Enhanced Visible Light Photoelectrochemical Performances With Nitrogen Doped Tio_2 Nanowire Arrays, Xiao-Jun Lv, Yue-Ming Li, Hao Zhang, Da Chen, Hensel Jennifer, Z Zhang Jin, Jing-Hong Li

Journal of Electrochemistry

Self-organized anodic anatase TiO2nanowire arrays doped with nitrogen have been successfully fabri-cated and their photoelectrochemical(PEC) properties have been characterized and found to be substantially im-proved compared to undoped nanowires or commercial P25 nanoparticles.Photocurrent measured with monochro-matic incident light showed that the incident photon-to-current efficiency(IPCE,%) values of nanowire arrayelectrodes with or without N-doping were obviously higher than that of commercial P25 nanoparticle electrodes,and nitrogen-doped TiO2nanowire arrays(NTNA) had noticeable absorption in the visible region.The NTNAelectrodes showed the highest photocurrent density and power conversion efficiency under 100 mW/cm2visiblelight illumination.A maximumolphotoconversion efficiency of 0.52% was achieved for the NTNA sample at anapplied potential of …