Engineering Science and Materials Commons^™

College Of Engineering Senior Design Competition Spring 2013, University Of Nevada, Las Vegas

Fred and Harriet Cox Senior Design Competition Projects

Senior Design Experience

Part of every UNLV engineering student's academic experience, the Senior Design project stimulates engineering innovation and entrepreneurship. Each student in their senior year chooses, plans, designs and prototypes a product in this required element of the curriculum. Working in teams, the senior design project encourages students to use everything learned in the engineering and computer design programs to create a practical, real world solution to an engineering challenge.

Beyond the classroom ...

Because of the requirement to work in teams, students also build good communication skills, presentation skills and even business writing skills. They also have to …

Plastic Deformation Of Astm A36 Steel Using Two-Stage Light Gas Gun, Shawoon Kumar Roy

College of Engineering: Graduate Celebration Programs

To characterize material deformation in high velocity impact. To validate material models for computation simulation purposes.

This ongoing research is an attempt to study the plastic deformation of A36 steel plate (0.5” thick) under hypervelocity impact. Plastic deformation of the target plate was simulated using finite element software LS-DYNA.

Analysis Of Bolted Joints Under Medium And High Impact Loading, Deepak Sankar Somasundaram, Mohamed Trabia, Brendan J. O'Toole

College of Engineering: Graduate Celebration Programs

• Develop test fixture for medium impact study on bolted joints
• Create FEA model that can replicate the experiment
• Develop test fixture for high impact loading
• Create FEA model and select material properties that can produce results that
  closely match experiments.
• Compare different modeling techniques for high impact loading

Numerical Characterization Of The Hydrodynamics And Thermal Behavior Of Air Flow In A "Flex-Duct" Air Distribution System, Samad Gharehdaghi, Samir Moujaes

College of Engineering: Graduate Celebration Programs

The aim of this research paper is to compute the hydrodynamic and heat transfer characteristics of the air flow inside a flexible duct used for residential/small commercial buildings. Various new information which manufacturers do not provide usually are produced numerically among which heat transfer coefficient, needed for estimating heat loss, is a principal one. Circulation zones in depressions are found to exist. It is shown that these regions act as an insulator and decrease the heat loss along the duct. The results show that fully developed conditions exist much earlier with regard to the inlet for both hydrodynamic and thermal …

Shock And Vibration Isolation System For Ambulatory And Litter Patients In Ground And Air Medical Transport, Mohamad R. Hachem

UNLV Theses, Dissertations, Professional Papers, and Capstones

This project explored the effectiveness of seat and litter air bladder technologies in reducing patient exposure to whole body shock and vibration during ground borne and airborne medical transport. Several seat and litter air bladder configurations were examined during field tests in a U.S. Army RG-33 MRAP ambulance and a U.S. Army HH-60M Black Hawk helicopter. The MRAP field tests were conducted at Ft. Detrick, Maryland. The Black Hawk field tests were conducted at Ft. Rucker, Alabama.

During the field tests, tri-axial vibration signals were recorded on a 16-channel CoCo90 Data Logger/Frequency Analyzer and then post processed in the laboratory …

Numerical Modeling Of High Temperature Bayonet Heat Exchanger And Decomposer For Decomposition Of Sulfur Trioxide, Vijaisri Nagarajan, Yitung Chen, Tzu-Chen Hung, Qiuwang Wang, Valery Ponyavin

College of Engineering: Graduate Celebration Programs

Motivation

• Hydrogen is an attractive energy carrier in the future energy technology.

• Hydrogen is produced from splitting of water through various process namely electrolysis, photo-electrolysis, photo-biological production and thermochemical water-splitting.

• The aim of this study is to numerically investigate fluid flow, heat transfer and chemical reaction in bayonet high temperature heat exchanger and decomposer.

• Parametric studies are performed to achieve maximum decomposition with less pressure drop.

Cellular Automaton For Simulation Of Oxide Layer Growth Influenced By Chromium Concentration Of Structure Material, Kuan-Che Lan, Yitung Chen, Ge-Ping Yu, Tzu-Chen Hung

College of Engineering: Graduate Celebration Programs

Chromium, an important alloying element, has been added in ferrous and nickel based alloy such as stainless steels and Inconel alloy to improve the corrosion resistance. High corrosion resistance of structural materials in extremely high working temperature is one crucial R&D objective of Gen IV nuclear power plants which propose to raise the thermal efficiency via high working temperature. A cellular automaton (CA) model based on the stochastic approach was proposed to simulate the process of oxidation and corrosion of structural material in flowing fluid. The relation of chromium concentration against oxide layer thickness during a specific period was found. …

Thermal Conductivity Measurement With 3Ω Method Background And Synopsis Of Its Implementation, Fiifi Blankson

College of Engineering: Graduate Celebration Programs

ABSTRACT

Continued advances in nanostructured materials have made it necessary to develop materials with specific thermoelectric properties. The 3ω Method provides an accurate measurement of one such property, thermal conductivity. It will be used in this research to find high electrical conductivity alloys with low thermal conductivity.

College Of Engineering Senior Design Competition Fall 2009, University Of Nevada, Las Vegas

Fred and Harriet Cox Senior Design Competition Projects

Each student in his or her senior year chooses, plans, designs, and prototypes a product in this required element of the curriculum. The senior design project encourages the student to use everything learned in the engineering program to create a practical, real-world solution to an engineering challenge.

A highlight of the year-long senior design project is the senior design competition. This competition, which usually takes place the week before finals each semester, helps focus the senior students on increasing the quality and potential for commercial application for their design projects.

Judges from local industry evaluate the projects on innovation, commercial …

Doppler Broadening Analysis Of Steel Specimens Using Accelerator Based In Situ Pair Production, V. Makarashvili, Douglas P. Wells, Ajit K. Roy

Mechanical Engineering Faculty Research

Positron Annihilation Spectroscopy (PAS) techniques can be utilized as a sensitive probe of defects in materials. Studying these microscopic defects is very important for a number of industries in order to predict material failure or structural integrity. We have been developing gamma‐induced pair‐production techniques to produce positrons in thick samples ( ∼4–40 g/cm2, or ∼0.5–5 cm in steel). These techniques are called ‘Accelerator‐based Gamma‐induced Positron Annihilation Spectroscopy’ (AG‐PAS). We have begun testing the capabilities of this technique for imaging of defect densities in thick structural materials. As a first step, a linear accelerator (LINAC) was employed to produce photon beams …

The Effect Of Silicon Content On Impact Toughness Of T91 Grade Steels, Ajit K. Roy, Pankaj Kumar, Debajyoti Maitra

Mechanical Engineering Faculty Research

The impact resistance of silicon (Si)-containing modified 9Cr-1Mo steels has been investigated within a temperature regime of -40 to 440°C using the Charpy method. The results indicate that the energies absorbed in fracturing the tested specimens were substantially lower at temperatures of -40, 25, and 75°C compared to those at elevated temperatures. Lower impact energies and higher ductile-to-brittle-transition-temperatures (DBTTs) were observed with the steels containing 1.5 and 1.9 wt.% Si. The steels containing higher Si levels exhibited both ductile and brittle failures at elevated temperatures. However, at lower temperatures, brittle failures characterized by cleavage and intergranular cracking were observed for …

The Role Of Silicon Content On Environmental Degradations Of T91 Steels, Ajit K. Roy, D. Maitra, Pankaj Kumar

Mechanical Engineering Faculty Research

T91 grade steels showed a gradual enhancement in tensile ductility at ambient temperature due to an increase in Si content from 0.5 to 2.0 weight percent (wt.%). However, the ultimate tensile strength was reduced only above 1.5 wt.% Si. The corrosion potential became more active in an acidic solution with increasing temperature. The cracking susceptibility in a similar environment under a slow-strain-rate (SSR) condition was enhanced at higher temperatures showing reduced ductility, time to failure, and true failure stress. Cathodic potentials applied to the test specimens in SSR testing caused an enhanced cracking tendency at 30 and 60°C, suggesting hydrogen …

Tensile Deformation Of A Nickel-Base Alloy At Elevated Temperatures, Ajit K. Roy, Anand Venkatesh, Vikram Marthandam

Mechanical Engineering Faculty Research

The results of tensile testing involving Waspaloy indicate that the failure strain was gradually reduced at temperatures ranging between ambient and 300 °C. Further, serrations were observed in the engineering stress versus strain diagrams in the temperature range of 300-600 °C. The reduced failure strain and the formation of serrations in these temperature regimes could be the result of dynamic strain aging of this alloy. The extent of work hardening due to plastic deformation was reduced at temperatures above 300 °C. A combination of ductile and intergranular brittle failures was seen at temperatures above 600 °C. γ′ was detected at …

College Of Engineering Senior Design Competition Spring 2007, University Of Nevada, Las Vegas

Fred and Harriet Cox Senior Design Competition Projects

Part of every UNLV engineering student’s academic experience, the senior design project stimulates engineering innovation and entrepreneurship. Each student in their senior year chooses, plans, designs, and prototypes a product in this required element of the curriculum. A capstone to the student’s educational career, the senior design project encourages the student to use everything learned in the engineering program to create a practical, real world solution to an engineering challenge.

The senior design competition helps to focus the senior students in increasing the quality and potential for commercial application for their design projects. Judges from local industry evaluate the projects …

College Of Engineering Senior Design Competition Spring 2006, University Of Nevada, Las Vegas

Fred and Harriet Cox Senior Design Competition Projects

Part of every UNLV engineering student’s academic experience, the senior design project stimulates engineering innovation and entrepreneurship. Each student in their senior year chooses, plans, designs and prototypes a product in this required element of the curriculum. A capstone to the student’s educational career, the senior design project encourages the student to use everything learned in the engineering program to create a practical, real world solution to an engineering challenge.

The senior design competition helps to focus the senior students in increasing the quality and potential for commercial application for their design projects. Judges from local industry evaluate the projects …

Experimental And Finite Element Analysis Of Preloaded Bolted Joints Under Impact Loading, Brendan O'Toole, Kumarswamy Karpanan, Masoud Feghhi

Mechanical Engineering Faculty Research

One of the primary parameters in analyzing bolted joints is preload in the bolt. We have considered several possible preload modeling techniques to analyze the effect of preload on the dynamic response of the bolted joints. Five different methods of applying preload in the nonlinear finite element analysis are evaluated. These methods are “force on bolt and nut”, “force on bolt shank”, “interference fit”, “thermal gradient” and “initial stress method”. Explicit and implicit analyses are used for transient response and preload generation in bolt respectively. Time history and shock response spectrum are used to compare experimental and simulation results. Simulation …

Cracking Of Martensitic Alloy Ep-823 Under Controlled Potential, Ajit K. Roy, M. K. Hossain

Mechanical Engineering Faculty Research

The susceptibility of martensitic Alloy EP-823 to stress corrosion cracking was evaluated with and without an applied cathodic potential using the slow-strain-rate (SSR) testing technique. The magnitude of the applied potential was based on the corrosion potential determined by cyclic polarization. The cracking susceptibility in an acidic environment at different temperatures was expressed in terms of the true failure stress (ơ_f), time to failure (TTF), and ductility parameters, including percent elongation (%El) and percent reduction in area (%RA). The data indicate that the magnitudes of ơ_r, TTF, %El, and %RA were reduced due to cathodic charging. …

Study Of Secondary Electron Emission From Niobium At Cryogenic Temperatures, Anoop George

UNLV Theses, Dissertations, Professional Papers, and Capstones

The objective of this project is to study the properties of secondary electron emission from niobium samples, cleaned at the Los Alamos National Laboratory, at cryogenic temperatures to enhance existing multipacting codes with data on the samples. The predominant cause of power loss in radio-frequency superconducting accelerators cavities is multipacting. This project studies the secondary electron distribution from niobium metal due to incident primary electrons. The experiments on the niobium sample are performed in an environment close to that present in a superconducting accelerator cavity.

The experiment is performed in a vacuum chamber capable of achieving ultra high vacuum levels …

Tensile Properties Of Martensitic Stainless Steels At Elevated Temperatures, Ajit K. Roy, Srinivasarao R. Kukatla, Bhagath Yarlagadda, V. N. Potluri, Martin Lewis, Brendan O'Toole

Mechanical Engineering Faculty Research

Tensile properties of quenched and tempered martensitic alloys EP-823, HT-9, and 422 were evaluated at temperatures ranging from ambient to 600 °C as a function of three different tempering times. The results indicated that the yield strength, ultimate tensile strength, and the failure strength were gradually reduced with increasing temperature. The ductility parameters were enhanced at elevated temperatures due to increased plastic flow. However, the tempering time did not significantly influence these properties. The evaluation of the fracture surfaces by scanning electron microscopy revealed reduced cracking and dimpled microstructures, indicating enhanced ductility at higher testing temperatures.

Residual Stress Characterization In Structural Materials By Destructive And Nondestructive Techniques, Ajit K. Roy, Anand Venkatesh, Vikram Marthandam, Satish Dronavalli, Douglas P. Wells, Ronald Rogge

Mechanical Engineering Faculty Research

Transmutation of nuclear waste is currently being considered to transform long-lived isotopes to species with relatively short half-lives and reduced radioactivity through capture and decay of minor actinides and fission products. This process is intended for geologic disposal of spent nuclear fuels for shorter durations in the proposed Yucca Mountain repository. The molten lead-bismuth-eutectic will be used as a target and coolant during transmutation, which will be contained in a subsystem vessel made from materials such as austenitic (304L) and martensitic (EP-823 and HT-9) stainless steels. The structural materials used in this vessel will be subjected to welding operations and …

Sub-Surface Corrosion Research On Rock Bolt System, Perforated Ss Sheets And Steel Sets For The Yucca Mountain Repository, Dhanesh Chandra, Jaak J.K. Daemen, Jaime Gonzalez, Raymond Keeler, Amy J. Smiecinski

Publications (YM)

The objective of the proposed investigation is to conduct corrosion research and predict the durability of rock-bolts and other underground metallic roof supports. In critical areas, it is possible to use highly corrosion resistant steels for rock bolts at Yucca Mountain (YM) repository, as the steel rock bolts, as well as other materials such as Bernold type shields for tunnels at YM site [1-4]. In addition, there is propensity for stress corrosion cracking as well as hydrogen induced cracking in rock bolts likely to occur in YM repository emplacement under drift conditions. As corrosion of these materials for underground support …

Stress Corrosion Cracking Resistance Of Martensitic Stainless Steels For Transmutation Applications, Phani P. Gudipati

UNLV Theses, Dissertations, Professional Papers, and Capstones

The susceptibility of Alloy EP-823 to stress corrosion cracking has been evaluated using smooth and notched cylindrical specimens in neutral and acidic solutions at ambient and elevated temperatures using constant load and slow strain rate testing (SSR) techniques. C-ring and U-bend specimens have also been tested in the acidic solution. The effect of hydrogen on the cracking susceptibility has been evaluated under controlled cathodic potential. While no failures were observed with smooth specimens at constant load, the notched specimens showed failure. The SSR test results indicate that the true failure stress (o'_f), time to failure and ductility parameters …

Cfd Analysis Of 3-D Thermalhydraulics Flow Effects On Wall Concentration Gradient Profiles For Lbe Loop Fittings, Narain Armbya

UNLV Theses, Dissertations, Professional Papers, and Capstones

The objective of the thesis is to study the effects of thermalhydraulics flows on the wall concentration gradient profiles in LBE loop fittings. To that end detailed models of the fittings have been constructed to study these effects. These fittings include sudden expansion, sudden contraction, t-joint and elbow. The typical flow rates chosen for these simulations are typical of design criteria chosen for the loop with Reynolds numbers expected around 200,000 and the usual axial temperature profiles which are being characterized in the DELTA loop at LANL. STAR-CD is the simulation package used to make these predictions, which include detailed …

Stress Corrosion Cracking And Hydrogen Embrittlement Of Martensitic Alloy Ep-823, Mohammad K. Hossain

UNLV Theses, Dissertations, Professional Papers, and Capstones

This investigation is focused on the evaluation of stress corrosion cracking (SCC), localized corrosion, and hydrogen embrittlement (HE) susceptibility of martensitic Alloy EP-823 in neutral and acidic solutions at ambient and elevated temperatures. While no failures were observed in smooth specimens in the neutral solution, failures were noticed in the 90°C acidic solution at constant-load (CL) leading to a threshold stress (O'_th) of 102 ksi. The presence of a notch reduced the O'_th value to 91 ksi in a similar environment. The ductility (%El and %RA), time-to-failure (TTF), and true failure stress (O'_r) were gradually …

Environmental Effects On Corrosion Properties Of Alloy 22, K. S. Raja, L. G. Mcmillion, Shantanu A. Namjoshi, Paige Russel, Raymond E. Keeler, Amy J. Smiecinski

Publications (YM)

During the regulatory life of the Yucca Mountain High Level Nuclear Waste (HLNW) repository the primary engineered barrier that is to prevent release of radioactive material into the environment is proposed to be a Corrosion-Resistant Material (CRM) outer shell covering the Waste Package (WP) container. The current selection for the CRM is Alloy 22 (UNS N06022), a Ni-Cr-Mo-W-Fe alloy. Alloy 22 forms a defective chromic oxide passive film which results in excellent corrosion resistance; the presence of molybdenum in Alloy 22 offers corrosion resistance in reducing environments as well as oxidizing environments.

Phase Stability And Segregation In Alloy 22 Base Metal And Weldments, Jeffrey Lacombe, Shantanu A. Namjoshi, Paige Russel, Raymond E. Keeler, Amy J. Smiecinski

Publications (YM)

The current design of the waste disposal containers relies heavily on encasement in a multi-layered container, featuring a corrosion barrier of Alloy 22, a Ni-Cr-Mo-W based alloy with excellent corrosion resistance over a wide range of conditions. The fundamental concern from the perspective of the Yucca Mountain Project, however, is the inherent uncertainty in the (very) long-term stability of the base metal and welds. Should the properties of the selected materials change over the long service life of the waste packages, it is conceivable that the desired performance characteristics (such as corrosion reistance) will become compromised, leading to premature failure …

Long-Term Mechanical Behavior Of Yucca Mountain Tuffs, And Its Variability, Jaak J.K. Daemen, George Danko, Jaime Gonzalez, Amy J. Smiecinski, Raymond E. Keeler

Publications (YM)

We propose to continue the investigation of the long term strength of Yucca Mountain tuffs, with particular emphasis on tuffs from and near the emplacement horizon. We propose to also continue and expand the investigation of the spatial variability of rock strength and stiffness. An intrinsic component of this planned rock testing is the testing of rock joints. Although the emphasis is on tests aimed at determining long term strength, as part of the testing measurements of stiffness also are collected, and will be collected, reported, and analyzed.

Environment-Induced Degradations In A Target Structural Material For Transmutation Applications, Ramprashad Prabhakaran

UNLV Theses, Dissertations, Professional Papers, and Capstones

This investigation is focused on the evaluation of stress corrosion cracking (SCC) and localized corrosion behavior of Type 422 stainless steel in aqueous environments at ambient and elevated temperature. The results of constant load SCC testing using smooth specimens showed no failure in the neutral solution but a threshold stress of 97 ksi was observed in the 90°C acidic environment. SCC testing by the slow-strain-rate test method indicate that the time-to-failure, true failure stress and ductility parameters were gradually reduced with increasing temperature, showing more pronounced effect in the acidic solution. The application of a controlled cathodic potential showed further …

Embrittlement And Localized Corrosion In Alloy Ht-9, Sudheer Sama

UNLV Theses, Dissertations, Professional Papers, and Capstones

This investigation is focused on the evaluation of stress corrosion cracking (SCC), hydrogen embrittlement (HE) and localized corrosion susceptibility of Alloy HT -9 in neutral and acidic solutions at 30, 60 and 90°C. Constant-load and slow-strain-rate (SSR) testing techniques were used to evaluate the SCC and HE behavior of this alloy by using smooth and notched tensile specimens. Hydrogen effect on the cracking behavior was evaluated by applying cathodic (negative) potential to the test specimens. Localized corrosion susceptibility was evaluated by cyclic potentiodynamic polarization technique. The results of constant load SCC testing showed a threshold stress at 80% of the …

Modeling, Optimization, And Flow Visualization Of Chemical Etching Process In Niobium Cavities, Sathish K. Subramanian

UNLV Theses, Dissertations, Professional Papers, and Capstones

Niobium cavities are important component of the linear accelerators. Researchers have concluded that buffered chemical polishing on the inner surface of the cavity improves its performance. However the mechanism of chemical polishing is not well understood. A finite element computational fluid dynamics (CFD) model was developed to simulate the fluid flow characteristics of chemical etching process inside the cavity. The CFD model is then used to optimize the baffle design. The analysis confirmed the observation of other researchers that the iris section of the cavity received more etching than the equator regions. The baffle, which directs flow towards the walls …