Materials Science and Engineering Commons^™

Recovery Of Lead From Lead Smelter Mattes, Cheng-Ping Chang

Masters Theses

"A by-product of lead smelting is a matte which consists mostly of lead and copper sulfides. Experiments were conducted to determine the feasibility of removing lead from molten matte by adding iron as a reducing agent. The effectiveness of iron at 1000 and 1100°C was a function of matte composition, but not of temperature except near iron saturation. The lead content of matte could be decreased to as low as 9.0 to 11.6 wt pct (2.3 to 3.0 at. pct) at 1000°C, depending on composition. The effect of oxygen in the matte on lead recovery from iron-saturated mattes was also …

Phase Equilibria In Aqueous Magnesium Chloride, Sulfate, Chromate And Phosphate Systems, Ladawan Urwongse

Doctoral Dissertations

"In the first part of the present study, which is presented in Paper I, solubility of MgO in aqueous HCl solutions at 23° ± 3°C was measured and combined with analyses of neat magnesium oxychloride cements to construct an equilibrium phase diagram for the system MgO-MgCl₂-H₂O. Invariant liquids in equilibrium with Mg(OH)₂ and 5Mg(OH)₂·MgCl₂·8H₂O (5.1.8), with 5·1·8 and 3Mg(OH)₂·MgCl₂·8H₂O (3·1·8), and with 3·1·8 and MgCl₂·6H₂O were located at 0.8 ± 0.2 MgO, 17.0 ±0.5 MgCl₂; at 1.0 …

Development Of Impervious Low Thermal Expansion Petalite Bodies, Suchinda Chotipanich

Masters Theses

"Impervious petalite bodies were formulated from petalite, lithium aluminosilicate frit and kaolin. Thermal expansion coefficients for selected bodies were less than 2 x 10⁻⁶ /°C(20 - 600 °C). Mineralogy and the reactions in systems containing petalite, lithium aluminosilicate frit and kaolin were observed. Silica-poor high quartz solid solution was found to be the reaction product formed from the reaction between frit and kaolin before conversion to ß-spodumene solid solution at higher temperatures. The crystallization of the ß-spodumene solid solution phases in this system did not occur at the same temperature resulting in variation in the size of the crystallites. The …

The Effect Of Antimony, Chloride Ion, And Glue On Copper Electrorefining, Thomas J. O'Keefe, L. R. Hurst

Materials Science and Engineering Faculty Research & Creative Works

A study has been made to determine the effect of antimony, chloride ion, and glue on copper electrorefining. All deposits were made at a temperature of 65° C on a titanium cathode. Current densities of 398 A m-2 and 133 A m-2 were used. The deposits were analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD) to determine morphology and crystal orientation. Atomic absorption (AA) and Auger spectroscopy (AES) were used to study the chemical composition of the deposits and a simple bend test was used to determine structural integrity. It was found that when the antimony concentration in …

An X-Ray Diffraction Analysis Of The Lacro₃-Laalo₃ Solid Solution Series, Robin Ashley Murphy

Masters Theses

"A crystallographic study was made of powders from the LaCr_1-x Al_xO₃, La_.90(Mg_.05 Cr_1-x Al_x )_.95O_2.83 , and La_1±xCrO₃ systems. The relationships between composition and thermal expansion, electrical conductivity, and vaporization were also investigated. The x-ray diffraction data of the LaCrCO₃ - LaAlO₃ compounds showed the system to form a single phase solid solution for any given sample from the series. The orthorhombic to rhombohedral phase transition was depressed to below room temperature at approximately 13% Al⁺³ substitution"--Abstract, page ii.

Discussion, Ronald A. Kohser

Materials Science and Engineering Faculty Research & Creative Works

No abstract provided.

Disk And Strip Forging With Side Surface Foldower: Part 2: Evaluation Of The Upper-Bound Solutions, Ronald A. Kohser, B. Avitzur

Materials Science and Engineering Faculty Research & Creative Works

The upper-bound solutions developed in Part 1 are evaluated with regard to their ability to produce a lower value for required power (load, pressure, or work). Comparisons made with existing solutions such as the triangular field solution and one-zone bulge solution show that for strip, each solution has a domain of geometry and friction in which it is superior. The new solution produces a lower upper-bound for conditions of high interface, friction and relatively thin specimen, the area where fold over is the observed mode of flow. For solid cylindrical disks, the solution fails to improve upon existing analyses, but …

Effect Of Collagen And Chloride Additions On Electrolytic Copper Deposits, William P. Lorenz, Thomas J. O'Keefe, Carlo B. Sonnino

Materials Science and Engineering Faculty Research & Creative Works

The effects of collagen concentration and molecular weight on the morphology and crystal orientation of electrolytic copper deposits have been determined and compared. The effect of chlorides in the presence of collagen on the above properties has also been investigated. Three different molecular weight collagens were studied and the consumption rate of each was determined by chemical analysis of the electrolyte before and after electrodeposition. Two-hour deposits were made in an electrolyte containing the subject collagens in concentrations ranging from 1.2 to 38.4 mg 1-1. Scanning electron and light microscopes and X-ray diffraction were used to evaluate the electrodeposits. © …

The Effects Of Certain Impurities And Their Interactions On Zinc Electrowinning, Donald R. Fosnacht

Doctoral Dissertations

“The effects of germanium, antimony, arsenic, cobalt, glue, and free acid concentration were studied on both commercial and synthetic electrolytes. The effects of a single factor and the combined effects of multiple factors were elucidated. The temperature, zinc concentration, and current density were also varied. It was found that the acid concentration was the most critical factor when impurity levels were at normal plant solution concentrations. The ranges where the effect of the impurity became apparent were: greater than 20 ppb for antimony; 40 ppb for germanium; 120 ppb for arsenic; and 7-8 mg/l for cobalt for a solution containing …

Evaluation Of Organic Additives For Use In Zinc Electrowinning, R. C. Kerby, H. E. Jackson, Thomas J. O'Keefe, Yar Ming Wang

Materials Science and Engineering Faculty Research & Creative Works

Organic additives are used extensively in zinc electrowinning to assist in controlling the process. A cyclic voltammetry technique has been developed to provide a rapid, quantitative evaluation of the effectiveness of selected organic additives in minimizing the deleterious effects that impurities, such as antimony, have on zinc deposition. Results have indicated that animal glues are more effective than the other organic additives tested, which included several gums, enzymes, and amino acids, in relation to the current efficiency of zinc production. Of the various animal glues compared in this research, the most effective appeared to have average molecular weights in the …

Dense Chromium Sesquioxide, P. D. Ownby

Materials Science and Engineering Faculty Research & Creative Works

A sintered, fine grained, polycrystalline, essentially fully dense, essentially single phase Cr₂O₃ body is prepared by sintering Chromium Sesquioxide (Cr₂O₃) at essentially the equilibrium oxygen partial pressure (P_O2) for the formation of CrO ₃ from its elements at the sintering temperature. To achieve optimum theoretical density a second metal oxide dopant such as MgO, capable of controlling the grain size, is added. In addition, Cr₂O₃ bodies are rendered more stable, and thus have a longer life, by maintaining over the body an atmosphere which is essentially equilibrium Po, …

Evaluation Of Organic Additives For Use In Zinc Electrowinning, R. C. Kerby, H. E. Jackson, Thomas J. O'Keefe, Yar Ming Wang

Materials Science and Engineering Faculty Research & Creative Works

Organic additives are used extensively in zinc electrowinning to assist in controlling the process. A cyclic voltammetry technique has been developed to provide a rapid, quantitative evaluation of the effectiveness of selected organic additives in minimizing the deleterious effects that impurities, such as antimony, have on zinc deposition. Results have indicated that animal glues are more effective than the other organic additives tested, which included several gums, enzymes, and amino acids, in relation to the current efficiency of zinc production. Of the various animal glues compared in this research, the most effective appeared to have average molecular weights in the …

Positron Lifetime As A Function Of Grain Size, Hollis P. Leighly

Materials Science and Engineering Faculty Research & Creative Works

Published data on positron annihilation lifetime in copper as a function of grain size have been analyzed to show that there is a linear relationship between the internal grain boundary surface area, per unit volume, S v, and the positron lifetime, τ. The analysis indicates that grain boundaries are important in the trapping of positrons. It is suggested that the slope of the resulting straight line, dS v/dτ, can be used to determine the annihilation rate of the grain boundaries. © 1977 Springer-Verlag.

Low Order Correction For Subsurface Contributions In Diffusion Experiments, D. Powers, Manfred Wuttig

Materials Science and Engineering Faculty Research & Creative Works

No abstract provided.

The Al2o3‐Sio2‐Zro2 Liquidus Surface: A Discussion, Charles A. Sorrell

Materials Science and Engineering Faculty Research & Creative Works

No abstract provided.

Glass In The Year 2000, Norbert J. Kreidl

Materials Science and Engineering Faculty Research & Creative Works

No abstract provided.

Subsolidus Equilibria And Stabilization Of Tetragonal Zro2 In The System Zro2‐Al2o3‐Sio2, Charles A. Sorrell

Materials Science and Engineering Faculty Research & Creative Works

The irreversible reaction between zircon and alumina to form mullite and zirconia was observed to proceed very slowly at 1480°C, confirming the existence of a stable join between mullite and zirconia in addition to the join between mullite and zircon. Attempts to determine equilibrium assemblages in powder samples of several combinations of the constituents at 1300° and 1400°C were unsuccessful. Metastable tetragonal ZrO₂ was observed in fired powder samples containing kaolinite, in fired zircon‐alumina samples, and in calcined gels prepared from zirconyl nitrate, aluminum nitrate, and colloidal silica in water. Tetragonal ZrO₂ was the dominant crystalline phase in …

Suggested Chemistry Of Zinc Oxychloride Cements, Charles A. Sorrell

Materials Science and Engineering Faculty Research & Creative Works

Solutions of ZnCl₂ were prepared from ZnCl₂·nH₂O and by reaction of zinc metal with HCl. Specific gravities and pH values were determined as a function of composition. A ternary phase, 4ZnO·ZnCl₂·5H₂O, was precipitated when the ZnCl₂ solutions were diluted to a pH of 5.48 ± 0.05. Mixtures of ZnO with ZnCl, and HCI solutions were equilibrated in sealed containers and analyzed by X‐ray diffraction. The resulting phase diagram shows 2 ternary phases, 4ZnO·ZnCl₂·5H₂O (4·1·5) and ZnO·ZnCl₂·2H₂O (1.1.2), both of which are soluble …

Evaluation Of Zinc Sulfate Electrolytes By Cyclic Voltammetry And Electron Microscopy, Bruce A. Lamping, Thomas J. O'Keefe

Materials Science and Engineering Faculty Research & Creative Works

A cyclic voltammetric technique has been developed for approximating the quantities of active chemical species present in zinc sulfate electrolytes. The experimental apparatus consisted of a Pyrex "H" cell, an aluminum cathode encased in a Teflon holder, a carbon anode and a mercurous sulfate reference electrode. Voltammograms were obtained using industrial, purified neutral leach solution (Cominco Ltd., Trail, BC) acidified to give a final concentration of 0.77 M Zn++ and 1 M H2SO4. The polarization curves were then evaluated and used as reference standards to compare with results obtained when various organic and inorganic additions were made. The deposit morphologies …

Intermetallic Reactions In Vacuum-Deposited Nickel And Gold Films On (111) Silicon Single Crystals, K. H. Yoon, Gordon Lewis, L. L. Levenson

Materials Science and Engineering Faculty Research & Creative Works

Pure nickel and gold thin films were vacuum-deposited on (111) silicon single crystals. When Ni/Au/Si or Au/Ni/Si samples were heated to about 550° in situ, hexagonal or deformed hexagonal shaped crystallites were formed on the silicon substrates. The composition of these crystallites was determined by using x-ray diffraction, scanning electron microscopy and scanning Auger microprobe methods. The crystallites were identified as NiSi2. The crystal-lites on the (111) silicon plane parallel to the surface appeared as regular hexagons while the inclined crystal-lites resembled trapezia. The results of Auger spectra and in-depth composition profiles for Ni, Au, and Si showed that the …

Electrical Degradation In High Purity Barium Titanate, Jeffrey Duncan Keck

Doctoral Dissertations

"The stability of BaTiO₃-type insulators to DC fields has long been recognized as one of the important factors in determining the quality of a capacitor which uses such a material as its dielectric. The slow increase of the electrical conductivity of an insulator which is stressed by DC fields at levels below the breakdown strength is normally termed degradation. Since degradation is a very common malady to the ceramic capacitor manufacturers, many studies have been conducted over the past two decades in efforts to learn how to remedy the problem.

The results of previous studies have shown that …

On The Effects Of Antimony And Glue On Zinc Electrocrystallization Behaviour, D. J. Robinson, Thomas J. O'Keefe

Materials Science and Engineering Faculty Research & Creative Works

An investigation has been made to determine the effects that additions of glue and antimony have on the electrowinning of zinc from acid sulphate solutions. In particular, the zinc crystal growth and cathode current efficiencies were studied in an attempt to establish a correlation between morphology and the nature of the additives. Operating conditions of 55 A ft-2* and 35°C were used for most of the experiments with electrolyte concentrations of approximately 55 gl-1 zinc and 150 gl-1 H2SO4. Additional runs were made at 40,75 and 100 Aft-2 at 30,40 and 50°C in order to verify certain trends. Primarily by …

Interpretation Of Some Of The Basic Features Of Field-Ion Image Projections From A Hemispherical To A Planar Surface Using Moire Patterns, P. D. Ownby, Robert M. Doerr, Walter Bollmann

Materials Science and Engineering Faculty Research & Creative Works

No abstract provided.

The Effect Of Receiver Pressure On The Observed Flow Pattern In The Hydrostatic Extrusion Of Bimetal Rods, Ronald A. Kohser

Materials Science and Engineering Faculty Research & Creative Works

No abstract provided.

The Martensite Transformation, Manfred Wuttig, Tetsuro Suzuki

Materials Science and Engineering Faculty Research & Creative Works

No abstract provided.

Void-Strengthening In Aluminum And Its Nature, P. G. Manusmare, Hollis P. Leighly

Materials Science and Engineering Faculty Research & Creative Works

Temperature and strain rate dependence of yield strength were used to analyze the nature of aluminum strengthened by the formation of voids. Aluminum rods 99.999% pure were quenched and heat treated to form voids with an approximate density of 1013-1014 voids/cm3. Voids in selected samples were observed by electron microscopy. The yield strength of the void strengthened samples was measured at various temperatures from 77 to 593 K and at two strain rates, 3.33 x 10-2/s and 1.67 x 10-3/s. Tests at room temperature and at 77 K were made at various strain rates. The similarity of Coulomb's approach to …

A Suboptimal Control Law To Improve The Transient Stability Of Power Systems, Aditya Kumar, Earl F. Richards

Materials Science and Engineering Faculty Research & Creative Works

The application of optimal control theory to damp the electromechanical oscillations associated with the transient conditions in power systems has been given little attention. A suboptimal control law which minimizes the sum of the performance indices of the two linear systems given by a piecewise linear model of a power system improves the transient stability better than the usual "optimal" control law obtained from a linearized model. Further, the suboptimal control law presented in this paper assures stability of the system for all disturbances resulting in rotor oscillations of magnitudes less than a preselected limit. Copyright © 1976 by The …

Anion Grain-Boundary Diffusion In Soidum Chloride, K. S. Sabharwal, J. Mimkes, Manfred Wuttig

Materials Science and Engineering Faculty Research & Creative Works

The grain-boundary diffusion of 131I in Harshaw pure and Ca-doped NaCl was investigated in the temperature range between 430 and 560°C. The Arrhenius plot of the grain-boundary diffusivity parameter Dδ displays a marked dip at around 510°C. It is proposed that this dip is due to a phase transformation occurring at the grain boundary, possibly calcium segregation.

Subsolidus Equilibria And Metastable Phase Development In The System Zro₂-Al₂O₃-Sio₂, Charles Christopher Sorrell

Bachelors Theses

"Subsolidus equilibria in the low silica portion of the system ZrO₂-Al₂O₃-SiO₂ were studied by X-ray diffraction of quenched samples fired at 1300°, 1400°, and 1480°C. Samples prepared as powders from combinations of a-Al₂O₃, Al(OH)₃, silicic acid, ZrO₂, and kaolinite reacted very slowly at 1300° and 1400°C and the trends toward equilibria are not apparent. A mixture of zircon and Al(OH)₃ reacted slowly at 1480°C to form mullite and ZrO₂, indicating that the latter phases are the stable assemblage rather than zircon and alumina. A gel prepared from aluminum nitrate, zirconyl nitrate, and colloidal silica reacted at 1480°C to form alumina, …

The Influence Of Oxygen Activity On Sintering Of Strontium Doped Lanthanum Chromite., Leslie Groupp

Masters Theses

"The influence of oxygen activity upon the sintering of lanthanum chromite (La_1-xSr_x CrO₃) with x ranging from Oto 0.2 was investigated using chemically prepared powders of <0.1 microns particle size. The results show that at a temperature of 1740 ° C densities of >92% of theoretical could be achieved if the oxygen activities were maintained in the 10^-11 to 10^-12 atm. range. If oxygen activity exceeds 10^-10 atm., densities of not >80% theoretical could be obtained. For the compositions studied, room temperature X-ray analysis of both the starting powders and sintered compacts show the compositions to be orthorhombic and single phase. The ambient lattice parameters and resistivity measurements decreased …