Analysis Of The Use Of Waste Material In 3d Printing, Alexander Laurence
Analysis Of The Use Of Waste Material In 3d Printing, Alexander Laurence
Materials Engineering
Globally, only 9% of plastic by mass is recycled. Allowing consumers to directly convert polyethylene terephthalate (PET) waste into 3D filament can increase the recycling rate by reducing contamination and costs from traditional large-scale recycling methods. This was tested by heating strips of PET to various temperatures within its glass transition region and pressing a roller with a 1.75 mm indentation against it to observe strip deformation. PET was also placed in a hemispherical well with a 1.75 mm diameter hole at the bottom and heated above its melting temperature to determine the mass of PET required to extrude 3D …
Preparation Of A Polylactic Acid With Hydroxyapatite Reinforcement Composite, Odessa N. Quezon
Preparation Of A Polylactic Acid With Hydroxyapatite Reinforcement Composite, Odessa N. Quezon
Materials Engineering
Biodegradable polymers are a prime material choice for temporary biomedical devices due to its ability to degrade into non-toxic products for their use in vivo. However, polylactic acid (PLA) by itself lacks the sufficient strength and stiffness to permit their use as its properties begin to decrease as the polymer degrades. To improve the polymer’s mechanical properties, hydroxyapatite (HA) will be added to the PLA solution to act as reinforcement. The chemical property, glass transition temperature of a polymer, also plays a key role in the mechanical properties of the polymer. PLA’s glass temperature is 130⁰F. A polymer that …