Compressive Creep Of Basic Refractories, Maurice E. Green

Masters Theses

"The microstructure and mineralogical composition of direct bonded, 50 wt.% magnesia - 50 wt.% chrome ore refractory compositions containing controlled additions of silica were correlated with their compressive creep behavior in the temperature range 1450⁰ to 1550⁰C under stresses of 100 to 175 psi. Steady state creep rates were determined from the linear regression of the steady state regions of deformation on time. Apparent activation energies and deformation flow characteristics were determined from the temperature and stress dependence of the steady state creep rates. Silica contents up to 3.5 wt.% increased the amount of direct intergranular bonding which decreased the …

Kinetics Of The Formation Of Strontium Zirconate, W. H. Parker

Masters Theses

"The decomposition rate of strontium carbonate (SrC0₃) was measured using a TGA apparatus. It was found to deviate slightly from zero order classical reaction. The rate of formation of strontium zirconate (SrZr0₃) from zirconium oxide (ZrO₂) and strontium oxide (SrO) in the form of the decomposition product of SrCO₃ was measured using quantitative x-ray diffraction for mineralogical analysis. It was found to most nearly follow the Zhuravlev-Lesokhin-Tempel' man rate equation. The rate of decomposition of strontium carbonate was found to be more rapid than the rate of formation of strontium zirconate such that for the most part strontium oxide is …

Cutting Nbs Budget, Norbert J. Kreidl

Materials Science and Engineering Faculty Research & Creative Works

No abstract provided.

Optical Reflectance Spectra Of Chromium (Iii) In Mgo-Ss, Thomas Spencer Montgomery

Doctoral Dissertations

"The valence state and coordination site of the transition-metal ion, chromium, was investigated in a MgO host lattice. The chromium ion incorporated into poly-crystalline MgO by quenching from elevated temperatures allowed investigation of a single crystalline phase, MgO-solid solution (ss). The chromium ion was confirmed to occur in the trivalent state and to occupy octahedral cation sites in the MgO lattice by the use of optical reflectance spectroscopy. The effect of the concentration of the chromium ion on the crystal field splitting energy, 10 Dq, permitted analysis over a range of Dq/B values. In conjunction, MgO-ss lattice parameters examined as …

Decomposition Of Cr(Oh)₃ To Form Active Cr₂C₃, Timothy A. Clancy

Doctoral Dissertations

"This study was concerned with the sinterability of Cr₂C₃ powders produced by the calcination of a Cr(OH)₃ gel. The decomposition of the gel was investigated by thermogravimetric analysis, X-ray analysis and microscopic examination. Comparison was made between the size of crystallites as determined by X-ray line broadening and the size of aggregated particles as determined by independent means. These lineal measurements were compared to surface area measurements on the calcined powders. The degree of sinterability was judged from the density measurements on Cr₂C₃ pellets fired under air, oxygen and nitrogen atmospheres. Energies of activation of 25 and 20 kilocalories per …

Compressive Creep Of High Alumina Refractories, Vernon Lee Burdick

Masters Theses

"The deformation of refractory materials consisting of 90% sintered or fused alumina plus 10% silica was measured at temperatures from 1450 to 1515⁰C and a compressive stress of 100 psi. Creep rates and activation energies were determined from the steady state portion of deformation vs. time data and correlated with the mineralogical composition. Supplemental measurements included x-ray diffraction, electron probe microanalysis, apparent porosity and tensile strength. conditions having an important effect upon the mineralolgical composition were: (1) duration of heat treatment, (2) amount of sodium oxide impurity, and (3) reactivity of the alumina grain. Prolonged heat treatment and sodium oxide …

Relationship Of Feldspar Properties To Surface And Volume Defects In Porcelains, Macy Wiiliam Vance

Masters Theses

"Four levels of particle size distribution and four compositions of feldspar ranging from high-potash to high-soda content were evaluated in their effect on body and surface defects and selected engineering properties of an electrical porcelain. It was found that surface blistering defects occurred at a high incidence in porcelain specimens slightly overfired at 1225⁰C in a body composition containing 33% albite (soda), 67% high-potash feldspar blend and a relatively coarse, 140 mesh grind, of the feldspar. The occurrence of surface and volume blisters was correlated with the formation of a microscopic bleb structure in the porcelain matrix. It was also …

Vapor Pressure And Evaporation Coefficient Of Cadmium Oxide, R. Tom Coyle Jr.

Masters Theses

"Knudsen effusion experiments were carried out on CdO in fused silica crucibles at temperatures of 918°K, 1008°K with orifice areas from 2.742x10^-3 cm² to 30.52x10^-2 cm². The experiments were made in a molybdenum-wire, resistance-heated vacuum furnace. Several orifice areas were used at each temperature and reciprocal pressure versus orifice area plots were made. These plots yielded an upper limit to the evaporation coefficient of. 4.15x10^-2. An equilibrium constant for the vaporization reaction

CdO(s) = Cd(g) + 1/20₂ (g)

of

log Keq = 11.12 - 1.952x10⁴/T.

was obtained. Second and third …

Tensile Strength Of Prereacted Porcelain Compositions, Chester Lee Hill

Masters Theses

"The tensile strengths of two porcelain compositions containing prereacted silica and feldspar have been determined with the diametral loading technique. A comparison was made between the strength of the prereacted samples and the strength of samples of the same compositions, but prepared in the conventional manner. At the optimum firing temperature, no significant differences in tensile strengths were observed between the prereacted and control samples for the two compositions studied. At temperatures below and above the optimum firing temperature, the prereacted samples had the higher tensile strengths. The tensile strengths are correlated with the average size of the quartz particles …

The Elastic And Anelastic Constants Of A Synthetic Fluor-Mica Formed By Glass-Ceramic Fabrication Techniques, John H. Ainsworth

Masters Theses

"A tetrasilicic fluor mica, K₂Mg₅Si₈O₂₀F₄, was synthesized using glass forming techniques. Density changes, weight losses, and shrinkage, as well as elastic and anelastic properties, were measured on bars heat-treated at selected temperatures between 500°C and 1150°C to determine the characteristics of this material. Phase changes were followed by determining thermal expansion, logarithmic decrement, and modulus of elasticity from room temperature to 800°C.

It was found that the elastic and anelastic constants decreased gradually with heat treatments from 600°C to 1000°C. This indicated progressively increased structural ordering. Heat treatments above 1000°C …

The Dielectric Properties Of A Synthetic Fluor-Mica Formed By Glass-Ceramic Fabrication Techniques, Ray Fred Schumacher

Masters Theses

"A tetrasilicic fluor-mica, K₂Mg₅Si₈O₂₀F₄, was synthesized, utilizing glass forming techniques and subsequent heat treating of the mica glass. Discs, approximately two inches in diameter, were formed and heat-treated at selected temperatures between 700⁰C. and 1150⁰C. for various time periods. Density change, weight loss, shrinkage, and dielectric properties were measured to determine the characteristics of this material"--Abstract, page ii.

Internal Friction Of Mixed-Alkali Silicate Glasses, James E. Shelby

Doctoral Dissertations

"The mixed alkali effect in silicate glasses was examined from internal friction measurements made over the temperature range from -190 to 500⁰C and at a frequency of 0.4 Hz. Supplemental measurements of the activation energy for the different internal friction peaks, dynamic shear modulus, density, and index of refraction were also made. All measurements were confined to silicate glasses containing mixtures of Li-Na, Li-K, Li-Rb, Li-Cs, Na-K, Na-Rb, Na-Cs, and K-Rb. Rötger's interpretation of the internal friction of mixed-alkali silicate glasses is shown to be incorrect. A previously unreported internal friction peak was observed whenever two different alkali oxides were …

Influence Of Quartz Particle Size And Concentration On The Fracture Stresses Of Triaxial Alumina Porcelain., John David Weyand

Masters Theses

"Quartz particles were introduced into a typical triaxial alumina porcelain. Three levels of particle size and three levels of concentration were studied. The strength sample sizes were large. A diametral- compression loading method was used for strength testing. It was found that the porcelain strength decreased with increasing grain size and concentration of quartz particles. A linear relationship existed between log quartz concentration and mean fracture stress"--Abstract, p. ii

A Preliminary Study Of The Controlled Crystallization Of A Bottle Glass., Narayan M. Sedalia

Masters Theses

The effect of addition of Ti0₂ as a nucleating agent was studied with a bottle glass composition of 74 weight percent Si0₂, l percent Al₂O₃, 5.4 percent Cao, 3.7 percent MgO, 15. 3 percent Na₂O, and 0.6 percent K₂O as a base or original composition. The addition of titanium dioxide ii varied from 3 to 20 weight percent. The composition of this bottle glass was changed by increasing the following ingredients and keeping the other ingredients in the same ratios:

1. Increased 5 weight percent of Al₂O …

A Study Of Crystallization Of Synthetic Fluor-Glaucophane Compositions, Kartini Tjokroatmodjo

Masters Theses

"The ability to form a stable glass and the crystallization properties of four compositions close to that of glaucophane, Na₂Mg₃Al₂Si₈O₂₂(OH)₂ studied. Three glasses were compared with a fourth glass containing no fluorine. The crystallization products of all four glasses were examined between the temperature range 600 - 1200°C. The crystallization products of the three fluorine containing glasses were similar, consisting of mica below 1000°C and of mica, fluor-glaucophane, enstatite and forsterite above 1000°C. In the fluorine free glass, enstatite was the only crystalline phase present below 1000°C, however, forsterite …

Development Of A Fluor-Mica Dielectric Using Glass-Ceramic Fabrication Methods., James Joseph Tuzzeo

Masters Theses

"A tetrasilicic fluor-mica, K₂Mg₅si₈o₂₀F₄, was synthesized using glass-ceramic fabrication methods. Bubbles, rods, and disks of glass-mica were formed, and heat treated at selected temperatures between 620°c and 1160°c for various time periods. Density changes were correlated to mica content to determine the relative amounts of crystalline mica phase precipitated after heat treatment. Dielectric losses and dielectric constants of the glass-mica disks were measured for correlation to mica content"--Abstract, p/ ii

Densification Studies Of Three-Component Refractory Grog Systems., Jerome Dale Patterson

Masters Theses

"The bulk density and crushing strength properties of three-component refractory grog systems that were formed by mechanical impact or by mechanical vibration were determined.

Aqueous alkali silicate solutions of various types, concentrations, and amounts were investigated as room temperature binders for these grog systems. Compositions having maximum bulk densities were determined for each of six different three-component refractory grog systems. The densification rate curves for systems formed by mechanical impact were determined"--Abstract, p. ii

The Effects Of Surface Flaw Density And Configuration On Fracture Stresses Of A Triaxial Porcelain., William H. Daniels

Masters Theses

"The fracture behavior of a model brittle solid containing artificial surface flaws was studied. An industrial ceramic porcelain body was employed as the model brittle material. Sample groups of specimens containing 6, 11, 24, 49,. and 90 sharp surface notches uniformly distributed over a four inch length were broken under pure bending. The fracture data we-re compared to those of an identically treated control group containing no artificial flaws.

The mean strengths of the two groups of lowest flaw density were identical, both being significantly less than that for the control group. Further increases in flaw density resulted in increased …

Solid Solubility Of Sodium Oxide In Tricalcium Aluminate, Joel A. Conwicke

Masters Theses

"The tie line connecting the compounds 3CaO·Al₂O₃ and Na₂O·8CaO·3Al₂O₃ in the ternary system CaO-Al₂O₃-Na₂O was studied at 1250° Celsius.

It was determined that Na₂O can exist in crystalline solution with 3CaO·Al₂O₃ in percentages of about 2.3% or less without any apparent change in the structure of 3CaO·Al₂O₃. X-ray diffraction peaks in the back-reflection region shifted to lower d-spacing values on increasing Na₂O contents.

At a Na₂O content of about 2.7%, each major x-ray …

Mechanism Of Siliconizing Of Molybdenum And Tantalum By Vapor Deposition, Gordon Pu Kong Chu

Doctoral Dissertations

"Molybdenum and tantalum were siliconized in an enclosed system by the hydrogen reduction of silicon tetrachloride with induction heating between 900°C and 1450°C.

The siliconizing process was primarily influenced by the gaseous composition, temperature, time, molar flow ratio (SiCl₄/H₂), geometrical shape and ionization charges. The rate of siliconizing, measured as the weight gain by the fused quartz helix balance, generally follows a parabolic law, y = k t^1/2, where y = weight gain, t = time, and k = rate constant. The activation energy is estimated at 21.6 k cal/mole for siliconizing of molybdenum. …

A Preliminary Study Of The Dielectric Properties Of Bismuth Ferrate Ceramics., John Joseph Schwaller

Masters Theses

"In this investigation some of the results of Fedulov¹⁸ for a composition of 30 percent lead titanate - 70 percent bismuth ferrate were verified. The system of lead zirconatebismuth ferrate was studied with sintering data determined for the series. By X-ray and microscopic analysis the system was determined to be not a solid solution. The dielectric measurements show a linear relation between the dielectric constant and the percent lead zirconate from 100 percent BiFeo₃ to 10 percent BiFeo₃ - 90 percent PbZro₃"--Abstract, p. ii

Influence Of Porosity On The Fracture Stresses Of Electrical Porcelain., Edward Anton Snajdr

Masters Theses

"Spherical pores were induced in a typical quartz electrical porcelain body. Three levels of pore size and four levels of concentration were studied. Large strength sample sizes were employed using a three-point loading and diametral loading method. Data for induced quartz particles is also included"--Abstract, p.ii

Preliminary Investigation Of Acid Treatment For The Stabilization Of Doloma, Deward Pan

Masters Theses

"The work presented in this thesis is the result of an investigation to develop an economical and successful means for producing a stable, hydration resistant compound on the surface of doloma particles by an acid treatment, which does not significantly alter the refractoriness of the material. Granite, a commercial doloma, from Valley Dolomite Corporation, was treated with different concentrations of inorganic acid-water solutions and organic acid-alcohol solutions for varying time at atmospheric pressure and temperature. The treated doloma was examined by (l) X-ray diffraction and (2) the hydration test.

It was found that the organic acid acted as a coating …

A Preliminary Study Of The Effect Of Heat Treatment On The Strength And Microstructure Of A Glass-Ceramic Material, P. D. Ownby

Masters Theses

"The strength and microstructure of a glass-ceramic material of the composition 53 percent SiO₂, 19 percent Al₂O₃, 15 percent MgO, and 13 percent Li₂O were studied. Cylindrical specimens of glass were formed and heat-treated to six different temperature levels for various time periods. The method of strength testing used was a diametral compression loading technique. It was found that the strength of this material increased initially with heat-treatment but then decreased. The strength characteristics of the completely crystallized glass ceramic material were found to be dependent on the initial nucleation period. Some factors which influenced anomalous crystal growth are described. …

Preliminary Investigation Of The Effects Of Seeding Fusion Cast Refractories, Thomas Spencer Montgomery

Masters Theses

"The crystallization process in a zirconia-alumina- silica melt of high viscosity was studied, A system was used of the same composition found in commercial electrocast glass tank refractories. Artificial nucleation was tried in an attempt to control the process of crystallization; the method involved the addition of suitable "seeding" material.

It was found that introduction of nucleation agents consisting of the major component oxides of the system had noted effect upon the course of crystallization. Preferred orientation normally found in unseeded electrocast refractories was diminished with the addition of zirconia grains and amplified with particles of tabular alumina.

Results obtained …

Statistical Analysis Of Fracture Stresses Of Triaxial Porcelain Bodies, Robert E. Moore

Doctoral Dissertations

"Triaxial porcelain bodies containing various forms of silica, quartz, cristobalite and fused silica, were strength tested in bending. Significance tests were employed to discern real differences in the strength sample statistics caused by the various forms of silica. Firings were performed at three temperature levels. The differences in strength sample statistics were correlated to the microstructures of these silica porcelains.

A triaxial alumina porcelain body was employed as a model brittle solid for a study of the effect of flaw density on mean fracture stress. The flaws were introduced in the form of large diameter (d̄ = 115 microns) rounded …

A Vacuum Induction Furnace For Pyrometric Cone Equivalent Determinations, Robert E. Farris

Masters Theses

"Various furnaces which are commonly used for P.C.E. determinations were compared from a literature review. The inadequacies of these furnaces were noted and a furnace was designed, constructed, and evaluated in an effort to minimize or eliminate some of the indicated problems. For this furnace heat is developed in opposed cones (susceptors), which are fabricated from 0.005” molybdenum sheet, by induced (induction) currents from a 10 KW vacuum tube generator. The furnace components are enveloped by a pyrex cylinder in which a vacuum (approximately 1 to 5 micron pressure absolute) is maintained during operation"--Abstract, page ii.

Some Properties Of Chrome-Magnesite Mixtures And Calcium Aluminate Cement-Magnesite Mixtures, Edward Charles Duderstadt

Masters Theses

"The knowledge of the physical and chemical properties of refractories is of great importance in determining their usefulness and application. The thermal expansion of refractories is of particular importance in that it affects the thermal stability of the product. A high coefficient of thermal expansion leads to greater spalling and destruction of the bricks in use. It is, therefore, desirable to develop compositions having low coefficients of thermal expansion. This investigation was undertaken (1) to determine some of the properties of chromite-magnesite refractory mixtures in an attempt to determine the optimum composition of these mixtures, the specific properties including thermal …

Phase Relationships In The Quaternary System Lime-Titania-Zirconia-Silica, Robert Martin Gruver

Doctoral Dissertations

"The phase compatibility relationships for the quaternary system lime-titania-zirconia-silica have been determined by a solid-phase-reaction technique.

Preliminary division of the system into Alkemade tetrahedra was based on the phases found in samples by X-ray diffraction analysis. These samples covered the entire volume of the tetrahedron in a systematic fashion. When the quaternary system had been divided into regions or compatible phases, an analytical method was used to calculate the phase composition of each sample. The relative amounts of each phase in a sample determined by X-ray analysis were compared with the calculated quantities, and agreement between the two methods verified …

Nanbo₃ - Batio₃ - Basno₃ Ceramic Dielectrics, William Dean Mckee

Doctoral Dissertations

"A. The Problem.

The purpose of this investigation was to form by ceramic processes a number of compositions in the ternary system NaNbO₃ - BaSnO₃ - BaTiO₃, to determine certain dielectric properties of these, to study them by means or x-ray diffraction, and to determine the extent or correlation possible between the compositional variation of dielectric properties and the x-ray results.

Compositions investigated contained 50 mole percent or less BaSnO₃. Materials and methods of forming were chosen with the intent that the final bodies should be pure oxide compositions as represented in the ternary …