Nanoscience and Nanotechnology Commons^™

Maximum Screening Fields Of Superconducting Multilayer Structures, Alex Gurevich

Physics Faculty Publications

It is shown that a multilayer comprised of alternating thin superconducting and insulating layers on a thick substrate can fully screen the applied magnetic field exceeding the superheating fields H_sof both the superconducting layers and the substrate, the maximum Meissner field is achieved at an optimum multilayer thickness. For instance, a dirty layer of thickness ~0.1μm at the Nb surface could increase H_s similar or equal to 240 mT of a clean Nb up to H_s similar or equal to 290 mT. Optimized multilayers of Nb₃Sn, NbN, some of the iron pnictides, or alloyed …

Ultrafast Electron Diffraction Study Of The Dynamics Of Antimony Thin Films And Nanoparticles, Mahmoud Abdel-Fattah

Electrical & Computer Engineering Theses & Dissertations

The ultrafast fast phenomena that take place following the application of a 120 fs laser pulse on 20 nm antimony thin films and 40 nm nanoparticles were studied using time-resolved electron diffraction. Samples are prepared by thermal evaporation, at small thickness (< 10 nm) antimony nanoparticles form while at larger thicknesses we get continuous thin films.

The samples are annealed and studied by static heating to determine their Debye temperatures, which were considerably less than the standard value. The thermal expansion under static heating also yielded the expansion coefficient of the sample material. Nanoparticle samples gave a very accurate thermal expansion coefficient (11 × 10^-6 K^-1).

Ultrafast time resolved electron diffraction …