Adsorptive Properties And On-Demand Magnetic Response Of Lignin@Fe3o4 Nanoparticles At Castor Oil–Water Interfaces, Mohammad J. Hasan, Emily Westphal, Peng Chen, Abishek Saini, I-Wei Chu, Sarah J. Watzman, Esteban E. Ureña-Benavides, Erick S. Vasquez
Adsorptive Properties And On-Demand Magnetic Response Of Lignin@Fe3o4 Nanoparticles At Castor Oil–Water Interfaces, Mohammad J. Hasan, Emily Westphal, Peng Chen, Abishek Saini, I-Wei Chu, Sarah J. Watzman, Esteban E. Ureña-Benavides, Erick S. Vasquez
Chemical and Materials Engineering Faculty Publications
Lignin@Fe3O4 nanoparticles adsorb at oil–water interfaces, form Pickering emulsions, induce on-demand magnetic responses to break emulsions, and can sequester oil from water. Lignin@Fe3O4 nanoparticles were prepared using a pH-induced precipitation method and were fully characterized. These were used to prepare Pickering emulsions with castor oil/Sudan red G dye and water at various oil/water volume ratios and nanoparticle concentrations. The stability and demulsification of the emulsions under different magnetic fields generated with permanent magnets (0–540 mT) were investigated using microscopy images and by visual inspection over time. The results showed that the Pickering emulsions were more stable at the castor oil/water …
Preparation, Cure, And Characterization Of Cyanate Ester-Epoxy Blends Containing Reactive Flame Retardants, Mustafa Mukhtar, Donald A. Klosterman
Preparation, Cure, And Characterization Of Cyanate Ester-Epoxy Blends Containing Reactive Flame Retardants, Mustafa Mukhtar, Donald A. Klosterman
Chemical and Materials Engineering Faculty Publications
Cyanate ester resins are sometimes mixed with lower cost epoxy monomers to modify cost, toughness, and processing capabilities. Despite the high performance of these thermosetting polymers, flame retardancy remains an issue. This study examined blends of three different commercial cyanate ester monomers (LVT-100, LECy, and XU-71787.02) and diglycidyl ether of bisphenol A (DGEBA) at 50/50 wt% of each type. The blends were successfully reacted with two reactive flame retardants (FR): 9,10-dihydro-9-ox-9-phosphaphenanthrene-10-oxide (DOPO) and poly(m-phenylene methylphosphonate) (PMP) at phosphorus contents ranging from 0 to 3 wt%. The curing behavior of EP/CE blends was investigated using differential scanning calorimetry (DSC). It was …