Preparation And Characterization Of The Silane-Phosphonic Acid Composite Passivation Coating For Electrogalvanized Steel, Yong Guan, Jian-Guo Liu, Chuan-Wei Yan
Preparation And Characterization Of The Silane-Phosphonic Acid Composite Passivation Coating For Electrogalvanized Steel, Yong Guan, Jian-Guo Liu, Chuan-Wei Yan
Journal of Electrochemistry
A new silane-phosphonic acid composite passivation coating process has been developed for the protection of electrogalvanized steel based on N-(β-aminoethyl)-γ-aminopropyltrimethoxysilane(AAPTMS),γ-(2,3-epoxypropoxy)propyltrimethoxy-silane(GPTMS) and 1-hydroxy ethylidene-1,1-diphosphonic acid(HEDP).The results of X-ray photoelectron spectroscopy(XPS),Fourier transform infrared spectroscopy(FTIR),potentiodynamic polarization scan,electrochemical impedance spectroscopy(EIS) and neutral salt spray(NSS) tests indicated that the major structure of the prepared silane-phosphonic acid composite passivation coating consisted mainly of Si—O—Si and Si—O—P bonds.The area of white rust was not more than 5% of the total panal after 120 h NSS test,which could be compared favourably with the chromate colour passivation coating.However,the corrosion reaction on the anode of the silane-phosphonic acid composite passivation …
Study On Preparing Technology And Corrosion Resistance Of Ti/Zr Based Chromium-Free Chemical Conversion Coating On Zinc Electroplating Layer, Yong Guan, Jian-Guo Liu, Chuan-Wei Yan
Study On Preparing Technology And Corrosion Resistance Of Ti/Zr Based Chromium-Free Chemical Conversion Coating On Zinc Electroplating Layer, Yong Guan, Jian-Guo Liu, Chuan-Wei Yan
Journal of Electrochemistry
In this paper,we obtained environmental-friendly chromium-free chemical conversion coating on the non-cyanide alkaline zinc electroplating layer by employing the optimized Ti/Zr based conversion technique.At the same time,the performances of the Ti/Zr based conversion coating were compared with chromate colour passivation coating.The corrosion resistances of the conversion coatings were investigated by using neutral salt spray(NSS) test,potentiodynamic polarization and electrochemical impedance spectroscopy(EIS).The results showed that the white rust appeared after 96 hours when the NSS test was performed on the Ti/Zr based conversion coating,which was close to the corrosion resistance rating of chromate colour passivation coating.Compared with the chromate passivation coating,the Ti/Zr …