Research On Electrochemical Performance Of Lithium-Ion Battery Cathode Material Lini_(1/3)Co_(1/3)Mn_(1/3)O_2 In Aqueous Lino_3 Solution, Jun Zheng, Xin Jia, Chong Wang, Ming-Sen Zheng, Quan-Feng Dong
Research On Electrochemical Performance Of Lithium-Ion Battery Cathode Material Lini_(1/3)Co_(1/3)Mn_(1/3)O_2 In Aqueous Lino_3 Solution, Jun Zheng, Xin Jia, Chong Wang, Ming-Sen Zheng, Quan-Feng Dong
Journal of Electrochemistry
The cathode material of LiNi1/3Co1/3Mn1/3O2 synthesized by sol-gel method shows excellent high rate performance,and high output power density during discharge process. A well-ordered layered α-NaFeO2 structure was confirmed by XRD and a primary particle size of about 500 nm was indicated by SEM. Galvanostatic charge-discharge test indicates that LiNi1/3Co1/3Mn1/3O2 in 2 mol·L-1 LiNO3 aqueous solution with pH 12 reached a ca-pacity of 147 mAh/g while charged and discharged at 2C. The capacities were 64、33、16 mAh/g with 80C ( 14. 4 A/g) 、150C( 27 A/g) and 220C ( 39. 6 A/g) charge/discharge rates,while the power densities of the battery were 2574 …
Synthesis Of High-Performance Lini_(1/3)Co_(1/3)Mn_(1/3)O_2 Cathode Materials Via Azeotropic Distillation Method, Sheng-An Xia, Li-Xia Yuan, Ze Yang, Zhao-Hui Wang, Yun-Hui Huang, Shuang Li, Wu-Xing Zhang, Ya-Bin Meng, Wei-Gong Zheng
Synthesis Of High-Performance Lini_(1/3)Co_(1/3)Mn_(1/3)O_2 Cathode Materials Via Azeotropic Distillation Method, Sheng-An Xia, Li-Xia Yuan, Ze Yang, Zhao-Hui Wang, Yun-Hui Huang, Shuang Li, Wu-Xing Zhang, Ya-Bin Meng, Wei-Gong Zheng
Journal of Electrochemistry
Layered LiNi1/3Co1/3Mn1/3O2 is one of the most promising alternative materials for LiCoO2 in lithium ion batteries due to its low cost,large capacity and excellent cyclability.In this paper,LiNi1/3 Co1/3 Mn1/3 O2 was synthesized via azeotropic distillation method with isobutyl alcohol as an azeotropic agent.The structure and surface morphology were characterized by X-ray diffraction(XRD) and scanning electron microscope(SEM),respectively.The as-prepared LiNi1/3Co1/3Mn1/3O2 shows a layered α-NaFeO2 structure;the particles are small and uniformly distributed.As compared with the sample prepared by traditional method,the present cathode material exhibits superior cyclability and rate capability,which can be ascribed to the enhanced Li + diffusion due to smaller and more …