Tribology Commons^™

Tribological Performance Of Novel Nickel-Based Composite Coatings With Lubricant Particles, Ignacio Tudela, Andrew J. Cobley, Yi Zhang

Friction

The present study is focused on the evaluation of the tribological performance of novel Ni/hBN and Ni/WS2 composite coatings electrodeposited from an additive-free Watts bath with the assistance of ultrasound. Lubricated and non-lubricated scratch tests were performed on both novel composite coatings and on standard Ni deposits used as a benchmark coating to have an initial idea of the effect of the presence of particles within the Ni matrix. Under lubricated conditions, the performance of the Ni/hBN composite coating was very similar to the benchmark Ni coating, whereas the Ni/WS2 behaved quite differently, as the latter did not only show …

A Comparison Between Graphene And Ws2 As Solid Lubricant Additives To Aluminum For Automobile Applications, Sara Rengifo

FIU Electronic Theses and Dissertations

The purpose of this thesis was to compare graphene nanoplatelets (GNP) and WS₂ as solid lubricant additives to aluminum in order to reduce friction and wear. The central hypothesis of this work relied on lubricating properties of 2D materials, which consist layers that slip under a shear force.

Two aluminum composites were made (Al-2 vol.% GNP and Al-2 vol.% WS₂) by spark plasma sintering. Tribological properties were evaluated by ball-on-disk wear tests at room temperature (RT) and 200^°C.

WS₂ not only presented the lowest COF (0.66) but also improved the wear resistance of aluminum …