Articles 1 - 4 of 4

Full-Text Articles in Tribology

Effects Of Shot-Peening On High Cycle Fretting Fatigue Behavior Of Ti-6al-4v, Halil I. Yuksel Mar 2002

Effects Of Shot-Peening On High Cycle Fretting Fatigue Behavior Of Ti-6al-4v, Halil I. Yuksel

Theses and Dissertations

Effects of Shot-peening on High Cycle Fretting Fatigue behavior of Ti-6Al-4V were investigated. Experiments were performed with 6.35 mm thick specimens which provided S/N curves. After the tests, it was observed that the specimens failed near the trailing edge of contact. Scanning Electron Microscopy showed that cracks initiated on the contact surface for 6.35 mm, and at the depth of specimen ranging from 200 to 300 microns for 3.81 mm thick specimens. Initial crack orientation was around 37 and 42 degrees respectively for 6.35 and 3.81 mm thicknesses. Finite Element Analysis (FEA) was conducted, and using FEA results, Smith-Watson-Topper, Findley, …

Go to article

Examination Of Contact Width On Fretting Fatigue, Russell S. Magaziner Mar 2002

Examination Of Contact Width On Fretting Fatigue, Russell S. Magaziner

Theses and Dissertations

The primary goal of this study was to find the effects on the fretting fatigue life when systematically holding the fretting fatigue variables, peak contact pressure, maximum/minimum nominal bulk stress, and the ratio of shear traction to pressure force constant while varying the contact semi-width through changes in pad radius and normal load. Experimental tests were performed on a test setup capable of independent pad displacement. Analytical and finite element simulations of the different experimental tests were performed. The local mechanistic parameters were inspected. Five different critical plane based fatigue predictive parameters lacked effectiveness in predicting changes in life with …

Go to article

Fretting Fatigue Behavior Of A Titanium Alloy Ti-6al-4v At Elevated Temperature, Onder Sahan Mar 2002

Fretting Fatigue Behavior Of A Titanium Alloy Ti-6al-4v At Elevated Temperature, Onder Sahan

Theses and Dissertations

The purpose of this research is to investigate the fretting fatigue behavior of the titanium alloy Ti-6Al-4V at elevated temperature is investigated. Fretting and plain fatigue experiments are conducted at 260 °C. Crack initiation location and crack initiation orientation is measured and fretting and plain fatigue life data of the specimens from these tests are obtained. Fatigue parameters capable of predicting the number of cycles to specimen failure, the crack location and the crack orientation along the contact surface are analyzed. The parameters are calculated by using the computed stresses and strains obtained from the finite element analysis. The mechanisms …

Go to article

Piezoelectric In Situ Transmission Electron Microscopy Technique For Direct Observations Of Fatigue Damage Accumulation In Constrained Metallic Thin Films, Xiaoli Tan, T. Du, J.K. Shang Jan 2002

Piezoelectric In Situ Transmission Electron Microscopy Technique For Direct Observations Of Fatigue Damage Accumulation In Constrained Metallic Thin Films, Xiaoli Tan, T. Du, J.K. Shang

Xiaoli Tan

A piezoelectricin situtransmission electron microscopy(TEM) technique has been developed to observe the damage mechanism in constrained metallic thin films under cyclic loading. The technique was based on the piezoelectric actuation of a multilayered structure in which a metallic thin film was sandwiched between a piezoelectric actuator and a silicon substrate. An alternating electric field with a static offset was applied on the piezoelectric actuator to drive the crack growth in the thin metallic layer while the sample was imaged in TEM. The technique was demonstrated on solder thin films where cavitation was found to be the dominant fatigue damage mechanism.