Journal of Electrochemistry

Articles 1411 - 1440 of 2026

Full-Text Articles in Engineering

The Synthesis, Characteristics And Performance Of Cnt Composites As Anodic Materials In Litium-Ion Battery, Quan-Feng Dong, Ming-Sen Zheng, Zhen-Cai Huang, Ming-Gang Jin, Ya-Ding Zhan, Zu-Geng Lin May 2005

The Synthesis, Characteristics And Performance Of Cnt Composites As Anodic Materials In Litium-Ion Battery, Quan-Feng Dong, Ming-Sen Zheng, Zhen-Cai Huang, Ming-Gang Jin, Ya-Ding Zhan, Zu-Geng Lin

Journal of Electrochemistry

As an anodic material for lithium ion battery the carbon nano-tube (CNT) and some compounds based on tin have ever been investigated intensively. The fruited progress has not been made yet, however. In this paper the composites of CNT and Sn/SnO2 were synthesized employing two methods and characterized by SEM and XRD. And the electrochemical performance of the composites was investigated.

Go to article

Preparation And Characterization Of Mcm-41/Pvdf-Hfp Composite Microporous Polymer Electrolytes For Li-Ion Batteries, Zuo-Feng Chen, Yan-Xia Jiang, Quan-Chao Zhuang, Quan-Feng Dong, Shi-Gang Sun May 2005

Preparation And Characterization Of Mcm-41/Pvdf-Hfp Composite Microporous Polymer Electrolytes For Li-Ion Batteries, Zuo-Feng Chen, Yan-Xia Jiang, Quan-Chao Zhuang, Quan-Feng Dong, Shi-Gang Sun

Journal of Electrochemistry

MCM-41/vinylidine fluoride-hexafluropropene copolymer (PVdF-HFP) composite microporous polymer electrolytes were prepared with mixed solvent of N, N-Dimethylformamide (DMF) and acetone. The influence of MCM-41 and nano-SiO2 on the porous structure of the microporous polymer electrolytes were studied with SEM. The results show that MCM-41 could take the place of the plasticizer in the process of making pores, and bring the preparation of microporous membranes easily. The preliminary electrochemical tests showed that the ion conductivity of composite microporous polymer electrolyte with 10% MCM-41 was about 10-3 S cm-1, and the performance of batteries was improved. The mesoporous MCM-41selected …

Go to article

Potential Fluctuations Of 7075 Aluminum Alloy Under Thin Electrolyte Layers, Su-Jing Chen, Qing-Ming Yuan, Jian-Ping He, Xiao-Lei Liu May 2005

Potential Fluctuations Of 7075 Aluminum Alloy Under Thin Electrolyte Layers, Su-Jing Chen, Qing-Ming Yuan, Jian-Ping He, Xiao-Lei Liu

Journal of Electrochemistry

Lens tissues adsorbing 3.5% sodium chloride solution were used to simulate thin electrolyte layers. The 7075 aluminum alloy was immersed under the thin electrolyte layers for 0, 4, 6, 8 and 12 h respectively. Then the fluctuations of natural-corrosion potentials of the alloy were monitored. The fluctuations of natural-corrosion potential were observed rather small in the initial corrosion stages after 6h immersion, and the positive peaks of potential appeared. However the amplitudes reached 20mV after 4h and 12h immersion. The RMS of natural-corrosion potentials decreased with corrosion time at first and then increased. It reached a minimum at 4 h. …

Go to article

Application Of Nickel Foam Electrode For Electroreduction Intermediate Of Purine, Hui-Wen Yang, Xi-En Hu, Xue-Jun Wang May 2005

Application Of Nickel Foam Electrode For Electroreduction Intermediate Of Purine, Hui-Wen Yang, Xi-En Hu, Xue-Jun Wang

Journal of Electrochemistry

Nickel foam with weight uniformity, good porosity ,pore size and low resistivity as a three-dimensional cathode was used in a filter-press electrochemical reactor. The H2SO4 as supporting electrolyte, separator of cation ion exchange membrane, and the lead plate as an anode were used. The cyclic system consisted of electroreduction reactor, pump, store tank and ampere meter. NAU was electroreduced in the cathode chamber of the reactor. Purine intermediate was synthesized with DAU, and the results were compared with those of iron powder reduction process. A peak current in the electroreduction process was detected. The current density of …

Go to article

Investigation On Ru-Ti-Ir-Sn Oxide Anode Coatings For Electrolyzing Seawater, Ke Wang, Yan Han, Lei-Yuan Wang, Xiao-Ling Zhang, Yu-Pu Sun May 2005

Investigation On Ru-Ti-Ir-Sn Oxide Anode Coatings For Electrolyzing Seawater, Ke Wang, Yan Han, Lei-Yuan Wang, Xiao-Ling Zhang, Yu-Pu Sun

Journal of Electrochemistry

The anode coatings of Ru-Ti-Ir-Sn oxide with various compositions were prepared by thermal decomposition. The physical and electrochemical properties of the coatings were characterized by scanning electron microscope (SEM), energy dispersive X-ray detector (EDX), accelerated life, current efficiency, anti-Mn2+ contamination, polarization curveandcyclic voltammetry tests. The results showed thatthe anode coating with optimized formula possessed excellent overall properties for electrolyzing seawater.

Go to article

Ni-Mo-P Alloy By Electroless Deposition And Its Properties, Sen-Lin Wang, Xin-Ren Lan, Ting-Ting Huang, Jun-Mo Jin, Ji-Bei Ling, Zhi-Ming Chen May 2005

Ni-Mo-P Alloy By Electroless Deposition And Its Properties, Sen-Lin Wang, Xin-Ren Lan, Ting-Ting Huang, Jun-Mo Jin, Ji-Bei Ling, Zhi-Ming Chen

Journal of Electrochemistry

The electroless Ni-Mo-P alloy has been deposited from the alkaline bath containing boric acid as a buffer agent and sodium citrate as a complexing agent. The effect of deposition parameters, such as pH and concentration of (NH4)6Mo7O24·4H2O on the plating rate, the composition, the structure and the microhardness of the coating was examined. It was found that the presence of molybdenum has an inhibitory effect on the alloys deposition. As a consequence, the percentage of molybdenumin the Ni-Mo-P coatings never reaches high values, which was lower than 20 at%. It …

Go to article

Structure And Corrosion Electrochemical Properties Of Self-Assembled (3-Mercaptopropyl) Trimethoxysilane Films On Copper Electrode, Ling Huang, Ke-Fa Lin, Fang-Zu Yang, Shu-Kai Xu, Shao-Min Zhou May 2005

Structure And Corrosion Electrochemical Properties Of Self-Assembled (3-Mercaptopropyl) Trimethoxysilane Films On Copper Electrode, Ling Huang, Ke-Fa Lin, Fang-Zu Yang, Shu-Kai Xu, Shao-Min Zhou

Journal of Electrochemistry

A self-assembled monolayer of (3-mercaptopropyl) trimethoxysilane(MPTS) was formed on a electrochemical polished copper surface electrode. The corrosion protection abilities of the monolayer were evaluated in 5% NaCl solution using electrochemical linear polarization. The effects of deposition time and silane concentration on corrosion of copper were also discussed. The surface structure of MPTS films was measured by FT-IR and SEM. It was found that the corrosion resistance of copper was reduced markedly owing to the MPTS monolayers formation on copper. The MPTS monolayer retarded the reduction of dissolved oxygen and inhibited the growth of copper oxide in the NaCl solution. FT-IR …

Go to article

Selective Electroless Copper Plating Micro-Pattern On Ceramics Without Sensitisation And Activation, Zhen-Lin Xu, Qi-Long Guo, Yi-Cheng Shen, Xiong-Chao Zhao, Yan-Ping Hong, Zhi-Jun Gu May 2005

Selective Electroless Copper Plating Micro-Pattern On Ceramics Without Sensitisation And Activation, Zhen-Lin Xu, Qi-Long Guo, Yi-Cheng Shen, Xiong-Chao Zhao, Yan-Ping Hong, Zhi-Jun Gu

Journal of Electrochemistry

The purpose of this article is to provide a new technology of electroless copper plating without palladium activation steps. By combining the technology of laser micro-etching with the new copper-plating bath, copper plating on ceramics was obtained. The experimental results showed that the solution used for copper electroless plating was stable and the copper coating obtained was bright, dense with good electrical conductivity.The line definition was about 40 μm. The electroless Cu films deposited from this system were gentle and required simple operating conditions.

Go to article

Study On Synthesis Of M-Phenoxy Benzoic Acid By Electrolysis Oxidation Method, Wei Xu, Chong-Tao Zhao May 2005

Study On Synthesis Of M-Phenoxy Benzoic Acid By Electrolysis Oxidation Method, Wei Xu, Chong-Tao Zhao

Journal of Electrochemistry

The m-phenoxy benzoic acid was synthesized by oxidation m-phenoxy toluene using Cr(Ⅵ)as oxidation media, which was prepared by electrolysis oxidation of Cr(Ⅲ)in the electrochemical bath using Nafion 417 as a diaphragm, Pb-PbO2 as an anode and Pb as cathode. The effect factors on the electrochemical oxidation of Cr(Ⅲ)to Cr(Ⅵ)in this electrolysis were studied. Furthermore, the optimal conditions for electronic synthesis of m-phenoxy benzoic acid were also discussed.

Go to article

Using Electrodeposition To Fabricate Mould For Polymer Microfluidic Chip, Yi Luo, De-Nan Chu, Zhi-Feng Lou, Chong Liu, Li-Ding Wang May 2005

Using Electrodeposition To Fabricate Mould For Polymer Microfluidic Chip, Yi Luo, De-Nan Chu, Zhi-Feng Lou, Chong Liu, Li-Ding Wang

Journal of Electrochemistry

Many researches have been focused on polymer microfluidic chip in recent years and the mould plays an important role in its fabrication process. Using electrodepositingmethod to fabricate a metal mould for polymer microfluidic chip has been presented in this paper. An ultra-thick photoresist SU-8 was coated on a pretreated metal plate, after photolithography, nickel was electrodeposited in the patterned SU-8, then was removed the SU-8 to obtain a final metal mould. This methodreduces workload of electrodeposit largely. Applying counter current before deposit, adding additive to solution and vacuum anneal after demould have been used to improve the binding force between …

Go to article

The Effect Of Oxidant On Structure And Properties Of Pan/Ptfe Conducting Composite Membrane, Chang-Yuan Tao, Jing Chen, Jun Du, Cai-Xin Sun May 2005

The Effect Of Oxidant On Structure And Properties Of Pan/Ptfe Conducting Composite Membrane, Chang-Yuan Tao, Jing Chen, Jun Du, Cai-Xin Sun

Journal of Electrochemistry

The PAn/PTFE conducting composite membrane was prepared by means of in-situ permeating chemical polymerization, with (NH4)2S2O8 and Na3VO4 being used as an oxidant respectively. The polymerization-growth behavior of the aniline by using different oxidant was compared. In addition, the oxidant effect on the structure and properties of conducting composite membrane was discussed. The results of SEM micrographs, pore size distribution and electrochemical methods suggested that using either oxidants could also induce the product with small pore size and dense pore structure. Compared with (NH4)2S2O …

Go to article

Preparation, Characterization And Electrochemical Properties Of Nano Tio2-Cnt-Pt On Ti Substrate Complex Electrode, Dao-Bao Chu, De-Xiang Feng, Jin-Hua Zhang, Xiao-Hua Li May 2005

Preparation, Characterization And Electrochemical Properties Of Nano Tio2-Cnt-Pt On Ti Substrate Complex Electrode, Dao-Bao Chu, De-Xiang Feng, Jin-Hua Zhang, Xiao-Hua Li

Journal of Electrochemistry

The nanoTiO2-CNT-Pt on Ti substrate complex electrodes were prepared from precursor of (Ti(OEt)4) directly hydrolyzed and by cyclic voltammograms electroplating method . The XRD and SEM results showed that the nano TiO2 (anatase) particle sizes ranged 5~10 nm and the Pt nanoparticle (average size 9nm) dispersed uniformly on nanoTiO2-CNT film surface. The electrocatalytic activity of Ti/nanoTiO2-CNT-Pt electrode was investigated by cyclic voltammetry and chronopotentiogram. The results indicated that the Ti/nanoTiO2-CNT-Pt electrode exhibited very high electrocatalytic activity and stability for the electro-oxidation of methanol at room temperature. When Pt loading …

Go to article

Initial Process Of Pyrophosphate Copper Electroplating, Shao-Bin Feng, Shi-Bo Shang, Li-Ting Feng May 2005

Initial Process Of Pyrophosphate Copper Electroplating, Shao-Bin Feng, Shi-Bo Shang, Li-Ting Feng

Journal of Electrochemistry

The relationship between the type of on changes of copper electroplating potential time and the adhesion of coating layer was examined by chronopotentiometry. The conception of critical initial current density DKC was put forward. When the initial working current DKI was higher than the critical initial current, the iron electrodewas polarized to activation potential of iron surface firstly, then to the activation of the substratesurface, and finally to depositionpotentialof copper ion. The coating deposited on the active surface and had goodadhesion. On the contrary ,when DKI was lower than DKC, the coating deposits on the …

Go to article

A Comparison On Structural Sensitive Adsorption Of Sb On Au Single Crystalline Electrodes, Jia-Wei Yang, Wang-Huo Shang, Qiong Wu, Bing-Wei Mao May 2005

A Comparison On Structural Sensitive Adsorption Of Sb On Au Single Crystalline Electrodes, Jia-Wei Yang, Wang-Huo Shang, Qiong Wu, Bing-Wei Mao

Journal of Electrochemistry

We compare the behaviors of irreversible adsorption of Sb(III) and its reduction, underpotential deposition of Sbon Au(111) and Au(100) as well as mutual interactions of the processes. Based on in-situ scanning tunneling microscopic and cyclic voltammetric results, the substrate structure not only influence anion adsorptionbehavior and thus the Sb adsorption structure, but also the stability of its own structure. On Au(111) surface,the irreversibly adsorbed dense and disordered SbO+ film structure remains after reduction of the film; while on Au(100)surface, due to the coadsorption of SO42-, an ordered(2×2)structure is formed after reduction. UPD of Sb on Au(111) …

Go to article

The Preparation And Performance Of The Aqueous Matrix For Molten Carbonate Fuel Cells, Hua-Xin Lin, Mo-Jie Ceng, Bao-Lian Yi May 2005

The Preparation And Performance Of The Aqueous Matrix For Molten Carbonate Fuel Cells, Hua-Xin Lin, Mo-Jie Ceng, Bao-Lian Yi

Journal of Electrochemistry

PVA matrix of MCFC was prepared from the α-LiAlO2 powder, and polyvinylalcohol(PVA), Compared with the conventional PVB matrix, higher porosity, higher thermal weight loss and smaller maximum pore diameter were achieved for PVA matrix. Single cell was assembled with PVA matrix. At reaction gas pressure of 0.9 MPa, under reaction gas utilization of 20%, at 300 and 428.57 mA·cm-2, the cell voltage was 0.849 and 0.739 V respectively, and the output power density was 254.7 and 316.7 mW·cm-2 respectively, which are higher than those of the cell assembled with PVB matrix. During thermal cycles, the cell …

Go to article

Fabrication Of Nano Capacitor And Its Electrical Properties, Ling Liu, Qin Zhou, Neng-Qin Jia, Zhi-Yu Jiang May 2005

Fabrication Of Nano Capacitor And Its Electrical Properties, Ling Liu, Qin Zhou, Neng-Qin Jia, Zhi-Yu Jiang

Journal of Electrochemistry

A step-by-step assembling method was developed for preparing nano capacitors using anodic aluminum oxide (AAO) membrane as templates. The nano capacitor consisted of three parts: electrochemically polymerized PPy electrode/ el ectrochemically precipitated porous TiO2 separator/chemically polymerized PPy electrode, and demonstrated the charge/discharge behavior as a typical electrochemical supercapacitor with good cyclic ability.

Go to article

Studies On Polymer Light-Emitting Electrochemical Cells ——Introduction Of The Studies On The Electrochemistry Of Conducting Polymers In Cas Key Laboratory Of Organic Solids (Ⅱ), Yong-Fang Li Feb 2005

Studies On Polymer Light-Emitting Electrochemical Cells ——Introduction Of The Studies On The Electrochemistry Of Conducting Polymers In Cas Key Laboratory Of Organic Solids (Ⅱ), Yong-Fang Li

Journal of Electrochemistry

Polymer light-emitting electrochemical cell (LEC) is composed of a conjugated polymer(CP)/polymer electrolyte blend film sandwiched between an ITO anode and an Al cathode. When a bias voltage greater than Eg/e (where Eg is the energy gap of the CP, e is the electron charge) is applied on the two electrodes, the CP in the polymer blend film at the anode side will be oxidized (to form a p-doped region), and that at the cathode side will be reduced (to form a n-doped region), then a p-i-n junction will be produced. Light-emission occurs in the intrinsic region between the p- and …

Go to article

Fabrication And Studies Of A Novel Ag/Agcl Reference Electrode In High Temperature Molten Chloride Salts, Pei Gao, Xian-Bo Jin, Di-Hua Wang, Xiao-Hong Hu, Zheng Chen Feb 2005

Fabrication And Studies Of A Novel Ag/Agcl Reference Electrode In High Temperature Molten Chloride Salts, Pei Gao, Xian-Bo Jin, Di-Hua Wang, Xiao-Hong Hu, Zheng Chen

Journal of Electrochemistry

A new method for the easy fabrication of a stable and long life silver/silver chloride reference electrode in molten chloride salts is described in this paper. The method is based on the fact that simply placing the silica glass in molten NaCl or its vapour in the presence of oxygen resulted in satisfactory conductivity for sodium ion and possibly calcium ion in the material.The performance of such made electrode has been investigated in a few typical chloride systems at temperatures ranging from 400 to 900℃. Due to the wholly sealed construction, the reference electrode is stable, temperature-reversible, contamination free to …

Go to article

Corrosion Behavior Of Mg2-XLaXNi And Mg2-XCeXNi Hydrogen Storage Alloy, Hai-Chang Zhang, Hua-Bin Yang, Jun-Hong Wang, Zuo-Xiang Zhou Feb 2005

Corrosion Behavior Of Mg2-XLaXNi And Mg2-XCeXNi Hydrogen Storage Alloy, Hai-Chang Zhang, Hua-Bin Yang, Jun-Hong Wang, Zuo-Xiang Zhou

Journal of Electrochemistry

The corrosion behavior of Mg-base hydrogen storage alloys has been investigated by potentiodynamic polarization and EIS. The results showed that the corrosion current density (icorr) and the electrochemical polarized resistance of Mg2-xCexNi alloys decreased with x increase, while icorr of Mg2-xLaxNi alloys increased and the electrochemical polarized resistance of Mg2-xLaxNi alloys increased first, then decreased with x increase. SEM results showed that the surface of Mg1.85Ce0.15Ni alloy was relatively even while the surface of Mg2-xLaxNi alloy had …

Go to article

Anodic Polarization Behaviors Of Carbon Steel In Bicarbonate Solution, Jing-Mao Zhao, Yu Zuo Feb 2005

Anodic Polarization Behaviors Of Carbon Steel In Bicarbonate Solution, Jing-Mao Zhao, Yu Zuo

Journal of Electrochemistry

The anodic polarization curves of mild steel were measured in sodium bicarbonate solution of various concentrations, and the surface products were analyzed by XPS. Two anodic current peaks and two passive zones are observed in all the curves. When HCO3- ions concentration is below 0.1mol/L, the two peaks are so close that the first passive zone is difficult to be observed. When HCO3- ions concentration is above 0.1 mol/L, the first peak appears clear, while the second becomes smaller. The XPS results indicate that the out layer of film formed at a higher potential is mainly …

Go to article

Preparation And Characterization Of Lini0.85Co0.10(Timg)0.025O2 As Cathode Materials For Lithium-Ion Batteries, Xian-Jun Zhu, Hong-Hao Chen, Hui Zhan, Dai-Ling Yang, Yun-Hong Zhou Feb 2005

Preparation And Characterization Of Lini0.85Co0.10(Timg)0.025O2 As Cathode Materials For Lithium-Ion Batteries, Xian-Jun Zhu, Hong-Hao Chen, Hui Zhan, Dai-Ling Yang, Yun-Hong Zhou

Journal of Electrochemistry

Cathode material of LiNi0.85Co0.10(TiMg)0.025O2 were prepared by solid state reaction at 725℃ for 24 h from LiOH·H2O, Ni2O3, Co2O3, TiO2 and Mg(OH)2 under flowing oxygen, and were characterized by TG-DTA, XRD, SEM and electrochemical tests. Effort to simultaneously doped LiNiO2 with Co-Ti-Mg has been tried to improve the cathode performance. The results show that co-doping definitely has a large beneficial effect in increasing the capacity (182.7mAh/g of the first discharge capacity for  LiNi0.85Co0.10(TiMg)0.025O2 …

Go to article

Electrochemical Performance Of Gel Polymer Electrolyte Prepared By Thermal Initiating Polymerization Of Acrylates, Jin-Dan Piao, Li-Xia Yuan, Xin-Ping Ai, Han-Xi Yang, Yu-Liang Cao Feb 2005

Electrochemical Performance Of Gel Polymer Electrolyte Prepared By Thermal Initiating Polymerization Of Acrylates, Jin-Dan Piao, Li-Xia Yuan, Xin-Ping Ai, Han-Xi Yang, Yu-Liang Cao

Journal of Electrochemistry

A gel polymer electrolyte was prepared by thermal initiating polymerization of the acrylates in the EC/EMC/DMC electrolyte solution at 100℃. The LiCoO2/MCMB polymer cells were assembled and their electrochemical properties were evaluated at various charge-discharge rate and temperatures. The ionic conductivity of the polymer electrolyte containing 85wt.% liquid electrolyte is around 3.2×10-3 S·cm-1  at 20℃ and 5.6×10-4 S·cm-1 at -30℃ respectively. The gel polymer electrolyte has good electrochemical stability up to 4.5V versus Li/Li+.The first charge-discharge efficiency of the polymer cell at 0.2C rate is almost 92.1%. The discharge capacity of the …

Go to article

The Electrophoretic Deposition Of Nano Hydroxyapatite Coating On Titanium Surface, Fei Chen, Chang-Jian Lin, Zhou-Cheng Wang Feb 2005

The Electrophoretic Deposition Of Nano Hydroxyapatite Coating On Titanium Surface, Fei Chen, Chang-Jian Lin, Zhou-Cheng Wang

Journal of Electrochemistry

A hydroxyapatite coating with nano-structure on the roughened titanium surface was prepared by electrophoretic deposition process. To decrease sintering temperature the HAp nanoparticles synthesizedby a wet chemical method was used. It is observed that the coating is uniform without cracks. After sintering the nano-strueture of HAp coating remains unchanged. The surface treatment of Ti is applied to form a distribution of small pits and TiO2 thin layer that improve the adhesion of coatingto Ti substrate. It is shown that the bonding strength of coating is as high as 18±2.5MPa. The hardness and Young's modulus are 40.6 and 0.42 GPa, …

Go to article

Preparation And Electrochemical Property Of Aao Nano-Channels Filled With Nio, Chi Gu, Jun-Mei Yan, Yong Yang Feb 2005

Preparation And Electrochemical Property Of Aao Nano-Channels Filled With Nio, Chi Gu, Jun-Mei Yan, Yong Yang

Journal of Electrochemistry

The AAO template with nano-channels was synthesized and filled with transient metal-oxide NiO by sol-gel method, and their electrochemical properties were primarily studied. The results showed that the porous nano-channels were well defined with the diameter about 50nm. The nano-structured NiO was filled into the template's nano-channels successfully. Cyclic voltammetry studies show that the NiO in AAO template has good cycle stability. It was suggested that the AAO-metal-oxides composites could be used as novel anode materials for Lithium ion battery.

Go to article

Research On Phenol Wastewater Treatment By Electrochemical Oxidation, Tian-Cheng Li, Shen-Lin Zhu Feb 2005

Research On Phenol Wastewater Treatment By Electrochemical Oxidation, Tian-Cheng Li, Shen-Lin Zhu

Journal of Electrochemistry

Electrochemical oxidation is an effective technology for the phenol wastewater treatment, and the anode properties are important to the electrochemical oxidationefficiency. The over-potentials of oxygen evolution have been measured for thestainless steel, feasible graphite and SnO2/Ti anode respectively. Moreover, the synthetic phenol wastewater was treated by the electrochemical oxidation with the stainless steel or feasible graphite anodes. The experimental results showed that the order of the over-potential is SnO2/Ti > graphite > stainless steel; meanwhile, the COD values of purified water were approaching to or less than 100 mg·L-1, and the phenol concentrations in the purified …

Go to article

Corrosion Resistance For Tio2 Thin Films Coated 316l Stainless Steel In The Nacl Solution, Guang-Xia Shen, Yi-Cong Chen, Chang-Jian Lin Feb 2005

Corrosion Resistance For Tio2 Thin Films Coated 316l Stainless Steel In The Nacl Solution, Guang-Xia Shen, Yi-Cong Chen, Chang-Jian Lin

Journal of Electrochemistry

The nano-TiO2 thin films have been deposited on the 316L stainless steel by sol-gel and the dip-coating methods. Hydrothermal post-treatment leads to crack-free coatings. Meanwhile, the surface structure and properties are optimized. Surface morphology, structure and properties are characterized by XRD, and SEM technologies. The results have shown that the surface of coatings is porous, uniform and orderly, the particle diameters are in the range of 15~18 nm and the pores are about 4~8 nm and TiO2 is anatase. The results of electrochemical measurements show that in the NaCl solution with pH ≥ 2 and concentration below 1mol/L, …

Go to article

Calcium Zincate Prepared By Ball Mill Method, Sheng-Xian Li, Shuan-Bao Tian, Shao-Shan Zhu Feb 2005

Calcium Zincate Prepared By Ball Mill Method, Sheng-Xian Li, Shuan-Bao Tian, Shao-Shan Zhu

Journal of Electrochemistry

Calcium zincate was prepared by ball milling method and the factors that influence its synthesis were investigated. The composition of the compound was Ca(OH)2·2Zn(OH)2·2H2O, which was verified by XRD and TG-DTA methods. The results of powder microelectrode and in simulated batteries showed that the material had excellent cyclic performance.

Go to article

Influence Of Rare Earth Oxide On The Performance Of Secondary Zinc Electrodes, Xian-Ling Meng, Hua-Bin Yang, Jun-Hong Wang, Zuo-Xiang Zhou Feb 2005

Influence Of Rare Earth Oxide On The Performance Of Secondary Zinc Electrodes, Xian-Ling Meng, Hua-Bin Yang, Jun-Hong Wang, Zuo-Xiang Zhou

Journal of Electrochemistry

Influence of La(OH)3 or Ce(OH)3 in secondary zinc electrode was investigated by the cyclic voltammetry, potentiodynamic polarizationand potentiostatic polarization tests and influence of La2O3 or CeO2 in the charge/discharge performance of Zn/Ni battery was studied by galvanostatic charge/discharge experiment. The results showed that the film of rare earth hydroxide prevented the zincate species from transferring toward solution, enhanced hydrogen overpotential and decreased thecorrosion current density (icorr), and therefore inhibited zinc corrosion. The potentiostatic polarization results at100mV overpotential showed that La(OH)3 or Ce(OH)3 oated on the zinc electrode effectively suppressed the …

Go to article

The Fabrication And Electrochemical Studies On Carbon Nanotube Array Electrodes, Quan-Yong Gao, Jing Zhang, Yong Yang Feb 2005

The Fabrication And Electrochemical Studies On Carbon Nanotube Array Electrodes, Quan-Yong Gao, Jing Zhang, Yong Yang

Journal of Electrochemistry

An improved technique for fabrication of carbon nanotube array electrodes has been proposed in this work. Firstly, carbon nanotubes (CNs) array electrodes were prepared by combsination of Chemical Vapor Decomposition (CVD) method and sputtering techniques in anodized aluminum oxide (AAO) membrane. The CNs/AAO was immersed into HF solution to remove the barrier layer. Controlling the immersing time, the CNs array electrodes with different length contacted with electrolyte can be prepared. The morphology of CNs array electrodes was observed by SEM. The electrochemical properties of CNs array electrodes were investigated by cyclic voltammetry and electrochemical impedance spectroscopy. Cyclic voltammetric curves of …

Go to article

A Study Of Metal Borides As High Capacity Anode Materials For Aqueous Primary Batteries, Ya-Dong Wang, Xin-Ping Ai, Han-Xi Yang Feb 2005

A Study Of Metal Borides As High Capacity Anode Materials For Aqueous Primary Batteries, Ya-Dong Wang, Xin-Ping Ai, Han-Xi Yang

Journal of Electrochemistry

The transition metal borides VB2 and TiB2 were tested as high capacity anode materials and their electrochemical behaviors were studied by cyclic voltammetry and discharge measurements. The experimental results indicated that transition metal borides VB2 and TiB2 electrodes can deliver exceptionally high discharge capacity of over 3100 mAh/g and 1 600 mAh/g respectively, corresponding to 11- and 6-electron oxidation reaction, although their parent elements V, Ti and boron, are almost completely electrochemically inert. The different electrochemical activitis were probably due to the electrochemical activation of boron, which clamp the potential to passivation for Ti and activity …

Go to article