Prerapation And Supercapacitor Property Of Mesoporous Carbon Nanofibers, Yong-Wen Wang, Ming-Bo Zheng, Jian Cao, Jie-Ming Cao, Guang-Bin Ji, Jie Tao
Prerapation And Supercapacitor Property Of Mesoporous Carbon Nanofibers, Yong-Wen Wang, Ming-Bo Zheng, Jian Cao, Jie-Ming Cao, Guang-Bin Ji, Jie Tao
Journal of Electrochemistry
Two different mesoporous carbon nanofibers with large mesopore or core-shell structure were prepared by using the resol/F127 mixture to fill the AAO template. The morphology and structural parameters of the samples were characterized by SEM,TEM,and N2 adsorption-desorption analysis. The supercapacitive behaviors of the electrodes were tested by cyclic voltammetry and galvanostatic charge-discharge. The results show that the specific capacitances of mesoporous carbon nanofibers increased obviously and the fine supercapacitive performances were achieved at high scan rate or large current density.
Preparation And Characterization Of Sulfur/Mesoprous Carbon Composite Cathodes, Wen-Hua Zhang, Yao Chen, Xin-Ping Ai, Yu-Liang Cao
Preparation And Characterization Of Sulfur/Mesoprous Carbon Composite Cathodes, Wen-Hua Zhang, Yao Chen, Xin-Ping Ai, Yu-Liang Cao
Journal of Electrochemistry
A sulfur/mesoporous carbon composite was prepared by thermally treating a mixture of sublimed sulfur and mesoporous carbon.The microstructure of the mesoporous carbon was characterized by BET analysis and X-ray diffraction(XRD).The electrochemical performance of the S/C composite as cathode materials was evaluated by the galvanostatic method.The results confirmed that the mesoporous carbon could not only greatly enhance the electrochemical activity of sulfur electrode,but also effectively confine the diffusion of dissolved polysulfides in organic electrolyte.As a result,the S/C composites showed high capacity,good cycle performance and excellent rate capability.The specific capacity of the S/C composite was more than 1200 mAh/g for the first …