Enhanced Covalent Interface, Crosslinked Network And Gas Barrier Property Of Functionalized Graphene Oxide/Styrene-Butadiene Rubber Composites Triggered By Thiol-Ene Click Reaction, Long Zheng, Stephen Jerrams, Tian Su, Zongchao Xu, Liqun Zhang, Li Liu, Shipeng Wen
Enhanced Covalent Interface, Crosslinked Network And Gas Barrier Property Of Functionalized Graphene Oxide/Styrene-Butadiene Rubber Composites Triggered By Thiol-Ene Click Reaction, Long Zheng, Stephen Jerrams, Tian Su, Zongchao Xu, Liqun Zhang, Li Liu, Shipeng Wen
Articles
The high gas barrier property of a rubber composite is of great significance for reducing the exhaust gas emissions due to tire rolling resistance and hence the contribution this factor makes to environmental protection. Enhanced covalent interfaces and crosslinked networks are crucial to the gas barrier property of rubber composites. In this research, γ-mercaptopropyltriethoxysilane (MPS) modified GO (MGO)/styrene-butadiene rubber (SBR) composites were prepared by a synergetic strategy of latex compounding method and thiol-ene click reaction. It was found that the mercapto groups in MGO reacted with the vinyl groups in SBR molecules through thiol-ene click reaction during the crosslinking process …
The Fabrication And Properties Of Magnetorheological Elastomers Employing Bio-Inspired Dopamine Modified Carbonyl Iron Particles, Yanfen Zhou, Lele Li, Wenyue Li, Shipeng Wen, Liang Jiang, Stephen Jerrams, Jianwei Ma, Shaojuan Chen
The Fabrication And Properties Of Magnetorheological Elastomers Employing Bio-Inspired Dopamine Modified Carbonyl Iron Particles, Yanfen Zhou, Lele Li, Wenyue Li, Shipeng Wen, Liang Jiang, Stephen Jerrams, Jianwei Ma, Shaojuan Chen
Articles
To obtain magnetorheological elastomers (MREs) with improved mechanical properties and exhibiting an enhanced magnetorheological (MR) effect, bio-inspired dopamine modification has been used to improve the functionality at the surface of carbonyl iron (CI) particles. Various techniques including x-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to confirm that a polydopamine (PDA) layer of about 27.5 nm had been successfully deposited on the surface of the carbonyl iron particles prior to their inclusion in the MRE composites. The magnetic properties of PDA modified CI particles were shown to be almost the same as those …