-PbO₂ powders were prepared using simple chemical synthetic methods, and their crystalline structures and surface morphologies were characterized with X-ray powder diffraction spectroscopy and scanning electron microscopy. Using the as-synthesized α-PbO₂ and β-PbO₂ powders as positive active materials, the electrochemical performance of the two PbO₂ materials was investigated by means of cyclic voltammetry, galvanostatic charge-discharge tests, and electrochemical impedance spectroscopy. The results indicate that the discharge capacity of α-PbO₂ electrode is larger than that of β-PbO₂; moreover, the composite electrodes made by α-PbO₂ and β-PbO₂ mixtures with …

An In Situ Ftir Spectroelectrochemical Study On Methanol Oxidation At Pt-Mo2C/Gc Catalyst, Hai-Ping Huang, Xi-Yu Yao, Pei-Kang Shen

Journal of Electrochemistry

A 40% Pt on Mo₂C/GC catalyst has been prepared by ion exchange method. The mechanism of methanol electrooxidation on Pt-Mo₂C/GC and commercial Pt/C catalysts in acidic media was studied by cyclic voltammetry, XRD measurements and in-situ Fourier transform infrared spectroelectrochemistry. The results revealed that the Pt nanoparticles were uniformly dispersed on Mo₂C/GC with an average particle size of 3 nm. The cyclic voltammetric and chronopotentiometric experiments indicated that Pt-Mo₂C/GC catalyst exhibited a better performance for methanol oxidation than that of Pt/C in acid solution. A negative shift over 90 mV of the …

Recent Experimental Progresses On Electrochemical Atr-Seiras, Yao-Yue Yang, Han-Xuan Zhang, Wen-Bin Cai

Journal of Electrochemistry

Technical aspects on developing electrochemical ATR surface-enhanced infrared absorption spectroscopy are briefly accounted mainly based on our recent investigations, including wet-fabrication of metallic film electrodes on Si prism, design and construction of a wide-frequency combination optical window and a spectroelectrochemical cell switchable for external and internal reflection modes.

Applications Of Ellipsometry In The Investigations Of Electrode-Solution Interface, Jing-Lei Lei, Liang-Liu Wu, Ling-Jie Li, Sheng-Mao Wu, Sheng-Tao Zhang

Journal of Electrochemistry

Ellipsometry is an optical technique with high-sensitivity to quantitatively obtain surface/interface properties such as thickness andrefractive index by analyzing the changes in polarized light reflected from the surface/interface. Its noncontacting and nondestructivenature makes it possible to acquire thein situreal-time information of the change at the surface/interface. Therefore, ellipsometry has been used widely in the electrochemical investigations. In this paper, based on the brief introduction of the measurementprinciple of ellipsometry, the current progress and the future trends of ellipsometry in electrochemistry arediscussed. The applications of ellipsometry in the fields of conversion and storage of electrochemical energy, electrochemistry ofmaterials science,electroanalysisand bioelectrochemistry are …

Oxygen Reduction Reaction On Glycin Modified Pt(111) Electrode, Ming-Fang Li, Jing Kang, Ling-Wen Liao, Yan-Xia Chen, Shen Ye

Journal of Electrochemistry

O

xygen reduction reaction (ORR) on glycin (NH₂CH₂COOH) modified Pt(111) electrode has been investigated using hanging meniscus rotating disk electrode system (HMRD) in 0.05 mol•L^-1 H₂SO₄ and 0.1 mol•L^-1 HClO₄ solutions, respectively. Cyclic voltammograms of the glycin modified Pt (111) electrode measured in 0.05 mol•L^-1 H₂SO₄ solution similar to that of CN^- modified Pt(111) electrodes, demonstrating that sulfate adsorption is strongly inhibited at the glycin modified Pt(111). From the polarization curve of ORR recorded in 0.05 mol•L^-1 H₂SO₄ solution, it is …

Porous Electrodes With High Pt Utilization Obtained By Ion-Exchange/Electrodeposition, Si-Guo Chen, Wei Ding, Xue-Qiang Qi, Li Li, Zi-Hua Deng, Zi-Dong Wei

Journal of Electrochemistry

We report a novel method based on ion-exchange/electrodeposition (IEE) for constructing high Pt utilization porous electrodes. The electrode prepared using IEE was assessed by linear sweep voltammetry (LSV), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and single cell test. The preliminary results show that the undesired ion-exchange between Pt anion and surface functional group in carbon black can be eliminated through the electrode preparation process, and every Pt particle prepared by IEE is expected to be deposited on the three-phase reaction zone and thus can be fully utilized in fuel cell reactions. The Pt particle size, shape and distribution …