The Dawn Of New Quantum Dots: Synthesis And Characterization Of Ge1-Xsnx Nanocrystals For Tunable Bandgaps., Richard J. Esteves
The Dawn Of New Quantum Dots: Synthesis And Characterization Of Ge1-Xsnx Nanocrystals For Tunable Bandgaps., Richard J. Esteves
Theses and Dissertations
Ge1-xSnx alloys are among a small class of benign semiconductors with composition tunable bandgaps in the near-infrared spectrum. As the amount of Sn is increased the band energy decreases and a transition from indirect to direct band structure occurs. Hence, they are prime candidates for fabrication of Si-compatible electronic and photonic devices, field effect transistors, and novel charge storage device applications. Success has been achieved with the growth of Ge1-xSnx thin film alloys with Sn compositions up to 34%. However, the synthesis of nanocrystalline alloys has proven difficult due to larger discrepancies (~14%) in …
Laser Vaporization Controlled Condensation And Laser Irradiation In Solution For The Synthesis Of Supported Nanoparticle Catalysts, Vitaly Kisurin Mr.
Laser Vaporization Controlled Condensation And Laser Irradiation In Solution For The Synthesis Of Supported Nanoparticle Catalysts, Vitaly Kisurin Mr.
Theses and Dissertations
Solid catalyst supports of SiOx-RGO (Reduced Graphene Oxide) and UiO-67 (Universitet i Oslo) have been successfully synthesized and were loaded with palladium nanoparticles to test for a series of heterogeneous reactions. The SiOx/RGO catalysts were synthesized through laser ablation of silicon and graphite oxide micron powder and UiO-67 metal-organic framework (MOF) was synthesized through mixing of precursors with DMF/HCl solution and washing the resultant powder from impurities. The SiOx/RGO supports were later impregnated with palladium precursors which were then subject to Microwave Irradiation (MWI). The UiO-67 framework was impregnated with palladium precursors and was irradiated with pulsed Nd:YAG 532 nm …
Systematic Postsynthetic Modification Of Nanoporous Organic Frameworks And Their Performance Evaluation For Selective Co2 Capture, Timur Islamoglu
Systematic Postsynthetic Modification Of Nanoporous Organic Frameworks And Their Performance Evaluation For Selective Co2 Capture, Timur Islamoglu
Theses and Dissertations
Porous organic polymers (POPs) with high physicochemical stability have attracted significant attention from the scientific community as promising platforms for small gas separation adsorbents. Although POPs have amorphous morphology in general, with the help of organic chemistry toolbox, ultrahigh surface area materials can be synthesized. In particular, nitrogen-rich POPs have been studied intensively due to their enhanced framework-CO2 interactions. Postsynthetic modification (PSM) of POPs has been instrumental for incorporating different functional groups into the pores of POPs which would increase the CO2 capture properties. We have shown that functionalizing the surface of POPs with nitro and amine groups …