Articles 1 - 3 of 3
Full-Text Articles in Physics
Temperature Dependence Of Step Density On Vicinal Pb(111), Z. H. Zhang, H. E. Elsayed-Ali
Temperature Dependence Of Step Density On Vicinal Pb(111), Z. H. Zhang, H. E. Elsayed-Ali
Electrical & Computer Engineering Faculty Publications
The temperature dependence of step density on the vicinal Pb(111) surface is investigated using reflection high-energy electron diffraction. When the temperature is increased from 323 to 590 K. the average terrace width and the average string length at the step edge decrease from 85±25 to 37±16 Å and from 220±33 to 25±8 Å, respectively. Thermal step collapse on the Pb(111) surface near its bulk melting temperature is not observed. Above 530±7 K, the change in the string length at the step edge with temperature becomes small, and the intensity of the (00) beam is significantly decreased. We conclude that partial …
Surface Morphology Of Laser-Superheated Pb(111) And Pb(100), Z. H. Zhang, Bo Lin, X. L. Zeng, H. E. Elsayed-Ali
Surface Morphology Of Laser-Superheated Pb(111) And Pb(100), Z. H. Zhang, Bo Lin, X. L. Zeng, H. E. Elsayed-Ali
Electrical & Computer Engineering Faculty Publications
The surface step density on the vicinal Pb(111) and the surface vacancy density on Pb(100) after laser superheating and melting are investigated using reflection high-energy electron diffraction. With ∼100-ps laser pulses, Pb(111) surface superheating does not significantly change the density of the steps and step-edge roughness. However, after laser surface melting, the average terrace width and the string length at the step edge become as large as those at room temperature. The average terrace width at 573 K changes from 38±15 to 64±19 Å after laser surface melting, while the average string length at the step edge changes from 90±14 …
Femtosecond Photoemission Study Of Ultrafast Electron Dynamics In Single-Crystal Au(111) Films, J. Cao, Y. Gao, H. E. Elsayed-Ali, R. J. D. Miller, D. A. Mantell
Femtosecond Photoemission Study Of Ultrafast Electron Dynamics In Single-Crystal Au(111) Films, J. Cao, Y. Gao, H. E. Elsayed-Ali, R. J. D. Miller, D. A. Mantell
Electrical & Computer Engineering Faculty Publications
The energy-dependent relaxation of photoexcited electrons has been measured by time-resolved two-photon photoemission spectroscopy on single-crystal Au(111) films with thickness ranging from 150 to 3000 Å. It is found that the energy-dependent relaxation does not show any significant thickness dependence, which indicates that electron transport is a much slower dynamical process in the near-surface region than expected from bulk properties. Furthermore, lifetimes of the photoexcited electrons can be fitted well by the Fermi-liquid theory with a scaling factor plus an effective upper lifetime. This observation enables separation of electron-electron scattering, and to a lesser extent electron-phonon scattering, processes from electron-transport …