Interface Engineered Diamond Coatings For Dry Machining Applications, Humberto Arturo Gomez Vega

USF Tampa Graduate Theses and Dissertations

Several studies have been propose to improve the adhesion of diamond films on cemented carbide tool materials, however a systematic study in identifying the role of the factors that affect the final diamond adhesion and the resulting machining performance of the tool under real manufacturing conditions is still unexplored. CVD diamond film's extraordinary qualities bring little benefit if the film fails to adhere sufficiently to the substrate. Inadequate adhesion undermines tool performance and longevity, causing unpredictable behavior under load and possibly leading to unexpected failure of the tool in the production line. This dissertation investigates the effects of different surface …

Diamond Based-Materials: Synthesis, Characterization And Applications, Qiang Hu

USF Tampa Graduate Theses and Dissertations

The studies covered in this dissertation concentrate on the various forms of diamond films synthesized by chemical vapor deposition (CVD) method, including microwave CVD and hot filament CVD. According to crystallinity and grain size, a variety of diamond forms primarily including microcrystalline (most commonly referred to as polycrystalline) and nanocrystalline diamond films, diamond-like carbon (DLC) films were successfully synthesized. The as-grown diamond films were optimized by changing deposition pressure, volume of reactant gas hydrogen (H2) and carrier gas argon (Ar) in order to get high-quality diamond films with a smooth surface, low roughness, preferred growth orientation and high sp3 bond …

Polydimethylsiloxane Mechanical Properties Measured By Macroscopic Compression And Nanoindentation Techniques, Zhixin Wang

USF Tampa Graduate Theses and Dissertations

In this thesis, the relationship between the elastic modulus of PDMS and the base/agent ratio (the amount of crosslinking) is studied. Reliable macroscopic compression test instrument was developed. Preload method was applied for the nanoindentation flat punch test to develop full contact.

In chapter 2, an easy instrument setup for macroscopic compression test is described. A series of PDMS samples with different base/agent ratios were tested using the macroscopic compression method. The relationship between PDMS elastic modulus and its base/agent ratio was established.

In chapter 3, PDMS nanoindentation DMA tests provide stable data with different test control models. The storage …