The Sol-Gel Synthesis And Electrochemical Performance Of Li_3v_2(Po_4)_3/C Cathode Material For Lithium Ion Battery, Li-Ying Liu, Lian Chen, Hai-Yan Zhang, Yu-Chun Zhai
The Sol-Gel Synthesis And Electrochemical Performance Of Li_3v_2(Po_4)_3/C Cathode Material For Lithium Ion Battery, Li-Ying Liu, Lian Chen, Hai-Yan Zhang, Yu-Chun Zhai
Journal of Electrochemistry
Li3V2(PO4)3/C was synthesized by sol-gel method with citric acid as chelate and C sources.Physical and electrochemical performances of as-prepared materials were characterized through XRD,SEM and galvanostatic charge-discharge tests,etc.The results showed that products produced by calcining at 800 ℃ for 12 h had a single phase crystal structure and relatively small particle sizes with uniform distribution.At 0.1 C,0.5 C and 1 C,the initial specific discharge capacities were 153.0,143.1 and 130.6 mAh·g-1,respectively,and capacity efficiencies were 93.1%,85.4% and 77.3% after 50 cycles,respectively.Charge efficiencies were all above 80% and discharge voltages were higher.
Application Of Sol-Gel Technology In The Of Activation Process Of Chemical Plating Pretreatment, Lin Zhang, Wei Wang, Qian-Zhen Wu
Application Of Sol-Gel Technology In The Of Activation Process Of Chemical Plating Pretreatment, Lin Zhang, Wei Wang, Qian-Zhen Wu
Journal of Electrochemistry
Using KH-550 as precursors,gel thin films were formed on fabric by sol-gel method.By complexed with palladium ions due to the presences of amido and hydroxide in the gel thin films,the aggregation of palladium particles was inhibited.Therefore,Palladium could exhibit better catalytic activity in the process of electroless plating.The surface morphology of fabric was observed by SPM and SEM.Campared with the traditional pretreatment process,no SnCl2 was needed.This method reduced pollution,shortened process flow and reduced the amount of noble metals.