Full-Text Articles in Metallurgy
Time-Dependent Crack Growth Behavior Of Alloy 617 And Alloy 230 At Elevated Temperatures, Shawoon Kumar Roy
Time-Dependent Crack Growth Behavior Of Alloy 617 And Alloy 230 At Elevated Temperatures, Shawoon Kumar Roy
UNLV Theses, Dissertations, Professional Papers, and Capstones
Two Ni-base solid-solution-strengthened superalloys: INCONEL 617 and HAYNES 230 were studied to check sustained loading crack growth (SLCG) behavior at elevated temperatures appropriate for Next Generation Nuclear Plant (NGNP) applictaions with constant stress intensity factor (K max = 27.75 MPa[checkmark]m) in air. The results indicate a time-dependent rate controlling process which can be characterized by a linear elastic fracture mechanics (LEFM) parameter - stress intensity factor (K). At elevated temperatures, the crack growth mechanism was best described using a damage zone concept. Based on results and study, SAGBOE (stress accelerated grain boundary oxidation embrittlement) is considered the primary reason for …
Mechanical Behavior Of Alloy 230 At Temperatures Relevant To Ngnp Program, Sudin Chatterjee
Mechanical Behavior Of Alloy 230 At Temperatures Relevant To Ngnp Program, Sudin Chatterjee
UNLV Theses, Dissertations, Professional Papers, and Capstones
Identification and selection of suitable structural materials for heat exchanger application within the purview of the next generation nuclear plant (NGNP) program constitute a major challenge. This challenge stems from the lack of many desired metallurgical and mechanical properties of conventional metallic materials and alloys for applications at temperatures approaching 950 oC. Nickel (Ni)-base Alloy 230 has been highly recommended as a suitable structural material for such application due to its excellent resistance to high-temperature plastic deformation and superior corrosion resistance in many hostile environments. Systematic studies on tensile, fracture toughness, creep, stress-rupture and creep-fatigue behavior of this alloy have …
Stress Corrosion Cracking Resistance Of Martensitic Stainless Steels For Transmutation Applications, Phani P. Gudipati
Stress Corrosion Cracking Resistance Of Martensitic Stainless Steels For Transmutation Applications, Phani P. Gudipati
UNLV Theses, Dissertations, Professional Papers, and Capstones
The susceptibility of Alloy EP-823 to stress corrosion cracking has been evaluated using smooth and notched cylindrical specimens in neutral and acidic solutions at ambient and elevated temperatures using constant load and slow strain rate testing (SSR) techniques. C-ring and U-bend specimens have also been tested in the acidic solution. The effect of hydrogen on the cracking susceptibility has been evaluated under controlled cathodic potential. While no failures were observed with smooth specimens at constant load, the notched specimens showed failure. The SSR test results indicate that the true failure stress (o'f), time to failure and ductility parameters …
Environment Assisted Cracking Of Target Structural Materials Under Different Loading Conditions, Venkataramakrishnan Selvaraj
Environment Assisted Cracking Of Target Structural Materials Under Different Loading Conditions, Venkataramakrishnan Selvaraj
UNLV Theses, Dissertations, Professional Papers, and Capstones
Martensitic Alloy HT-9 has been tested for its evaluation of stress corrosion cracking resistance in neutral and acidic solutions at ambient and elevated temperatures incorporating smooth and notched cylindrical specimens under constant load and slow strain rate (SSR) conditions. C-ring and U-bend specimens have also been tested for stress corrosion cracking evaluation in the acidic solution. The role of hydrogen on the cracking tendency has been evaluated by cathodic applied potential.
The results of constant load testing enabled the determination of the threshold stress for stress corrosion cracking in susceptible environments. The magnitudes of ductility parameters were reduced with increasing …